• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.453-453
• /
• 2010

In this study, zinc germanate ($Zn_2GeO_4$) thin films has been synthesized by using radio frequency magnetron sputtering and the divalent manganese-activated luminescence was characterized. X-ray diffraction patterns of the as-deposited $Zn_2GeO_4$:Mn films showed only a broad feature, indicative of an amorphous structure. Scanning electron microscopy images revealed that the as-deposited $Zn_2GeO_4$:Mn has a smooth surface morphology. The $Zn_2GeO_4$:Mn films were found to be crystallized by annealing in air ambient at temperatures as low as $700^{\circ}C$. The annealed $Zn_2GeO_4$:Mn possessed a rhombohedral polycrystalline structure. The broad-band photoluminescent emission spectrum from 470 to 650nm was obtained at room temperature from the $Zn_2GeO_4$:Mn films. The emission peak was centered at around 535nm in the green range, which originates from the intrashell transition of manganese $3d^5$ electrons from $^4T_1$ excited-state level to the $^6A_1$ ground state. The PL emission spectrum had an asymmetric line shape, which results from the $^3d_5$ electron transitions of divalent manganese ions located at different sites of the zinc germanate host crystal lattice. Electroluminescent devices were fabricated using $Zn_2GeO_4$:Mn as an emission layer. The fabricated devices showed a green EL emission similar to the PL emission. The CIE chromaticity color coordinates of the EL emission were determined to be x=0.308 and y=0.657.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.6
• /
• pp.466-474
• /
• 2021

[011] poled ternary Pb(In_1/2Nb_1/2)O₃-Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃ (PIN-PMN-PT) single crystals have been investigated for active materials for acoustic transducers because of their high piezoelectric properties in both shear and transverse modes. In order to use [011] poled PIN-PMN-PT single crystals for acoustic transducers, the characterization of full-matrix material properties is required. In this study, full sets of compliance, dielectric, and piezoelectric constants of [011] poled rhombohedral PIN-PMN-PT were measured by a resonance method. Dimensions and geometries of 12 samples were proposed for measuring 17 independent material constants of [011] poled rhombohedral PIN-PMN-PT single crystals. Two sets of samples with different PT concentrations, 0.24PIN-0.49PMN-0.27PT and 0.24PIN-0.46PMN-0.30PT, were fabricated and their material properties were measured. Measured impedance spectra and simulated impedance spectra of the samples were compared to check the accuracy of the measurements.

• Journal of the Korean Chemical Society
• /
• v.58 no.2
• /
• pp.205-209
• /
• 2014

Hematite iron oxide (${\alpha}$-$Fe_2O_3$) nanowalls were fabricated on aluminum substrate by a facile solvent-assisted hydrothermal oxidation process. The XRD and EDS patterns indicate that the sample has a rhombohedral phase of hematite $Fe_2O_3$. FE-SEM, TEM, HR-TEM, SA-ED were employed to characterize the resulting materials. $N_2$ adsorption-desorption isotherms was used to study a BET surface area. Their capability of catalytic degradation of titan yellow GR azo dye with air oxygen in aqueous solution over $Fe_2O_3$ catalysts was studied. The result indicates that the as-prepared product has a high catalytic activity, because it has a larger surface area. Langmuir and Freundlich isotherms of adsorption dye on the catalysts surface were investigated and the decomposition of titan yellow GR follows pseudo-first order kinetic.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.29 no.4
• /
• pp.77-84
• /
• 2015

PZT ceramics, usually used pyroelectric materials exhibited a relatively highly Curie temperture(Tc) of $250-450^{\circ}C$ and permittivity constant of 500-1600. In this paper, the pyroelectric infrared detectors are applied two different types of pyroelectric materials, that is tetragonal crystal of ferroelectric $PbTiO_3$ and rhombohedral crystal of $Pb(Zr,Ti)O_3$. PZT ceramics shows not only highly Curie temperture but also excellent pyro and piezoelectric properties at the Zr/Ti(=52/48) ratio. Therefor in this paper, the pyroelectric infrared detectors are applied PZT ceramics, and obtained sensitive sensing characteristics by expriment case studies.

• Journal of the Korean Ceramic Society
• /
• v.24 no.3
• /
• pp.263-269
• /
• 1987

It is investigated that the determination of the correlation between the change of microstructure and electrical properties. Yttria is added to the compositiojn of rhombohedral region in Pb(Mg1/3Nb2./3)O3-PbTiO3-PbZrO3 ternary system. Average grian size, lattice parameters and distribution of yttrium are characterized by XRD, SEM and EDS. Electrical properties are determined by measurement of Curie temperature, piezoelectric properties and hysteresis loops. The results are as follows; 1. Both lattice parameters, a and ${\alpha}$, are changed by addition of yttria to the composition of rhomboheadral region in Pb(Mg1/3Nb2./3)O3-PbTiO3-PbZrO3 ternary system and Curie temperature is proportional to the values at (90-${\alpha}$).

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1242_1243
• /
• 2009

The heterolayered BT-BNT thick films were fabricated by screen printing techniques on alumina substrates electrodes with Pt. We report the improved ferroelectric and dielectric properties in the heterolayered teteragonal/rhombohedral structure composed of the BT and the BNT thick films. We investigated the effects of deposition conditions on the structural and electrical properties of the heterolayered BT-BNT thick films. The dielectric properties of the heterolayered BT-BNT thick films were superior to those of single composition BNT, and those values for the heterolayered BT-BNT thick films were 1455, 0.025 and $12.63{\mu}C/cm^2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.1
• /
• pp.31-38
• /
• 2004

PMN-PT, a piezoelectric single crystal, has many useful applications such as sensors and actuators. In this paper, all the elastic, piezoelectric, and dielectric constants of the PMN-32％PT single crystals were measured by the resonance method. For the rhombohedral symmetry, a total of twelve independent material constants were measured such as six elastic compliance constants at constant electric field, two dielectric constants at constant stress, and four piezoelectric constants d. Seven sets of crystal samples of each different geometry were prepared for the measurement of length-thickness extensional, thickness extensional, radial, length extensional and thickness shear modes of vibration, respectively. In order to check the validity of the measurement, experimental impedance spectrum of the PMN-PT crystal was compared with numerical data spectrum calculated with the measured material constants. The good agreement between the two spectra confirmed validity of the results in this paper.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.219-220
• /
• 2006

In this study, m order to develop multilayer ceramics vibrator for ultrasonic nozzle, PMN-PNN-PZT ceramics were fabricated using $Li_2CO_3-Na_2CO_3$ as sintering aids and their piezoelectric and dielectric characteristics were investigated according to the aomunt of PbO. With increasing PbO contents. secondary phases were increased and phase structure were changed from tetragonal structure to rhombohedral structure and also electromechanical coupling factor were linearly decreased. At the composition ceramics with the sintering temperature of $870^{\circ}C$ and 1 mol% excess PbO, density, electromechanical coupling factor, dielectric constant, piezoelectric d constant and mechanical quality factor showed the optimum value of $7.879g/cm^2$, 0.55, 1149, 328pC/N, 1224, respectively for multilayer ceramics vibrator application for ultrasonic nozzle.

• Journal of the Korean Ceramic Society
• /
• v.34 no.11
• /
• pp.1182-1186
• /
• 1997

La0.8Ca0.2Cr0.98O3 powder was prepared using the modified Pechini process. Various crystalline phases formed during thermal decomposition were investigated. (La,Ca)CrO4 phase, first formed from the precursor, was transformed to (La,Ca)CrO3 and CaCrO4 above 80$0^{\circ}C$, which remained up to 110$0^{\circ}C$. However, only (La,Ca)CrO3 phase consisting of orthorhombic and intermediate rhombohedral polymorphs was observed after sintering at 125$0^{\circ}C$. The specimens sintered at 140$0^{\circ}C$ exhibited 98% of relative density and rather wide grain size distribution with average grain size of 3-4 ${\mu}{\textrm}{m}$. Densification and grain growth of the specimens observed above 125$0^{\circ}C$ were presumably attributed to liquid phase sintering resulted from melting of Ca3(CrO4)2 phase.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.109-114
• /
• 2002

Aging stabilities of the operating frequency of piezoelectric devices such as filter, oscillator and discriminator are very important. In this study it was studied aging stabilities of the length-extensional vibration mode of Pb(Zr$\_$y/Ti$\_$1-y/)O$_3$+x[wt%]Cr$_2$O$_3$ ceramics. PZT ceramics in Morphotropic phase boundary have higher aging rates of k$\_$31/ and resonant frequency than those in tetragonal phase or rhombohedral phase. Thermal aging moves the composition with maximum aging rate to Zr-rich side in Cr not added PZT system. Aging rate of resonant frequency of the ceramics with x=0.1, y=0.53 and x=0.3, y=0.53 increased by thermal aging.