• Journal of Conservation Science
• /
• v.23
• /
• pp.1-10
• /
• 2008

Consolidants based on tetraethoxysilane (TEOS) such as alkoxysilanes have been widely used for the consolidation of decaying stone heritages. Low-viscosity alkoxysilanes penetrate inside the decaying stone and polymerize within the porous structure of the decaying stone, significantly increasing the cohesion of the material. However, TEOS-based consolidants suffer from practical drawbacks, such as crack formation of the gel during the drying phase due to the developed capillary force, which is typical for TEOS-based consolidants. We prepared new consolidants TEOS-based consolidants containing flexible (3-glycidoxypropyl)trimethoxysilane (GPTMS) and silica nanoparticles (or polyhedral oligomeric silsesquioxanes (POSS)) in order to reduce capillary force development during gel drying. Since the consolidants should have a good interaction with the component of the stone in order to connect the isolate grains of decaying stone, the adhesion interaction of the developed consolidants on the surface of the granite was macroscopically investigated by the ISO 2409 cross cutting test. The adhesion interaction decreased with the addition of silica nanoparticle and POSS while it increased with the addition of GPTMS in TEOS solution.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1993.10a
• /
• pp.118-123
• /
• 1993

The purpose of this study is to put to practical use the economical high-strength lightweight concrete manufactured by domestic materials, through the analysis on the properties of lightweight concrete with the natural zeolite and mud stone abundant in domestic and compare them with those with silica fume. As a result, it was possible to gain proper workability in the lightweight concrete with admixtures through using the superplasticizer. the optimum replacement rate of zeolite and mud stone powder is respectively 5~10%, 10~15% on unit-cement amount. The strength development rate for plain concrete is 27%, 18% at optimum replacement rate.

• Magazine of the Korea Concrete Institute
• /
• v.6 no.2
• /
• pp.108-117
• /
• 1994

This study was performed to investigate the Alkali-Silica Reaction(ASR) of crushed stones using chemical analysis, polarization microscope, XRD, chemical method(KS F 2545, ASTM C 289), mortar-bar method( KS F 2546, ASTM C 227) and Scanning Electron Microscope (SEM ) and Energy Dispersive X-ray Analysis(EDXA) of reaction products by ASK in the mortar bars and to investigate the influence on alkali content and kind of added alkali to the ASR. Test results show that one kind of domestic crushed stone is estimated as deleterious by ASTM chemical method and mortar bar method, and reaction product is proved as alkali silicate gel by EDXA.

• Resources Recycling
• /
• v.26 no.4
• /
• pp.19-25
• /
• 2017

The ways of producing metal silicon include a carbon reduction method, a plasma reduction method, and a thermite reaction method. The carbon reduction process produces metal silicon by metallurgical refining. The carbon reduction method is produced by adding a raw material mixed with quartz and coke to an electric arc furnace which is for carbon reduction. The cost of high energy costs and environmental protection facilities is an issue when producing metal silicon using electric arc furnaces. For this reason, there is no metal silicon production facility in Korea yet. Therefore, the optimal manufacturing conditions by the carbon reduction method are being studied through the experimental facilities by the companies and research institutes. The present study investigated the change of metal silicon purity according to the purity of silicon when extracting metal silicon using the thermit reaction, which has a relatively lower manufacturing cost than the carbon reduction method.

• Journal of Conservation Science
• /
• v.36 no.5
• /
• pp.339-350
• /
• 2020

This study attempted to apply a hybrid technology that integrated mineral-based fillers and water-repellent agents to control the efflorescence that results from the use of inorganic binders, for the conservation treatment (surface finishing) of cultural heritage materials made up of stone. Herein, different types of mixing ratios of a filler (silica fume 3.4%) and a water repellent (silane-siloxane 1%) were selected for fabricating the inorganic binder, and it was determined that the ratio selected by weight is effective in controlling efflorescence substances. In addition, it was identified that the inorganic binder with the mixing ratio resulted in a higher compressive strength than the standard (20MPa), and the water permeability resistance was high with low water absorption. The result of ion elution from the bilder showed that a smaller number of ions was observed to affect the efflorescence (directly and indirectly) as compared to that of the control group, which was considered to be relatively stable.

• Journal of the Korea Concrete Institute
• /
• v.18 no.5 s.95
• /
• pp.687-693
• /
• 2006

The Stone Powder Sludge(below SPS) is the by-product from the process that translates stone power of 8mm under as crushed fine aggregate. It is the sludge as like cake that has average particle size of $7{\mu}m$, absorbing water content of 20 to 60%, and $SiO_2$ content of 60% over. Because of high water content of SPS, it is not only difficult to handle, transport, and recycle, but also makes worse the economical efficiency due to high energy consuming to drying. This study is aim to recycle SPS as it is without drying. Target product is the lightweight foamed concrete that is made from the slurry mixed with pulverized mineral compounds and foams through hydro-thermal reaction of CaO and $SiO_2$. Although in the commercial lightweight foamed concrete CaO source is the cement and $SiO_2$ source is high purity silica powder with $SiO_2$ of 90%, we tried to use the SPS as $SiO_2$ source. From the experiments with factors such as foam addition rate and replacement proportion of SPS, we find that the lightweight foamed concrete with SPS shows the same trends as the density and strength of lightweight foamed concrete increases according to decrease of foam addition rate. But in the same condition, the lightweight foamed concrete with SPS is superior strength and density to that with high purity silica. This trends is distinguished according to increase of replacement proportion of SPS, also the analysis of XRF shows that the hydro thermal reaction translates SPS to tobermorite. Although SPS has low $SiO_2$ contents, the lightweight foamed concrete with SPS has superior strength and density, because it reacts well with CaO due to extremely fine particles. We conclude that it is possible to replace the high purity silica as SPS in the lightweight foamed concrete experimentally.

• Journal of Conservation Science
• /
• v.27 no.4
• /
• pp.431-440
• /
• 2011

The thermal expansion coefficient of epoxy/inorganic additives composites was controlled by changing the amount of the inorganic additives such as talc and fused silica. The epoxy resin comprises hydrogenated bisphenol A (HBA)-based epoxide, difunctional polyglycidyl epoxide (DPE) as a diluent and isophorone-diamine (IPDA) as a crosslinking agent, which was subsequently mixed with inorganic additives (talc and fused silica). The thermal expansion coefficient was decreased by increasing amount of inorganic additives, nearly to fresh granite. Fused silica was more effective than talc in lowering the thermal expansion coefficient. Additionally, lexural and tensile strengths of the composites were getting lower and higher with the amount of the inorganic fillers, respectively. It was thus concluded that an epoxy composite containing inorganic fillers was developed to show much lower thermal expansion coefficient, similar to fresh granite, than the neat epoxy resin, and also proper mechanical strengths for applications.

• Journal of the Korea Concrete Institute
• /
• v.17 no.1 s.85
• /
• pp.129-137
• /
• 2005

In Korea, due to the insufficiency of natural aggregates and increasing needs of crushed stones, it is necessary to examine the alkali-silica reaction of the crushed stones. The reaction produces an alkali-silica reaction gel which can imbibe pore solution and swell to generate cracks that are visible In affected concrete. In general, crushed stones are tested by petrograptuc examination, chemical method and mortar-bar method, but the most reliable method Is mortar-bar test. This study tested alkali-silica reactivity of crushed stones of various rock types using ASTM C 227 and C 1260, and compared the results of two test methods. This study also analyzed effects of particle size and grading of reactive aggregate on alkali-silica reaction expansion of mortar-bar. The effectiveness of mineral admixtures to reduce detrimental expansion caused by alkali-silica reaction was investigated through the ASTM C 1260 method. The mineral admixtures used were nv ash, silica fume, metakaolin and ground granulated blast furnace slag. The replacement ratios of 0, 5, 10, 15, 25 and $35\%$ were commonly applied for all the mineral admixtures and the replacement ratios of 45 and $55\%$ were additional applied for the admixtures that could maintain workability. The results indicate that replacement ratios of $25\%$ for ay ash, $10\%$ for silica fume, $25\%$ for metakaolin or $35\%$ for ground granulated blast furnace slag were most effective to reduce alkali-silica reaction expansion under the experimental conditions.

• Journal of the Korean Ceramic Society
• /
• v.31 no.6
• /
• pp.609-616
• /
• 1994

Investigation for the high strength grouts using ordinary cement mortar, melamine formaldehyde condensate (MFC) with various admixtures was carried out. The physical properties of the grouts were investigated through the observation of the microstructure and the application of fracture mechanics. When the lime stone and fly ash was added with 6 wt% to the grouts, the compressive strength was about 72 MPa, 69 MPa respectively, and the flexural strength was about 11.9 MPa, 11.4 MPa respectively, the Young's modulus was about 4.3 GPa, 3.9 GPa, and the critical stress intensity was about 7.3 ×10-1MNm-1.5, 6.8×10-1MNm-1.5 respectively. When the silica fume was added with 6 wt% to the grouts, the compressive strength and the flexural strength were 81 MPa, 12.3 MPa, Young's modulus was 4.8 GPa and the critical stress intensity was about 8.4×10-1MNm-1.5.

• Journal of the Korea Concrete Institute
• /
• v.21 no.4
• /
• pp.531-537
• /
• 2009

In this study alkali reactivity of crushed stone was conducted according to the ASTM C 227 that is traditional mortar bar test, and C 1260 that is accelerated mortar bar test method. The morphology and chemical composition of products formed in mortar bar, 3 years after the mortar bar tests had been performed, were examined using scanning electron microscopy (SEM) with secondary electron imaging (SEI) and electron probe microanalysis (EPMA) with backscattered electron imaging (BSEI). The crushed stone used in this study was not identified as being reactive by ASTM C 227. However, mortar bars exceeded the limit for deleterious expansion in accelerated mortar bar test used KOH solution. The result of SEM (SEI) analysis, after the ASTM C 227 mortar bar test, confirmed that there were no reactive products and evidence of reaction between aggregate particles and cement paste. However, mortar bars exposed to alkali solution (KOH) indicated that crystallized products having rosette morphology were observed in the interior wall of pores. EPMA results of mortar bar by ASTM C 227 indicated that white dots were observed on the surface of particles and these products were identified as Al-ASR gels. It can be considered that the mortar bar by ASTM C 227 started to appear sign of alkali-silica reaction in normal condition. EPMA results of the mortar bar by ASTM C 1260 showed the gel accumulated in the pores and diffused in to the cement matrix through cracks, and gel in the pores were found to be richer in calcium compared to gel in cracks within aggregate particles. In this experimental study, damages to mortar bars due to alkali-silica reaction (ASR) were observed. Due to the increasing needs of crushed stones, it is considered that specifications and guidelines to prevent ASR in new concrete should be developed.