• Korean Journal of Materials Research
• /
• v.28 no.12
• /
• pp.709-713
• /
• 2018

To improve the etch rate of $Si_3N_4$ thin film, $H_2SiF_6$ is added to increase etching rate by more than two times. $SiO_3H_2$ is gradually added to obtain a selectivity of 170: 1 at 600 ppm. Moreover, when $SiO_3H_2$ is added, the etching rate of the $SiO_2$ thin film increases in proportion to the radius of the wafer. In $Si_3N_4$ thin film, there is no difference in the etching rate according to the position. However, in the $SiO_2$ thin film, the etching rate increases in proportion to the radius. At the center of the wafer, the re-growth phenomenon is confirmed at a specific concentration or above. The difference in etch rates of $SiO_2$ thin films and the reason for regrowth at these positions are interpreted as the result of the flow rate of the chemical solution replaced with fresh solution.

• Korean Journal of Materials Research
• /
• v.3 no.1
• /
• pp.19-27
• /
• 1993

Abstract The PZT thin film was deposited by usin. RF magnetron sputtering with PZT(52/48) target. The formation of perovskite structure PZT thin film started at 55$0^{\circ}C$ on Si substrate. The AES results showed an oxide layer formed at the between Si and PZT film during the annealing. And, Ti$O_2$ layer appeared at the between TiN and PZT film for the annealing. But, the perovskite phase PZT film was formed after the annealing on the Si$O_2$/Si substarte. The ratio in PZT film was constant across the asdeposited PZT film, but, Pb have diffused into the Si substrate and Si have out-diffused into PZT layer during the post annealing at 75$0^{\circ}C$. The dielectric constants of PZT film indicated about 1300( thickness: 1500$\AA$, at 10KHz) but, the cracks were appeared to surface for annealing.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.100-103
• /
• 2001

In order to investigate the magnetic properties of CoCr-based bilayered thin films on kind of underlayer, we introduced amorphous Si layer to Co-Cr(-Ta) magnetic layer as underlayer. With the thickness of CoCr, CoCrTa single layer, crystalline orientation and perpendicular coercivity was improved. It was revealed that by introducing the Si underlayer, the c-axis orientation of CoCr, CoCrTa magnetic layer was improved largely. However, with increasing Si film thickness, perpendicular coercivity and saturation magnetization of Cocr/si, CoCrTa/Si bilayered thin films was decreased. Grain size of bilayered thin films became larger.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.489-490
• /
• 2005

We studied the nematic liquid crystal (NLC) aligning capabilities using the new alignment material of the SiC (Silicon Carbide) thin film. The SiC thin film exhibits good chemical and thermal stability. The good thermal and chemical stability makes SiC an attractive candidate for electronic applications. A vertical alignment of nematic liquid crystal by ion beam exposure on the SiC thin film surface was achieved. The about $87^{\circ}$ of stable pretilt angle was achieved at the range from $30^{\circ}$ to $45^{\circ}$ of incident angle. The good LC alignment is main-tained by the ion beam alignment method on the SiC thin film surface at high annealing temperatures up to 300.

• Korean Journal of Materials Research
• /
• v.24 no.12
• /
• pp.715-719
• /
• 2014

(PDDA/$SiO_2$) thin films that consisted of positively charged poly (diallyldimethylammonium chloride) (PDDA) and negatively charged $SiO_2$ nanoparticles were fabricated on a glass substrate by an applying voltage layer-by-layer (LBL) self-assembly method. In this study, the microstructure and optical properties of the (PDDA/$SiO_2$) thin films coated on glass substrate were measured as a function of the applied voltage on the Pt electrodes. When 1.0 V was applied to a Pt electrode in a PDDA and $SiO_2$ solution, the thickness of the $(PDDA/SiO_2)_{10}$ thin film increased from 79 nm to 166 nm. The surface roughness also increased from 15.21 nm to 33.25 nm because the adsorption volume of the oppositely charged PDDA and $SiO_2$ solution increased. Especially, when the voltage was applied to the Pt electrode in the $SiO_2$ solution, the thickness increase of the (PDDA/$SiO_2$) thin film was larger than that obtained when using the PDDA solution. The refractive index of the fabricated (PDDA/$SiO_2$) thin film was ca. n = 1.31~1.32. The transmittance of the glass substrate coated by (PDDA/$SiO_2$)6 thin film with a thickness of 106 nm increased from ca. 91.37 to 95.74% in the visible range.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.24 no.3
• /
• pp.453-458
• /
• 1987

Amorphous silicon thin-film transtors (TFT's) have been designed and fabricated on glass substrates. The hydrogenated amorphous silicon (a-Si:H) thin-film has been deposited by decomposing silane(SiH4) in hydorgen ambient by rf glow discharge method. Amorphous silicon nitride(a-Si:H) has been chosen as the gate dielectric material. It has been prepared by decomposing the mixed gas of silane(SiH4) and ammonia(NH3). The electrical properties and performance characteristics of the thin-film transistrs have been measured and compared with the requirements for the switching elements in liquid crystal flat panel display. The results show that liquid crystal flat panel displays can be fabricated using the thin-film transistors described in this paper.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.6
• /
• pp.439-444
• /
• 2012

For the application of photo-detector as active layer, we have studied how to deposit SiGe thin film using an independent Si target and Ge target, respectively. Both targets were synthesized by purity of 99.999%. Plasma generators were generated by radio frequency (rf, 13.56 MHz) and direct current (dc) power. When Ge and Si targets were sputtered by dc and rf power, respectively, we could observe the growth of highly crystalline Ge thin film at the temperature of $400^{\circ}C$ from the result of raman spectroscopy and X-ray diffraction method. However, SiGe thin film did not deposit above method. Inversely, we changed target position like that Ge and Si targets were sputtered by rf and dc power, respectively. Although Ge crystalline growth without Si target sputtering deteriorated considerably, the growth of SiGe thin film was observed with increase of Si dc power. SiGe thin film was evaluated as microcrystalline phase which included (111) and (220) plane by X-ray diffraction method.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.377-378
• /
• 2005

In this study, $SiO_2$ thin film was deposited on variable conditions of the RF power and working pressure by RF magnetron sputtering to apply to the Bragg reflector of the SMR type FBAR device. A crystal orientation and microstructure of $SiO_2$ thin film was studied by using the XRD, AFM and SEM. The best condition was obtained through analyzing the structural characteristics of thin film. Finally, FBAR device was fabricated with applying the best condition of $SiO_2$ thin film and the resonant characteristics was investigated by network analyzer to verify application possibility as a efficient device.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.05a
• /
• pp.501-504
• /
• 2003

In this paper, for enhancement of property on a-Si:H TFTs We measure interface characteristics of ferroelectrics thin film and a-Si:H thin film. First, SrTiO$_3$ thin film is deposited bye-beam evaporation. Deposited films are annealed for 1 hour in N2 ambient at 150$^{\circ}C$ ∼ 600$^{\circ}C$. Dielectric characteristics of deposited SrTiO$_3$ films are very good because dielectric constant shows 50∼100 and breakdown electric field are 1∼1.5MV/cm. a-SiN:H,a-Si:H(n-type a-Si:H) are deposited onto SrTiO$_3$ film to make MFNS(Metal/ferroelectric/a-SiN:H/a-Si:H) by PECVD. After the C-V measurement for interface characteristics, MFNS structure shows no difference with MNS(Metal/a-SiN:H/a-Si:H) structure in C-V characteristics but the insulator capacitance value of MFNS structure is much higher than the MNS because of high dielectric constant of ferroelectrics.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.135.2-135.2
• /
• 2014

Photon conversion technology for thin film solar cells is reviewed. The high-energy photons which are hardly absorbed in solar cells can be transformed the low energy photon by the photon conversion process such as down conversion or down shift, which can improve the solar cell efficiency over the material limit. CdSe-based quantum dot materials commonly used in LED can be used as the photon conversion layer for Si thin film solar cells. The photon conversion structure of CdSe-based quantum dot for Si thin film solar cells will be presented and the pros and cons for the Si thin film solar cells integrated with the photon conversion layers will be discussed.