The influence of co-existing gases on the hydrogen permeation without sweep gas was studied through a Pd-coated $V_{99.8}B_{0.2}$ alloy membrane. Membranes have been investigated in the pressure range 1.5-8.0 bar under pure hydrogen, hydrogen-carbon dioxide and hydrogen-carbon monoxide gas mixture without sweep gas at $400^{\circ}C$. Preliminary hydrogen permeation experiments without sweep gas have been confirmed that hydrogen flux was $40.7mL/min/cm^2$ for a Pd-coated $V_{99.8}B_{0.2}$ alloy membrane (thick : 0.5 mm) using pure hydrogen as the feed gas. In addition, hydrogen flux was $21.4mL/min/cm^2$ for $V_{99.8}B_{0.2}$ alloy membrane using $H_2/CO_2$ as the feed gas. The hydrogen permeation flux decreased with decrease of hydrogen partial pressure irrespective of pressure when $H_2/CO_2$and $H_2/CO$mixture applied as feed gas respectively and permeation fluxes were satisfied with Sievert's law in different feed conditions. It was found from XRD, SEM/EDX results after permeation test that the Pd-coated $V_{99.8}B_{0.2}$ alloy membrane had good stability and durability for various mixtures feeding condition.

• Journal of Adhesion and Interface
• /
• v.4 no.1
• /
• pp.28-34
• /
• 2003

Steel tire cords were subjected to plasma polymerization coating of acetylene in order to enhance the adhesion to rubber compounds. Plasma polymerization coating was varied to plasma polymerization coating of acetylene, argon plasma etching+plasma polymerization, or argon plasma. etching+plasma polymerization with Ar carrier gas. Adhesion was evaluated via TCAT samples and compared to those with brass coated tire cord. For durability study, plasma polymer cooled tire cords were aged in lab atmosphere for 1, 3, 5, 10 or 15 days, while TCAT specimens prepared with plasma polymer coated tire cords were aged in distilled water, 10% NaCl solution or $100^{\circ}C$ oven for 1, 2, 3 or 4 weeks. After testing, failure surfaces were analyzed with SEM/EDX. Among the treatments, the highest adhesion was obtained by Ar etching+acetylene plasma. polymerization coating with Ar carrier gas, providing almost same pull-out force as the brass coated tire cords. Upon the aging of the tire cords in the lab atmosphere, brass coated tire cords provided better adhesion than plasma polymer coated tire cords, while the TCAT samples with plasma polymer coated tire cords exhibited similar or slightly superior durability to those with brass coated tire cords.

• Polymer(Korea)
• /
• v.38 no.1
• /
• pp.74-79
• /
• 2014

Microfibrillated cellulose (MFC) was chemically modified with two different silane coupling agents (3-aminopropyltriethoxysilane and 3-mercaptopropyltriethoxysilane) and lauroyl chloride. The surface modification of MFC was confirmed by infrared spectroscopy (FTIR), energy dispersive X-ray spectroscopy (EDX), and contact angle measurements. Composite paper was successfully prepared with surface modified MFC and polyamide (PA) fiber. The surface modification of MFC not only prevented aggregation of MFC but also improved adhesive property between PA fiber and surface modified MFC. It was impossible to prepare papers of only PA fiber because there is no binder to connect PA fibers. That is, surface modified MFC as a binder in PA fiber played a crucial role in making composite paper. Composite paper with silane modified MFC showed higher tensile strength and modulus than composite paper with lauroyl moiety modified MFC. The structure, morphology, and mechanical properties of composite paper were analyzed by scanning electron microscope (SEM) and universal testing machine (UTM).

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.17 no.2
• /
• pp.127-137
• /
• 2019

Zr electrorefining is demonstrated herein using Zirlo tubes in a chloride-fluoride mixed molten salt in the presence of $AlF_3$. Cyclic voltammetry reveals a monotonic shift in the onset of metal reduction kinetics towards positive potential and an increase in intensity of the additional peaks associated with Zr-Al alloy formation with increasing $AlF_3$ concentration. Unlike the galvanostatic deposition mode, a radial plate-type Zr growth is evident at the top surface of the salt during Zr electrorefining at a constant potential of -1.2 V. The diameter of the plate-type Zr deposit gradually increases with increasing $AlF_3$ concentration. Scanning electron microscopy-energy-dispersive X-ray spectroscopy (SEM-EDX) and X-ray photoelectron spectroscopy (XPS) analyses for the plate-type Zr deposit show that trace amount of Al is incorporated as Zr-Al alloys with different chemical compositions between the top and bottom surface of the deposit. Addition of $AlF_3$ is effective in lowering the residual salt content in the deposit and in improving the current efficiency for Zr recovery.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.2A
• /
• pp.297-304
• /
• 2008

It is well known that cracks in concrete decrease permeability and durability of concrete because cracks enhance the penetration of water or corrosive chemicals like as chlorides, carbon dioxides, sulfates and some others. But some of cracks in hardened cements may be sealed in case of contacting water. This phenomenon is called "self healing" and it has a close relation to hydration products newly formed on surfaces of cracks. Many studies on self healing in concretes commonly showed that CSH gel has been observed on crack surfaces. And some studies have reported that calcium hydroxides and ettringite were observed as well as CSH gel on crack surfaces. This study was carried out to investigate hydration products formed by self healing process and also examine the influence of waterproof admixture for concretes on self healing of cement. As a result of XRD, DSC, SEM and EDX analysis of crack surfaces, it was found that self healing of cement was related to CSH gel, calcium hydroxides and ettringite. And waterproof admixture increased fibrous (needle-like) hydration products which were in network form. It is estimated that such fibrous products are effective for self healing process of cement system.

• Journal of the Korean Institute of Rural Architecture
• /
• v.25 no.4
• /
• pp.9-16
• /
• 2023

In this study, the status and characteristics of fine dust and its impact on neighboring areas were investigated to proactively respond to the government's environmental regulations expected in the future and to minimize the damage by the fine dust generated at construction waste intermediate treatment plants. In addition, since there are no such plants that can affect the surroundings with no houses or other waste treatment sites nearby, an independently located construction waste intermediate treatment plant was selected to compare the characteristics of fine dust with that from the construction waste intermediate treatment sites located in the downtown area. The conclusions of the study are as follows. (1) The measurement results of PM10 at 4 points in the plant showed that the location where the crushing facility was operating had an elevated level of fine dust at 80㎍/m³ on average and a maximum of 124㎍/m³, and the level rose to 110㎍/m³ at points where vehicles frequent. (2) The PM2.5 measurement results inside the plant showed that the average concentration of the reference point was 16㎍/m³ and the maximum value was 20㎍/m³, which was distributed within the management standard. (3) It was found that the average concentration of PM10 in the nearby area ranged from 28 to 38㎍/m³, which was similar to or lower than 36㎍/m³ of the reference point. Therefore, the concentration of the fine dust generated in the plant had a negligible effect on the increase in concentration of fine dust in nearby areas. (4) The heavy metal contents were measured from the filter paper collected from the plant. The PM10 was found to be about 14 to 26ng/m³, and PM 2.5 was 25 to 28ng/m³, which was the average of domestic atmospheric concentrations. (5) The SEM-EDX analysis results showed that the PM10 contained Si and O around 40% similarly for both. The SiO2, a component of silica occupied the most and C was present as CaCO3, which was assumed to be a limestone component. The remaining components included NaO, Al2O3, and CaO as trace oxides. (6) The SEM-EDX analysis results showed that the PM 2.5 contained 5 to 7% of Cl, which is a chlorine ion, and a small amount of K was detected at 2.51% in the sample from the shutdown plant.

• Composites Research
• /
• v.37 no.3
• /
• pp.238-245
• /
• 2024

In this study, as part of the development of a monitoring system for the efficient maintenance of steel pipes, an experimental study was conducted to evaluate the performance of steel pipes treated with modified polyethylene coating. In the case of the conventional mechanical pre-coating method, there was a deterioration in polyethylene adhesion during expansion testing, which led to the application of a chemical pre-treatment process using a calcium-mixed phosphate zinc film to resolve this issue. SEM and EDX analyses showed that the densest structure was observed at a Zn/Ca ratio of 1.0, and improved heat resistance compared to the conventional method was confirmed. Additionally, to prevent coating detachment during expansion, an evaluation of adhesion and elongation was conducted on steel pipes with modified polyethylene coating, incorporating materials such as elastomers based on maleic anhydride grafting, metal oxides, blocking agents, and slip agents. Experimental results showed that the specimen (S4) containing all modified materials exhibited more than a 25% performance improvement compared to the specimen (S2) containing only metal oxides. Lastly, the development and performance evaluation of wedge-shaped socketing and pressing wheels, which are part of the pipe fixing accessories, were conducted to prevent surface coating damage on the completed pipes.

• Journal of Korea Foundry Society
• /
• v.44 no.4
• /
• pp.97-102
• /
• 2024

In this study, the properties of Zr-14Cu-7.5Ni-2.6Al wide ribbon with amorphous structure and properties were analyzed using Hall effect, SEM-EDX, and XRD. Made by melt spinning method, this Zr-14Cu-7.5Ni-2.6Al based alloy ribbon is not more than 96 ㎛ thick and 100 mm wide. This amorphous alloy exhibited tensile strength of 1,641 MPa, yield strength of 1,541 MPa, elongation of 1% and elastic modulus of 98GPa. The bulk concentration, resistivity, and mobility values are midway between general heavy doping ceramics and metals, and they are about 100 times weaker than ordinary metals, so they are close to Si and have good electrical conductivity. In addition, folding tests were conducted at extreme temperatures, withstanding 150,000 times at -20℃, 300,000 times at 24℃, and 150,000 times at 60℃, with no folding defects observed. These results demonstrate the excellent durability and reliability of the Zr-14Cu-7.5Ni-2.6Al wide ribbon alloy and suggest the possibility of developing electronic products using this alloy.

• Advances in environmental research
• /
• v.9 no.3
• /
• pp.161-173
• /
• 2020

The removal of two dyes, namely Methylene Blue (MB) and Reactive Brillant Red (RR) from aqueous solution was investigated using magnetite iron coated pumice (MIP) composite in the Fenton-like oxidation process. A weight ratio of 2.5 g (with the molar ratio of Fe³⁺ to Fe²⁺ to be 2) (5%) of iron to the total pumice (50 g) was enabled during synthesis of catalyst. Surface composition and characteristics of the catalyst were assessed by SEM-EDX, FT-IR, Raman spectral analysis. The effect of the amount of pumice solely used or MIP, H₂O₂ concentration, pH and initial concentration of MB or RR dyes on Fenton-like process efficiency was investigated. EDAX spectrums of pumice and MIP showed that oxygen and silisium are the major elements. The Fe content of MIP increased to 2.24%. SEM, FT-IR and Raman spectrums confirmed the impregnation of Fe on pumice surface. The experimental results revealed that high removal rates of dyes could be obtained using MIP that demonstrated a higher stability for removal of MB dye. pH affected the removal efficiency of both dyes and the degradation of both dyes was sharply dropped when pH was increased above 4. The removal of dyes did not significantly change with increasing H₂O₂ concentration. Degradation rates of both MB and RR dyes increased 3.3 and 2.8 times with the use of MIP compared to pumice alone, respectively. Furthermore, MIP enabled a good removal efficiency at higher dye concentrations. It can be emphasized that MIP composite can be used in the heterogeneous Fenton-like systems considering the economic and easily separation aspects.

• Bulletin of the Korean Chemical Society
• /
• v.27 no.9
• /
• pp.1423-1428
• /
• 2006

In this study, we have prepared pitch binded AC (activated carbon)/$AC/TiO_2$ composites photocatalysts through carbon tetrachloride solvent method. The developed samples were characterized with surface properties, structural crystallinity between AC and $AC/TiO_2$, elemental identification and photocatalytic activity. The results of the textural surface properties demonstrate that there are slight increases in the BET surface area and adsorbed volume from adsorption isotherm of composite samples with increasing of the amount of AC. The SEM results present to the characterization of porous texture on the pitch/AC/$AC/TiO_2$ composites and homogenous compositions in the particle for all the materials used. From XRD data, a weak and broad carbon peak of graphene remained rutile peaks kept with anatase structure were observed in the X-ray diffraction patterns for the pitch/AC/$AC/TiO_2$ composites. The EDX spectra show the presence of C, O and S with strong Ti peaks. Most of these samples are richer in carbon and major Ti metal than any other elements. Finally, the excellent photocatalytic activity of the pitch/AC/$AC/TiO_2$ composites between relative concentration ($c/c_o$) of MB and UV irradiation time could be attributed to the both effects between photocatalysis of the supported $AC/TiO_2$ and adsorptivity of the two kinds of carbons.