• Restorative Dentistry and Endodontics
• /
• 제27권1호
• /
• pp.34-43
• /
• 2002

The purpose of this study was to compare microleakage and marginal hybrid layer in class V restorations using two one-bottle adhesives and one self-etching adhesive. Class V cavity preparations with occlusal margins in enamel and gingival margins in dentin were pre-pared on buccal and lingual surfaces of 30 extracted human molar teeth. Prepared teeth were randomly divided into three treatment groups (n=30) and restored with three adhesives and composites: Single Bond/Filtek Z-250 (Group 1), Prime&BondNT/Esthet.X (Group 2), UniFil Bond/UniFil F (Group 3). For microleakage, samples were stored in room temperature water for 24 hours, thermocycled stained with 2% methylene blue dye, sectioned into halves, scored and analysed using Mann-whitney test and Wilcoxon signed rank sum test. For marginal hybrid layer, samples were sectioned into halves, treated with 10% phosphoric acid for 5 seconds, stored in 5% NaOCL solution for 24 hours, dried and gold coated. Occlusal and gingival margins of each sample were inspected under SEM. The results of this study were as follows ; 1. Microleakage at the occlusal margins was not evident in group 1 and group 2, but it showed in group 3 (p<0.05). 2. Microleakage in group 1 and group 3 was significantly lower than in group 2 at gingival margins (p<0.05). 3. Microleakage at gingival margins was greater than at occlusal margins in group 1 and group 2, but microleakage at occlusal margins was greater than at gingival margins in group 3 (p<0.05). 4. In group 1 and group 2, no gaps at occlusal margins showed. But gaps showed in group 3. Occlusal margins were free from a hybrid layer in all groups 5. The thickness of the marginal hybrid layers was 2.5~5 $\mu\textrm{m}$ thick in group 5 $\mu\textrm{m}$ thick in group 2 and 1.5 $\mu\textrm{m}$ thick in group 3. 6 There was no corelation between microleakage and thickness of marginal hybrid layer. In coclusion, the effect of dentin adhesives on microleakge in class V composite restorations was excellent when one-bottle adhesives were applied on enamel margin, and it was good when a self-etching adhesive was applied on dentinal margin. There was no corelation between microleakage and thickness of marginal hybrid layer.

• 대한치과보존학회:학술대회논문집
• /
• 대한치과보존학회 2008년도 Spring Scientific Meeting(the 129th) of Korean Academy if Conservative Dentistry
• /
• pp.224-234
• /
• 2008

이 연구의 목적은 6종의 자가부식 프라이머 접착시스템에서 제조사에서 추천한 프라이머 적용시간과 2배의 프라이머 적용시간에 따른 법랑질에 대한 미세전단 결합강도와 전자현미경적 소견을 비교하기 위하여 시행하였다. 이 연구의 결과 법랑질에 대한 자가부식 프라이머 접착제의 결합강도는 제조사에서 추천한 프라이머의 적용시간보다 프라이머의 적용시간을 2배 증가시킨 경우 높게 나타났으며, 특히 pH가 높은 프라이머를 사용하였을 때 통계학적으로 높은 결합강도를 나타내었다. 이는 법랑질에서 pH가 높은 프라이머를 사용할 경우, 제조사에서 추천한 시간보다 더 긴 시간동안 적용하는 것이 결합강도를 증가시킬 수 있을 것으로 생각된다.

• Restorative Dentistry and Endodontics
• /
• 제33권3호
• /
• pp.224-234
• /
• 2008

이 연구의 목적은 6종의 자가부식 프라이머 접착시스템에서 제조사에서 추천한 프라이머 적용시간과 2배의 프라이머 적용시간에 따른 법랑질에 대한 미세전단 결합강도와 전자현미경적 소견을 비교하기 위하여 시행하였다. 이 연구의 결과 법랑질에 대한 자가부식 프라이머 접착제의 결합강도는 제조사에서 추천한 프라이머의 적용시간보다 프라이머의 적용시간을 2배 증가시킨 경우 높게 나타났으며, 특히 pH가 높은 프라이머를 사용하였을 때 통계학적으로 높은 결합강도를 나타내었다. 이는 법랑질에서 pH가 높은 프라이머를 사용할 경우, 제조사에서 추천한 시간보다 더 긴 시간동안 적용하는 것이 결합강도를 증가시킬 수 있을 것으로 생각된다.

• 대한치과교정학회지
• /
• 제40권4호
• /
• pp.267-275
• /
• 2010

이번 연구의 목적은 맹출 또는 미맹출된 치아에 교정용 버튼을 부착 후 자가부식 접착제(self-etching adhesive)의 사용 유무에 대한 전단결합강도(shear bond strength)와 탈락모드를 비교하고자 함이다. 각각 84개의 맹출 또는 미맹출된 제3대구치를 사용하였다. 각각 치아의 협측면을 다음의 부착시스템 그룹으로 할당하였다. A, 기존방식: 1, Transbond XT (3M Unitek); 2, Prime & Bond NT (Dentsply/Caulk); 3, Single Bond (3M ESPE); B, 자가부식 접착제; 4, Clearfil SE Bond (Kuraray); 5, Transbond Plus (3M Unitek); 6, Clearfil S3 (Kuraray); 7, G Bond (GC). 부착물의 전단강도와 접착제 잔류지수를 측정하였으며 결과값은 ANOVA와 independent t-test 및 chi-square 검증을 통해 분석되었다. 맹출 또는 미맹출된 치아의 전단결합강도를 비교하였을 때 Clearfil SE와 G Bond에서 유의한 차이가 관찰되었다. Single Bond를 제외한 모든 접착시스템에서 맹출보다는 미맹출 치아면에서 높은 접착강도가 관찰되었다. 기존 접착제를 사용하는 경우 맹출 또는 미맹출 치아에 대한 접착강도에는 차이가 없을 수 있다. 그러나 임상의사는 사용 전에 self-etching system의 종류를 고려할 필요가 있다.

• Restorative Dentistry and Endodontics
• /
• 제36권5호
• /
• pp.385-396
• /
• 2011

연구목적: 본 연구는 치근벽의 전처리 개념과 접착제의 중합방법이 레진계 근관충전제의 치근단 밀폐능에 미치는 영향을 평가하였다. 연구 재료 및 방법: 3가지 다른 접착변수를 조합하여 충전한 Resilon-RealSeal 시스템의 근단미세누출을 색소침투법을 이용하여 통상의 가타퍼쳐 충전과 비교하였다. 실험군은 자가부식형 RealSeal primer와 이중중합형 RealSeal sealer를 이용하여 Resilon 충전한 SEDC군, 산부식없이 Scotchbond Multi-Purpose primer를 적용한 후 접착제는 광중합하고 Resilon을 충전한 NELC군, 및 Scotchbond Multi-Purpose의 접착강화제와 접착제를 total etch/wet bonding과 광중합의 술식을 정확하게 지켜서 Resilon을 충전한 TELC군으로 구분하였다. 대조군(GPCS)에서는 통상의 AH26 plus sealer를 사용하여 가타퍼쳐를 충전 하였다. 결과: 치아장축방향의 색소침투는 TELC군에서 GPCS군과 SEDC군에 비해 유의하게 작았다(Kruskal-Wallis test, p < 0.05). 횡단면의 미세누출 점수도 TELC군이 근첨으로부터 2 - 5 mm의 범위에서 다른 군에 비해 유의하게 낮았다(Kruskal-Wallis test, p < 0.05). 결론: 레진계 근관충전제를 사용 시에는, 자가부식형 전처리제와 이중중합형 sealer보다는, total etch/wet bonding 개념과 적절한 광중합을 도모하는 전처리제 및 접착제의 사용이 치근단 미세누출을 감소시키므로 추천된다.

• Journal of Korean Dental Science
• /
• 제2권2호
• /
• pp.5-11
• /
• 2009

Objectives : This study investigated the hypothesis that the dentin bond strength of self-etching adhesives (SEAs) may be improved by applying a coat of hydrophobic, neutral adhesive resin in addition to SEA. Method and Materials : The bond strengths of two SEAs - Experimental SEA (EX) and Adper Prompt (AP) - were measured with three bonding protocols. The D/E resin of All-Bond 2 was applied as the hydrophobic, neutral adhesive. Clearfil SE Bond (SE, self-etching primer system) and All-Bond 2 (AB, total etching system) were used as references. The following protocols were used: (1) EX1 (EX 1 coat); (2) EX2 (EX 2 coats); (3) EX+ (EX 1 coat + D/E resin); (4) AP1 (AP 1 coat); (5) AP2 (AP 2 coats); (6) AP+ (AP 1 coat + D/E resin); (7) SE (SE primer + SE bond); (8) SE+ (SE primer + D/E resin); (9) AB (etching + AB primer + D/E resin). Filtek Z250 composite resin was built up and the microtensile bond strength (MTBS) values of the specimens were compared. The fractured surfaces were observed using SEM. Results : When SEA was used as self-etching primer and hydrophobic, neutral adhesive was applied as well, MTBS was significantly higher than that when either one coat or two coats of SEA only were used (p < 0.05). Conclusion : The hydrophobic, neutral adhesive improved the integrity of the bonded interface obtained with SEA.

• Restorative Dentistry and Endodontics
• /
• 제28권5호
• /
• pp.363-368
• /
• 2003

The purpose of this study is to evaluate the effect of additional enamel etching with phosphoric acid on the microleakage of the adhesion of self-etching primer system. Class V cavity($4mm{\times}3mm{\times}1.5mm$) preparations with all margins in enamel were prepared on buccal surface of 42 extracted human upper central incisor teeth. Prepared teeth were randomly divided into 3 groups. Group 1：no additional pretreatment with 37% phosphoric acid (NE). Group 2：additional pretreatment with 37% phosphoric acid for 10 seconds (E10s). Group 3：additional pretreatment with 37% phosphoric acid for 20 seconds (E20s). The adhesives(Clearfil SE $Bond^{\circledR}$, Kuraray, Osaka, Japan) and composite resins(Clearfil $AP-X^{\circledR}$, Osaka, Kuraray, Japan) were applied following the manufacturer's instructions. All the specimens were finished with the polishing disc(3M dental product, St Paul, MN, USA), thermocycled for 500 cycles between $5^{\circ}C$ and $55^{\circ}C$ and resected apical 3-mm root. 0.028 stainless steel wire was inserted apically into the pulp chamber of each tooth and sealed into position with sticky wax. Surrounding tooth surface was covered with a nail varnish 2 times except areas 1mm far from all the margins. After drying for one day, soaked the samples in the distilled water. Microleakage was assessed by electrochemical method(System 6514, $Electrometer^{\circledR}$), Keithley, USA) in the distilled water. In this study, the microleakage was the lowest in group 1 (NE) and the highest in group 3(E20s)(NE

• Restorative Dentistry and Endodontics
• /
• 제35권5호
• /
• pp.321-334
• /
• 2010

연구목적: 본 연구는 상아질 접착제의 잔류 용매가 접착 효율에 미치는 영향을 평가하고자 하였다. 연구 재료 및 방법: 본 연구에서는 5세대 2단계 산부식형 접착제와 7세대 단일과정 자가부식형 접착제를 사용하였다. 상아질 접착제의 증발률과 전환률, 적용 후 용매의 공기건조 방법에 따른 미세인장결합강도를 측정하였으며 접착 계면을 FE-SEM을 이용하여 관찰하였다. 결과: 1. 시간에 따라 접착제의 증발률은 증가하나 접착제의 종류에 따라 증가 양상이 서로 달랐다. 2. 대부분 전환률은 증발률에 비례하는 경향을 나타내었다. 3. 공기건조 방법에 따라 결합강도는 대부분 under군, control군, over군 순으로 증가하는 양상을 나타내었다. 4. FE-SEM에서 아세톤을 용매로 사용하는 접착제는 공기건조 방법에 따라 droplet이나 gap이 관찰되었다. 결론: 상아질 접착제의 잔류 용매는 접착 효율에 부정적인 영향을 미치기 때문에, 상아질 접착제의 선택과 사용 시 용매의 종류와 특징에 대한 적절한 이해가 필요할 것이다.

• Restorative Dentistry and Endodontics
• /
• 제28권3호
• /
• pp.222-231
• /
• 2003

The purpose of this study was to compare shear bond strength and interfacial pattern of composite bond-ed to dentin using self-etching adhesive systems. Sixty extracted human molars with exposed occlusal dentin were divided into four groups and bonded with four adhesives and composites. Single Bond/Filtek Z 350(SB), Tyrian SPE-One-Step Plus/Aelitefil(TY), Prompt L-Pop/Filtek Z 250(LP), and One-Up Bond F/palfique Toughwell(OU). The results of this study were as follows; 1 Shear bond strength for OU was significantly lower than that of other groups(p＜0.05). No significant difference was founded among SB, TY, and LP. 2. Failure modes to dentin showed adhesive and mixed for SB TY and LP, but them for OU showed adhesive in all spceimens. 3. Dentin-resin interface showed close adaptation for SB, TY, and LP, but it showed gap for OU. 4. The hybrid layers for TY, LP OU were thinner than that of SB. Adhesive layers were observed between composite and hybrid layer, which were 5 $\mu\textrm{m}$ thick for TY and 10 $\mu\textrm{m}$ thick for OU.

• Restorative Dentistry and Endodontics
• /
• 제32권3호
• /
• pp.222-235
• /
• 2007

이 논문의 목적은 열순환이 4종 상아질 접착 시스템의 결합 내구성에 미치는 영향을 측정한 것이다. 제3대구치의 상아질층을 노출시킨 후, 무작위로 8개군으로 나눈다: 3단계 산부식 시스템 (Scotchbond Multi-Purpose Plus; SM, All Bond-2 ; AB), 2 단계 산부식 시스템 (Single Bond; SB, One Step plus, OS), 2단계 자가부식 시스템 (Clearfil SE Bond; SE, AdheSE; AD), 1 단계 자가부식 시스템 (Promp L-Pop ; PL, Xeno III; XE). 8개 군에 각 상아질 접착제를 제조사의 지시에 따라 도포하고 복합레진 (Z250)을 적층한 후, 광조사한다. $37^{\circ}C$ 증류수에서 24시간 보관한 후, 각 군마다 정해진 프로그램으로 0, 1000, 2000회 열순환한 후, 저속 diamond saw로 $1\times1mm$ 막대형 시편을 제작한다. Universal testing machine (EZ-test; Shimadzu, Japan)으로 미세인장 결합강도를 측정하였고, 유의수준 0.05 level에서 ANOVA / Duncan's test로 통계분석 하였다. 상아질측 파단면과 접착계면에 대한 주사전자현미경 관찰을 시행하였다. 이 연구의 결과는 다음과 같다; 1. 3단계 상아질 접착제의 결합강도는 열순환 전후에 통계학적으로 유의한 변화를 나타내지 않았다. 2단계 산부식형 상아질 접착제의 결합강도는 열순환 처리에 의하여 유의하게 감소되었다. 2. 2단계 자가부식형 접착제 (SE)의 결합강도가 가장 높았고, 1단계 자가부식 접착제 (PL, XE)는 실험군 중 가장 낮은 결합강도를 보였다. 3. 모든 접착제는 주로 접착성 파괴가 발생하였고, 열순환에 의하여 산부식형 접착제는 접착성 파괴가, 1단계 자가부식형 접착제에서는 혼합형 파괴가 증가하는 경향을 나타내었다. 이상의 결과로, 상아질 접착제의 접착단계/과정이 결합내구성에 영향을 미침을 알 수 있었다. 따라서 접착과정의 단순화가 반드시 접착에 효과적이라고 할 수 없다.