• Tribology and Lubricants
• /
• v.16 no.3
• /
• pp.173-181
• /
• 2000

Friction, wear and corrosion characteristics of various MoS$_2$ bonded film lubricants were investigated to apply them to automotive wheel joints. MoS$_2$ bonded film lubricants were formulated by combinations of several additives and binders, and they were coated onto the pre-treated surfaces of specimens. Friction and wear characteristics were evaluated with Falex pin & vee-block test and LFW-1 block-on-ring test. For the corrosion resistant characteristics of the films, salt solution spray corrosion tests were performed. Results showed that MoS$_2$ bonded films containing both inorganic and organic corrosion-resistant additives yielded a synergy effect on anti-corrosion resistance. Also, binders having the better water-proof and thermal stability showed the lower friction and higher corrosion resistance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.6
• /
• pp.95-103
• /
• 2013

Half Cell Potential (HPC) technique has been widely adopted for its quantitative evaluation of corrosion possibility. In this study, RC specimens with three different cover depths (10mm, 30mm, and 60mm) and w/c ratios (0.35, 0.55, and 0.70) are prepared and accelerated salt spray test (SST) is performed for 45 days. Steel corrosion occurs in the specimens with 0.55 of w/c and 10mm of cover depth. In the case of 0.70 of w/c and 30mm of cover depth, steel corrosion is also monitored. Considering the effect of cover depth and w/c ratio, HCP evaluation equation is proposed and the condition which can control steel corrosion is obtained. Furthermore, anti-corrosive conditions containing w/c ratio and cover depth are analyzed through Life 365 program and the conditions are compared with the results from this study.

• Steel and Composite Structures
• /
• v.33 no.4
• /
• pp.615-627
• /
• 2019

This paper aims to study the compressive behavior of circular hollow and concrete-filled steel tubular stub columns under simulated marine atmospheric corrosion. The specimens after salt spray corrosion were tested under axial compressive load. Steel grade and corrosion level were mainly considered in the study. The mechanical behavior of circular CFST specimens is compared with that of the corresponding hollow ones. Design methods for circular hollow and concrete-filled steel tubular stub columns are modified to consider the effect of marine atmospheric corrosion. The results show that linear fitting curves could be used to present the relationship between corrosion rate and the mechanical properties of steel after simulated marine atmospheric corrosion. The ultimate strength of hollow steel tubular and CFST columns decrease with the increase of corrosion rate while the ultimate displacement of those are hardly affected by corrosion rate. Increasing corrosion rate would change the failure of CFST stub column from ductile failure to brittle failure. Corrosion rate would decrease the ductility indexes of CFST columns, rather than those of hollow steel tubular columns. The confinement factor ${\xi}$ of CFST columns decreases with the increase of corrosion rate while the ratio between test value and nominal value shows an opposite trend. With considering marine atmospheric corrosion, the predicted axial strength of hollow steel tubular and CFST columns by Chinese standard agree well with the tested values while the predictions by Japanese standard seem conservative.

• Conservation and Restoration of Cultural Heritage
• /
• v.1 no.1
• /
• pp.29-37
• /
• 2012

The West Stone Pagoda at Gameunsaji Temple Site constructed in the 7th century is mainly composed of dark grey dacitic tuff bearing small numerous dioritic xenoliths. These xenoliths resulted in small holes due to differential weathering process from the host rocks. Physical strength of the pagoda was decreased due to weathering and damage caused by petrological, biological and coastal environmental factors. The southeastern part of the pagoda was extremely deteriorated that the rock surface showed exfoliation, fracture, open cavity, granular decomposition of minerals and salt crystallization by seawater spray from the eastern coast. The stone blocks were intersected by numerous cracks and contaminated by subsequent material such as cement mortar and iron plates. Also, the pagoda was colonized by algae, fungi, lichen and bryophytes on the roof rock surface and the gaps between the blocks. As a result of ultrasonic test, the rock materials fell under Highly Weathered Grade (HW) or Completely Weathered Grade (CW). Thus, conservational intervention is essentially required to prevent further weakening of the rock materials.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.25 no.1
• /
• pp.85-92
• /
• 2011

The role of RCDs(Residual Current Protective Device) that are installed before the load is very important for preventing electric shock and electrical fire. However, although fault rate of RCD is increasing due to deterioration and long period usage, the RCD is permanently used without a checking of performance evaluation and it causes the electrical accident. In this paper, the amount of airborne chloride is researched in domestic costal area and the accelerated life test is conducted using a salt water spray tester in order to decide the life time of RCD. Aa a result of an accelerated life test, the MTTF(Mean Time To Failure) of RCD is 110.81 hours and B10 life time of RCD is 45.81 hours for the all samples. when an accelerated life test result is applied to within 2 km costal area, the life time of RCD is predicted about 5 years.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.124.2-124.2
• /
• 2016

Corrosion resistance and adhesion of electro-paint (E-paint) with fluoride conversion coating (FCC) on AZ31 Mg alloy were studied. Corrosion resistance and adhesion were studied as a function of FCC-treatment time and concentration of FCC-bath. Aqueous hydrogen fluoride (HF) solutions, with concentrations ranging from 0.5 M to 5 M, were used to form FCC on chemically polished AZ31 Mg alloy samples for six different times; 10, 30, 60, 90, 120, and 180s. The results from salt spray test (SST) showed that corrosion resistance of E-paint appeared to decrease with increasing FCC treatment times in low concentration FCC baths. The number of blisters formed on the FCC-treated samples increased with increasing FCC treatment time of more than 1 min in low concentration (0.5 M to 1 M) solutions. On the other hand, samples treated in the 5 M HF solution for 120s showed no delamination or blistering even after 1200h of SST.

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.1455-1456
• /
• 2011

한국전력공사의 초고압 또는 고압 송변전 및 배전선로에서 알루미늄 전선을 이용한 선로에 사용되는 알루미늄 및 알루미늄 합금으로 된 금구류가 여러 종류가 있다. 이러한 선로에서 사용된 많은 알루미늄 금구류들이 시간이 지나면서 표면부식이나 임계부식이 많이 발생하여 안정적인 전기 공급에 많은 문제를 유발한다. 따라서 이러한 부식에 대한 사전검사로 이용되고 있는 염수분무 부식시험의 시험방법 및 그 결과에 대한 판정방법에 대하여 살펴보고자 한다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.189-189
• /
• 2012

여기서는 오스테나이트 스테인리스강에 내구성능을 부여하기 위하여 여러 가지 공정온도 조건 중에서 플라즈마 이온질화 처리하여 질화층을 제작하였다. 이와같은 이온질화 층들에 대해서 형성기구를 해석함을 물론 경도, 마모 및 충격 시험들의 기계적 특성과 염수분무시험(Salt Spray Test), 침지 자연전위($E_{coor}$), 전기화학적 양분극 부식 특성을 평가하였다. 이들 층은 표면, 경화 깊이, 미세조직 및 결정구조를 분석하였고, 질화층 표면의 기계적 특성 및 부식 특성과의 상관관계를 해명-정리하였다.

• Journal of the Korea Safety Management & Science
• /
• v.2 no.3
• /
• pp.197-210
• /
• 2000

In this paper, sensor ring for antilock brake system was studied using the 400 series ferrite stainless steel powder. Because of more excellent corrosion resistance and mechanical characteristics than iron, sensor ring has been manufactured by P/M(Powder Metallurgy) method 400 series ferrite stainless steel. the results are following. 1, Compared with sensor ring made by iron, 400 series ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. thus the decreasing production process has been obtained. 2. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.150-150
• /
• 2013

Al-Mg films were prepared onto steel sheet according to deposition condition by eco-friendly electron beam vacuum evaporation method. The influence of Al-Mg films on corrosion resistance was evaluated by salt spray test and electrochemical method etc.. From the experimented results, it was found that the Al-Mg films which showed good corrosion resistance tend to have fine structure with homogenious composition distribution. In addition, it was shown that the property of coating films can be improve by controlling thickness ratio and uniform distribution of intermetallic compounds in Al-Mg films.