• Journal of Powder Materials
• /
• v.29 no.4
• /
• pp.309-313
• /
• 2022

In this study, additive manufacturing of a functionally graded material (FGM) as an alternative to joining dissimilar metals is investigated using directed energy deposition (DED). FGM consists of five different layers, which are mixtures of austenitic stainless steel (type 316 L) and low-alloy steel (LAS, ferritic steel) at ratios of 100:0 (A layer), 75:25 (B layer), 50:50 (C layer), 25:75 (D layer), and 0:100 (E layer), respectively, in each deposition layer. The FGM samples are successfully fabricated without cracks or delamination using the DED method, and specimens are characterized using optical and scanning electron microscopy to monitor their microstructures. In layers C and D of the sample, the tensile strength is determined to be very high owing to the formation of ferrite and martensite structures. However, the elongation is high in layers A and B, which contain a large fraction of austenite.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.2
• /
• pp.16-22
• /
• 2006

Stainless steel has widely been used in various industrial fields because it has high corrosion resistance. But, we have little design data about the creep life prediction of SUS316L stainless steel. Therefore, in this study, a series of creep tests and study on them under 16 constant stress and temperature combined conditions have been performed to get the creep design data and life prediction of SUS316L stainless steels and we have gotten the following results. First, the stress exponents decrease as the test temperatures increase. Secondly, the creep activation energy gradually decreases as the stresses become bigger. Thirdly, the constant of Larson-Miller parameters on this alloy is estimated about 10. And last, the creep rupture fractographs show the intergranular ductile fracture with many dimples.

• Journal of Advanced Marine Engineering and Technology
• /
• v.33 no.4
• /
• pp.539-544
• /
• 2009

The constraint effect $A_2$ has to be evaluated within plastic region near crack tip front using opening displacement. Plastic boundary and stress or strain conditions in the vicinity of the crack tip using recrystallization heat treatment was represented. It was found that the plastic deformation boundary by recrystallization heat treatment method was the true strain of ${\epsilon}t$ = 0.05mm/mm. With the estimation of constraint effects $A_2$, the region of proper displacement measurement point near crack tip was between 0mm and 1mm distance toward direction of crack propagation, and was between 1mm to 3mm distance toward direction of load line.

• Proceedings of the KWS Conference
• /
• 1999.05a
• /
• pp.81-83
• /
• 1999

• Proceedings of the KWS Conference
• /
• 1999.05a
• /
• pp.88-90
• /
• 1999

• Journal of Welding and Joining
• /
• v.33 no.4
• /
• pp.37-43
• /
• 2015

Characteristics of dissimilar metal welds between STS 316L and carbon steel ASTM A516 Gr.70 made with GTAW have been evaluated in terms of microstructure, ferrite content, chemical analysis, hardness and corrosion resistance. Three heat inputs of 9.00, 11.25, 13.00kJ/cm were employed to make joints of dissimilar metals with ER309 wire. Based on microstructural examination, the amount of vermicular type of ${\delta}$-ferrite was increased with increasing heat input due to the increase of Creq/Nieq in the second layer of welds. Based on the EDX analysis of weld metals, Cr and Ni content in the 2nd layer increased while those content in the first layer of welds decreased with heat inputs. Cellular solidification mode in the 1st layer and dendritic solidification mode in the 2nd layer due to different cooling rates were prevailed, respectively. Heat affected zone which formed hard microstructure showed higher hardness than the weld metal. The salt spray test of dissimilar metals weld joints showed that the carbon steel surfaces only corroded. The weight loss rate due to corrosion increased up to 100hours but it decreased above 100 hours. There was little difference in the weight loss caused by corrosion regardless of heat inputs.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.1
• /
• pp.38-42
• /
• 2008

316L stainless steel welding tube was electrolytically polished and the inner surface characteristics of the tube were tested. Electro-polishing variables such as current, voltage, concentration of electrolyte and electropolishing time were changed to seek for optimum condition. These makes a optimum conditions for the electro-polishing as 4000 A, 9 V, 1.7 specific gravity of electrolyte, and 30 minute of electro-polishing time. It makes the surface roughness as Ra < $0.25{\mu}m$. XPS test resulted as the ratio of CrO/FeO equals or more to 3/1. AES test resulted as the thickness of CrO film of $38{\AA}$. DTA test resulted as the tube did not react with $N_2,\;H_2\;and\;O_2$ gas below 1073K. As summarize above results, the electro- polished 316L stainless steel welding tube satisfied the conditions to apply as a pipeline for semi- conductor production facility and clean room.

• Journal of Power System Engineering
• /
• v.14 no.2
• /
• pp.71-77
• /
• 2010

This paper was studied on microstructure, mechanical properties and corrosion characteristics of 316L stainless steel pipe welds was fabricated by orbital welding process. S-Ar specimen was fabricated by using Ar purge gas and S-$N_2$ specimen was fabricated by using $N_2$ purge gas. Ferrite was not detected in weld metal of S-$N_2$ specimen but the order of 0.13 Ferrite number(FN) was detected in weld metal of S-Ar specimen. Oxygen and Nitrogen concentration of S-$N_2$ specimen was higher than S-Ar specimen on HAZ and inner bead. The welds microstructural characteristics of S-Ar and S-$N_2$ specimens are similar. The microvickers hardness values of S-Ar and S-$N_2$ specimens welds were similar and average values of each regions were in the range of 174~194. The microstructures of S-Ar and S-$N_2$ weld metal were full austenite by primary austenite solidification. The Solidification structures of S-Ar and S-$N_2$ weld metal were formed directional dendrite toward bead center. The potentiodynamic polarization curve of STS 316L pipe welds exhibited typical active, passive, transpassive behaviour. Corrosion current density$(I_{corr.})$ and corrosion rate values of S-Ar specimen in 0.1M HCl solution were $0.95{\mu}A/cm^2$ and $0.31{\mu}A$/year respectively. The values of S-$N_2$ specimen were $1.4{\mu}A/cm^2$ and $0.45{\mu}m$/year.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.1
• /
• pp.53-63
• /
• 2002

Ni coating was carried out by pulse plating at room temperature. So, experimental conditions for Ni-coating were based on Watt's bath, and new additives(propionic acid) were introduced in the Watt's bath electrolyte as $H_3$$BO_3$ alternatives. By adding propionic acid, coating layer demonstrated a good adhesion and uniformity without special pre-treatment of the 316L stainless steel at room temperature. With a decrease of amount of propionic acid and applied average current density, cathode current efficiency increased. Also, edge effect was decreased with decreasing a peak current and increasing a pulse frequency in the same bath condition. It was found that the optimum condition for Ni coating was a current density of 10~20mA/$\textrm{cm}^2$ at below 500 mA peak current in the $5m\ell/\ell$ propionic acid solution.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.19 no.2
• /
• pp.102-108
• /
• 2023

A Chloride-induced stress corrosion cracking (CISCC) of austenite stainless steel in dry cask storage system (DCSS) can occur with extending service time than originally designed. Cold spray coating (CSC) not only form a very dense microstructure that can protect from corrosive environments, but also can generate compressive stress on the surface. This characteristic of CSC process is very helpful to increase the resistance for CISCC. CSC with several powders, such as 304L, 316L and Ni can be optimized to form very dense coating layer. In addition, the impact energy generated as the CSC powder collides with the surface of base metal at a speed of Mach 2 or more can remove the residual tensile stress of welding area and serve the compress stress. CSC layers include no oxidation and no contamination with under 0.2% porosity, which is enough to protect from the penetration of corrosive chloride. Therefore, the CSC coating layer can be accompanied by a function that can be disconnected from the corrosive environment and an effect of improving the residual stress that causes CISCC, so the canister's CISCC resistance can be increased.