• 한국분말재료학회지
• /
• 제19권1호
• /
• pp.1-5
• /
• 2012

In order to improve the remanence of (Nd, Dy)-Fe-B sintered magnets, we investigated the influence of compaction conditions such as packing density, applied field and green density on the magnetic properties. While the remanence decreased with increasing the packing density and green density, it increased with the increase of the applied field. In addition, XRD analysis revealed that the remanence was enhanced as the degree of powder alignment was improved. The green density was more influential on the remanence than the packing density and applied field.

• 한국광물학회지
• /
• 제24권1호
• /
• pp.37-42
• /
• 2011

지구의 암권에서 가장 중요한 자성광물은 자철석이다. 암석 내에 존재하는 자철석의 성분과 입자 크기에 관한 정보를 알아내는데 저온 자화특성을 이용하려 한다. 물리적 방법의 하나인 저온 자화특성 실험은 비파괴적이며 운석과 같이 연구 대상 시료의 수량이 제한된 경우 특히 유용하게 사용된다. 금번 연구에서는 세 종류의 합성 자철석 시료와 세 종류의 자철석 함유 암석 시료에 대해 저온포화잔류자화의 가열실험과 실온포화잔류자화의 냉각/가열 실험을 수행하였다. 실험 결과 저온포화잔류자화는 가열함에 따라 자철석의 버웨이변환온도(~105~120 K)를 지나며 급격히 감소한다. 자철석의 버웨이변환온도와 등방점(135 K)를 모두 거치는 실온포화잔류자화의 냉각과 가열 실험 결과에서는 저온포화잔류자화의 가열 실험 결과와 비교하였을 때 자화회복력이 뛰어나고, 자화상실이 상대적으로 완만히 진행된다. 저온포화잔류자화와 실온포화잔류자화 모두 자철석의 입자 크기가 증가할수록 소실되는 포화잔류자화의 비가 증가한다. 결국 저온포화잔류자화기억도와 실온포화잔류자화기억도 모두 자철석의 입자가 커질수록 감소한다. 따라서 저온 자화특성을 이용하면 암석 내 자철석 입자의 크기를 비파괴적인 방법으로 유추할 수 있다.

• 비파괴검사학회지
• /
• 제22권1호
• /
• pp.65-73
• /
• 2002

2.25Cr-1M 강이 $540^{\circ}C$에서 장시간 노출되었을 때 일어나는 미세조직 변화를 모사하기 위해 인공 열화를 실시하였으며 이에 대해 미세조직(탄환화물의 평균등가크기 및 단위면 개수), 기계적 성질 (인장강도 및 경도), 자기적 성질(보자력 및 잔류자화)을 측정하였다. 이들 결과를 비교함으로써 열화에 따른 자기적 성질의 변화와 미세조직 사이의 상관관계률 규명하였다. 탄화물을 그 형장에 따라 막대상, 구상, 침상으로 분류하였으며 침상의 탄화물은 열화 초반부에 급격히 소멸되는 경향을 보였다. 또한 보자력과 잔류자화는 열화 초반부에 급격히 감소한 후 점차 완만히 감소하는 경향을 보였다. 기계적 성질과 보자력 및 잔류자화 사이에는 선형적 상관관계가 존재하였다.

• 한국재료학회지
• /
• 제13권2호
• /
• pp.81-87
• /
• 2003

Microstructures and mechanical properties of variously heat treated 0.85% carbon steel(eutectoid steel) were evaluated by magnetic property measurements. Microstructural analysis (pearlite interstellar spacing), measurement of mechanical properties(Rockwell hardness, yield stress, fracture stress) and magnetic properties(coercivity, remanence, hysteresis loss, saturation magnetization) were performed to clarify mutual relationships among these parameters. Water quenched specimens with martensite structure showed much higher coercivity and remanence than air cooled or furnace cooled specimens with pearlite structure. The linear dependence of coercivity and remanence on pearlite interlamellar spacing as well as on Rockwell hardness, yield stress and fracture stress was observed in the pearlitic steel. Hysteresis loss and saturation magnetization showed no distinct trend with pearlite interlamellar spacing.

• 열처리공학회지
• /
• 제14권6호
• /
• pp.323-329
• /
• 2001

Artificial aging was performed to simulate the microstructural degradation in 2.25CrMo steel arising from long time exposure at $540^{\circ}C$. The carbide morphologies were classified as acicular, pipe and globular type, and the number of carbides per unit area was measured for each type of carbides. The fine acicular carbides were found to diminish drastically in the initial stage of aging. An attempt was made to evaluate the microstructural degradation in artificially aging heat treated 2.25CrMo steel by the magnetic property measurements such as saturation magnetization, coercivity and remanence. The saturation magnetization showed no distinct trend with aging time. However, the coercivity and remanence were observed to decrease rapidly in initial 920 hours of aging time and then decrease slowly afterwards.

• 한국세라믹학회지
• /
• 제26권6호
• /
• pp.747-754
• /
• 1989

The effects of CuO and SiO2 on the sintered density, grain growth and magnetic properties of Sr-ferrite were investigated. The sintered density of Sr-ferrite is increased with increasing the amount of CuO or SiO2 addition. The grain of Sr-ferrite grow uniformly with the addition of CuO, so remanence increases and coercivity decreases. The addition of SiO2 increase coercivity but does not affect remanence prominently. The sintering temperature above 125$0^{\circ}C$ and SiO2 addition above 0.8wt% causes abnormal grain growth in Sr-ferrite. When CuO and SiO2 are added simultaneouly, remanence does not decrease but coercivity shows low value.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.404-407
• /
• 1995

Magnetic properties of model exchange-spring magnets, which are composed of magnetically soft and hard grains, were calculated by means of computer simulation. The dependence of the magnetic properties on the strength of intergrain exchange interaction and the amount of soft grains was studied. The existence of soft grains enhanced the remanence remarkably, and the remanence over $0.8M_{s}$ was obtained in the model magnets containing 25% or more soft grains by volume. The calculated coercivity vs. the strength of the exchange interaction curves showed a peak at a critical strength of the exchange interaction, although the remanence increased monotonously with increase in the strength of the exchange interaction. Thus the maximum energy product also reached a peak around the same critical strength. The calculated maximum energy product exceeded $300kJ/m^{3}$ when the magnet is assumed to be composed of $Fe_{3}B$ and $Nd_{2}Fe_{14}B$.

• 한국광물학회지
• /
• 제24권3호
• /
• pp.189-194
• /
• 2011

화성의 암권 진화 연구에서 최근 각광받는 광물은 적철석으로 대표되는 3가철 산화물이다. 물리적 방법의 하나인 잔류자화기억도 실험은 비파괴적이고 지구 기원이 아닌 고체 시료의 자화특성 규명에 유용하게 사용된다. 금번 연구에서는 알루미늄 농도를 조절하며 열수반응과 탈수반응을 통해 총 8개 성분의 3 가철 산화물을 합성하였다. 이들 시료에 대해 잔류자화기억도와 자화상실온도($T_N$)를 측정하였다. 3가철 산화물의 격자상수는 알루미늄의 3가철 함량이 증가하며 감소한다. 3 가철 산화물의 자화상실 온도 역시 알루미늄의 몰농도가 증가하며 감소한다. 알루미늄이 거의 첨가되지 않은 적철석의 $T_N$은 광물의 합성방법과 무관하게 대략 $690^{\circ}C$로 수렴한다. 탈수반응으로 합성된 3가철 산화물의 잔류자화기억도는 알루미늄의 함량에 거의 무관하게 매우 높지만, 열수반응으로 합성된 3가철 산화물의 잔류자화기억도는 알루미늄 함량이 증가하며 동반 상승한다. 상대적으로 쉽고 측정이 간단하며 비파괴적인 잔류자화기억도를 이용하면 추후 암석 내 3가철 산화물 입자의 성인 유추가 가능하며, 특히 화성의 암권 진화 규명에도 일조하리라 예상된다.

• Journal of Magnetics
• /
• 제1권1호
• /
• pp.24-30
• /
• 1996

The relationship between effective permeability and the remanence ratio of an Fe-based amorphous alloy (Metglas 2605S3A) is investigated over a wide frequency range, in an effort to understand magnetization behavior of the alloy. In the frequency range from 1 to 200 kHz, the permeability is maximum at the remanence ratio of 0.4-0.5 and, at frequencies over 500 kHz, the correlation with negative coefficients emerges indicating that the permeability decreases with the remanent ratio, except for the ribbon coated with an insulating layer of MgO which exhibits both high values of the effective permeability and remanence ratio. It is considered from the correlation results that the boundary at which the dominant magnetization mechanism changes from domain wall motion to spin rotation is near 500 kHz. The core loss is also investigated as a function of annealing time when the samples are annealed at a fixed temperature of $435^{\circ}C$. The core loss in most cases decreases with the annealing time, the degree of the loss may consist of the hysteresis loss and anomalous eddy current loss. The two loss components are considered to be of similar magnitudes at low frequencies while, at high frequencies, the dominant contribution to the total loss is the anomalous loss.

• 한국분말재료학회지
• /
• 제17권1호
• /
• pp.23-28
• /
• 2010

HDDR treated anisotropic Nd-Fe-B powders have been widely used for the sheet motors and the sunroof motors of hybrid or electric vehicles, due to their excellent magnetic properties. Microstructural alignment of HDDR treated powders are mostly depending on the hydrogen reaction in disproportionation step, so the specific method to control hydrogenation reaction is required for improving magnetic properties. In disproportionation step, hydrogenation pressure and reaction time were controlled in the range of 0.15~1.0 atm for 15~180 min in order to control the micorstructural alignment of $Nd_2Fe_{14}B$ phase and, at the same time, to improve remanence of HDDR treated magnet powders. In this study, we could obtain a well aligned anisotropic Nd-Fe-B-Ga-Nb alloy powder having high remanence of 12 kG by reducing hydrogen pressure down to 0.3 atm in disproportionation step.