• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1996년도 춘계학술강연 및 발표대회 강연 및 발표논문 초록집
• /
• pp.15-15
• /
• 1996

• 대한금속재료학회지
• /
• 제56권12호
• /
• pp.878-884
• /
• 2018

In the present work, we selected a polymer, polyvinylidene fluoride (PVDF), as an additive to improve the hydrogenation and dehydrogenation properties of Mg. 95 wt% Mg + 5 wt% PVDF (designated Mg-5PVDF) samples were prepared via milling in hydrogen atmosphere (reactive milling), and the hydrogenation and dehydrogenation characteristics of the prepared samples were compared with those of Mg milled in hydrogen atmosphere. The dehydrogenation of magnesium hydride formed in the as-prepared Mg-5PVDF during reactive milling began at 681 K. In the fourth cycle (n=4), the initial hydrogenation rate was 0.75 wt% H/min and the quantity of hydrogen absorbed for 60 min, $H_a$ (60 min), was 3.57 wt% H at 573 K and in 12 bar $H_2$. It is believed that after reactive milling the PVDF became amorphous. The milling of Mg with the PVDF in hydrogen atmosphere is believed to have produced defects and cracks. The fabrication of defects is thought to ease nucleation. The fabrication of cracks is thought to expose fresh surfaces, resulting in an increase in the reactivity of the particles with hydrogen and a decrease in the diffusion distances of hydrogen atoms. As far as we know, this investigation is the first in which a polymer PVDF was added to Mg by reactive milling to improve the hydrogenation and dehydrogenation characteristics of Mg.

• 열처리공학회지
• /
• 제26권6호
• /
• pp.279-287
• /
• 2013

Oxide Dispersion Strengthened (ODS) Fe with $Al_2O_3$ dispersoid was successfully produced by reactive milling with a mixture of Fe, $Fe_3O_4$ (Magnetite), $Fe_2O_3$ (Hematite) and Al reactants at cryogenic temperature. The milled powders were consolidated by Vacuum Hot Press (HP) at 1323 K, and the consolidated materials were characterized by Transmission Electron Microscopy (TEM), Scanning Transmission Electron Microscopy (STEM), and Energy Dispersive Spectroscopy (EDS); the yield strength and the hardness of the consolidated materials were determined by compressive test and Vickers hardness test at room temperature. The grain size of the materials was estimated by X-ray Diffraction technique using the scherrer's formula. The TEM observations showed that the microstructure was comprised with a mixture of nanocrystalline Fe matrix and $Al_2O_3$ nano-dispersoids with a bimodal size distribution; the 0.2% off-set yield strength of the materials was as high as $758{\pm}29$ MPa and the Vickers hardness was $358{\pm}2$. The effect of the cryogenic milling and addition of extra Fe powder was discussed on the suppression of MSR (Mechanically induced Self-sustaining Reaction) for the desired microstructural evolution of ODS alloys.

• 한국세라믹학회지
• /
• 제47권6호
• /
• pp.534-539
• /
• 2010

$HfB_2$-HfC composites were prepared by reactive hot pressing using Hf and $B_4C$ at temperatures of 1800 and $1900^{\circ}C$ for 60 min under 32 MPa in an Ar atmosphere. The reaction sequences of the $HfB_2$-HfC composite were studied through series of pressureless heat treatments ranging from 800 to $1600^{\circ}C$. The effect of size reduction of the starting powders on densification was investigated by vibration milling. Fully dense $HfB_2$-HfC composites were obtained by size reduction of the starting powders via vibration milling. The oxidation behaviour of the $HfB_2$-HfC composites at $1500^{\circ}C$ in air showed formation of a non-protective $HfO_2$ scale with linear mass gain. Examination of the mechanical properties showed that particle size reduction via vibration milling also led to improved flexural strength, hardness and fracture toughness.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2008년도 Asian Magnetics Conference
• /
• pp.287.1-287.1
• /
• 2008

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.77-77
• /
• 2011

These days, a growing demand for memory device is filled up with the flash memory and the dynamic random access memory (DRAM). Although DRAM is a reasonable solution for current demand, the universal novel memory with high density, high speed and nonvolatility, needs to be developed. Among various new memories, the magnetic random access memory (MRAM) device is considered as one of good candidate memories because of excellent features including high density, high speed, low operating power and nonvolatility. The etching of MTJ stack which is composed of magnetic materials and insulator such as MgO is one of the vital process for MRAM. Recently, MgO has attracted great interest in the MTJ stack as tunneling barrier layer for its high tunneling magnetoresistance values. For the successful realization of high density MRAM, the etching process of MgO thin films should be investigated. Until now, there were some works devoted to the investigations on etch characteristics of MgO thin films. Initially, ion milling was applied to the etching of MgO thin films. However, ion milling has many disadvantages such as sidewall redeposition and etching damage. High density plasma etching containing the magnetically enhanced reactive ion etching and high density reactive ion etching have been employed for the improvement of etching process. In this work, inductively coupled plasma reactive ion etching (ICPRIE) system was adopted for the improvement of etching process using MgO thin films and etching gas mixes of $CH_4$/Ar and $CH_4$/$O_2$/Ar have been employed. The etch rates are measured by a surface profilometer and etch profiles are observed using field emission scanning emission microscopy (FESEM). The effects of gas concentration and etch parameters such as coil rf power, dc-bias voltage to substrate, and gas pressure on etch characteristics will be systematically explored.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.727-728
• /
• 2006

The present work studies the influence of high-energy milling (HEM) and sintering cycle of Ti and Al powders on the obtainment of TiAl. This study shows that HEM modifies the diffusion processes during the sintering stage. The samples were obtained by cold uniaxial and isostatic pressing, pre-sintered at different temperatures, and heated up to the sintering temperature. This study also shows the effect of powder additions processed by HEM on the sintering behavior of elemental Ti and Al powders.

• 한국염색가공학회지
• /
• 제16권5호
• /
• pp.1-7
• /
• 2004

Because acid dyes and reactive dyes require acidic condition for adsorption and alkaline condition for fixation respectively, it is difficult to dye nylon/cotton blends in one-bath one-step dyeing method. In this paper we tried to find out the suitable dye and dyeing condition for one-bath one-step dyeing of nylon/cotton blends. MNT type reactive dyes showed higher exhaustion on cotton as compared with MCT type dyes at neutral pH, which means that the MNT type reactive dyes are preferable for one-bath one-step dyeing method. The optimum condition for one-bath one-step dyeing of nylon/cotton blends was found to be pH 7. Wash fastness of fabrics dyed with half-milling type acid dyes was superior to that of fabrics dyed with levelling type acid dyes, when MNT type reactive dyes were used together.

• 자원리싸이클링
• /
• 제18권6호
• /
• pp.24-29
• /
• 2009

나노크기의 산화세륨 분말을 제조하기 위해서는 출발물질로 탄산세륨[$Ce_2(CO_3)3{\cdot}XH_2O$]이 널리 사용되고 있는데, 탄산세륨은 소성을 통하여 탄산기체와 수증기를 방출하면서 더욱 작은 입자들로 쪼개진 다공성 구조의 산화세륨이 형성되며 이러한 다공성의 산화세륨을 분쇄함으로서 나노크기의 산화세륨을 얻을 수 있다. 본 연구에서는 염화세륨용액으로부터 중탄산암모늄을 첨가하여 제조된 탄산세륨의 소성온도, 분쇄시간, 유성밀의 회전속도, 분산제 첨가량 및 장입된 분쇄 볼 크기 등의 변화에 따라 얻어지는 산화세륨의 평균 입자크기 분석을 통하여 탄산세륨으로부터 나노크기의 산화세륨 제조공정 특성에 대하여 알아보았으며, 소성온도 $700^{\circ}C$, 분쇄시간 5시간 조건에서 평균 입자크기 160 nm의 산화세륨 분말을 제조할 수 있었다.

• 한국재료학회지
• /
• 제30권7호
• /
• pp.350-358
• /
• 2020

A variety of composite powders having different aluminum and carbon contents are prepared using various organic solvents having different amounts of carbon atoms in unit volume as ball milling agents for titanium and aluminum ball milling. The effects of substrate temperature and post-heat treatment on the texture and hardness of the coating are investigated by spraying with this reduced pressure plasma spray. The aluminum part of the composite powder evaporates during spraying, so that the film aluminum content is 30.9 mass%~37.4 mass% and the carbon content is 0.64 mass%~1.69 mass%. The main constituent phase of the coating formed on the water-cooled substrate is a non-planar α₂ phase, obtained by supersaturated carbon regardless of the alloy composition. When these films are heat-treated at 1123 K, the main constituent phase becomes γ phase, and fine Ti₂AlC precipitates to increase the film hardness. However, when heat treatment is performed at a higher temperature, the hardness is lowered. The main constitutional phase of the coating formed on the preheated substrate is an equilibrium gamma phase, and fine Ti₂AlC precipitates. The hardness of this coating is much higher than the hardness of the coating in the sprayed state formed on the water-cooled substrate. When hot pressing is applied to the coating, the porosity decreases but hardness also decreases because Ti₂AlC grows. The amount of Ti₂AlC in the hot-pressed film is 4.9 vol% to 15.3 vol%, depending on the carbon content of the film.