• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.3
• /
• pp.214-218
• /
• 2020

In this study, Mg_xZn_1-xO thin films, which can be applied not only to active layers of light-emitting devices (LEDs), such as UV-LEDs, but also to solar cells, high mobility field-effect transistors, and power semiconductor devices, are fabricated using the sol-gel method. ZnO and Mg_0.3Zn_0.7O solution synthesized by the sol-gel method and the thin film were grown by spin coating on a Si (100) substrate and sapphire substrate. The solutions are synthesized by dissolving precursor materials in 2-methoxyethanol (2-ME) solvent, and then monoethanolamine (MEA) was added to the mixed solution as a sol stabilizer. Zinc acetate dihydrate is used as a ZnO precursor, while Mg nitrate hexahydrate and Mg acetate tetrahydrate are used as an MgO precursor. Then, the optical and structural characteristics of the fabricated thin films are compared. The molar concentration of the Zn precursor in the solvent is fixed at 0.3 M, and the amount of the Mg precursor is 30% of Mg²⁺/Zn²⁺. The optical characteristics are measured using an UV-vis spectrophotometer, and the transmittance of each wavelength is measured. Structural characteristics are measured using X-ray diffraction (XRD) and transmission electron microscopy (TEM). Composition analyses are performed using energy dispersive X-ray spectroscopy (EDS). The Mg_0.3Zn_0.7O thin film was well formed at the ratio of the Mg precursor added regardless of the type of Mg precursor, and the c-axis of the thin film was decreased, while the band gap was increased to 3.56 eV.

• Journal of the Microelectronics and Packaging Society
• /
• v.30 no.2
• /
• pp.71-75
• /
• 2023

In this study, inorganic perovskite films with different compositions were grown by thermal chemical vapor deposition depending on the substrate and their optical properties were compared. Inorganic perovskite crystals were grown on SiO₂/Si and c-Al₂O₃ substrates using CsBr and PbBr₂, respectively, under the same growth conditions. Cs₄PbBr₆-CsPbBr₃ crystallites were grown on the SiO₂ with polycrystalline structure, while a CsPbBr₃ (100) dominant thin film was formed on the c-Al₂O₃ substrate with single crystal structure. From the photoluminescence measurement, CsPbBr₃ showed typical green emission centered at 534 nm with a full width at half maximum (FWHM) of about 91 meV. The Cs₄PbBr₆-CsPbBr₃ mixed structure exhibits blue-shifted emission at 523 nm with a narrow FWHM of 63 meV and a fast decay time of 6.88 ns. These results are expected to be useful for application in photoelectric devices such as displays, solar cells, and light sensors based on inorganic metal perovskites.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.97.1-97.1
• /
• 2010

유연금속기판위에 DC 마그네트론 스퍼터링을 이용하여 Ag/ZnO 이중구조의 후면반사막을 증착하고 Ag 표면조도 변화에 따른 후면반사막의 반사특성 변화와 플렉서블 비정질 실리콘 박막 태양전지의 셀 특성에 미치는 영향을 조사하였다. Substrate구조를 갖는 플렉서블 실리콘 박막 태양전지에서는 실리콘 박막 광흡수층의 상대적으로 낮은 광 흡수율로 인하여 입사광에 대한 태양전지 내에서의 광 산란 및 포획이 태양전지 효율을 증대시키는데 매우 중요한 역할을 하는 것으로 알려져 있다. 플렉서블 실리콘 박막 태양전지에서의 후면반사막은 광 흡수층에서 흡수되지 않는 입사광을 다시 반사시켜 광 흡수를 증대시키며 이때 후면반사막 표면에서 반사 빛을 효율적으로 산란시켜 이동경로를 증대시킴으로써 광 흡수율을 더욱 향상시킬 수 있다. 본 연구에서는 유연금속 기판위에 Ag와 ZnO:Al($Al_2O_3$ 2.5wt%) 타겟을 사용한 DC 마그네트론 스퍼터링법으로 Ag/AZO 이중구조의 후면반사막을 제조하고, Ag 박막의 표면형상 변화와 이에 따른 후면반사막의 반사도 변화를 비교, 분석하였다. 증착 조건 변화에 따른 표면 형상 및 반사 특성은 Atomic Force Mircroscope(AFM), Scanning electron miroscopy(SEM), UV-visible-nIR spectrometry를 통하여 분석하였다. 서로 다른 표면 거칠기를 갖는 후면반사막 위에 n-i-p구조의 a-Si:H 실리콘 박막 태양전지를 제조한 후 태양전지 동작 특성에 미치는 영향을 조사하였다. n,p층은 13.56MHz PECVD, i층은 60MHz VHF CVD를 사용하여 각각 제조 하였으며, Photo I-V, External Quantum Efficiency(EQE) 분석을 통하여 태양전지 특성을 조사 하였다. SEM 분석결과 공정 온도가 증가 할수록 Ag 박막의 표면 결정립 크기도 증가하였으며, AFM분석을 통한 Root-mean-square(Rms)값은 상온에서 $500^{\circ}C$로 증착온도가 증가함에 따라 6.62nm에서 46.64nm까지 증가하였다. Ag 박막의 표면 거칠기 증가에 따라 후면반 사막의 확산 반사도도 함께 증가하였다. 공정온도 $500^{\circ}C$에서 증착된 후면반사막을 사용하여 a-Si:H 태양전지를 제조하였을 때 상온에서 제조한 후면반사막에 비하여 단락전류밀도 (Jsc)값은 9.94mA/$cm^2$에서 13.36mA/$cm^2$로 증가하였으며, 7.6%의 가장 높은 태양전지 효율을 나타내었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.289-289
• /
• 2013

While there are plenty of studies on synthesizing semiconducting germanium nanowires (Ge NWs) by vapor-liquid-solid (VLS) process, it is difficult to inject dopants into them with uniform dopants distribution due to vapor-solid (VS) deposition. In particular, as precursors and dopants such as germane ($GeH_4$), phosphine ($PH_3$) or diborane ($B_2H_6$) incorporate through sidewall of nanowire, it is hard to obtain the structural and electrical uniformity of Ge NWs. Moreover, the drastic tapered structure of Ge NWs is observed when it is synthesized at high temperature over $400^{\circ}C$ because of excessive VS deposition. In 2006, Emanuel Tutuc et al. demonstrated Ge NW pn junction using p-type shell as depleted layer. However, it could not be prevented from undesirable VS deposition and it still kept the tapered structures of Ge NWs as a result. Herein, we adopt $C_2H_2$ gas in order to passivate Ge NWs with carbon sheath, which makes the entire Ge NWs uniform at even higher temperature over $450^{\circ}C$. We can also synthesize non-tapered and uniformly doped Ge NWs, restricting incorporation of excess germanium on the surface. The Ge NWs with carbon sheath are grown via VLS process on a $Si/SiO_2$ substrate coated 2 nm Au film. Thin Au film is thermally evaporated on a $Si/SiO_2$ substrate. The NW is grown flowing $GeH_4$, HCl, $C_2H_2$ and PH3 for n-type, $B_2H_6$ for p-type at a total pressure of 15 Torr and temperatures of $480{\sim}500^{\circ}C$. Scanning electron microscopy (SEM) reveals clear surface of the Ge NWs synthesized at $500^{\circ}C$. Raman spectroscopy peaked at about ~300 $cm^{-1}$ indicates it is comprised of single crystalline germanium in the core of Ge NWs and it is proved to be covered by thin amorphous carbon by two peaks of 1330 $cm^{-1}$ (D-band) and 1590 $cm^{-1}$ (G-band). Furthermore, the electrical performances of Ge NWs doped with boron and phosphorus are measured by field effect transistor (FET) and they shows typical curves of p-type and n-type FET. It is expected to have general potentials for development of logic devices and solar cells using p-type and n-type Ge NWs with carbon sheath.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.23.1-23.1
• /
• 2011

최근 화석연료를 대체하기 위한 지속가능한 신에너지에 대한 요구가 증대됨에 따라 태양광 발전에 대한 연구도 폭발적으로 늘어가고 있는 추세이다. 태양광이 화석연료 대체에너지로 실효성을 가지기 위해서는 태양광 발전 시스템의 발전효율을 높이고 생산 비용을 저감하는 문제가 선결되어야 한다. 기존 실리콘 태양전지 시스템 설비 비용의 60% 이상을 차지하는 모듈의 제조과정에서 소재 손실을 최소화함으로써 저가격화를 실현하고자 박막형 태양전기 기술이 태동되었다. 현재 박막 태양전지와 관련하여 활발한 기술 개발이 진행되고 있으며 상당한 시장 점유율을 보이고 있는 실정이다. 박막 태양전지 분야에서 CIGS와 같은 화합물 반도체 박막 태양전지 시장이 확대되고 있는 실정을 고려한다면 실리콘 박막 태양전지의 경우 고효율화 저가격화 달성은 더욱 절실한 문제이다. 실리콘 박막의 경우 독성이 없으며 고갈 우려가 없는 소재이면서 기존의 직접회로 산업의 인프라 구조를 활용할 수 있어 많은 기대와 관심을 끌고 있는 박막 태양전지 후보이다. 박막 태양전지 제조에 있어서 핵심기술은 도핑된 실리콘층과 광흡수를 위한 진성 실리콘층을 합성하는 공정 기술이다. 현재 박막 태양전지 산업에서 실리콘 박막 소재의 합성은 주로 PECVD법에 의해 이루어지고 있다. 그러나 스퍼터 공정을 이용한 실리콘 박막 합성 연구 또한 20년 이상의 오랜 기간 동안 연구되어 오고 있다. 스퍼터 공정을 이용한 실리콘 박막합성는 독성 가스를 사용하지 않으며, 디스플레이와 같은 기존의 소자 공정 기술을 채용할 수 있다는 장점을 가지고 있어 주목 받고 있다. 실제로 반응성 마그네트론 스퍼터링에 의해 제조된 실리콘 박막은 PECVD공정에 의한 실리콘 박막에 상응하는 우수한 광전자적 특성을 보인다. 스퍼터 공정에서는 박막 성장을 위한 수송 물질들이 열적 평형 상태에 근접한 라디칼들이라기 보다 대부분 고에너지 원자종과 이온들이 주류를 이루고 있어 합성된 실리콘 박막의 결함 제어가 어렵다는 문제가 있다. 박막 합성 기구의 규명을 통하여 이러한 문제를 해결하기 위한 시도들이 이루어 지고 있으며, 본 발표를 통하여 스퍼터 공정을 이용한 태양전지용 실리콘 박막 합성기술에 대한 현황을 소개하고자 한다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.5-5
• /
• 2009

Thin-film-transistors (TFTs) that can be prepared at low temperatures have attracted much attention because of the great potential for transparent and flexible electronics. One of the mainstreams in this field is the use of organic semiconductors such as pentacene. But device performance of the organic TFTs is still limited due to low field-effect mobility and rapid degradation after exposing to air. Alternative approach is the use of amorphous oxide semiconductors as a channel. Amorphous oxide semiconductors (AOSs) based TFTs showed the fast technological development, because AOS films can be fabricated at room temperature and exhibit the possibility in application like flexible display, electronic paper, and larges solar cells. Among the various AOSs, a-IGZO has lots of advantages because it has high channel mobility, uniform surface roughness and good transparency. [1] The high mobility is attributed to the overlap of spherical s-orbital of the heavy post-transition metal cations. This study demonstrated the effect of the variation in channel thickness from 30nm to 200nm on the TFT device performance. When the thickness was increased, turn-on voltage and subthreshold swing was decreased. The a-IGZO channels and source/drain metals were deposited with shadow mask. The a-IGZO channel layer was deposited on $SiO_2$/p-Si substrates by RF magnetron sputtering, where RF power is 150W. And working pressure is 3m Torr, at $O_2/Ar$ (2/28 sccm) atmosphere. The electrodes were formed with electron-beam evaporated Ti (30 nm) and Au (70 nm) bilayer. Finally, Al (150nm) as a gate metal was thermal-evaporated. TFT devices were heat-treated in a furnace at 250 $^{\circ}C$ and nitrogen atmosphere for 1hour. The electrical properties of the TFTs were measured using a probe-station. The TFT with channel thickness of 150nm exhibits a good subthreshold swing (SS) of 0.72 V/decade and on-off ratio of $1{\times}10^8$. The field effect mobility and threshold voltage were evaluated as 7.2 and 8 V, respectively.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.100.2-100.2
• /
• 2010

Superstrate형 실리콘 박막 태양전지에서 전면전극으로 사용되는 투명전도막의 표면형상은 태양전지내로 입사하는 태양광의 표면산란에 영향을 미치며 표면산란 증가를 통한 광 포획 및 단락전류밀도 향상을 통하여 태양전지 효율을 증대시키는 중요한 역할을 한다. 기존에 실리콘박막 태양전지용으로 많이 사용되는 상용 Asahi-U형 투명전도막은 수소 플라즈마에 대한 안정성이 낮고 입사광의 장파장 대역에서의 산란특성이 낮아 실리콘 박막 태양전지의 고효율화에 한계점이 있었다. 최근에 Asahi-U형 투명전도막을 대신하여 ZnO계 투명전도막을 전면전극으로 사용하려는 연구가 활발히 진행되고 있으며 Al을 토핑원소로 사용하는 ZnO:Al 투명전도막은 우수한 전기적, 광학적 특성과 수소플라즈마 안정성 및 저 비용 등의 우수한 장점을 갖고 있다. 스퍼터링 방식으로 제조된 ZnO:Al 투명전도막의 표면형상은 일반적으로 증착 후 습식식각을 통하여 조절되며 식각 전 박막의 미세구조에 영향을 받는 것으로 알려져 있다. 또한 습식 식각 이후의 표면거칠기에 따라 다양한 광학적, 전기적 특성을 나타낸다. 본 연구에서는 in-line RF-magnetron sputter 장비를 이용하여 다양한 공정조건하에서 ZnO:Al 투명전도막을 제조하고 증착된 박막의 미세구조 특성에 따른 습식식각 이후의 표면형상 변화 및 전기적 광학적 특성 변화를 조사하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.159-159
• /
• 2009

RF 스퍼터링법을 이용하여 유리기판위에 ZnO:Al 박막을 증착하고 다양한 조건 하에서 후 열처리를 실시하여 이에 따른 박막의 구조적, 전기적 및 광학적 특성과 HCl 습식 식각 후의 표면형상 변화를 조사하였다. ZnO:Al 투명전도막은 우수한 전기적, 광학적 특성, 수소 플라즈마 안정성 및 저 비용 등으로 실리콘 박막 태양전지 전면 전극용으로 많은 관심을 받고 있다. 기존의 비정질 실리콘 박막 태양전지용으로 많이 사용되고 있는 상용 Asahi-U형 ($SnO_2:F$) 투명전도막의 경우는 수소 플라즈마에 대한 안정성이 낮고 입사광의 장파장 대역에서의 낮은 산란특성으로 인하여 실리콘 박막 태양전지의 고효율화를 위한 적용에 한계를 나타내고 있다. 이를 개선하기 위하여 스퍼터링법으로 우수한 전기적 특성을 갖는 ZnO:Al 박막을 제조한 후 습식 식각을 통한 표면형상 변화를 통하여 입사광의 산란특성을 향상시키는 방법이 개발되어 많은 연구가 이루어지고 있다. 본 연구에서는 2.5 wt%의 $Al_2O_3$가 함유된 ZnO 타겟을 이용하여 ZnO:Al 박막을 RF 스퍼터링으로 증착한 후 $N_2$ 분위기와 진공 분위기 하에서 다양한 시간과 온도에 따라 후열처리를 하여 열처리 전 박막과의 물질 특성을 상호 비교하고 1%로 희석된 HCl로 습식 식각하여 열처리 전 박막의 구조적 특성이 습식 식각 후의 박막 표면형상 변화에 미치는 영향을 조사하였다. 이로부터 후열처리를 통한 ZnO:Al 투명전도막의 특성을 최적화하고 Asahi-U형 투명전도막과의 특성 비교를 통하여 실리콘 박막 태양전지용 전면전극으로의 적용 가능성을 조사하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.137-137
• /
• 2009

Thin-film transistors (TFTs) that can be prepared at low temperatures have attracted much attention due to the great potential for flexible electronics. One of the mainstreams in this field is the use of organic semiconductors such as pentacene. But device performance of the organic TFTs is still limited by low field effect mobility or rapidly degraded after exposing to air in many cases. Another approach is amorphous oxide semiconductors. Amorphous oxide semiconductors (AOSs) have exactly attracted considerable attention because AOSs were fabricated at room temperature and used lots of application such as flexible display, electronic paper, large solar cells. Among the various AOSs, a-IGZO was considerable material because it has high mobility and uniform surface and good transparent. The high mobility is attributed to the result of the overlap of spherical s-orbital of the heavy pest-transition metal cations. This study is demonstrated the effect of thickness channel layer from 30nm to 200nm. when the thickness was increased, turn on voltage and subthreshold swing were decreased. a-IGZO TFTs have used a shadow mask to deposit channel and source/drain(S/D). a-IGZO were deposited on SiO2 wafer by rf magnetron sputtering. using power is 150W, working pressure is 3m Torr, and an O2/Ar(2/28 SCCM) atmosphere at room temperature. The electrodes were formed with Electron-beam evaporated Ti(30nm) and Au(70nm) structure. Finally, Al(150nm) as a gate metal was evaporated. TFT devices were heat treated in a furnace at $250^{\circ}C$ in nitrogen atmosphere for an hour. The electrical properties of the TFTs were measured using a probe-station to measure I-V characteristic. TFT whose thickness was 150nm exhibits a good subthreshold swing(S) of 0.72 V/decade and high on-off ratio of 1E+08. Field effect mobility, saturation effect mobility, and threshold voltage were evaluated 7.2, 5.8, 8V respectively.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.06a
• /
• pp.205-208
• /
• 2005

최근 열선 화학 기상 증착법(HWCVD)은 낮은 온도에서 TFT용 Poly Si 중착을 할 수 있다는 점과 실리콘 박막을 빠른 속도로 증착할 수 있다는 점에서 각광을 받고 있다. 본 연구에서는 HWCVD를 이용하여 태양전지를 제조하고 그 특성을 평가하였다. 조건에 따른 실리콘 박막의 특성 변화를 알기 위해 corning glass 및 실리콘 wafer에 다양한 조건에서 단위 박막(intrinsic layer)을 증착하였고 이 결과를 바탕으로 p/i/n 구조의 태양전지를 제조하였다. Ta 열선 온도는 1700-2000도였고 가스 원료인 $SiH_4$와 수소의 비율을 조절하면서 그 영향을 관찰하였다. 태양전지의 경우 p충과 n충은 PECVD로 증착하였으며 단위박막 및 태양전지 i충 증착시 기판과 열선간의 거리는 7cm, 기판 온도는 $200^{\circ}C$와 $250^{\circ}C$로 고정하였고 작업압력은 30mTorr였다. 단위 박막 특성 평가를 위해 암/광 전도도, SEM, Raman Scattering, FT-IR등을 사용하였으며 태양전지 특성 평가를 위해 I-V 및 Spectral response를 측정하였다. 열선 온도가 증가함에 따라 증착속도 및 결정화 분율은 증가하였다. 특히 비정질에서 결정질로 전이되는 구간은 매우 좁았으며 여러 분석 방법에서 일치되는 결과를 보였다. $SiH_4$ 유량이 늘어날수록 비정질이 결정질로 바뀌는 열선 온도가 증가하였으며 기판 온도가 낮을 경우 또한 결정으로 바뀌는 열선 온도가 증가하였다. 태양전지의 경우 열선 온도가 증가함에 따라 $V_{oc}$ 및 W가 낮아졌으며 $J_{sc}$, 는 증가하는 경향을 보였으며 결정질 비율이 증가하는 것을 관찰할 수 있었다. 이러한 경향은 quantum efficiency 결과에서도 확인할 수 있었다.용을 반복하면서 석재 내부와 외부의 암석 및 결정에 균열과 미세열극 등이 생성되어 석재 자체의 구조적 안정성에 영향을 주고 있다. 따라서 감은사지 석탑은 지리적 환경 차이로 인해 일반적인 환경의 석조물들과는 다른 형태의 풍화양상을 보이고 있어서 풍화양상 및 풍화형태에 대한 정확한 연구와 이해를 바탕으로 보존대책이 마련되어야 한다.되었다. 이런 모든 시편들을 각 탈염방법에 따라 탈염처리한 후 XRD와 SEM-EDS으로 분석한 결과 인철광과 침철광은 어떠한 변화도 보이지 않았고, 다만 적금광으로 동정된 시편만이 잔존하지 않았다. 철기 제작별 $Cl^-$ 이온 추출량과 탈염효과에 대한 비교 실험은 이온 크로마토그래피 분석 결과와 마찬가지로 단조 철제유물이 주조 철제보다 $Cl^-$ 이온을 많이 가지고 있었으며, 탈염 처리 후에는 $Cl^-$ 이온은 전혀 발견되지 않았다. 이상의 결과 $K_2CO_3$와 Sodium 용액은 탈염처리에서 가장 적합한 탈염처리 용액으로 알수가 있었으며 특히 어떠한 탈염 용액으로 유물을 처리한다 해도 철제유물에 생성된 부식물은 제거되지 않는다는 것을 알게 되었다. 따라서 보존처리자는 유물 표면의 부식 상태만을 보고 처리하기 보다는 철기제작물로 고려하여 처리하는 것이 필요하다. 또한 금속에 부식을 야기시키는 $Cl^-$ 이온과 부식물을 완전하게 제거하여 탈염처리를 하는 것이 유물 부식을 최대한 지연시킬 수 있는 것이라 생각된다.TEX>$88\%$)였다.(P=0.063). 결론: 본 연구에서는 MTHFR C/T & T/T 유전자 다형성이 위암의 발생과 그 위치에 대해 관련이 있는 것으로 여겨지고, 흡연력, 음주력과는 관련이 없는 것으로 여겨진다.험이 커지는 경향을 보였으나, 나이 및 병기, 종양의 크기, MD-BED $Gy_{10}$ 등의 예후 인자를 보정한 다변