• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.6
• /
• pp.454-459
• /
• 2003

We investigate the structure and properties of SiC (Silicon Carbide) nanotubes using molecular dynamics simulation based on the Tersoff bond-order potential. For small diameter tubes, the Si-C bond distance of SiC nanotubes decreases as the nanotube diameter is decreased, due to curvature of the nanotube surface. We find that Young's modulus of SiC nanotubes is somewhat smaller than that of the other nanotubes considered so far. However, Young's modulus for SiC nanotubes is larger than that of ${\beta}$-SiC and almost equal to the experimental value for SiC nanorod and SiC whisker. The strain energy of the SiC nanotubes is also lower than that of the other nanotubes. The lower strain energy of SiC nanotubes raises the possibility of synthesis of SiC nanotubes.

• Korean Journal of Materials Research
• /
• v.14 no.3
• /
• pp.175-180
• /
• 2004

SiC nanotubes were synthesized by CNT-confined reaction. Evaporated SiO gas reacted with carbon nanotubes by VS growth mechanism. By confineded reaction, carbon nanotube was changed to SiC nanotube, and synthesized SiC nanotube was filled partly by the gas reaction in the nanotubes. SiC nanotube's mean diameters were not changed than carbon nanotubes because of means ratio of $CO_2$ and SiO gas was maintained evenly during the process. This result was same of data of simulation. By TEM observastion, SiC nanotube was filled by reaction of inner wall of CNT and SiO gas through the VS reactions. Converted SiC nanotube's compositions were revealed Si and C of 1: 1 ratios at all sites of nanotube by EDS.

• Korean Journal of Materials Research
• /
• v.14 no.2
• /
• pp.83-89
• /
• 2004

SiC nanotubes were synthesized by SLS growth mechanism using various metal catalysts. Synthesized nanotubes had mean diameters of 20~50 nm and several $\mu\textrm{m}$ length. The kind of catalysts affected microstructures of SiC nanotubes by different diffusion routes. These differences are attributed to catalysts' physical properties and relative activities to the graphite substrate. Fe acted as a good catalyst of SLS growth mechanism. But in case of Ni, SiC nanotubes grew slowly. Optical property was measured by photoluminescence measurement. Relatively broad peak was obtained and mean peak positioned at about 430 nm. This result was the same as other nanocrystalline SiC materials, but was different from the results of bulk SiC probably due to quantum confinement effect and defect in the grown SiC nanotube.

• Journal of IKEEE
• /
• v.18 no.4
• /
• pp.620-624
• /
• 2014

In this study, the electrical characteristics of Ni/CNT/$SiO_2$ structures were investigated in order to analyze the mechanism of carbon nanotubes in 4H-SiC MIS device structures. We fabricated 4H-SiC MIS capacitors with or without carbon nanotubes. Carbon nanotubes were dispersed by isopropyl alcohol. The capacitance-voltage (C-V) is characterized at 300 to 500K. The experimental flat-band voltage ($V_{FB}$) shift was positive. Near-interface trapped charge density and oxide trapped charge density values of Ni/CNT/$SiO_2$ structure were less than values of reference samples. With increasing temperature, the flat-band voltage was negative. It has been found that its oxide quality is related to charge carriers or defect states in the interface of 4H-SiC MIS capacitors. Gate characteristics of 4H-SiC MIS capacitors can be controlled by carbon nanotubes between Ni and $SiO_2$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.212-212
• /
• 2000

Since the first obserbvation of carbon nanotubes, extensive researches have been done for the synthesis using arc discharge, laser vaporization, and plasma-enhanced chemical vapor deposition. Carbon nanotubes have unique physical and chemical properties and can allow nanoscale devices. Vertically aligned carbon nanotubes with high quality on a large area is particularly important to enable both fundamental studies and applications, such as flat panel displays and vacuum microelectronics. we have grown vertically aligned carbon nanotubes on a large area of Si substrates by thermal chemical vapor deposition using C2H2 gas at 750-950$^{\circ}C$. we deposited catalytic metal on Si susbstrate using thermal evaporation. The nanotubes reveal highly purified surface. The carbon nanotubes have multi-wall structure with a hollow inside and it reveals bamboo structure agreed with base growth model. Figure 1 shows SEM micrograph showing vertically aligned carbon nanotubes whih were grown at 950$^{\circ}C$ on a large area (20mm${\times}$30mm) of Si substrates. Figure 2 shows TEM analysis was performed on the carbon nanotubes grown at 950$^{\circ}C$ for 10 min. The carbon nanotubes are multi-wall structure with bamboo shape and the lack of fringes inside the nanotube indicates that the core of the structure is hollow. In our experiment, carbon nanotubes grown by the thermal CVD indicate base growth model.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.8
• /
• pp.451-454
• /
• 2000

We have grown vertically aligned carbon nanotubes in a large area of Co-Ni codeposited Si substrates by the thermal CVD usign $C_2H_2$ gas. Since the discovery of carbon nanotubes, growth of carbon nanotubes has been achieved by several methods such as laser vaporization, arc discharge, and pyrolysis. In particular, growth of vertically aligned nanotubes is important to flat panel display applications. Recently, vertically aligned carbon nanotubes have been grown on glass by PECVD. Aligned carbon nanotubes can be also grown on mesoporous silica and Fe patterned porous silicon using CVD. In this paper, we demonstrate that carbon nanotubes can be vertically aligned on catalyzed Si substrate when the domain density of catalytic particles reaches a certain value. We suggest that steric hindrance between nanotubes at an initial stage of the growth forces nanotubes to align vertically and each nonotubes are grown in bundle.

• Journal of the Korean Ceramic Society
• /
• v.41 no.3
• /
• pp.247-252
• /
• 2004

노튜브의 길이는 급격히 증가하였지만 촉매금속의 적층방법에 따른 탄소나노튜브의 성장 형태는 큰 차이가 없었다. 특히, ICBD 방법에 의해 Ni 촉매금속을 증착한 경우 다른 방법에 비하여 직선적인 탄소나노튜브가 관찰되었다. ^x Carbon nanotubes were grown on SiO$_2$/Si substrates by applying $C_2$H$_2$ gas through chemical vapor deposition process. It was found that carbon nanotubes were grown successfully on the substrates with catalytic films under 20 $\AA$ total thickness. The increase in reaction temperature from 50$0^{\circ}C$ to 80$0^{\circ}C$ resulted in longer carbon nanotube, but there was no clear tendencies with different types of catalytic layers. It was evident that carbon nanotubes became more straight on the substrate with Ni catalytic film produced by ICBD method.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.9
• /
• pp.3025-3032
• /
• 2012

Carbon microcapsules containing silicon nanoparticles (Si NPs)-carbon nanotubes (CNTs) nanocomposite (Si-CNT@C) have been fabricated by a two step polymerization method. Silicon nanoparticles-carbon nanotubes (Si-CNT) nanohybrids were prepared with a wet-type beadsmill method. A polymer, which is easily removable by a thermal treatment (intermediate polymer) was polymerized on the outer surfaces of Si-CNT nanocomposites. Subsequently, another polymer, which can be carbonized by thermal heating (carbon precursor polymer) was incorporated onto the surfaces of pre-existing polymer layer. In this way, polymer precursor spheres containing Si-CNT nanohybrids were produced using a two step polymerization. The intermediate polymer must disappear during carbonization resulting in the formation of an internal free space. The carbon precursor polymer should transform to carbon shell to encapsulate remaining Si-CNT nanocomposites. Therefore, hollow carbon microcapsules containing Si-CNT nanocomposites could be obtained (Si-CNT@C). The successful fabrication was confirmed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). These final materials were employed for anode performance improvement in lithium ion battery. The cyclic performances of these Si-CNT@C microcapsules were measured with a lithium battery half cell tests.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.64-64
• /
• 2000

Since its discovery in 1991, the carbon nanotube has attracted much attention all over the world; and several method have been developed to synthesize carbon nanotubes. According to theoretical calculations, carbon nanotubes have many unique properties, such as high mechanical strength, capillary properties, and remarkable electronical conductivity, all of which suggest a wide range of potential applications in the future. Here we report the synthesis in the catalytic decomposition of acetylene at ~65 $0^{\circ}C$ over Ni deposited on SiO2, For the catalyst preparation, Ni was deposited to the thickness of 100-300A using effusion cell. Different approaches using porous materials and HF or NH3 treated samples have been tried for synthesis of carbon nanotubes. It is decisive step for synthesis of carbon nanotubes to form a round Ni particles. We show that the formation of round Ni particles by heat treatment without any pre-treatment such as chemical etching and observe the similar size of Ni particles and carbon nanotubes. Carbon nanotubes were synthesized by chemial vapour deposition ushin C2H2 gas for source material on Ni coated Si substrate. Ni film gaving 20~90nm thickness was changed into Ni particles with 30~90nm diameter. Heat treatment of Ni fim is a crucial role for the growth of carbon nanotube, High-resolution transmission electron microscopy images show that they are multi-walled nanotube. Raman spectrum shows its peak at 1349cm-1(D band) is much weaker than that at 1573cm-1(G band). We believe that carbon nanotubes contains much less defects. Long carbon nanotubes with length more than several $\mu$m and the carbon particles with round shape were obtained by CVD at ~$650^{\circ}C$ on the Ni droplets. SEM micrograph nanotubes was identified by SEM. Finally, we performed TEM anaylsis on the caron nanotubes to determine whether or not these film structures are truly caron nanotubes, as opposed to carbon fiber-like structures.

• Proceedings of the IEEK Conference
• /
• 1999.06a
• /
• pp.275-278
• /
• 1999

We have grown vertically aligned carbon nanotubes in a large area of Co-Ni codeposited Si substrates by the thermal CVD using $C_2$H$_2$gas. Since the discovery of carbon nanotubes, Synthesis of carbon nanotubes for mass production has been achieved by several methods such as laser vaporization, arc discharge, and pyrolysis. In particular, growth of vertically aligned nanotubes is of technological importance for applications to FED. Recently, vertically aligned carbon nanotubes have been grown on glass by PECVD. Aligned carbon nanotubes can be also grown on mesoporous silica and Fe patterned porous silicon using CVD. Despite such breakthroughs in the growth, the growth mechanism of the alignment are still far from being clearly understood. Furthermore, FED has not been clearly demonstrated yet at a practical level. Here, we demonstrate that carbon nanotubes can be vertically aligned on catalyzed Si substrate when the domain density reaches a certain value. We suggest that steric hindrance between nanotubes at an initial stage of the growth forces nanotubes to align vertically and then nanotubes are further grown by the cap growth mechanism.