• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.858-868
• /
• 1995

Texture development and martensitic phase transformation, on rolling, are compared in two Hadfield's steels, one having low carbon content(0.65wt% C), the other high carbon content(1.35wt%). In spite of small difference in stacking fault energy(about 2 mJm$^{-2}$ ) between two Hadfield's steels, the differences in texture development are observed. In low carbon steel, the textures developed are similar to those of low stacking fault energy metals in low strain range. However, the abnormal textures such as {111} , {110} <001> are strongly developed at high strain, which are due to the disturbance of u martensite in the development of textures formed at the packets of shear bands or at the grain boundaries. In contrast to low carbon Hadfield's steel( LCHS), the texture development of high carbon Hadfield's steel(HCHS) is simitar to those of low stacking fault energy metals in the whole strain range. This may be due to the fact that the amount of deformation induced martensite was small, as observed by A.C. magnetic susceptibility and iron particle tests.

• Korean Journal of Metals and Materials
• /
• v.46 no.3
• /
• pp.135-143
• /
• 2008

The inhomogeneous texture through the thickness direction can be developed during hot rolling deformation in aluminum alloy. In this study, the inhomogeneous texture evolution through the thickness direction during hot rolling deformation in Al-5 wt%Mg alloy produced by a new strip casting technology was measured experimentally. Macrotexture measurement was conducted using X-ray diffractometer. A finite element analysis with ABAQUS/StandardTM and rate sensitive polycrystal model were used to predict the evolution of hot rolling texture. The experimental results of Al-5 wt%Mg alloy were compared with calculated results. The shear texture components tend to be increased at the surface region of the hot-rolled specimen. It is found that triclinic sample symmetry is more accurate assumption for texture analysis and simulation in the surface region of hot-rolled aluminum alloy.

• Korean Journal of Metals and Materials
• /
• v.47 no.6
• /
• pp.363-371
• /
• 2009

The effect of lubrication on the evolution of strain states during shape rolling in AA5052 sheet was studied by the finite element method (FEM) simulation. The strain states calculated by FEM were verified by texture analysis. Shape rolling with and without lubrication produces shape-rolled samples in fairly similar outer shapes, since the distribution of normal strain components is nearly independent of the lubrication condition. In contrast, the distribution of shear strain components strongly depends on the lubrication condition. Shape rolling without lubrication gives rise to the development of strong shear strain gradients leading to the formation of highly inhomogenous textures and microstructures. The {011}//ND fiber develops during rolling with the operation of plane strain plus ${\dot{\varepsilon}}_{22}$.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.05a
• /
• pp.96-98
• /
• 2003

The evolution of texture and microstructure during continuous confined strip shearing (CCSS) in aluminum 3003 alloy sheets was investigated. The tools of CCSS based on the equal channel angular pressing (ECAP) were designed to provide a constant shear deformation of the order of 0.5 per pass while preserving the original sheet shape. FEM results indicated that the shear formation is not homogeneous throughout the sample thickness, in particular at the surface layers. A randomization of textures took place during the CCSS deformation. Observations by TEM and EBSD revealed the formation of sub-micrometer sized grains after CCSS.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.460-462
• /
• 2005

Asymmetrical rolling was performed with different working roll speeds of upper and lower rolls. In order to promote the shear deformation during asymmetrical rolling, various deformation parameters of initial sheet thickness, rolling reduction, roll speed ratio and roll radius are considered. The evolution of texture during asymmetrical rolling was shown by the calculation of orientation distribution function (ODF). The effect of deformation parameters on shea. deformation were investigated by simulations with the finite element method (FEM). Asymmetrical rolling gave rise to the development of pronounced strain gradients throughout the thickness layers which resulted in the formation of strong texture gradients in the sheet.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.05a
• /
• pp.105-108
• /
• 2003

Sheets of aluminum alloy 1100 were asymmetrically cold rolled in a rolling mill with different roll speeds. In order to promote the shear deformation during asymmetrical rolling, cold rolling without lubrication was performed. The evolution of texture components during asymmetrical rolling was investigated by the calculation of the orientation distribution function (ODF) using the monoclinic sample symmetry. The strain state during asymmetrical rolling was tackled by means of FEM calculations. Asymmetrical rolling gave rise to the development of pronounced strain gradients throughout the thickness layers which resulted in the formation of strong texture gradients in the aluminum sheet.

• Transactions of Materials Processing
• /
• v.12 no.3
• /
• pp.244-250
• /
• 2003

Sheets of aluminum alloy 1100 were asymmetrically cold rolled in a rolling mill with different roll speeds. In order to promote the shear deformation during asymmetrical rolling, cold rolling without lubrication was performed with a roll speed ratio of 1.5/l.0. The evolution of texture components during asymmetrical rolling was investigated by the calculation of the orientation distribution function (ODF) using the monoclinic sample symmetry. The strain state during asymmetrical rolling was tackled by means of FEM calculations. Asymmetrical rolling gave rise to the development of pronounced strain gradients throughout the thickness layers which resulted in the formation of strong texture gradients in the aluminum sheet.

• Transactions of Materials Processing
• /
• v.18 no.6
• /
• pp.448-452
• /
• 2009

Superplastic deformation behavior and texture evolution after equal channel angular pressing (ECAP) of Zn-0.3Wt%Al alloy were investigated in this study. ECAP was conducted at temperatures from $60^{\circ}C$ to $160^{\circ}C$ on the plate type specimens of 5 mm thickness and 20 mm width. The specimens obtained by ECAP showed typical texture with basal poles tilted away from the ND toward ED, which is called shear texture. Tensile tests were carried out at $100^{\circ}C$ for ECAPed specimens under the strain rate of 0.0002/s. After ECAP of the Zn-0.3Wt%Al alloy, elongation was dramatically increased up to 500% at $100^{\circ}C$. The effect of ECAP on the anisotropy in the superplastic deformation behavior was negligible.

• Transactions of Materials Processing
• /
• v.16 no.4 s.94
• /
• pp.276-281
• /
• 2007

The hardening and the constitutive equation based on the crystal plasticity are introduced for the numerical simulation of hemispherical sheet metal forming. For calculating the deformation and the stress of the crystal, Taylor's model of the crystalline aggregate is employed. The hardening is evaluated by using the Taylor factor, the critical resolved shear stress of the slip system, and the sum of the crystallographic shears. During the hemispherical forming process, the texture of the sheet metal is evolved by the plastic deformation of the crystal. By calculating the Euler angles of the BCC sheet, the texture evolution of the sheet is traced during the forming process. Deformation texture of the BCC sheet is represented by using the pole figure. The comparison of the strain distribution and punch force in the hemispherical forming process between the prediction using crystal plasticity and experiment shows the verification of the crystal plasticity-based formulation and the accuracy of the hardening and constitutive equation obtained from the crystal plasticity.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.477-479
• /
• 2008

Drawability and other mechanical properties of sheet metals are strongly dependent on their crystallographic orientations. In this paper the formability of the AA 5052 Al alloy sheets was investigated after asymmetric rolling and subsequent heat treatment. In most cases, after asymmetric rolling specimens showed a fine grain size and subsequent heat treated specimens showed that the ND//<111> texture component were observed. The anisotropy of formability is often described by the plastic strain ratios (r-value) as a function of the angle to the rolling direction in sheet metal. For a good formability, a high r-value is required in sheet metals. In the asymmetry rolled and subsequent heat treated Al alloy sheet, the variation of the plastic strain ratios have been investigated in this study. The plastic strain ratios of the asymmetry rolled and subsequent heat treated AA 5052 Al alloy sheets were higher than those of the original Al sheets. These could be related to the formation of ND//<111> texture components through asymmetric rolling in Al sheet.