• 대한기계학회논문집A
• /
• 제29권2호
• /
• pp.341-349
• /
• 2005

Damage often occurs on the surface of railway wheel by wheel-rail contact fatigue. It should be removed before reaching wheel failure, because wheel failure can cause derailment with loss of life and property. The increase or decrease of the contact fatigue life by the metal removal of the contact surface were shown by many researchers, but it has not explained precisely why fatigue life increases or decreases. In this study, the effect of metal removal depth on the contact fatigue life for railway wheel has been evaluated by applying finite element analysis. It has been revealed that the residual stress and the plastic flow are the main factors determining the fatigue life. The railway wheel has the initial residual stress formed during the manufacturing process, and the residual stress is changed by thermal stress induced by braking. It has been found that the initial residual stress determines the amount of metal removal depth. Also, the effects of the initial residual stress and metal removal on the contact fatigue lift has been estimated, and an equation is proposed to decide the optimal metal removal depth for maximizing the contact fatigue life.

• 한국정밀공학회지
• /
• 제27권8호
• /
• pp.13-19
• /
• 2010

A design method of railway wheel profile with objective function of equivalent conicity considering wheel dimension constraint, two points contact problem between wheel and rail was proposed. New design method shows good results. New wheel profile generated from optimization process shows better dynamic performance compared with initial profile as the purpose of wheel profile design. And to verify the design method with testing the stability of new wheel profile, we conducted a critical speed test for new wheel profile using scale model applied scaling method of railway vehicle dynamics. The result of critical speed test show good agreement with that of numerical analysis. From the above results, it is seen that the design method with objective function of equivalent conicity is feasible and it could be applied to design new wheel profile efficiently.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2010년도 춘계학술대회 논문집
• /
• pp.963-969
• /
• 2010

The railway vehicle consists of wires, bodies, bogies and wheelsets, and each part has very complex mechanism. In this paper, wheel-rail contact algorithm is implemented using C++ and inserted into the ODYN which is a dynamic analysis program. To analyze wheel-rail contact mechanism, information such as contact points, contact angle and rolling radius is calculated according to the wheel and rail profile. Using this information, a table for the calculation of the wheel-rail contact analysis is made according to the lateral displacement. And, the creepage and normal force are calculated and a creep force is estimated by the FASTSIM. To verify the reliability of the wheel-rail contact algorithm, results of the program are compared with the ADAMS/Rail and paper. Finally, a wheelset of the railway vehicle is modeled using ODYN and simulated static and dynamic analysis. And, to verify the reliability of the simulation results, a displacement, velocity, acceleration and force are compared with results of ADAMS/Rail.

• Journal of Mechanical Science and Technology
• /
• 제19권spc1호
• /
• pp.411-421
• /
• 2005

The development and implementation of an appropriate methodology for the accurate geometric description of track models is proposed in the framework of multibody dynamics and it includes the representation of the track spatial geometry and its irregularities. The wheel and rail surfaces are parameterized to represent any wheel and rail profiles obtained from direct measurements or design requirements. A fully generic methodology to determine, online during the dynamic simulation, the coordinates of the contact points, even when the most general three dimensional motion of the wheelset with respect to the rails is proposed. This methodology is applied to study specific issues in railway dynamics such as the flange contact problem and lead and lag contact configurations. A formulation for the description of the normal contact forces, which result from the wheel-rail interaction, is also presented. The tangential creep forces and moments that develop in the wheel-rail contact area are evaluated using : Kalker linear theory ; Heuristic force method ; Polach formulation. The methodology is implemented in a general multibody code. The discussion is supported through the application of the methodology to the railway vehicle ML95, used by the Lisbon metro company.

• 한국철도학회논문집
• /
• 제7권3호
• /
• pp.259-263
• /
• 2004

The running safety of a railway vehicle depends on the design parameters and contact condition between wheel and rail. In this study, the effect of the conicity of wheel tread is analyzed using ADAMS/RAIL software on running situation. Modal analysis shows in 0.6 Hz natural frequency of lateral mode in fully arranged the KTX cars. The excessive vibration of the tail cars occurs in the 17th car as the speed and the stiffness of the secondary suspension increases, and especially for 1/40 conicity of the GV40 wheel. Also, the analysis shows that combination of wheel profile, GV40 for power cars and XP55 for passenger cars can reduce the lateral vibration of the tail cars.

• International Journal of Railway
• /
• 제1권1호
• /
• pp.1-5
• /
• 2008

The railway system requires safety and reliability of service of all railway vehicles. Suitable technical systems and working methods adapted to it, which meet the requirements on safety and good order of traffic, should be maintained. For detection of defects, non-destructive testing methods-which should be quick, reliable and cost-effective - are most often used. Since failure in railway wheelset can cause a disaster, regular inspection of defects in wheels and axles are mandatory. Ultrasonic testing, acoustic emission and eddy current testing method and so on regularly check railway wheelset in service. However, it is difficult to detect a crack initiation clearly with ultrasonic testing due to noise echoes. It is necessary to develop a non-destructive technique that is superior to conventional NDT techniques in order to ensure the safety of railway wheelset. In the present paper, the new NDT technique is applied to the detection of surface defects for railway wheelset. To detect the defects for railway wheelset, the sensor for defect detection is optimized and the tests are carried out with respect to surface and internal defects each other. The results show that the surface crack depth of 1.5 mm in press fitted axle and internal crack in wheel could be detected by using the new method. The ICFPD method is useful to detect the defect that initiated in railway wheelset.

• 한국산학기술학회논문지
• /
• 제17권7호
• /
• pp.175-181
• /
• 2016

회전체는 질량 중심선이 축의 기하학적 중심선과 일치하지 않을 때 불평형이 발생한다. 윤축은 두 개의 차륜과 한 개의 차축으로 조립되어 철도차량을 주행시키는 회전체 역할을 하고, 차륜 재질의 불균일, 마모, 윤축 조립과정의 오차 등으로 인해 불평형이 발생할 수 있다. 또한 윤축은 축의 직경이 가늘고 고속으로 회전함으로 불평형 질량에 의한 진동의 영향이 더욱 두드러지게 나타나고 이로 인해 철도차량 고속 주행 시 주행안전성 및 주행거동에 영향을 미칠 수 있다. 그러므로 본 연구에서는 차륜 불평형이 고속철도차량의 동적 거동에 미치는 영향을 철도차량 다물체 동역학 해석 도구인 VI-Rail를 이용하여 해석을 수행하였다. 해석결과에서 차륜 불평형량이 증가할수록 철도차량 대차의 임계속도가 감소됨을 확인할 수 있었고, 차륜 불평형량이 주행 중 차량동적거동 악영향을 미침으로 고속주행에서는 반드시 차륜 불평형량에 대한 관리가 필요함을 확인할 수 있었다. 또한 이 연구로 차륜 불평형량의 정적 및 동적 관리 필요성을 국내 철도차량 운영기관에 제시하였다.

• 한국소음진동공학회:학술대회논문집
• /
• 한국소음진동공학회 2006년도 춘계학술대회논문집
• /
• pp.1453-1458
• /
• 2006

KTX Railway rolling stock wheel run its course to corrode, deteriorate and wear away through out the time. So it is natural that the performance and ability of wheel gets declined. The frequency characteristic analysis were accomplished to above trend and shock wave flow to wheels were examined. The result will be used to find Railway rolling stock wheel crack and maintenance method hereafter.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2007년도 추계학술대회 논문집
• /
• pp.1940-1945
• /
• 2007

The wheelsets are one of most important component: damages in wheel tread and press fitted axle are a significant cost for railway industry. Since failure in railway wheelset can cause a disaster, regular inspection of defects in wheels and axles are mandatory. Ultrasonic testing, acoustic emission and eddy current testing method and so on regularly check railway wheelset in service. However, it is difficult to use this method because of its high viscosity and because its sensitivity is affected by temperature. Also, due to noise echoes it is difficult to detect defects initiation clearly with ultrasonic testing. It is necessary to develop a non-destructive technique that is superior to conventional NDT techniques in order to ensure the safety of railway wheelset. In the present paper, the new NDT technique is applied to the detection of surface defects for railway wheelset. To detect the defects for railway wheelset, the sensor for defect detection is optimized and the tests are carried out with respect to surface and internal defects each other. The results show that the surface crack depth of 1.5 mm in press fitted axle and internal crack in wheel could be detected by using the new method. The ICFPD method is useful to detect the defect that initiated in the tread of railway wheelset.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2003년도 춘계학술대회 논문집
• /
• pp.641-644
• /
• 2003

The running safety of the rolling stock depends on the design characteristics and the contact condition between wheel and railway. In this study, it is analyzed how equivalent conicity of wheel tread or its characteristics has influence on the running safety.