• Computers and Concrete
• /
• v.4 no.3
• /
• pp.221-241
• /
• 2007

Based on the experiment results, the damage and fracture behavior of concrete at the ages of 1d, 2d, 7d and 28d, in three-point bending and uniaxial tensile tests, were simulated with a finite element program, ABAQUS. The critical stress intensity factor $K_{IC}^s$ and the critical crack tip opening displacement ($CTOD_C$) of concrete were calculated with effective-elastic crack approach for the three-point bending test of grade C30 concrete. Based on the crack band model, a bilinear strain-softening curve was derived to simulate the LOAD-CMOD curves and LOAD-Displacement curves. In numerical analysis of the uniaxial tension test of concrete of grade C40, the damage and fracture mechanics were combined. The smeared cracking model coupling with damaged variable was adopted to evaluate the onset and development of microcracking of uniaxial tensile specimen. The uniaxial tension test was simulated by invoking the damage plastic model which took both damage and plasticity as inner variables with user subroutines. All the numerical simulated results show good agreement with the experimental results.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.154-159
• /
• 1998

In order to assess the susceptibility of the environmentally assisted cracking(EAC) on SA508 Cl.3 steel in primary water condition, potential step test and slow strain rate test(SSRT) were conducted in a simulated crack tip condition. In this test, anodic dissolution was dominant in the crack tip environments. Proposed simple dissolution model is a modification of Hishida's anodic dissolution model at the plastic zone. One can predict actual crack growth rate with the smooth specimen through this model.

• Geomechanics and Engineering
• /
• v.8 no.1
• /
• pp.33-52
• /
• 2015

Based on the Mohr-Coulomb failure criterion, a gradient-dependent plastic model that considers the strain-softening behavior is presented in this study. Both triaxial shear tests on conventional specimen and precut-specimen, which were obtained from an ancient landslide, are performed to plot the post-peak stress-strain entire-process curves. According to the test results of the soil strength, which reduces from peak to residual strength, the Mohr-Coulomb criterion that considers strain-softening under gradient plastic theory is deduced, where strength reduction depends on the hardening parameter and the Laplacian thereof. The validity of the model is evaluated by the simulation of the results of triaxial shear test, and the computed and measured curves are consistent and independent of the adopted mesh. Finally, a progressive failure of the ancient landslide, which was triggered by slide of the toe, is simulated using this model, and the effects of the strain-softening process on the landslide stability are discussed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.1
• /
• pp.25-31
• /
• 2011

In the tensile test necking occurs at the maximum load point and non-uniform stress state is generated in this section. The equivalent stress becomes quite different from the axial stress as necking proceeds. Methods for obtaining the true stress-true strain curves, by overcoming difficulties due to the necking phenomena, have been developed by many authors. One of the methods based on the finite element analysis simulation is a very promising method. In this paper, general-purpose finite element program is used to simulate the tensile test. A round specimen and a flat specimen prepared from the same steel block are tested and simulated. The true stress-true strain curves are determined without assuming that the material follows Hollomon's law.

• Journal of the Korean Ceramic Society
• /
• v.27 no.6
• /
• pp.721-728
• /
• 1990

Hydroxyapatite powders were synthesized with Ca/P=1.67 and pH=11 by precipitaton method, after characterization of these specimen, behavior in Ringer's solution and biocompatibility of hydroxyapatite, such as cytotoxity test and implantation test, were investigated. The hydroxyapatite ceramics had structural stability in Ringer's solution, and hydroxyapatite ceramics did not prevent cell growing and exhibit any cytotoxic effects. In implantation of hydroxyapatite ceramics into muscle under abdome of guinea pig, hydroxyapatite ceramics did not show any symptom of rejection for cellular texture.

• Composites Research
• /
• v.22 no.2
• /
• pp.24-29
• /
• 2009

This study aims to investigate the residual strength of sandwich composites with Al honeycomb core and carbon fiber face sheets after the quasi-static indentation damage by the experimental investigation. The 3-point bending test and the edge-wise compressive strength test were used to find the mechanical properties, and the quasi-static point load was applied to introduce the simulated damage on the specimen. The damaged specimens were finally assessed by the 3-point bending test and the compressive strength test. The investigation results revealed the residual strength of the damaged specimens due to the quasi-static indentation. The both test results showed that the residual strength of the damaged specimen was decreased according to increases of the damaged depth.

• Composites Research
• /
• v.27 no.2
• /
• pp.77-81
• /
• 2014

In this study, it was performed damage assessment and repair of small scale aircraft adopted on composite. This aircraft adopted the sandwich structure to skin of wing. This study aims to investigate the residual strength of sandwich composites with nomex honeycomb core and carbon fiber face sheets after the open hole damage by the experimental investigation. The 4-point bending tests were used to find the bending strength, and the open hole was applied to introduce the simulated damage on the specimen. The bending strength test results after open hole were compared with the results of no damaged specimen test. In addition, The damaged composite structure was repaired using external patch repair method after removing damaged area. After that, this study presents comparison results of the experimental investigation between the damaged and the repaired specimen. It was found that the bending strength of repaired specimen was recovered up to 95% of undamaged specimen.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2010.10a
• /
• pp.491-496
• /
• 2010

The direct design modification of problematic component is disallowed in order to sacrifice other major factors such as a stability or a major performance. So, the best design policy is to risvise the immature structural medchanism under the minimal design change as soon as possible. For this paper presents a new design sensitivity analysis based on transmissibility rtio (TR) of response acceleration to find a proper candidate for the minimal design modification. The new sensitivity analysis is based on the fact that the sensitivity of TR over a small design change is inversly proportinal to the magnitude of TR. The theory of proposed design sensitivity analysis is simulated with the variance of TR over a dynamic change. Then, new methodology is appplied for a linear elastic specimen to detect the most sensitive node over a design change using measured accleration data during uni-axial vibration test, The physical verification of the sensitivity method is conducted on the CAE model of a linear elastic specimen by adding concentration mass and the vibration fatigue of the simple specimen is analyzed to estimate the relationship between fatigue behaviors and sensitivity consequences.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.38-42
• /
• 2002

HAZ(Heat Affected Zone of weldm ents) properties were investigated for a high nitrogen austenitic stainless steel with a chemical composition of Fe-0.02C-0.15Si-6.00Mn-10.0Ni-23.0Cr-2.00Mo-0.48N-0.14V. Thermal cycle of HAZ was simulated by the thermal cycle simulator (Gleeble 1500). The heat treatment was applied to the Charpy test size sample without notch under various peak temperatures and/or the holding times condition. V-notch Charpy test was performed at the temperature range of 273~77 K. Metallographic examination also was carried out by using optical microscopy, scanning electron microscopy and transmission electron microscopy. The simulated specimens revealed a slight embrittlement compared with the base materials. The impact toughness of the specimens deteriorated with the decreasing test temperature. The results from Charpy V-notch test, however, showed that significant degradation of absorbed energy caused by brittle fracture was not observed for the specimen tested in the test temperature range.

• Journal of Ocean Engineering and Technology
• /
• v.29 no.2
• /
• pp.199-206
• /
• 2015

Regular high-strength carbon steel is currently the most commonly used pipe material for onshore and offshore pipelines. The corrosion of offshore pipelines is a major problem as they age. The collapse of these structures as a result of corrosion may have a heavy cost is lives and assets. Therefore, their monitoring and screening is a high priority for maintenance, which may ensure the integrity and safety of a structure. Monitoring risers and subsea pipelines effectively can be accomplished using eddy current inspection to detect the average remaining wall thickness of corroded low-alloy carbon steel pipelines through corrosion scaling, paint, coating, and concrete. A test specimen for simulating the offshore pipeline is prepared as a standard specimen for an analysis and experiment with differential bobbin eddy current sensors. Using encircling coils, the signals for the defect in the simulated specimen are analyzed and evaluated in experiments. Differential bobbin eddy current sensors can diagnose the defects in a specimen, and experiments have been carried out using the developed bobbin eddy current sensor. As a result, the most optimum coil parameters were selected for designing differential bobbin eddy current sensors.