• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.267-270
• /
• 2003

We have studied the interfacial diffusion phenomena and the role of ${\alpha}-Al_2O_3$ buffer layer as a diffusion barrier in the $Ba-ferrite/SiO_2$ magnetic thin films for high-density recording media. In the interface of amorphous Ba-ferrite ($1900-{\AA}-thick)/SiO_2$ thin film during annealing, the interfacial diffusion started to occur at ${\sim}700^{\circ}C$. As the annealing temperature increased up to $800^{\circ}C$, the interfacial diffusion abruptly proceeded resulting in the high interface roughness and the deterioration of the magnetic properties. In order to control the interfacial diffusion at the high temperature, we introduced ${\alpha}-Al_2O_3$ buffer layer ($110-{\AA}-thick$) in the interface of $Ba-ferrite/SiO_2$ thin film. During the annealing of $Ba-ferrite/{\alpha}-Al_2O_3/SiO_2$ thin film even at ${\sim}800^{\circ}C$, the interface was very smooth. The smooth interface of the film was also clearly shown by the cross-sectional FESEM. The magnetic properties, such as saturation magnetization 3nd intrinsic coercivity, were also enhanced, due to the inhibition of interfacial diffusion by the ${\alpha}-Al_2O_3$ buffer layer. Our study suggests that the ${\alpha}-Al_2O_3$ buffer layer act as a useful interfacial diffusion barrier in the $Ba-ferrite/SiO_2$ thin films.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.88-88
• /
• 2012

High efficiency thin film photovoltaic device technology is reviewed. At present market situation, the industrial players of thin film technologies have to confront the great recession and need to change their market strategies and find technical alternatives again. Most recent technology trends and technical or industrial progress for Silicon thin film and CIGS are introduced and common interests for high efficiency and reliability are discussed.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2000.01a
• /
• pp.67-68
• /
• 2000

Polycrystalline silicon (poly-Si) thin film transistors (TFT's) employing vertical amorphous silicon (a-Si) offsets have been fabricated without additional photolithography processes. The a-Si offset has been formed utilizing the poly-Si grain growth blocking effect by thin native oxide film during the excimer laser recrystallization of a-Si. The ON current degradation of the new device after 4 hour's electrical stress was reduced by 5 times compared with conventional poly-Si TFT's.

• Korean Journal of Optics and Photonics
• /
• v.16 no.5
• /
• pp.476-478
• /
• 2005

We have fabricated a Fabry-Perot etalon around $1.3\;{\mu}m$ wavelength utilizing $Al_{2}O_3$ and a-Si thin films. A full width at half maximum of ${\sim}12.1nm$ and a finesse value of 53 were found from the measured resonant transmission spectra. Single thin film of $Al_{2}O_3$ was analyzed by spectroscopic ellipsometry. A refractive index of a-Si thin film was measured as 3.120 in the real part and 0.002 in the imaginary part, respectively. The thin-film pairs of $Al_{2}O_3$ and a-Si are applicable to output mirrors of vertical-cavity surface-emitting lasers at $1.3{\mu}m$ waveband.

• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.535-542
• /
• 1998

SOI(silicon oninsulator) was fabricated through the direct bonding of a hydrophilized single crystal Si wafer and a thermally oxidized SiO2 thin film to investigate the stacking faults in silicon at the Si/SiO2 in-terface. At first the oxidation kinetics of SiO2 thin film and the stacking fault distribution at the oxidation interface were investigated. The stacking faults could be divided into two groups by their size and the small-er ones were incorporated into the larger ones as the oxidation time and temperature increased. The den-sity of the smaller ones based critically lower eventually. The SOI wafers directly bonded at the room temperature were annealed at 120$0^{\circ}C$ for 1 hour. The stacking faults at the bonding and oxidation interface were examined and there were anomalies in the distributions of the stacking faults of the bonded region to arrange in ordered ring-like fashion.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.6
• /
• pp.509-513
• /
• 2000

The physical and electrical characteristics of MgO and Pt thin-films on it deposited by reactive sputtering and rf magnetron sputtering respectively were analyzed with annealing temperature and time by four point probe SEM and XRD. Under annealing conditions of 100$0^{\circ}C$ and 2 hr, MgO thin-film had the properties of improving Pt adhesion to SiO$_2$and insulation without chemical reaction to Pt thin-film and the sheet resistivity and the resistivity of Pt thin-film deposited on it were 0.1288 Ω/ and 12.88 $\mu$$\Omega$.cm respectively. We made Pt resistance pattern on SiO$_2$/Si substrate by life-off method and fabricated Pt thin-film type microheater for thermal microsensors by Pt-wire Pt-paste and SOG(spin-on-glass). In the temperature range of 25~40$0^{\circ}C$ we estimated TCR(temperature coefficient of resistance) and resistance ratio of thin-film type Pt-RTD(resistance thermometer device). We obtained TCR value of 3927 ppm/$^{\circ}C$ close to the bulk Pt value. Resistance values were varied linearly within the range of the measurement temperature. The thermal characteristics of fabricated thin-films type Pt micorheater were analyzed with Pt-RTD integrated on the same substrate. The heating temperature of Pt microheater could be up to 40$0^{\circ}C$ with 1.5 watts of the heating power.

• Proceedings of the Optical Society of Korea Conference
• /
• 2006.07a
• /
• pp.91-92
• /
• 2006

Liquid crystal (LC) alignment on $a-SiO_x$ thin film was investigated by means of X-ray photoemission spectroscopy and optical transmittance as we varied the deposition temperature and the target-to-substrate distance. LC molecules can be aligned vertically on $a-SiO_x$ film when the stoichiometric parameter x of $a-SiO_x$ is smaller than 1.56, but they can be aligned homogeneously when x is larger than 1.56. We also found that whether liquid crystals can be aligned vertically or homogeneously on $a-SiO_x$ film can be predicted simply by measuring the change in optical transmittance by deposition of $a-SiO_x$ thin film layers.

• Electrical & Electronic Materials
• /
• v.10 no.2
• /
• pp.126-133
• /
• 1997

In order to apply for the gas sensing layer and the piezoelectric thin film devices, we studied the effects of magnetron sputtering conditions and annealing temperature on the electrical and structual characteristics of the ZnO thin film. The optimal deposition conditions, in order to obtain a c axis of the ZnO (002) phase thin film which is perpendicular to SiO$_{2}$/Si substrate, were like these ; substrate temperature 150.deg. C, chamber pressure 2 mtorr, R.F. power 300 watts, gas flow ratio 0.4[O$_{2}$(Ar + $O_{2}$)]. When the ZnO thin film was annealed in 600.deg. C, $O_{2}$ gas ambient for 1 hr, the resistivity was 2.6 x 10$^{2}$.ohm.cm and the grain size of ZnO thin film was less than 1 .mu.m. So the ZnO thin film acquired from above conditions can apply for the gas sensing layer which require a c axis perpendicular to the substrate surface.

• Korean Journal of Crystallography
• /
• v.6 no.2
• /
• pp.134-140
• /
• 1995

SAW properties of SiNx/ZnO bilayer thin film structure were analyzed. ZnO thin films were deposited by rf magnetron sputter using O2 gas as an oxidizer. Structure of ZnO thin films was affected by Ar/O2 ratio. At the gas ratio of Ar/O2=67/33, the standard deviation of X-ray rocking curve of (002) preferred ZnO thin film was 2.17 degree. This value is sufficient to use ZnO thin films as an acoustic element. SAW velocity of glass/SiNx(7000Å)/Al/ZnO(5μm) structure was max. 2.2% faster than that of ZnO/glass.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.278-281
• /
• 1999

PLZT thin films on Pt/Ti/SiO$_2$/Si substrate were fabricated with different Thickness by pulsed laser deposition. 14/50/50 PLZT thin film showed a maximum dielectric constant value of $\varepsilon$$_{t}$=985 at 5000$\AA$, and $\varepsilon$$_{t}$=668 at 2000A. P-EI hysteresis loop of 14/50/50 PLZT thin film was slim ferroelectric. Leakage current density of 14/50/70 PLZT thin film was 10$^{-8}$ A/$\textrm{cm}^2$ at 2000$\AA$.EX>.