• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.6
• /
• pp.261-264
• /
• 2012

In this paper, we investigated characteristics of etching induced surface morphology variation by wet etching of GaN epilayer were grown on sapphire (0001) substrate by hydride vapor phase epitaxy (HVPE). As a results of scanning electron microscope (SEM) observation, three types of hexagonal etch pits (Edge, Screw, Mixed) were formed by the GaN epilayer thickness variations. A lot of etch pits, attributed to screw and mixed type TD, were observed at thinner epilayer, leading to high etch pit density. On the other hand, the thickness of GaN epilayer increased with the number of etch pits corresponding to edge and mixed dislocations, which are the majority of TDs are observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.207-210
• /
• 2005

In order to investigate the influence of the homo buffer layer on the microstructure of the ZnO thin film, undoped ZnO buffer layer were deposited on sapphire (0001) substrates by ultra high vaccum pulsed laser deposition (UHV-PLD) and molecular beam eiptaxy (MBE). After high temperature annealing at $600^{\circ}C$ for 30min, undoped ZnO buffer layer was deposited with various oxygen pressure (35~350mtorr). On the grown layer of undoped ZnO, Arsenic-doped(l, 3wt%) ZnO layers were deposited by UHV-PLD. The optical property of the ZnO was analyzed by the photoluminescence (PL) measurement. From $\Theta-2\Theta$ XRD analysis, all the films showed strong (0002) diffraction peak, and this indicates that the grains grew uniformly with the c-axis perpendicular to the substrate surface. Field emission scanning electron microscope (FE-SEM) revealed that microstructures of the ZnO were varied with oxygen pressure, arsenic doping level, and the deposition method of undoped ZnO buffer layers. The films became denser and smoother in the cases of introducing MBE-buffer layer and lower oxygen pressure during As-doped ZnO deposition. Higher As-doping concentration enhanced the columnar-character of the films.

• Transactions of Materials Processing
• /
• v.28 no.1
• /
• pp.43-48
• /
• 2019

Aluminum nitride (AlN) is used by the semiconductor industry, and is a compound that is required when manufacturing high thermal conductivity. The AlN films with c-axis orientation and thermal conductivity characteristic were deposited by using the Pulsed Laser Deposition (PLD). The AlN thin films were characterized by changing the deposition conditions. In particular, we have researched the AlN thin film deposited under optimal conditions for growth atmosphere. The epitaxial AlN films were grown on sapphire ($c-Al_2O_3$) single crystals by PLD with AlN target. The AlN films were deposited at a fixed temperature of $650^{\circ}C$, while conditions of nitrogen ($N_2$) pressure were varied between 0.1 mTorr and 10 mTorr. The quality of the AlN films was found to depend strongly on the $N_2$ partial pressure that was exerted during deposition. The X-ray diffraction studies revealed that the integrated intensity of the AlN (002) peak increases as a function the corresponding Full width at half maximum (FWHM) values decreases with lowering of the nitrogen partial pressure. We found that highly c-axis orientated AlN films can be deposited at a substrate temperature of $650^{\circ}C$ and a base pressure of $2{\times}10^{-7}Torr$ in the $N_2$ partial pressure of 0.1 mTorr. Also, it is noted that as the $N_2$ partial pressure decreased, the thermal conductivity increased.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.3
• /
• pp.83-88
• /
• 2022

To improve the crystallinity of GaN, there are researches on surface treatment to control the difference in physical properties between GaN and heterogeneous substrate. 'Low-temperature GaN (LT-GaN)' is one of the ways to solve the problem and we investigated the relationship between growth temperature and properties of LT-GaN in our homemade vertical type HVPE. The LT-GaN nuclei were formed on the sapphire surface at low growth temperatures and they presented differences in the density and crystallinity depending on the growth temperature. Significantly, the stress relaxation effect on the epitaxial GaN (epi-GaN) was affected by the crystallinity of LT-GaN. However, the high crystallinity of LT-GaN exacerbated the crystal quality of epi-GaN because they worked as a catalyst and seed of polycrystalline.

• Journal of Sensor Science and Technology
• /
• v.30 no.6
• /
• pp.446-450
• /
• 2021

Non-dispersive infrared (NDIR) gas sensors typically use an optical filter that transmits a discriminating 4.26 ㎛ wavelength band to measure carbon dioxide (CO2), as CO2 absorbs 4.26 ㎛ infrared. The filter performance depends on the transmittance and full width at half maximum (FWHM). This paper presents the fabrication, sensitivity, and selectivity characteristics of a distributed Bragg reflector (DBR)-based Fabry-Perot filter with a simple structure for CO2 detection. Each Ge and SiO2 films were prepared using the RF magnetron sputtering technique. The transmittance characteristics were measured using Fourier-transform infrared spectroscopy (FT-IR). The fabricated filter had a peak transmittance of 59.1% at 4.26 ㎛ and a FWHM of 158 nm. In addition, sensitivity and selectivity experiments were conducted by mounting the sapphire substrate and the fabricated filter on an NDIR CO2 sensor measurement system. When measuring the sensitivity, the concentration of CO2 was observed in the range of 0-10000 ppm, and the selectivity was measured for environmental gases of 1000 ppm. The fabricated filter showed lower sensitivity to CO2 but showed higher selectivity with other gases.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.31-31
• /
• 2010

The growth of the high-quality GaN epilayers is of significant technological importance because of their commercializedoptoelectronic applications as high-brightness light-emitting diodes (LEDs) and laser diodes (LDs) in the visible and ultraviolet spectral range. The GaN-based heterostructural epilayers have the polar c-axis of the hexagonal structure perpendicular to the interfaces of the active layers. The Ga and N atoms in the c-GaN are alternatively stacked along the polar [0001] crystallographic direction, which leads to spontaneous polarization. In addition, in the InGaN/GaN MQWs, the stress applied along the same axis contributes topiezoelectric polarization, and thus the total polarization is determined as the sum of spontaneous and piezoelectric polarizations. The total polarization in the c-GaN heterolayers, which can generate internal fields and spatial separation of the electron and hole wave functions and consequently a decrease of efficiency and peak shift. One of the possible solutions to eliminate these undesirable effects is to grow GaN-based epilayers in nonpolar orientations. The polarization effects in the GaN are eliminated by growing the films along the nonpolar [$11\bar{2}0$] ($\alpha$-GaN) or [$1\bar{1}00$] (m-GaN) orientation. Although the use of the nonpolar epilayers in wurtzite structure clearly removes the polarization matters, however, it induces another problem related to the formation of a high density of planar defects. The large lattice mismatch between sapphiresubstrates and GaN layers leads to a high density of defects (dislocations and stacking faults). The dominant defects observed in the GaN epilayers with wurtzite structure are one-dimensional (1D) dislocations and two-dimensional (2D) stacking faults. In particular, the 1D threading dislocations in the c-GaN are generated from the film/substrate interface due to their large lattice and thermal coefficient mismatch. However, because the c-GaN epilayers were grown along the normal direction to the basal slip planes, the generation of basal stacking faults (BSFs) is localized on the c-plane and the generated BSFs did not propagate into the surface during the growth. Thus, the primary defects in the c-GaN epilayers are 1D threading dislocations. Occasionally, the particular planar defects such as prismatic stacking faults (PSFs) and inversion domain boundaries are observed. However, since the basal slip planes in the $\alpha$-GaN are parallel to the growth direction unlike c-GaN, the BSFs with lower formation energy can be easily formed along the growth direction, where the BSFs propagate straightly into the surface. Consequently, the lattice mismatch between film and substrate in $\alpha$-GaN epilayers is mainly relaxed through the formation of BSFs. These 2D planar defects are placed along only one direction in the cross-sectional view. Thus, the nonpolar $\alpha$-GaN films have different atomic arrangements along the two orthogonal directions ($[0001]_{GaN}$ and $[\bar{1}100]_{GaN}$ axes) on the $\alpha$-plane, which are expected to induce anisotropic biaxial strain. In this study, the anisotropic strain relaxation behaviors in the nonpolar $\alpha$-GaN epilayers grown on ($1\bar{1}02$) r-plane sapphire substrates by metalorganic chemical vapor deposition (MOCVO) were investigated, and the formation mechanism of the abnormal zigzag shape PSFs was discussed using high-resolution transmission electron microscope (HRTEM).

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.2
• /
• pp.45-50
• /
• 2015

Compositionally graded AlGaN epilayer was grown by HVPE (hydride vapor phase epitaxy) on (0001) c-plane sapphire substrate. During the growth of graded AlGaN epilayer, the temperatures of source and the growth zone were set at $950^{\circ}C$ and $1145^{\circ}C$, respectively. The growth rate of graded AlGaN epilayer was about 100 nm/hour. The changing of Al contentes was investigated by field emission scanning electron microscope (FE-SEM) and energy dispersive spectroscopy (EDS). From the result of atomic force microscope (AFM), the average of roughness in 2 inch substrate of graded AlGaN epilayer was a few nanometers scale. X-ray diffraction (XRD) with the result that the AlGaN (002) peak ($Al_{0.74}Ga_{0.26}N$) and AlN (002) peak were appeared. It seems that the graded AlGaN epilayer was successfully grown by the HVPE method. From these results, we expect to use of the graded AlGaN epilayer grown by HVPE for the application of electron and optical devices.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.391-392
• /
• 2012

In these days, the desire for the precise and tiny displays in mobile application has been increased strongly. Currently, laser displays ranging from large-size laser TV to mobile projectors, are commercially available or due to appear on the market [1]. In order to achieve a mobile projectors, the semiconductor laser diodes should be used as a laser source due to their size and weight. In this presentation, the continuous etch characteristics of Pd and AlGaN/GaN superlattice for the fabrication of blue laser diodes were investigated by using inductively coupled $CHF_3$ and $Cl_2$ -based plasma. The GaN laser diode samples were grown on the sapphire (0001) substrate using a metal organic chemical vapor deposition system. A Si-doped GaN layer was grown on the substrate, followed by growth of LD structures, including the active layers of InGaN/GaN quantum well and barriers layer, as shown in other literature [2], and the palladium was used as a p-type ohmic contact metal. The etch rate of AlGaN/GaN superlattice (2.5/2.5 nm for 100 periods) and n-GaN by using $Cl_2$ (90%)/Ar (10%) and $Cl_2$ (50%)/$CHF_3$ (50%) plasma chemistry, respectively. While when the $Cl_2$/Ar plasma were used, the etch rate of AlGaN/GaN superlattice shows a similar etch rate as that of n-GaN, the $Cl_2/CHF_3$ plasma shows decreased etch rate, compared with that of $Cl_2$/Ar plasma, especially for AlGaN/GaN superlattice. Furthermore, it was also found that the Pd which is deposited on top of the superlattice couldn't be etched with $Cl_2$/Ar plasma. It was indicating that the etching step should be separated into 2 steps for the Pd etching and the superlattice etching, respectively. The etched surface of stacked Pd/superlattice as a result of 2-step etching process including Pd etching ($Cl_2/CHF_3$) and SLs ($Cl_2$/Ar) etching, respectively. EDX results shows that the etched surface is a GaN waveguide free from the Al, indicating the SLs were fully removed by etching. Furthermore, the optical and electrical properties will be also investigated in this presentation. In summary, Pd/AlGaN/GaN SLs were successfully etched exploiting noble 2-step etching processes.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.3
• /
• pp.214-218
• /
• 2020

In this study, Mg_xZn_1-xO thin films, which can be applied not only to active layers of light-emitting devices (LEDs), such as UV-LEDs, but also to solar cells, high mobility field-effect transistors, and power semiconductor devices, are fabricated using the sol-gel method. ZnO and Mg_0.3Zn_0.7O solution synthesized by the sol-gel method and the thin film were grown by spin coating on a Si (100) substrate and sapphire substrate. The solutions are synthesized by dissolving precursor materials in 2-methoxyethanol (2-ME) solvent, and then monoethanolamine (MEA) was added to the mixed solution as a sol stabilizer. Zinc acetate dihydrate is used as a ZnO precursor, while Mg nitrate hexahydrate and Mg acetate tetrahydrate are used as an MgO precursor. Then, the optical and structural characteristics of the fabricated thin films are compared. The molar concentration of the Zn precursor in the solvent is fixed at 0.3 M, and the amount of the Mg precursor is 30% of Mg²⁺/Zn²⁺. The optical characteristics are measured using an UV-vis spectrophotometer, and the transmittance of each wavelength is measured. Structural characteristics are measured using X-ray diffraction (XRD) and transmission electron microscopy (TEM). Composition analyses are performed using energy dispersive X-ray spectroscopy (EDS). The Mg_0.3Zn_0.7O thin film was well formed at the ratio of the Mg precursor added regardless of the type of Mg precursor, and the c-axis of the thin film was decreased, while the band gap was increased to 3.56 eV.

• Korean Journal of Materials Research
• /
• v.33 no.12
• /
• pp.525-529
• /
• 2023

β-Ga₂O₃ has become the focus of considerable attention as an ultra-wide bandgap semiconductor following the successful development of bulk single crystals using the melt growth method. Accordingly, homoepitaxy studies, where the interface between the substrate and the epilayer is not problematic, have become mainstream and many results have been published. However, because the cost of homo-substrates is high, research is still mainly at the laboratory level and has not yet been scaled up to commercialization. To overcome this problem, many researchers are trying to grow high quality Ga₂O₃ epilayers on hetero-substrates. We used diluted SiH4 gas to control the doping concentration during the heteroepitaxial growth of β-Ga₂O₃ on c-plane sapphire using metal organic chemical vapor deposition (MOCVD). Despite the high level of defect density inside the grown β-Ga₂O₃ epilayer due to the aggregation of random rotated domains, the carrier concentration could be controlled from 1 × 10¹⁹ to 1 × 10¹⁶ cm^-3 by diluting the SiH4 gas concentration. This study indicates that β-Ga₂O₃ hetero-epitaxy has similar potential to homo-epitaxy and is expected to accelerate the commercialization of β-Ga₂O₃ applications with the advantage of low substrate cost.