• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권9호
• /
• pp.527-532
• /
• 2000

The performance of ac plasma display panels (PDP) is influenced strongly by the surface glow discharge characteristics on the MgO thin films. This paper deals with the surface glow discharge characteristics and some physical properties of MgO thin films prepared by reactive RF planar unbalanced magnetron sputtering in connection with ac PDP. The samples prepared with dc bias voltage of -10V showed lower discharge voltage and lower erosion rate byion bombardment than those samples prepared by conventional magnetron sputtering or E-beam evaporation. The main factor that improves the discharge characteristics by bias voltage is considered to be due to the morphology changes or crystal structure of the MgO thin film by ion bombardement during deposition process.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2009년도 추계학술대회 초록집
• /
• pp.197-197
• /
• 2009

Indium tin oxide (ITO), Indium zinc oxide (IZO) 박막은 DC 마그네트론 스퍼터링 시스템을 이용하여 유리기판 위에 증착되었으며, Indium-zinc-tin oxide (IZTO) 박막은 두 개의 캐소드(DC, RF)를 사용한 마그네트론 이원동시방전 시스템에 의해 증착되었다. 모든 박막은 상온 증착 후 $200^{\circ}C$에서 후열처리 되었으며, IZO에 Sn이 소량 첨가됨에 따라 IZO보다 더 낮은 비저항을 갖는 것을 확인할 수 있었다.

• 열처리공학회지
• /
• 제13권6호
• /
• pp.398-404
• /
• 2000

The Ti-Al-V-N films have been deposited on various substrates by d.c and r.f reactive magnetron sputtering from a Ti-6Al-4V alloy target in mixed $Ar-N_2$ discharges. The films were investigated by means of XRD, AES, SEM/EDX, microhardness, TG and scratch test. The XRD and SEM results indicated that the films were of single B1 NaCl phase having dense columnar structure with the (111) preferred orientation. The composition of Ti-Al-V-N film was the Ti-7.1Al-4.3V-N(wt%) films. Adhesion and microhardness of Ti-Al-V-N films deposited by r.f magnetron sputtering method were better than those deposited by d.c magnetron sputtering method. The anti-oxidation properties of Ti-Al-V-N films were also superior to that of Ti-N film deposited by the same deposition conditions.

• 한국진공학회지
• /
• 제6권1호
• /
• pp.85-90
• /
• 1997

32cm직경의 $AlCu_x$(x=0.5%)음극 타겟과 회전 자석을 이용한 상용 마그네트론 스퍼 터링 장치에서 부가적인 플라즈마 여기 방법으로 스퍼터링된 입자들을 이온화시킨후, 수십 볼트의 직류 기판 바이어스로 이온의 방향성과 에너지를 조절하여 작은 트렌치나 via를 채 울 수 있는 공정을 개발하였다. 여기에서, 반경방향의 이온 플럭스비의 균일도 문제를 개선 하기 위하여, 입자들의 가시광선 영역의 방출선을 이용한 플라즈마 진단과, 패터닝된 웨이 퍼에 대한 직접 채우기로 플라즈마 내의 입자 분포와의 상관 관계를 찾고, RF 코일 설계의 개선을 도모하였다. 가시광 방출 분광에서 $Ar^{\circ},\;Ar^+;Al^+,\;Al^{\circ}$ 입자들의 방출선 세기는 1$\mu\textrm{m}$이 하의 크기를 갖는 트렌치와 via의 바닥과 top 두께비와 밀접한 관련이 있었다. RF코일의 직 경을 29cm에서 32cm로 증가 시키고, RF 입력부에 의한 비대칭을 개선하여 이온 플럭스비 의 척도가 되는 via 채우기의 바닥과 top의 두께비에서 7.5%에서 1.5%로의 균일도 향상을 얻었다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2006년도 제30회 학술논문발표회 초록집
• /
• pp.136-136
• /
• 2006

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.103-104
• /
• 2008

In this paper we report upon an investigation into the effect of DC bias voltage on the electrical and optical properties of Gallium doped zinc oxide (GZO) film. GZO films were deposited on glass substrate without substrate temperature by RF magnetron sputtering from a ZnO target mixed with 5 wt% $Ga_2O_3$. we investigated sample properties of bias voltage change in 0 to -60 V. We were able to achieve as low as $5.89\times10^{-4}$ ${\Omega}cm$ and transmittance over 87%. without substrate temperature.

• 한국표면공학회지
• /
• 제45권6호
• /
• pp.242-247
• /
• 2012

Yb-doped ITO (ITO:Yb) films were deposited on unheated non-alkali glass substrates by magnetron cosputtering using two cathodes (DC, RF) equipped with the ITO and $Yb_2O_3$ target, respectively. The composition of the ITO:Yb films was controlled by adjusting the RF powers from 0 W to 480 W in 120 W steps with the DC power fixed at 70 W. The ITO:Yb films had a higher crystallization temperature ($200^{\circ}C$) than that of the ITO films ($170^{\circ}C$), which was attributed to both larger ionic radius of $Yb^{3+}$ and higher bond enthalpy of $Yb_2O_3$, compared to ITO. This amorphous ITO:Yb film post-annealed at $170^{\circ}C$ showed a resistivity of $5.52{\times}10^{-4}{\Omega}cm$, indicating that a introduction of Yb increased resistivity of the ITO film. However, these amorphous ITO:Yb films showed a high etching rate, fine pattering property, and a very smooth surface morphology above the crystallization temperature of the amorphous ITO films (about $170^{\circ}C$). The transmittance of all films was >80% in the visible region.

• 한국전기전자재료학회논문지
• /
• 제22권5호
• /
• pp.373-376
• /
• 2009

In this paper we report upon an investigation into the effect of DC bias voltage on the electrical and optical properties of Gallium doped zinc oxide (GZO) film. GZO films were deposited on glass substrate without substrate temperature by RF magnetron sputtering from a ZnO target mixed with 5 wt% $Ga_{2}O_{3}$. we investigated sample properties of bias voltage change in 0 to -60 V. We were able to achieve as low as $5.89{\times}10^{-4}{\Omega}cm$ and transmittance over 88 %. without substrate heating.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.202-203
• /
• 2013

CIGS 단일 타켓을 DC 및 RF 마그네트론 스퍼터링을 이용하여 파워별로 Mo/SLG위에 증착하여 미세구조 및 화학조성 평가를 실시하였다. 파워가 증가함에 따라 이온의 운동에너지 증가에 따라서 결정성이 향상되었음을 확인할 수 있었다. DC 마그네트론 스퍼터링의 경우 40W에서 가장 결정성이 좋았으며, RF 마그네트론 스퍼터링은 80W에서 높은 결정성을 확인할 수 있었다. 이는 DC power 40W와 RF power 80W에서 박막의 조성이 화학양론을 만족하고 grain의 성장이 잘되었기 때문에 높은 결정성을 나타났다고 생각된다. 그리고 최적의 80W에서 기판온도를 100~400도까지 변화하여 증착해본 결과 300도에서 증착 시 가장 높은 결정성이 나타나는 것을 확인할 수 있었다. 이는 400도 이상 온도 증가 시 2차 핵생성 밀도 증가로 인해 결정성이 저하된다고 생각된다.

• 한국세라믹학회지
• /
• 제39권2호
• /
• pp.171-177
• /
• 2002

본 연구에서는 DC bias가 인가된 유도결합형 플라즈마 열선 화학기상증착법을 이용하여 580$^{\circ}C$의 저온에서 탄소나노튜브를 수직 배향시켰다. 성장된 탄소나노튜브의 기판으로는 강화유리 위에 촉매층으로 Ni과 전도층으로 Cr을 300/200 ${\AA}$(Ni/Cr) 증착된 것으로 R-F magnetron sputtering을 이용하여 제작하였다. 성장 시 RF power와 DC bias power는 150W와 80W이며 텅스텐 필라멘트 power는 7∼8 A로 인가하였다. 성장된 탄소나노튜브는 속이 비어 있는 다중벽으로 이루어 졌으며 성장된 탄소나노튜브 끝단에는 금속 촉매로 보이는 Ni이 존재하는 것을 알 수 있었다. 탄소나노튜브는 흑연화도가 우수하며 그에 따라 탄소나노튜브의 전계 방출 특성도 우수하게 평가되었다. 성장된 탄소나노튜브의 구동 전압은 약 3 V/${\mu}m$이었다.