• Transactions of Materials Processing
• /
• v.27 no.5
• /
• pp.267-275
• /
• 2018

The clad sheet material is produced by a roll-bonding process of one or more materials with different properties. Good formability of clad sheet material is an essential property in to deform a clad metal sheet into a part or component. Performance of the clad sheet material largely depends on interfacial bond strength between different materials. In this study, interfacial bond strength of STS/Al clad sheet was analyzed by varying experimental parameters using a blanking process. Experimental parameters are the punching speed, clearance, and stacking order of plate materials. In addition, blanking test results were compared with bond strengths measured by the T-peel test, that analyzes interface bonding strength of the standard clad sheet. The blanking process was analyzed by the finite element method under the sticking condition of interface of different materials, and experimental results and analysis results were compared.

• Korean Journal of Metals and Materials
• /
• v.49 no.11
• /
• pp.910-915
• /
• 2011

The microstructures and mechanical properties of roll-bonded STS439/Al1050/STS304 clad materials were investigated after an annealing process at various temperatures. Interfacial layer was developed at the STS439/Al1050 and Al1050/STS304 interfaces at $550^{\circ}C$. STS439/Al1050/STS304 clad metals fractured suddenly in a single step and the fracture decreased with increasing annealing temperatures at $450^{\circ}C$. After annealing at $550^{\circ}C$, samples fractured in three steps with each layer fracturing independently. Interfacial layers formed at $550^{\circ}C$ with a high Vickers microhardness were found to be brittle. During tensile testing, periodic parallel cracks were observed at the interfacial reaction layer. Observed micro-void between Al1050 and the interfacial layer was found to weaken the Al1050/reaction layer interface, leading to the total separation between Al1050 and the reaction layer.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1998.06b
• /
• pp.8-18
• /
• 1998

The effect of press warm forming in cylindrical deep drawing of stainless-aluminum clad sheet metals are examined . The temperature of die and blank holder is varied from room temperature to 20$0^{\circ}C$, while the punch is kept cooled during test to increase the fracture strength of workpiece on the punch corner area. Test materials chosen for experiments are STS304-Al050-STS304, STS304-A1050-STS430-, STS304 and Al050 metals and teflon film as a lubricant is used on both sides of a workpiece. The limit drawing ration as well as quality of drawn cups (distribution of thickness and hardness)are investigated and discussed.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.05a
• /
• pp.221-224
• /
• 2004

The clad samples of five plies of sheets comprising ferritic stainless steel (STS) and aluminum (Al) were prepared by roll-cladding at $350^{\circ}C$. The evolution of strain states and textures during roll-cladding of STS430/AA3003/AA3003/AA3 003/STS430 and STS430/AA3003/STS430/AA3003/STS430 was investigated by measurements of crystallographic textures and by simulations with the finite element method (FEM). Because the deformation mainly occurs in the Al layer during roll-cladding, the present investigation was focused on the Al layers located. The stacking sequence of sheet materials in the clad samples played an important role in the evolution of strain states during roll-cladding.

• Transactions of Materials Processing
• /
• v.14 no.1 s.73
• /
• pp.37-42
• /
• 2005

In order to invstigate the influence of die design variables on the quality of the sheared surface in cutting of sandwich sheet metals, the cut-off operation is carried out, which is the typical shearing process in sheet metal forming technology. For experiments we made the cut-off die which can be easily adjusted for die design variables such as blankholding force, pad force and clearance. The sandwich sheet metals considered are clad304(STS304-Al1050-STS304) and anti-vibration sheet metal. The shearing process is visualized by the computer vision system installed in front of the cut-off die and the sheared surface is measured and quantitatively compared with the help of the optical microscope after cut-off operation. From test results it is shown that the shearing mechanisms are different according the material of which sandwitch sheet metal is composed. The influence of die design variable is explored and we found optimal conditions for both sandwich sheet metals. It is expected that this investigation can be utilized to get the better sheared surface.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.05a
• /
• pp.57-61
• /
• 2004

in order to improve the quality of the sheared surface in cutting of sandwich sheet metals the cut-off operation is mainly investigated which is the typical shearing process in sheet metal forming technology. For experiments the cut-off die is made which can be easily adjusted by die design variables such as blankholding force, pad force, and clearance. The sheet metals chose as specimen are clad304(STS304-Al1050-STS304) and anti-vibration sheet metal. The shearing process is visualized by the computer vision system installed in front of the cut-off die and the sheared surface before and after cut-off operation is measured and quantitatively compared with the help of the optical microscope. From test results the good sheared surface was shown when the clearance gets small with large blankholding force.

• Transactions of Materials Processing
• /
• v.11 no.6
• /
• pp.482-486
• /
• 2002

Sandwich sheets composed of stainless steel/aluminum/stainless steel were produced by roll cladding. In order to investigate the effect of the friction between roll and cladding sample, the lubrication condition of the roll surface was varied. Clad rolling without lubrication gave rise to a small increment of the normal strain of aluminum in the rolling direction. This experimental result was confirmed by FEM modeling. Through-thickness hardness gradients in the mid aluminum layer was successfully explained by variations of the strain state through thickness layers. FEM modeling implied that cladding without lubrication led to a large shear strain variation at the surface of aluminum layer.

• Transactions of Materials Processing
• /
• v.20 no.3
• /
• pp.257-264
• /
• 2011

Multilayer(clad) sheets, composed of two or more materials with different properties, are fabricated using the roll-bonding process. A good formability is an essential property for a multilayered sheet in order to manufacture parts by plastic deformation. In this study, the influences of temperature and strain rate on the plastic properties of stainless steel-aluminum-magnesium multilayered(STS-Al-Mg) sheets were investigated. Tensile tests were performed at various temperatures and strain rates on the multilayered sheet and on each separate layer. Fracture of the multilayered sheet was observed to be temperature-dependent. At the base temperature of $200^{\circ}C$, all materials fractured simultaneously. At lower temperatures, the Mg alloy sheet fractured earlier than the other materials. Conversely, the other materials fractured earlier than the Mg alloy sheet at higher temperatures. The uniform and total elongations of the multilayered sheet were observed to be higher than that of each material at a temperature of $250^{\circ}C$. Larger uniform elongations were obtained for higher strain rates at constant temperature. The same trend was observed for the Mg alloy sheet, which exhibited the lowest elongation among the three materials. The tensile strengths and elongations of the single layer sheets were compared to those of the multilayer material. The strength of the multilayered sheet was successfully calculated by the rule of mixture from the values of each single layer. However, no simple correlation between the elongation of each layer and that of the multilayer was obtained.