• Korean Journal of Metals and Materials
• /
• v.50 no.10
• /
• pp.769-774
• /
• 2012

Mg-x wt% $Fe_2O_3-y$ wt% Ni samples were prepared by reactive mechanical grinding in a planetary ball mill, and their hydrogen-storage properties were investigated and compared. Activations of $Mg-5Fe_2O_3-5Ni$ was completed after one hydriding (under 12 bar $H_2$) - dehydriding (in vacuum) cycle at 593 K. At n = 2, $Mg-5Fe_2O_3-5Ni$ absorbed 3.43 wt% H for 5 min, 3.57 wt% H for 10 min, 3.76 wt% H for 20 min, and 3.98 wt% H for 60 min. Activated $Mg-10Fe_2O_3$ had the highest hydriding rate, absorbing 2.99 wt% H for 2.5 min, 4.86 wt% H for 10 min, and 5.54 wt% H for 60 min at 593 K under 12 bar $H_2$. Activated $Mg-10Fe_2O_3-5Ni$ had the highest dehydriding rate, desorbing 1.31 wt% H for 10 min, 2.91 wt% H for 30 min, and 3.83 wt% H for 60 min at 593 K under 1.0 bar $H_2$.

• Korean Journal of Materials Research
• /
• v.23 no.10
• /
• pp.562-567
• /
• 2013

A 90 wt% Mg-10 wt% $NbF_5$ sample was prepared by mechanical milling under $H_2$ (reactive mechanical grinding). Its hydriding and dehydriding properties were then examined. Activation of the 90 wt% Mg-10 wt% $NbF_5$ sample was not required. At n=1, the sample absorbed 3.11 wt% H for 2.5 min, 3.55 wt% H for 5 min, 3.86 wt% H for 10 min, and 4.23 wt% H for 30 min at 593K under 12 bar $H_2$. At n=1, the sample desorbed 0.17 wt% H for 5 min, 0.74 wt% H for 10 min, 2.03 wt% H for 30 min, and 2.81 wt% H for 60 min at 593K under 1.0 bar $H_2$. The XRD pattern of the 90 wt% Mg-10 wt% $NbF_5$ after reactive mechanical grinding showed Mg, ${\beta}-MgH_2$ and small amounts of ${\gamma}-MgH_2$, $NbH_2$, $MgF_2$ and $NbF_3$. The XRD pattern of the 90 wt% Mg-10 wt% $NbF_5$ dehydrided at n=3 revealed Mg, ${\beta}-MgH_2$, a small amount of MgO and very small amounts of $MgH_2$ and $NbH_2$. The 90 wt% Mg-10 wt% $NbF_5$ had a higher initial hydriding rate and a larger quantity of hydrogen absorbed for 60 min than the 90 wt% Mg-10 wt% MnO and the 90 wt% Mg-10 wt% $Fe_2O_3$, which were reported to have quite high hydriding rates and/or dehydriding rates. The 90 wt% Mg-10 wt% $NbF_5$ had a higher initial dehydriding rate (after an incubation period) and a larger quantity of hydrogen desorbed for 60 min than the 90 wt% Mg-10 wt% MnO and the 90 wt% Mg-10 wt% $Fe_2O_3$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.16 no.1
• /
• pp.25-30
• /
• 2005

수소 분위기에서 10wt.%MnO와 기계적인 분쇄(반응성 기계적 분쇄)에 의해 Mg의 수소 저장 성질을 향상시켰다. 회전 속도는 250 rpm, 밀링시간은 2 h, 그리고 시료 대 볼 중량비는 1/45이었다. 준비한 Mg-10wt.%MnO 시료는 활성화를 위한 수소화물 형성 분해 싸이클링이 필요없었으며, 첫 번째 싸이클 593k 12 bar $H_2$에서, 10분 동안에 3.12wt.%, 60분 동안에 3.95wt.%의 수소를 흡수하였다. 또한 Mg-10wt.%MnO는 593k 0.8 bar $H_2$에서 60분 동안에 2.12wt.%의 수소를 방출하였다. MnO와 Mg의 방응성 분쇄는, 핵생성을 용이케하고 (Mg 입자의 표면에 결함 형성과 첨가물에 의해), Mg 입자의 표면에 crack을 만들어 Mg의 입자 크기를 줄여 그 결과 수소 원자의 확산 거리를 작게 함으로써 수소 흡수 방출 속도를 증가시킨다. 수소화물 형성 분해 싸이클링은 Mg 입자의 표면에 crack을 만들고 Mg의 입자 크기를 줄여 수소 흡수 방출 속도를 증가시킨다.

• Biomolecules & Therapeutics
• /
• v.10 no.1
• /
• pp.1-6
• /
• 2002

The particle size of medicinal materials is an Important physical property that affects the phar-maceutical behaviors such as dissolution, chemical stability, and bioavailability of solid dosage forms. The size reduction of raw medicinal powder is needed to formulate insoluble drugs or slightly soluble medicines and to improve the pharmaceutical properties such as the solubility, the pharmaceutical mixing, and the dispersion. The objective of the present study is to evaluate physiological activity of amorphous and nano-particle prep-arations of insoluble drug, ursodeoxycholic acid (UDCA), which were made by three types of fine grinding mills. The change of physical properties of ground UDCA was conformed by Mastersiger microplus and X-ray diffraction. We have investigated hepatoprotective effects of the nano-particle preparations of UDCA by plan-etary mill, vibration rod mill and jet mill in $CCI_4$-induced oxidatively injured mouse liver. The results showed that nano-particle preparations of UDCA all decreased reactive oxygen sepecies generation and lipid peroxi-dation in $CCI_4$-induced oxidative stress mice. Among them, nano-particle preparations by vibration rod mill and jet mill showed more significantly hepatoprotective effects compared to intact UDCA and planetary mill-ground UDCA. These results suggest that ground UDCA with vibration rod mill and jet mill shows a high amorphous state and the improved dissolution.

• Transactions of the Korean hydrogen and new energy society
• /
• v.14 no.4
• /
• pp.313-320
• /
• 2003

볼밀링법을 이용하여 타이타늄 스펀지와 칩 또는 스크랩으로부터 상온애서 직접 타이타늄 수소와 분말을 재조하는 실험을 행하였다. 실험결과 진공중에서 볼링을 행한 타이타늄 스펀지와 칩의 경우 24시간외 후 합금분말의 크기는 약 20 um 정도의 크기를 갖는 것을 확인하였다. 그러나 수소화 분위기에서 볼밀링을 행한 경우에 12시간 후 수소화분말의 입도는 0.1-0.2 um로 극히 미세한 합금 분말이 제조되었다. 수소분위기에서의 볼밀링에 의한 타이타늄 분말제조는 기존의 방법에 비해 열을 가하지 않고 타이타늄 수소화분말을 얻을 수 있다는 장점과 나노크기의 미세한 수소화 분말을 얻을 수 있음을 알 수 있었다.

• Computers and Concrete
• /
• v.20 no.2
• /
• pp.197-204
• /
• 2017

Typically, high lime fly ash (Class C) has been characterized as a fly ash, which at lower replacement levels is not as effective as the low lime (Class F) fly ash, in mitigating alkali-silica reaction (ASR) in portland cement concrete. The influence of fineness of Class C, obtained by grinding virgin fly ash into finer particles, on its pozzolanic reactivity and ASR mitigation performance was investigated in this study. In order to assess the pozzolanic reactivity of mortar mixtures containing virgin or ground fly ashes, the strength activity index (SAI) test and thermo-gravimetric analysis (TGA) were conducted on the mortar cubes and paste samples, respectively, containing virgin fly ash or two ground fly ashes. In addition, to evaluate any improvement in the ASR mitigation of ground fly ashes compared to that of the virgin fly ash, the accelerated mortar bar test (AMBT) was conducted on the mortar mixtures containing different dosages of either virgin or ground fly ashes. In all tests crushed glass aggregate was used as a highly reactive aggregate. Results from this study showed that the finest fly ash (i.e., with an average particle size of 3.1 microns) could increase the flow ability along with the pozzolanic reactivity of the mortar mixture. However, results from this study suggested that the fineness of high lime fly ash does not seem to have any significant effect on ASR mitigation.

• Transactions of the Korean hydrogen and new energy society
• /
• v.17 no.2
• /
• pp.174-180
• /
• 2006

The eutectic Mg-23.5%Ni alloy was casted by melting and solidification. The powders of Mg-23.5%Ni and (Mg-23.5%Ni)-10% iron oxide were prepared by mechanical grinding of casted Mg-Ni alloy and casted Mg-Ni alloy+oxide, respectively. As milling time increases, hydriding and dehydriding rates of Mg-Ni and Mg-Ni-oxide alloy powders increase. The additions of iron oxide to Mg-Ni alloy and Mg-Ni-oxide increase hydriding rates and slightly decrease dehydriding rates.

• Korean Journal of Metals and Materials
• /
• v.49 no.12
• /
• pp.989-994
• /
• 2011

Samples with compositions of 80 wt% Mg-14 wt% Ni-6 wt% $Fe_2O_3$ (named $Mg-Ni-Fe_2O_3$), and 78 wt% Mg-14 wt% Ni-6 wt% $Fe_2O_3-2$ wt% CNT (named $Mg-Ni-Fe_2O_3-CNT$ ) were prepared by reactive mechanical grinding. Hydriding and dehydriding properties and effects of CNT addition on the hydriding and dehydriding rates of $Mg-Ni-Fe_2O_3$ were then investigated. Activation of the $Mg-14Ni-6Fe_2O_3$ sample was completed after three hydriding (under 12 bar $H_2$)-dehydriding (under 1.0 bar $H_2$) cycles at 573 K. The addition of CNT to the $Mg-14Ni-6Fe_2O_3$ sample made the activation process unnecessary, with a small decrease in the hydrogen-storage capacity.

• Economic and Environmental Geology
• /
• v.54 no.2
• /
• pp.285-297
• /
• 2021

Globally, nuclear-decommissioning facilities have been increased in number, and thereby hundreds of thousands of wastes, such as concrete, soil, and metal, have been generated. For this reason, there have been numerous efforts and researches on the development of technology for volume reduction and recycling of solid radioactive wastes, and this study reviewed and examined thoroughly such previous studies. The waste concrete powder is rehydrated by other processes such as grinding and sintering, and the processes rendered aluminate (C3A), C4AF, C3S, and ��-C2S, which are the significant compounds controlling the hydration reaction of concrete and the compressive strength of the solidified matrix. The review of the previous studies confirmed that waste concretes could be used as recycling cement, but there remain problems with the decreasing strength of solidified matrix due to mingling with aggregates. There have been further efforts to improve the performance of recycling concrete via mixing with reactive agents using industrial by-products, such as blast furnace slag and fly ash. As a result, the compressive strength of the solidified matrix was proved to be enhanced. On the contrary, there have been few kinds of researches on manufacturing recycled concretes using soil wastes. Illite and zeolite in soil waste show the high adsorption capacity on radioactive nuclides, and they can be recycled as solidification agents. If the soil wastes are recycled as much as possible, the volume of wastes generated from the decommissioning of nuclear power plants (NPPs) is not only significantly reduced, but collateral benefits also are received because radioactive wastes are safely disposed of by solidification agents made from such soil wastes. Thus, it is required to study the production of non-sintered cement using clay minerals in soil wastes. This paper reviewed related domestic and foreign researches to consider the sustainable recycling of concrete waste from NPPs as recycling cement and utilizing clay minerals in soil waste to produce unsintered cement.