• Restorative Dentistry and Endodontics
• /
• v.18 no.1
• /
• pp.55-72
• /
• 1993

The aim of this study was to compare the marginal leakage of class II light curing composite resin restoration according to filling methods. With using acid etching technique and dentin bonding agent, various methods were suggested to eliminate or reduce the marginal leakage. In this study, class II cavities were prepared in 100 extracted human premolars with cementum margin(1mm below the CEJ) and the teeth were randomly assigned to 5 groups of 20 teeth each. The teeth in group 1, 2, 3 and 4 were restored by direct filling methods using P-50 and Clearfil Photoposterior of 10 teeth each, but the method of insertion of the restorative materials varied with each group. And the teeth in group 5 were restored by inlay method using Kulzer Inlay and CR Inlay. Filling methods are as follows : Group 1 : The composite resin was inserted in one layer in the proximal box and one layer in the occlusal portion. Group 2 : Insertion was in two equally thick horizontal layers in the proximal box. Group 3 : Insertion was in two diagonally placed layers in the proximal box. Group 4 : The composite resin was inserted in the same way as in group 3 except that a glass ionomer liner was first placed on the axial wall and gingival floor. Group 5 : The teeth were restored by Inlay technique using dure cure resin cement. All the teeth were thermocycled, stained with 1 % methylene blue solution, sectioned mesiodistally, and scored for marginal leakage. To compare the marginal leakage, ANOVA and T-test were used in analysis. The following results were obtained : 1. In direct filling methods, there was no significant difference in marginal leakage at both occlusal and cervical margins. 2. In all groups, occlusal margin showed significantly less leakage than cervical margin. 3. In group using glass ionomer liner, there was no significant reduction of marginal leakage at the cervical margin. 4. The group restored by inlay method showed significantly less marginal leakage than groups restored by direct filling methods at both occlusal and gingival margins. 5. There was no significant difference in each group according to filling materials.

• Restorative Dentistry and Endodontics
• /
• v.18 no.1
• /
• pp.84-94
• /
• 1993

The purpose of this study was to evaluate flexure strength of composite resin inlay according to heat treatment and duration in comparasion with visible light-cured resin. In this study, materials were used 1 visible light-cured resin and 3 kinds of composite resin inlays. Control group was visible light cured resin (Photo Clearfil Posterior) and experimental groups were composite resin inlays (Brilliant Dentin, Brilliant Enamel and Clearfil CR Inlay). Experimental groups were divided 3 groups: First group was Brilliant Dentin and second group was Brilliant Enamel and -third group was Clearfil CR Inlay. Used experimental groups were calculated flexural strength according to heat treatment and duration. The following results were obtained: 1. Experimental groups were higher flexural strength than control group. 2. At $100^{\circ}C$ when heat treatment carried out 7 minutes flexural strength elevated third group, second group, first group in turn and when heat treatment carried out 15 minutes flexural strength elevated third group, second group, first group in turn but no difference was showed between first and second group. 3. At $125^{\circ}C$ when heat treatment was carried out 7 minutes flexural strength elevated third group, second group, first group in turn and when heat treatment was carried out 15 minutes flexural strength elevated third group, first group, second group in turn but no difference was showed between first and second group. 4. In spite of heat treatment and duration the third group was highest flexural strength in the others groups.

• Restorative Dentistry and Endodontics
• /
• v.15 no.2
• /
• pp.122-126
• /
• 1990

To examine the microleakage of posterior esthetic restorative materials, using 2% methylene blue dye solution, dye penetration was determined with 80 permanent posterior teeth after thermocycling. The following results were obtained. 1. Amalgam group showed the most severe dye penetration of all test groups through the enamel and dentin / cementum margins. 2. Clearfil group showed much more dye penetration than P-50 at the enamel margin and than resin inlay system at the dentin / cementum margin. 3. Through the etched enamel margin, P-50 and resin inlay system groups showed no dye penetration, if any, but through the dentin / cementum margin, all test groups showed dye penetration. 4. Resin inlay system showed the least dye penetration of all test groups through the dentin / cementum margin.

• Restorative Dentistry and Endodontics
• /
• v.21 no.2
• /
• pp.619-627
• /
• 1996

There are increasing use of composite resin in the posterior teeth and the new indirect inlay technique was introduced for compensating much troubles faced in direct technique. Many researchers insisted that overall properties of restorative materials were enhanced by an additional curing but this technique still has a problems about using cement material. Resin inlay obtains retention force from friction and another adhesion to tooth structure. A shape of cavity preparation was noted but studies about cement thickness and bond strength with cavity divergency are rare. The purpose of this study is to assess the effect of cavity divergency on cement thickness and bond strength of resin inlay. Cavities, which divergency was $6^{\circ}$, $16^{\circ}$, and $26^{\circ}$ in each group, were prepared and their divergency was verified by Adobe Photoshop program through the image capture with stereo microscope and FlexCam. Inlays were fixed into the cavities with a resin cement, Superbond and were handled under chemical (in 75% ethanol for 24 hrs.) and thermal stress (500 cycles from $5^{\circ}$ to $55^{\circ}C$). MXT 70 (x400) was used for measuring the cement thickness and bond strength was evaluated with a universal testing machine. Following results were obtained : 1. The cement thickness in Mean (S.D.) were; 35.58 (10.31)${\mu}m$ in $6^{\circ}$ group, 35.97 (10.49)${\mu}m$ in $16^{\circ}$ group, and 41.43 (9.33)${\mu}m$ in $26^{\circ}$ group. But there was no significant difference between groups. 2. The bond strength in Mean (S.D.) were ; 33.18 (5.53)kg in $6^{\circ}$ group, 23.47 (13.40)kg in $16^{\circ}$ group, and 19.75 (10.48)kg in $26^{\circ}$ group. $6^{\circ}$ group showed significantly higher value compared to $16^{\circ}$ and $26^{\circ}$ groups (p<0.05). Although the results of this study indicate $6^{\circ}$ divergency will be good for resin inlay, cavity preparation with this type will have lots of difficulties in manufacturing, try-in, and cementation procedures, such as deformation. So it is concluded that $16^{\circ}$ divergent cavity preparation is recommended in resin inlay technique.

• Restorative Dentistry and Endodontics
• /
• v.25 no.1
• /
• pp.17-40
• /
• 2000

Resin cements are used for cementing indirect esthetic restorations such as resin or porcelain inlays. Because of its limitations in curing of purely light cured resin cements due to attenuation of the curing light by intervening materials, dual cured resin cements are recommended for cementing restorations. The physical properties of resin cements are greatly influenced by the extent to which a resin cures and the degree of cure is an important factor in the success of the inlay. The purpose of this study was to evaluate the influence of porcelain thickness and exposure time on the polymerization of resin cements by measuring the microhardness and the degree of conversion, to investigate the nature of the correlation between two methods mentioned above, and to determine the exposure time needed to harden resin cements through various thickness of porcelain. The degree of resin cure was evaluated by the measurements of microhardness [Vickers Hardness Number(VHN)] and degree of conversion(DC), as determined by Fourier Transform Infrared Spectroscopy(FTIR) on one light cured composite resin [Z-100(Z)] and three dual cured resin cements [Duo cement(D), 3M Resin cement(R), and Dual cement(DA)] which were cured under porcelain discs thickness of 0mm, 1mm, 2mm, 3mm with light exposure time of 40sec, 80sec, 120sec, and regression analysis was performed to determine the correlation between VHN and DC. In addition, to determine the exposure time needed to harden resin cements under various thickness of porcelain discs, the changes of the intensity of light attenuated by 1mm, 2mm, and 3mm thickness of porcelain discs were measured using the curing radiometer. The results were obtained as follows ; 1. The values of microhardness and the degree of conversion of resin cements without intervening porcelain discs were 31~109VHN and 51~63%, respectively. In the microhardness Z was the highest, followed by R, D, DA. In the degree of conversion, D and DA was significantly greater than Z and R(p<0.05). 2. The microhardness and the degree of conversion of the resin cements decreased with increasing thickness of porcelain discs, and increased with increasing exposure time, D and R showed great variation with inlay thickness and exposure time, whereas, DA showed a little variation. 3. The intensity of light through 1mm, 2mm, and 3mm porcelain inlays decreased by 0.43, 0.25, and 0.14 times compared to direct illumination, and the respective needed exposure times are 53 sec, 70 sec, and 93 sec. In D and R, 40 sec of light irradiation through 2mm porcelain disc and 80 sec of light irradiation through 3mm porcelain disc were not enough to complete curing. 4. The microhardness and the degree of conversion of the resin cements showed a positive correlationship(R=0.791~0.965) in the order of R, D, Z, DA. As the thickness of porcelain discs increased, the decreasing pattern of microhardness was different from that of the degree of conversion, however.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.6
• /
• pp.762-771
• /
• 2003

Statement of problem. In dentistry, the minimally prepared inlay resin-bonded fixed partial denture (FPD) made of new ceromer / fiber-reinforced composite (FRC) was recently introduced. However, the appropriate dimensions for the long-term success and subsequent failure strength are still unknown. Purpose. The aim of this study was to investigate the most fracture-resistible thickness combination of the ceromer / FRC using a universal testing machine and an AE analyzer. Material and Methods. A metal jig considering the dimensions of premolars and molars was milled and 56-epoxy resin dies, which had a similar elastic modulus to that of dentin, were duplicated. According to manufacturer's instructions, the FRC beams with various thicknesses (2 to 4 mm) were constructed and veneered with the 1 or 2 mm-thick ceromers. The fabricated FPDs were luted with resin cement on the resin dies and stored at room temperature for 72 hours. AE (acoustic emission) sensors were attached to both ends, the specimens were subjected to a compressive load until fracture at a crosshead speed of 0.5 mm/min. The AE and failure loads were recorded and analyzed statistically. Results. The results showed that the failure strength of the ceromer/FRC inlay FPDs was affected by the total thickness of the connectors rather than the ceromer to FRC ratio or the depth of the pulpal wall. Fracture was initiated from the interface and propagated into the ceromer layer regardless of the change in the ceromer / FRC ratio. Conclusion. Within the limitations of this study, the failure loads showed significant differences only in the case of different connector thicknesses, and no significant differences were found between the same connector thickness groups. The application of AE analysis method in a fiber-reinforced inlay FPD can be used to evaluate the fracture behavior and to analyze the precise fracture point.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.3
• /
• pp.366-374
• /
• 2000

FRC/ceromer system provides the clinician with a durable, flexible, and esthetic alternative to conventional porcelain fused to metal crowns. FRC is the matrix which is silica-coated and embedded in a resin matrix. The ceromer material which is a second generation indirect composite resin contains silanized, microhybrid inorganic fillers embedded in a light-curing organic matrix. FRC/ceromer restoration has a several advantages: better shock absorption, less wear of occluding teeth, translucency, color stability, bonding ability to dental hard tissues, and resiliency. It has versatility of use including inlay, onlay, single crown, and esthetic veneers. With adhesive technique, it can be used for single tooth replacement in forms of inlay adhesion bridge. In single tooth missing case, conventional PFM bridge has been used for esthetic restoration. However, this restoration has several disadvantages such as high cost, potential framework distortion during fabrication, and difficulty in repairing fractures. Inlay adhesion bridge with FRC/ceromer would be a good alternative treatment plan. This article describes a cases restored with Targis/Vectris inlay adhesion bridge. Tooth preparation guide, fabrication procedure, and cementation procedure of this system will be dealt. The strength/weakness of this restoration will be mentioned, also. If it has been used appropriately in carefully selected case, it can satisfy not only dentist's demand of sparing dental hard tissue but also patient's desire of seeking a esthetic restorations with a natural appearance.

• Restorative Dentistry and Endodontics
• /
• v.25 no.3
• /
• pp.399-406
• /
• 2000

The effect of inlay surface treatment on bonding was investigated when resin inlay was bonded to resin-modified glass-ionomer base with resin cement. For the preparation of glass-ionomer base, resin-modified glass-ionomer cement (Fuji II LC, GC Co., Japan) was filled in class I cavities of 7mm in diameter and 2mm in depth made in plastic molds. Eighty eight resin inlay specimens were made with Charisma$^{(R)}$ (Kulzer, Germany) and then randomly assigned to the four different surface treatment conditions: Group I, $50{\mu}m$ aluminium oxide sandblasting and silane treatment ; Group II, silane treatment alone ; Group III, sandblasting alone, and Group IV (control), no surface treatment. After a dentin bonding agent with primer (One-Step$^{TM}$, Bisco Inc., IL., U.S.A.) was applied to bonding surface of resin inlay and base, resin inlay were cemented to glass-ionomer base with a resin cement (Choice$^{TM}$, Bisco Inc., IL., U.S.A.). Shear bond strengths of each specimens were measured using Instron universal testing machine (4202 Instron, lnstron Co., U.S.A.) and fractured surfaces were examined under the stereoscope. Statistical analysis was done with one-way ANOVA and Dunkan's multiple range test. The results were as follows: 1. Sandblasting and silane treatment provided the greatest bond strength(10.56${\pm}$1.95 MPa), and showed a significantly greater bond strength than sandblasting alone or no treatment (p<0.05). 2. Silane treatment provided a significantly greater bond strength(9.77${\pm}$2.04 MPa) than sandblasting alone or no treatment (p<0.05). However, there was no significant difference in bond strength between sandblasting treatment and silane one (p>0.05). 3. Sandblasting alone provided no significant difference in bond strength from no treatment (p>0.05). 4. Stereoscopic examination of fractured surface showed that sandblasting and silane treatment or silane treatment alone had more cohesive failure mode than adhesive failure mode. 5. In relationship between shear bond strength and failure mode, cohesive failure occurred more frequently as bond strength increased.

• Journal of Technologic Dentistry
• /
• v.42 no.1
• /
• pp.9-16
• /
• 2020

Purpose: The purpose of this study was to compare the marginal and internal fit of lithium disilicate ceramic inlay produced by heat pressing that inlay pattern made by subtractive manufacturing and additive manufacturing method. Methods: A mandibular lower first molar that mesial occlusal cavity (MO cavity) die was prepared. After fabricating an epoxy resin model using a silicone impression material, epoxy resin die was scanned with a dental model scanner to design an MO cavity inlay. The designed STL pile was used to fabricate wax patterns and resin patterns, and then lithium disilicate ceramic inlays were fabricated using hot-press method. For the measurement of the marginal and internal gap of the lithium disilicate, silicone replica method was applied, and gap was measured through an optical microscope (x 80). Data were tested for significant differences using the Mann-Whitney Utest. Results: The marginal fit was 103.56±9.92㎛ in the MIL-IN group and 81.57±9.33㎛ in the SLA-IN group, with a significant difference found between the two groups (p<0.05). The internal fit was 120.99±17.52㎛ in the MIL-IN group and 99.18±6.65㎛ in the SLA-IN group, with a significant difference found between the two groups (p<0.05). Conclusion: It is clinically more appropriate to apply the additive manufacturing than subtractive manufacturing method in producing lithium disilicate inlay using CAD/CAM system.

• Restorative Dentistry and Endodontics
• /
• v.24 no.1
• /
• pp.233-239
• /
• 1999

Recently, a second generation composite resin system(ceromer) was introduced with significantly improved mechanical properties. The purpose of this study was to compare a ceromer with the other restorative materials and to assess its clinical usefulness. In this study, we used four restorative materials : amalgam (BESTALOY$^{(R)}$), indirect composite resin (Clearfil CR Inlay$^{(R)}$), ceromer (Targis$^{(R)}$) and ceramic (Vintage$^{(R)}$). And then we devided into four groups. The materials of each group were as follows : Amalgam group : BESTALOY$^{(R)}$ (Dong Myung Dental Industrial Co.) Composite Resin group : Clearfil CR Inlay$^{(R)}$ (Kuraray) Ceromer group : Targis$^{(R)}$ Dentin (Ivoclar-Vivadent) Ceramic group : Vintage$^{(R)}$ (Shofu Inc.) According to the above classification, we made samples through the polymerization of BESTALOY$^{(R)}$, Clearfil CR Inlay$^{(R)}$ and Targis$^{(R)}$ with separable cylindrical metal mold and firing of Vintage$^{(R)}$ in a investment mold. And then, we measured and compared the value of compressive strength, diametral tensile strength and Vicker's microhardness of each sample. The results were as follows : 1. Amalgam showed the highest value of compressive strength (390.37${\pm}$42.22MPa) and the value of ceromer was somewhere between ceramic and indirect composite resin. There were significant differences among the experimental groups(p<0.001). 2. Indirect composite resin showed the highest value of diametral tensile strength (74.21${\pm}$15.33MPa) and there was no significant difference with ceromer. Ceromer was higher diametral tensile strength than amalgam and ceramic (p<0.001). 3. Ceramic showed the highest value of microhardness (538.44${\pm}$37.38Hv) and the value of ceromer was somewhere between ceramic and indirect composite resin. There were significant differences among the experimental groups (p<0.001).