• 한국전기전자재료학회논문지
• /
• 제22권8호
• /
• pp.671-676
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various deposition conditions. We investigated the effect of deposition condition on the surface morphology and dielectric properties of SBN thin films. The optimum of the rougness showed about 4.33 nm in 70/30 of Ar/$O_2$ ratio. The crystallinity and rougness of SBN thin films were increased with the increase of rf power. Also, Deposition rate of SBN thin films was about 4.17 nm/min in 70 W of rf power. The capacitance of SBN thin films were increased with the increase of Ar/$O_2$ ratio, rf power and deposition temperature respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.173-174
• /
• 2009

The SBN thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2/Si$) using RF sputtering method at various deposition conditions. The optimum conditions of RF power and $Ar/O_2$ ratio were 60[W] and 70/30, respectively. Also, The surface rougness showed about 4.33[nm] in RF power 60[W] and $Ar/O_2$ ratio 70/30.

• 전기학회논문지
• /
• 제59권6호
• /
• pp.1083-1086
• /
• 2010

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$ thin films were deposited on Si substrate using RF magnetron sputtering method. And the SBN thin films were annealed at 650~800$[^{\circ}C$]. The surface rougness showed about 0.42[nm] in annealed thin film at $650[^{\circ}C$]. The dielectric constant(150) of SBN thin film was obtained by annealing temperature above $700[^{\circ}C$]. The voltage dependence of dielectric loss showed a value within 0.02 in voltage ranges of -10~＋10[V]. The dielectric constant characteristics showed a stable value with the increase of frequency. Also, the SBN thin films annealed at $750[^{\circ}C$] showed a fatigue-free characteristics up to $1.0\times10^8$ cycles.

• 전기학회논문지
• /
• 제58권3호
• /
• pp.544-547
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_{2}O_{9}$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various deposition temperature. The optimum conditions of RF power and Ar/$O_2$ ratio were 60[W] and 70/30, respectively. Deposition rate of SBN thin films was about 4.17[nm/min]. The crystallinity of SBN thin films were increased with increase of deposition temperature in the temperature range of $100{\sim}400[^{\circ}C]$, the surface rougness showed about 4.33[nm]. The capacitance of SBN thin films were increased with the increase of deposition temperature.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.291-291
• /
• 2010

The SBN ceramic thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at substrate temperature of 300[$^{\circ}C$]. The grain and crystallinity of SBN thin films were increased with the increase of annealing temperature. The crystallinity of SBN thin films were increased with increase of annealing temperature in the temperature range of 600~800[$^{\circ}C$]. the surface rougness showed about 20 [nm].

• 반도체디스플레이기술학회지
• /
• 제8권2호
• /
• pp.11-14
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various $Ar/O_2$ ratio. We investigated the effect of deposition condition(specially $Ar/O_2$ ratio) on the structural properties of SBN thin film. As $Ar/O_2$ ratio was increased, the peaks in the XRD pattern became more sharp. Also, the peaks(008)(115)(220) in 80/20 of $Ar/O_2$ ratio were suddenly appeared. The optimum of the rougness showed about 4.33 nm in 70/30 of $Ar/O_2$ ratio. The crystallinity of SBN thin films were increased with the increase of $Ar/O_2$ ratio. Also, Deposition rate of SBN thin films was about 4.17 nm/min in 70/30 of $Ar/O_2$ ratio. The capacitance of SBN thin films were increased with the increase of $Ar/O_2$ ratio.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.185-186
• /
• 2008

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/SiO2/Si) using RF sputtering method at various substrate temperature. The optimum conditions of RF power and Ar/O2 ratio were 60[W] and 70/30, respectively. The rougness showed about 4.33[nm]. Deposition rate of SBN thin films was about 4.17[nm/min]. The capacitance of SBN thin films were increased with the increase of substrate temperature.

• 한국통신학회논문지
• /
• 제31권8C호
• /
• pp.786-794
• /
• 2006

본 논문에서는 초고해상도 영상을 복원하기 위한 최적화 기법으로 널리 사용되는 PCG(Preconditioned Conjugate Gradient) 기법을 위한 새로운 preconditioner를 제안하였다. 제안된 preconditioner는 기존의 블록 circulant preconditioner를 확장하여 roughness 벌칙 함수에 대해서 효과적인 수렴이 가능하도록 한 것으로써, 잡음에 민감한 기존 방법의 성능을 개선할 수 있는 것이다. 제안된 preconditioner의 성능을 확인하기 위한 실험과 시뮬레이션에서 제안된 PCG 방법은 기존 방법보다 우수한 수렴 속도를 보였다.

• 한국표면공학회지
• /
• 제29권6호
• /
• pp.745-752
• /
• 1996

Wear property of plasma spray coating in $Cr_2O_3$ powder manufatured of spray dry method on the aluminum substrate was inspected for the application of piston-ring of automotive enginel. The plama spray coatings were varied with feed rate and particle size. Used the ball-on disc type tribometer, wear volume, friction, surface rougness were investigated. The delamination of the coating layer were observed with SEM. Also the cross-section of wear track were investigated, using optical microscopy. As a result of experiment, wear mechanism was addressed in the various coating process.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.43-44
• /
• 2006

The production method of micro sacrificial plastic mold insert metal injection molding, namely ${\mu}-SPiMIM$ process has been proposed to solve specific problems involving the miniaturization of MIM. Two types of sacrificial plastic molds (SP-mold) with fine structures were used: 1) PMMA resist, 2) PMMA mold injected into Ni-electroform, which is a typical LIGA (${\underline{L}}ithographie-{\underline{G}}alvanoformung-{\underline{A}}bformung$) process. Stainless steel 316L feedstock was injection-molded into the SP-molds with multi-pillar structures. This study focused on the effects of metal particle size and processing conditions on the shrinkage, transcription and surface roughness of sintered parts.