• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.8
• /
• pp.505-509
• /
• 2016

We have investigated the characteristics of amorphous silicon (a-Si) thin-film solar cell by inserting barrier layer. The conversion efficiency of a-Si thin-film solar cells on graphite substrate shows nearly zero because of the surface roughness of the graphite substrate. To enhance the performance of solar cells, the surface morphology of the back side were modified by changing the barrier layer on graphite. The surface roughness of graphite substrate with the barrier layer grown by plasma enhanced chemical vapor deposition (PECVD) reduced from ~2 um to ~75 nm. In this study, the combination of the barrier layer on graphite substrate is important to increase solar cell efficiency. We achieved ~ 7.8% cell efficiency for an a-Si thin-film solar cell on graphite substrate with SiNx/SiOx stack barrier layer.

• Journal of the Korean Ceramic Society
• /
• v.52 no.3
• /
• pp.209-214
• /
• 2015

Silicon nitride films were deposited at $100^{\circ}C$ by using the catalytic chemical vapor deposition technique. The source gas mixing ratio, $R_N=[NH_3]/[SiH_4]$, was varied from 10 to 30, and the hydrogen dilution ratio, $R_H=[H_2]/[SiH_4]$, was varied from 20 to 100. The breakdown field strength reached a maximum value at $R_N=20$ and $R_H=20$, whereas the resistivity decreased in the same sample. The relative permittivity had a positive correlation with the breakdown field strength. The capacitance-voltage threshold curve showed an asymmetric hysteresis loop, which became more squared as $R_H$ increased. The width of the hysteresis window showed a negative correlation with the slope of the transition region, implying that the combined effect of $R_N$ and $R_H$ overides the interface defects while creating charge storage sites in the bulk region.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1996.06a
• /
• pp.31-31
• /
• 1996

• Proceedings of the Korean Vacuum Society Conference
• /
• 2006.02a
• /
• pp.175-175
• /
• 2006

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.113.2-113
• /
• 2000

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.59-59
• /
• 2000

• Proceedings of the Korean Vacuum Society Conference
• /
• 2007.08a
• /
• pp.252-252
• /
• 2007

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.6
• /
• pp.242-245
• /
• 2014

In order to increase the thickness uniformity in chemical vapor depositon of silicon carbide, we have carried out CFD studies for a CVD apparatus having a horizontally-rotated 3-stage susceptor. We deposited silicon carbide films of 3C-SiC phase showing quite uniform thickness between stages but not uniform one in the stage. The cause of this nonuniformity is thought to be originated from the high rotational speed. And the uniformity between stages can be further increased with the $120^{\circ}$ split type nozzles from CFD results. Through the formation of silicon carbide film on graphite substrates we can make oxidation-resistant and dust-free graphite components with high hardness for the semiconductor applications.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.12
• /
• pp.565-569
• /
• 2006

Plasma enhanced chemical vapor deposition(PECVD) is a well established technique for the deposition of hydrogenated film of silicon nitride (SiNx:H), which is commonly used as an antireflection coating as well as passivating layer in crystalline silicon solar cell. PECVD-SiNx:H films were investigated by varying the deposition and annealing conditions to optimize for the application in silicon solar cells. By varying the gas ratio (ammonia to silane), the silicon nitride films of refractive indices 1.85 - 2.45 were obtained. The film deposited at $450^{\circ}C$ showed the best carrier lifetime through the film deposition rate was not encouraging. The film deposited with the gas ratio of 0.57 showed the best carrier lifetime after annealing at a temperature of $800^{\circ}C$. The single crystalline silicon solar cells fabricated in conventional industrial production line applying the optimized film deposition and annealing conditions on large area substrate of size $125mm{\times}125mm$ (pseudo square) was found to have the conversion efficiencies as high as 17.05 %. Low cost and high efficiency silicon solar cells fabrication sequence has also been explained in this paper.

• Mass Spectrometry Letters
• /
• v.12 no.2
• /
• pp.47-52
• /
• 2021

Evaluating the impurity concentrations in semiconductor thin films using time of flight secondary ion mass spectrometry (ToF-SIMS) is an effective technique. The mass interference between isotopes and matrix element in data interpretation makes the process complex. In this study, we have investigated the doping concentration of phosphorus in, phosphorus doped silicon thin film on glass using ToF-SIMS in the dynamic mode of operation. To overcome the mass interference between phosphorus and silicon isotopes, the quantitative analysis of counts to concentration conversion was done following two routes, standard relative sensitivity factor (RSF) and SIMetric software estimation. Phosphorus doped silicon thin film of 180 nm was grown on glass substrate using hot wire chemical vapor deposition technique for possible applications in optoelectronic devices. Using ToF-SIMS, the phosphorus-31 isotopes were detected in the range of 10¹~10⁴ counts. The silicon isotopes matrix element was measured from p-type silicon wafer from a separate measurement to avoid mass interference. For the both procedures, the phosphorus concentration versus depth profiles were plotted which agree with a percent difference of about 3% at 100 nm depth. The concentration of phosphorus in silicon was determined in the range of 10¹⁹~10²¹ atoms/cm³. The technique will be useful for estimating distributions of various dopants in the silicon thin film grown on glass using ToF-SIMS overcoming the mass interference between isotopes.