Synthesis of sub-micron $2SnO{\cdot}(H_2O)$ powders by chemical reduction process was performed at room temperature as function of viscosity of methanol solution and molecular weight of PVP (polyvinylpyrrolidone). Tin(II) 2-ethylhexanoate and sodium borohydride were used as the tin precursor and the reducing agent, respectively. Simultaneous calcination and sintering processes were additionally performed by heating the $2SnO{\cdot}(H_2O)$ powders. In the synthesis of the $2SnO{\cdot}(H_2O)$ powders, it was possible to control the powder size using different combinations of the methanol solution viscosity and the PVP molecular weight. The molecular weight of PVP particularly influenced the size of the synthesized $2SnO{\cdot}(H_2O)$ powders. A holding time of 1 hr in air at $500^{\circ}C$ sufficiently transformed the $2SnO{\cdot}(H_2O)$ into $SnO_2$ phase; however, most of the PVP (molecular weight: 1,300,000) surface-capped powders decomposed and was removed after heating for 1 h at $700^{\circ}C$. Hence, heating for 1 h at $500^{\circ}C$ made a porous $SnO_2$ film containing residual PVP, whereas dense $SnO_2$ films with no significant amount of PVP formed after heating for 1 h at $700^{\circ}C$.

• 한국결정성장학회지
• /
• 제27권5호
• /
• pp.235-242
• /
• 2017

기공 제어가 가능한 다공질 인공 지지체를 제조하기 위해 HA 분말에 기공형성제 역할을 하는 PMMA 분말을 첨가하여 TBA를 용매로 한 slurry를 합성한 후 동결주조와 소결을 거쳐 주상형 기공채널이 상호 연결되어 있는 다공질 HA 지지체를 제조하였다. PMMA 분말의 첨가량에 따른 HA 지지체의 결정구조는 XRD로 측정하였고 SEM을 통하여 지지체의 표면 및 내부 단면을 관찰하였는데, 소결과정에서 PMMA의 탈지가 지지체의 내부구조와 HA 분말의 결정성에 영향을 미치는 것으로 결과가 나타났다. 또한 지지체의 물리적 및 기계적 특성을 평가하여 기공형성제의 첨가량을 조절함으로써 기공률 및 기공 크기와 압축 강도의 제어가 가능하였다. 본 연구 결과, HA 지지체가 천연 해면골과 구조 및 특성이 유사하였으며 이를 통해 PMMA 첨가 다공질 HA 지지체가 조직공학용 인공 골지지체로서 자가골을 대체하여 사용이 가능한 것으로 판단된다.

• 한국세라믹학회지
• /
• 제42권3호
• /
• pp.155-164
• /
• 2005

PVA론 이용한 solution-polymerization법에 의해 mullite싸 cordierite 및 mullite-cordierite 복합분말을 합성한 실험 결과를 바탕으펀, 소결조제로서 $TiO_2$를 액상 첨가한 후 mullite-cordierite 합성분말을 제조하고 그때의 소결특성을 조사하였다. 각 조성에 대해 $1300^{\circ}C$에서 하소한 후 planetary mill로 4시간 분쇄를 행하여 합성분말을 준비하였다. 이 합성분말을 사용하여 cordierite의 분해가 일어나지 않는 $1450^{\circ}C$로 소결을 행하였다. 그 결과, mullite $100\%$인 조성에서는 소결시간에 관계없이 원활한 소결이 이루어지지 않았으나, cordierite의 양이 증가함에 따라 상대밀도가 $98\%$ 이상으로 증가하며 소결성이 향상되어졌다 또한 소결시간이 증가함에 따라 mullite와 cordierite의 비율이 50 : 50인 조성의 경우, 16시간 소결하였을 때 복합체치 치밀화로 인해 190MPa의 강도값과 $3.07{\times}10^{-6}/^{\circ}C$의 열팽창계수값을 나타내었다. 하지만 그 이상의 조성에In-1는 cordierite로 인한 액상의 과다생성으로 인해 소결특성은 좋지 않았다. 소결조제로서의 $TiO_2$ 첨가 영향에 대한 조사에서도 $TiO_2$의 함량이 증가함에 따라 mullite의 주상으로의 성장자 cordierite의 액상 증가가 더 빠르게 일어남이 확인되었지만, 이 때문에 $5wt\%$에서는 오히려 특성값이 저하됨이 확인되었다.

• 멤브레인
• /
• 제32권2호
• /
• pp.150-162
• /
• 2022

수처리 및 의약바이오 분야에서 유효물질 분리에 활용되고 있는 알루미나 중공사 분리막은 얇은 두께로 인해 취급 및 적용시 쉽게 파괴되는 단점이 있기 때문에 분리막의 강도를 100 MPa 이상으로 향상시키기 위한 연구가 필요하다. 본 연구에서는 나노입자의 함량을 0, 1, 3, 5 wt%로 증가시켰을 때 제조된 중공사 분리막의 특성을 평가하였다. 그 결과, 나노입자의 함량이 증가함에 따라 중공사 분리막의 강도는 79 MPa에서 115 MPa로 증가하였으며, 밀도는 1.76 g/m³에서 1.88 g/m³으로 증가하였고 기공률과 평균기공크기는 각각 51%에서 48%로, 416 nm에서 352 nm로 감소한 것을 확인하였다. 스폰지구조가 발달하고 스폰지구조의 기공크기가 향상된 알루미나 중공사 분리막은 100 MPa 이상으로 기계적 강도가 향상되었으며, 약 100000 GPU의 높은 질소 투과도 및 약 3000 L/m²h의 높은 물 투과도를 나타내었다. 따라서, γ-알루미나 나노입자를 소결조제로 첨가하는 것은 α-알루미나 중공사 분리막의 기계적 강도를 효과적으로 증진시키고 높은 투과성능을 유지할 수 있는 매우 유효한 방법임을 확인하였다.

• 한국세라믹학회지
• /
• 제53권2호
• /
• pp.215-221
• /
• 2016

In this study, the utilization of the by-products of various industries was examined using raw materials of CSA high-functional cement such as coal bottom ash, red mud, phosphate gypsum, etc. Technology to improve energy efficiency and reduce $CO_2$ was developed as part of the manufacturing process; this technology included lower temperature sintering ($150{\sim}200^{\circ}C$) than is used in the OPC cement manufacturing process, replacement of CSA cement with the main raw material bauxite, and a determination of the optimum mix condition. In order to develop CSA cement, a manufacturing system was established in the Danyang plant of the HANIL Cement Co. Ltd., in Korea. About 4,200 tons of low purity expansion agent CSA cement (about 16%) and about 850 tons of the lime-based expansion agent dead burned lime (about 8%) were produced at a rate of 60 tons per hour at the HANIL Cement rotary kiln. To improve the OPC cement properties, samples of 10%, 13%, and 16% of CSA cement were mixed with the OPC cement and the compressive strength and length variation rate of the green cement were examined. When green cement was mixed with each ratio of CSA cement and OPC cement, the compressive strength was improved by about 30% and the expansibility of the green cement was also improved. When green cement was mixed with 16% of CSA cement, the compressive strength was excellent compared with that of OPC cement. Therefore, this study indicates the possibility of a practical use of low-cost CSA cement employing industrial wastes only.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2010년도 춘계학술발표대회
• /
• pp.19.2-19.2
• /
• 2010

Printed electronics using printing process has broadened in all respects such as electrics (lighting, batteries, solar cells etc) as well as electronics (OLED, LCD, E-paper, transistor etc). Copper is considered to be a promising alternative to silver for printed electronics, due to very high conductivity at a low price. However, Copper is easily oxidized, and its oxide is non-conductive. This is the highest hurdle for making copper inks, since the heat and humidity that occurs during ink making and printing simply accelerates the oxidation process. A variety of chemical treatments including organic capping agents and metallic coating have been used to slow this oxidation. We have established synthetic conditions of copper nanoparticles (CuNPs) which are resistant to oxidation and average diameter of 20 to 50nm. Specific resistivity should be less than $4\;{\mu}{\Omega}{\cdot}cm$ when sintered at lower temperature than $250^{\circ}C$ to be able to apply to conductive patterns of FPCBs using ink-jet printing. Through this study, the parameters to control average diameter of CuNPs were found to be the introduction of additive agent, the feeding rate of reducing agent, and reaction temperature. The CuNPs with various average diameters (58, 40, 26, 20nm) could be synthesized by controlling these parameters. The dispersed solution of CuNPs with an average size of 20 nm was made with nonpolar solvent containing 3 wt% of binder, and then coated onto glass substrate. After sintering the coated substrates at $250^{\circ}C$ for 30 minutes in nitrogen atmosphere, metallic copper film resulted in a specific resistivity of $4.2\;{\mu}{\Omega}{\cdot}cm$.

• 한국분말재료학회지
• /
• 제24권5호
• /
• pp.364-369
• /
• 2017

Ceramic powder, such as MgO, is added as a binder to prepare the green compacts of molten salts of an electrolyte for a thermal battery. Despite the addition of a binder, when the thickness of the electrolyte decreases to improve the battery performance, the problem with the unintentional short circuit between the anode and cathode still remains. To improve the current powder molding method, a new type of electrolyte separator with porous MgO preforms is prepared and characteristics of the thermal battery are evaluated. A Spherical PMMA polymer powder is added as a pore-forming agent in the MgO powder, and an organic binder is used to prepare slurry appropriate for tape casting. A porous MgO preform with $300{\mu}m$ thickness is prepared through a binder burnout and sintering process. The particle size of the starting MgO powder has an effect, not on the porosity of the porous MgO preform, but on the battery characteristics. The porosity of the porous MgO preforms is controlled from 60 to 75% using a pore-forming agent. The batteries prepared using various porosities of preforms show a performance equal to or higher than that of the pellet-shaped battery prepared by the conventional powder molding method.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.477-480
• /
• 2014

An $Al_2O_3$-CuO-ZnO (ACZ) precursor powder was synthesized by a facial sol-gel process using a nonionic surfactant span 80 as the chelating agent to improve the surface area and morphology. When creating a hydrogen membrane, several kinds of properties are required, such as easy dissociation of hydrogen molecules, fast hydrogen diffusion, high hydrogen solubility, and resistance to hydrogen embrittlement. ACZ-Ni composite membranes (cermet) were prepared with this precursor and pure Ni powder via the hot press sintering (HPS) method. The ACZ powder was characterized by XRD, BET, and FE-SEM. Hydrogen permeation experiments were performed by Sievert's type of hydrogen permeation membrane equipment. The hydrogen permeability of ACZ/Ni 10 wt% and ACZ/Ni 20 wt% was obtained as 7.2 and $10molm^{-2}s^{-1}$ at RT, respectively. These values of the corresponding membranes were slightly increased with increasing pressures.

• 한국세라믹학회지
• /
• 제26권5호
• /
• pp.637-644
• /
• 1989

Beta-sialon powder(Z=1) was synthesized by the simultaeous reduction and nitridation of the mixed powders of Hadong kaolin and silica. Silicon hydroxide was prepared from Si-alkoxide by a hydrolysis method and amorphous silica was obtained from the calcination of the prepared silicon hydroxide. Hadong kaolin was mixed with both the silicon hydroxide and amorphous silica, respectively. The average particle size was 4${\mu}{\textrm}{m}$ and the morphology of particle was rod-like and equiaxed in the case of beta-sialon powder prepared form Hadong kaolin and silicon hydroxide(COMPOSITION A), whereas the average particle size was 3${\mu}{\textrm}{m}$ and the morphology of particle was equiaxed in the case of beta-sialon powder prepared from Hadong kaolin and amorphous silica(COMPOSITION B). The synthesized beta-sialon powders were hot-pressed at 175$0^{\circ}C$ for 2 hours under 30 MPa in a nitrogen atmosphere after YAG composition(8wt%) was added to these powders as a sintering agent. The hot-pressed specimens were annealed a 140$0^{\circ}C$ for 4 hours in a nitrogen atmosphere. The mechanical properties of sintered bodies were investigated in terms of M.O.R., fracture toughness and hardness. The measured values are as follows. COMPOSITION A : M.O.R. 508MPa, KIC 3.5MN/m3/2, hardness 13.6GPa. COMPOSITION B : M.O.R. 653MPa, KIC 5.4MN/m3/2, hardness 13.5GPa.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.381-381
• /
• 2011

In this study, a TiO2 colloidal sol was synthesized by sol-gel process, which was used as a "glue" agent to enhance interconnection of TiO2 particles in low temperature process for plastic dye sensitized solar cell. The crystalline phase of this TiO2 glue is pure anatase with average particles size of 5 nm, which was characterized by powder X-ray diffraction and high revolution-TEM. The viscous alcoholic paste without any organic binder was prepared from the mixture of commercial P25 powder and glue. Paste composition and sintering process parameters were optimized for high photovoltaic performance based on low temperature process. The electrochemical impedance spectroscopy and photocurrent-photovoltage transient spectroscopy were also employed to investigate the mechanism of electron transport in this binder free TiO2 film system.