• Journal of the Korean Society for Heat Treatment
• /
• v.32 no.1
• /
• pp.12-16
• /
• 2019

In this study, strain-controlled low cycle fatigue test for hot rolled STS304 steel was carried out at $400^{\circ}C$ and $600^{\circ}C$, respectively. High temperature fatigue test was done using an electric furnace attached on the hydraulic fatigue test machine. The results of this study show that STS304 hot rolled steel has excellent static strength and fatigue characteristics. The hysteresis loop at half life was obtained in order to calculate the elastic and plastic strain. Also, Relationship between strain amplitude and fatigue life was examined in order to predict the low cycle fatigue life of STS304 steel by Coffin-Manson equation.

• Korean Journal of Metals and Materials
• /
• v.47 no.4
• /
• pp.235-241
• /
• 2009

The STS304 stainless steel was oxidized isothermally and cyclically at temperatures between 1050 and $1200^{\circ}C$ for 1 hr in air. During isothermal oxidation, it displayed good oxidation resistance at $1050^{\circ}C$. However, it suffered from breakaway oxidation above $1100^{\circ}C$, being accompanied with internal oxidation. During cyclic oxidation, it also displayed good oxidation resistance at $1050^{\circ}C$, but it suffered from massive weight loss above $1125^{\circ}C$. The oxide scales formed consisted primarily of $Fe_2O_3$, $Fe_3O_4$ with and without $Cr_2O_3$. They were generally non-adherent.

• Journal of Welding and Joining
• /
• v.9 no.4
• /
• pp.28-39
• /
• 1991

The change of microstructure in the bonded interlayer and mechanical properties of the joints were investigated during Transient Liquid Phase Diffusion Bonding(TLP bonding) of STS304/SM17C and STS304/SM45C couples using Ni base amorphous alloys added boron and prepared alloy as insert metal. Main experimental results obtained in this study are as follows: 1) Isothermal solidification process was completed much faster than theoretically expected time, 14ks at 1473K temperature. Its completion times were 3.6ks at 1423K, 2.5ks at 1473K and 1.6ks at 1523K respectively. 2) As the concentration of boron in the insert metal increased, the more borides were precipitated near bonded interlayer and grain boundary of STS304 side during isothermal solidification process, its products were $M_{23}P(C,B)_6}_3)$ The formation of grain boundary during isothermal solidification process was completed at structural carbon steel after starting the solidfication at STS304 stainless steel. 4) The highest value of hardness was obtained at bonded interface of STS304 side. The desirable tensile properties were obtained from STS304/SM17C, STS304/SM45C using MBF50 and experimentally prepared insert metal with low boron concentration.

• Journal of Ocean Engineering and Technology
• /
• v.26 no.4
• /
• pp.64-69
• /
• 2012

Laser welding was carried out on austenitic 304 (STS 304) and 22 APU stainless steels. In this case, the differences between the corrosion characteristics of the welding zones of the two stainless steels were investigated using electrochemical methods. The Vickers hardness values of the weld metal (WM) zones in both cases, the STS 304 and 22 APU stainless steels, showed relatively higher values than those of other welding zones. The corrosion current densities of the heat affected zone (HAZ) of the 22 APU and the base metal (BM) zone of the STS 304 exhibited the highest values compared to the other welding zones. It is generally accepted that when STS 304 stainless steel is welded using a general welding method, intergranular corrosion is often observed at the grain boundary because of its chromium depletion area. However, when laser welding was performed on both the STS 304 and 22 APU stainless steels, no intergranular corrosion was observed at any of the welding zones. Consequently, it is considered that the intergranular corrosion of stainless steel can be controlled with the application of laser welding.

• Proceedings of the KWS Conference
• /
• 2000.04a
• /
• pp.87-90
• /
• 2000

• Journal of the Korean institute of surface engineering
• /
• v.51 no.4
• /
• pp.218-223
• /
• 2018

In this study, we proposed a new ultrasonic-chemical decontamination process for decontaminating radioactive corrosion products during the maintenance of reactor coolant pump (RCP). The actual decontamination process was reproduced in the laboratory. And the corrosion characteristics of stainless steel (STS), constituting the RCP interior parts, were examined. The weight-loss measurment and polarization experiment were carried out in order to determine the corrosion characteristics of STS 304 and STS 415 by repeated decontamination processes. The STS 304 presented a little corrosion damage, which was almost indistinguishable from visual observation. The weight-loss rate of STS 304 was also significantly lower. On the other hand, STS 415 showed severe corrosion damage on its surface, greater weight-loss rate and higher corrosion current density than STS 304.

• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.6
• /
• pp.311-317
• /
• 2007

This study examined the phase changes, nitride precipitation and variation in mechanical properties of STS 304, STS 321 and STS 316L austenitic stainless steels after high temperature gas nitriding (HTGN) at temperature ranges from $1050^{\circ}C\;to\;1150^{\circ}C$. Fine round type of $Cr_2N$ nitrides were observed in the surface layers of 304 and 316L steels, even more in STS 321. Additionally, square type of TiN was found in STS 321 austenitic matrix too. As a result of many precipitates in the surface layer of the STS 321, it was seen $370{\sim}470Hv$ hardness variation depending on the HTGN treatment conditions, and interior region of austenite represented 150Hv. The surface hardness value of STS 304 and STS 316L showed $255{\sim}320Hv$, respectively. The nitrogen content was shown 0.27, 1.7 and 0.4% respectively at the surface layers of the STS 304, STS 321 and STS 316L. After the HTGN it was shown the improvement of corrosion resistance of the STS 321 and STS 316L compared with solution annealed steels in the solution of 1N $H_2SO_4$ whereas the STS 304 was not.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.5
• /
• pp.297-302
• /
• 2018

The important drawback of hardware fasteners consisted of 304 stainless steel (STS) is a frequent galling caused by a combination of friction and adhesion between the sliding surface. To improve the anti-galling effect, Sn-Al coatings by a thermal diffusion have been developed. The thermal diffusion by pack cementation with an $AlCl_3$ activator at $250^{\circ}C$ for 1 hour produced an Sn-Al alloy coating layer with an average thickness of $9.9{\pm}0.5{\mu}m$ on the surface of 304 STS fasteners. Compared with the galling frequency of the 304 STS fasteners, Sn-Al coatings on the surface of 304 STS fasteners demonstrated about 2.8-time reduction of the galling frequency.

• International journal of steel structures
• /
• v.18 no.4
• /
• pp.1139-1152
• /
• 2018

Many studies on the application of stainless steels as structural materials in buildings and infra-structures have been performed thanks to superior characteristics of corrosion resistance, fire resistance and aesthetic appeal. Experimental investigation to estimate the ultimate strength and fracture mode of the fillet-welded connections of cold-formed austenitic stainless steel (STS304L) with better intergranular corrosion resistance than that of austenitic stainless steel, STS304 commonly used has carried out by authors. Specimens were fabricated to fail by base metal fracture not weld metal fracture with main variables of weld lengths according to loading direction. All specimens showed a block shear fracture mode. In this paper, finite element analysis model was developed to predict the ultimate behaviors of welded connection and its validity was verified through the comparison with test results. Since the block shear behavior of welded connection due to stress triaxiality and shear-lag effects is different from that of bolted connection, stress and strain distributions in the critical path of tensile and shear fracture section were investigated. Test and analysis strengths were compared with those by current design specifications such as AISC, EC3 and existing researcher's proposed equations. In addition, through parametric analysis with extended variables, the conditions of end distance and longitudinal weld length for block shear fracture and tensile fracture were suggested.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.2
• /
• pp.89-96
• /
• 2001

N- or O-doped STS304 stainless films were synthesized by an unbalanced magnetron sputtering process with various argon and reactive gas ($N_2$, $O_2$) mixtures. These films were examined by scanning electron microscopy (SEM), X-ray diffraction (XRD), Auger electron spectroscopy (AES) and Knoop microhardness tester. The Results from X-ray diffraction (XRD) analysis showed that a STS304 stainless steel film synthesized without reactive gas using a bulk STS304 stainless steel target had a ferrite bcc structure ($\alpha$ phase), while the N-doped STS304 stainless film was consisted of a nitrogen supersaturated fcc structure, which hsa a strong ${\gamma}$(200) phase. In the O-doped films, oxide Phases ($Fe_2$$O_3$ and $Cr_2$$O_3$) were observed from the films synthesized under an excess $O_2$ flow rate of 9sccm. AES analysis showed that nitrogen content in N-doped films increased as the nitrogen flow rate increased. Approximately 43 at.%N in the N-doped film was measured using a nitrogen flow rate of 8sccm. In O-doped film, approximately 15 at.%O was detected using a $O_2$ flow rate of 12sccm. the Knoop microhardness value of N-doped film using a nitrogen flow rate of 8 sccm was measured to be approximately $H_{ k}$ 1200 and this high value could be attributed to the fine grain size and increased residual stress in the N-doped film.