• Journal of the Korean Ceramic Society
• /
• v.18 no.2
• /
• pp.83-90
• /
• 1981

In this study, the effect of additions on magnetic properties in the system of [$Ni_{0.32}Zn_{0.68}$] 1-x Mx $Fe_2O_4$ have been investigated. The additions, Co or Mg or Cu, was added in turn in place of M, and its composition was varied from 0.1 mo1% to 0.5 mo1%. The materials were blended by hot petroleum drying method, and sintered with the rate of 30$0^{\circ}C$/h in the air. The sintering temperatures were varied from 110$0^{\circ}C$ to 130$0^{\circ}C$, with the intervals of 5$0^{\circ}C$, and matured for 3hrs. The results are: 1) The permeability decreased when the addition, MgO or CoO, was added, and it increased when CuO was added. 2) Resistivity had the lowest Value when CuO was added.

• Korean Journal of Materials Research
• /
• v.17 no.10
• /
• pp.526-531
• /
• 2007

The sintering behavior and electrical property of $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics were investigated with the iron oxide concentration ranging from 0 to 5 mol%. Both the sintered density and grain size were found to increase up to 2 mol% $Fe_2O_3$, and then to decrease with further additions. At a higher $Fe_2O_3$ content above 3 mol%, grain size decreased by a pinning effect induced by different shape grains. The electrical conductivity was also increased with increasing $Fe_2O_3$ content up to 2 mol%. Total conductivity of 2 mol% $Fe_2O_3-added$ specimen showed the maximum conductivity of $2{\times}10^{-2}{\Omega}{\cdot}cm^{-1}$ at $500^{\circ}C$. The addition of $Fe_2O_3$ was found to promote the sintering properties and electrical conductivities of $Gd_2O_3-dope\;CeO_2$.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1200-1201
• /
• 2006

Attempts have been made to describe the influence of production process parameters on the microstructure and properties of W-Ag and Mo-Ag composites. The compositions of powder mixtures are W+30% Ag and Mo+30%Ag. Silver additions assists densification during sintering by a liquid phase sintering process. The main goal of this work is to compare properties and microstructure of as-sintered and as-infiltrated composites.

• Proceedings of the KIEE Conference
• /
• 2008.05a
• /
• pp.175-176
• /
• 2008

In this study, the sintering properties and structural properties of the $Mg_5Ta_4O_{15}$cation-deficient perovskite ceramics with $Li_2CO_3$ additions are investigated. The cation-deficient perovskite ceramics are prepared through the solid-state route. According to the XRD pattern, $Mg_4Ta_2O_9$, $MgTa_2O_6$ and $Mg_5Ta_4O_{15}$ phase existed in sintered pure $Mg_5Ta_4O_{15}$ ceramics. With $Li_2CO_3$, additions, the peak intensities of $Mg_4Ta_2O_9$ and $MgTa_2O_6$ phase were reduced. Also, diffraction intensity of the $Mg_5Ta_4O_{15}$ phase was increased with increments of $Li_2CO_3$ additions. The bulk densities were increased with increasing of $Li_2CO_3$ amount and approach the theoretical density of the $Mg_5Ta_4O_{15}$ ceramics, more and more. Microstructure of the $Mg_5Ta_4O_{15}$ ceramics were densified more and more by additions of $Li_2CO_3$. The bulk density of $Mg_5Ta_4O_{15}$+5wt% $Li_2CO_3$ ceramics sintered at $1500^{\circ}C$ for 10 hours was $5.88g/cm^3$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1989.06a
• /
• pp.93-96
• /
• 1989

NTC thermistor was prepared by adding TiO$_2$and MnO$_2$on Fe$_2$O$_3$and the effects of additions were investigated. And the effects of compating pressure, sintering temperature, and sintering time were also experimented. Fe$_2$O$_3$is insulator in stoichiometric state and will be semiconductor by introducing Ti$^{+4}$, Sn$^{+4}$. These semiconducting material will show large negative temperature coeffecients and can be used as NTC thermistor.tor.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2003.04a
• /
• pp.16-17
• /
• 2003

• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.169-176
• /
• 1996

The specimens which were prepared from $\alpha$-Si3N4 with additions of YAG(3Y2O3.5Al2O3)-10 wt% and various AlN contents were sintered in N2 atmosphere at 1$700^{\circ}C$ The effect of $\alpha$,$\beta$-solid solution contents and sintering time on mechanical properties were investigated. As the content of $\beta$-solid solution and sintering time increased the hardness is reduced but the hardness of specimen sintered over 10 hours is constant irrespective of sintering time. While the fracture toughness increased with increasing of $\beta$-solid solution and sintering time. The fracture toughness of specimen with 80% $\beta$-solid solution content increased from 3.89 to 6.66 MPam1/2 with sintering sintering up to 20 hours/ But the amount of increased fracture toughness of specimen with below 20% $\beta$-solid solution content is not significant.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.727-728
• /
• 2006

The present work studies the influence of high-energy milling (HEM) and sintering cycle of Ti and Al powders on the obtainment of TiAl. This study shows that HEM modifies the diffusion processes during the sintering stage. The samples were obtained by cold uniaxial and isostatic pressing, pre-sintered at different temperatures, and heated up to the sintering temperature. This study also shows the effect of powder additions processed by HEM on the sintering behavior of elemental Ti and Al powders.

• Proceedings of the KIEE Conference
• /
• 2008.10a
• /
• pp.169-170
• /
• 2008

In this study, low temperature sintering property of the $0.6TiTe_3O_8-0.4MgTiO_3$ ceramics with sintering adds were investigated for LTCC application which enable to cofiring with Ag electrode. $TiTe_3O_8$ mixed with $MgTiO_3$ to improve the temperature property. In the X-ray diffraction patterns, the columbite structure of $TiTe_3O_8$ phase and ilmenite structure of $MgTiO_3$ phase were coexisted in all specimens. In the case of SnO addition, the bulk density and dielectric constant were increased but quality factor was decreased with amount of SnO additions. The TCRF of the $0.6TiTe_3O_8-0.4MgTiO_3$+xwt%SnO ceramics were shifted to negative direction. The dielectric constant, quality factor and TCRF of the $0.6TiTe_3O_8-0.4MgTiO_3$ ceramics with 2.5wt% addition of SnO sintered at $830^{\circ}C$ for 1hr were 29.86, 35,800 GHz, -0.58 ppm/$^{\circ}C$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.131-134
• /
• 2003

[ $ZnWO_4$ ] shows excellent frequency selectivity due to its high quality factor($Q{\times}f$) at microwave frequencies. However, in order to use $ZnWO_4$ as multilayered wireless communication components, its other properties such as sintering temperature($1050^{\circ}C$), ${\tau}_f$ ($-70ppm/^{\circ}C$) and ${\varepsilon}_r(15.5)$ should be modified. In present study, $TiO_2$ and LiF were used to improve the microwave dielectric and sintering properties of $ZnWO_4$. $TiO_2$ additions to $ZnWO_4$ changed ${\tau}_f$ from negative to positive value, and also increased ${\varepsilon}_r$ due to its high ${\tau}_f$ ($+400ppm/^{\circ}C$) and ${\varepsilon}_r$(100). At 20 mol% $TiO_2$ addition, ${\tau}_f$ was controlled to near zero $ppm/^{\circ}C$ with ${\varepsilon}_r=19.4$ and $Q{\times}f=50000GHz$. However, the sintering temperature was still high to $1100^{\circ}C$. LiF addition to the $ZnWO_4+TiO_2$ mixture was greatly reduced the sintering temperature from $1100^{\circ}C$ to $850^{\circ}C$ due to liquid phase formation. Also LiF addition decreased the ${\tau}_f$ value due to its high negative ${\tau}_f$ value. Therefore, by controlling the $TiO_2$ and LiF amount, temperature stable LTCC material in the $ZnWO_4$-TiO_2-LiF$ system could be fabricated.