• Journal of Sensor Science and Technology
• /
• v.14 no.1
• /
• pp.52-55
• /
• 2005

Ni oxide thin films with thermal sensitivity superior to Pt and Ni thin films were formed through annealing treatment after Ni thin films were deposited by a r.f. magnetron sputtering method. Resistivity values of Ni oxide thin films were in the range of $10.5{\mu}{\Omega}cm$ to $2.84{\times}10^{4}{\mu}{\Omega}cm$ according to the degree of Ni oxidation. Also temperature coefficient of resistance(TCR) values of Ni oxide thin films depended on the degree of Ni oxidation from 2,188 ppm/$^{\circ}C$ to 5,630 ppm/$^{\circ}C$ in the temperature range of $0{\sim}150^{\circ}C$. Because of the high linear TCR and resistivity characteristics, Ni oxide thin films exhibit much higher sensitivity to flow and temperature changes than pure Ni thin films and Pt thin films.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.1352-1353
• /
• 2008

In this study, aluminium - doped zinc oxide (ZnO:Al) transparent conducting film was deposited on PET(polyethylen terephthalate) substrate by r.f. magnetron sputtering method. PET substrate was surface-treated in an atmospheric pressure DBD(dielectric barrier discharge) plasma to increase deposition rate and to improve electrical propesties. Morphological changes by DBD plasma were obsered using contact angle measurement. The contact angle of water on PET was reduced from 62$^{\circ}$ to 42$^{\circ}$ by DBD plasma surface treatment. The plasma treatment also increased deposition rate and electrical propesties. The electrical resistivity as low as $4.97{\times}10^{-3}[{\Omega}-cm]$ and the deposition rate of 234[${\AA}$-m/min] were obtained in ZnO:Al film with surface treatment time of 5min, and 20min., respectively.

• Journal of the Korean Ceramic Society
• /
• v.37 no.8
• /
• pp.731-738
• /
• 2000

KLN(K3Li2Nb5O15) has attracted a great deal of attention for their potential usefulness in piezoelectric, electro-optic, nonlinear optic, and pyroelectirc devices. Especially, the KLN single crystal has been studied in the field of optics and electronics. However it is hard to produce good quality single crystals due to the crack propagation during crystal growing. One of the solutions of this problem is prepartion of thin film. But the intensive study has not been conducted so far. In this study, after the KLN thin film were prepared by R.F. magnetron Sputtering method on SiO2/Si substrate, the post-annealing methods of RTA(rapid thermal annealin) and IPA(insitu post annealing) were employed. The deposition condition of KLN thin film was RF power(100 W), Working pressure(100 mtorr). The commonness of both RAT and IPA was that the higher were deposition and post annealing temperature, the higher was the intensity of XRD but the less surface roughness. The difference of post-annealing methods affected XRD phase and surface condition very much. And in IPA process, the influence of O2 had much effect on the formation of KLN phase.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.1
• /
• pp.61-66
• /
• 1999

The Spin-dependent tunneling magnetoresistance (TMR) effect was observed in $NiFe/Al_2O_3$/Co thin films. The samples were prepared by magnetron sputtering in a system with a base pressure of $3\times10^{-6}$Torr. the insulating $Al_2O_3$layer was prepared by r.f. plasma oxydation method of a metallic Al layer. The ferromagnetic and insulating layers were deposited through metallic masks to produce the cross pattern form. The junction has an active area of $0.3\times0.3\textrm{mm}^2$ and the $Al_2O_3$layer is deposited through a circular mask with a diameter of 1mm. It is very important that insulating layer is formed very thinly and uniformly in tunneling junction. The ferromagnetic layer was fabricated in optimum conditions and the surface of that was very flat, which was observed by AFM. Tunneling junction was confirmed through nonlinear I-V curve. $NiFe/Al_2O_3$/Co junction was observed for magnetization behavior and magnetoresistance property and magnetoresistance property is dependent on magnetization behavior and magnetoresistance property and magnetoresistance property is dependent on magnetization behavior of t재 ferromagnetic layer. The maximum magnetoresistance ratio was about 6.5%.

• Journal of the Korean Ceramic Society
• /
• v.39 no.4
• /
• pp.377-385
• /
• 2002

The possibility of $ZrO_2$ thin film as insulator for Metal-Ferroelectric-Insulator-Semiconductor(MFIS) structure was investgated. $SrBi_2Ta_2O_9$ and $SrBi_2Ta_2O_9$(SBT) thin films were deposited on P-type Si(111) wafer by R. F. magnetron sputtering method. The electrical properties of MFIS gate were relatively improved by inserting the $ZrO_2$ buffer layer. The window memory increased from 0.5 to 2.2V in the applied gate voltage range of 3-9V when the thickness of SBT film increased from 160 to 220nm with 20nm thick $ZrO_2$. The maximum value of window memory is 2.2V in Pt/SBT(160nm)/$ZrO_2$(20nm)/Si structure with the optimum thickness of $ZrO_2$. These memory windows are sufficient for practical application of NDRO-FRAM operating at low voltage.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1425_1426
• /
• 2009

In this study, commercially available polyethylene terephthalate(PET), which is widely used as a substrate of flexible electronic devices, was modified by dielectric barrier discharge(DBD) method in an air condition at atmospheric pressure, and aluminium - doped zinc oxide (ZnO:Al) transparent conducting film was deposited on PET substrate by r. f. magnetron sputtering method. Surface analysis and characterization of the plasma-treated PET substrate was carried out using contact angle measurements, X-ray Photoelectron Spectroscopy(XPS) and Atomic Force Microscopy (AFM). Especially the effect of surface state of PET substrate on some important properties of ZnO:Al transparent conducting film such as electrical and morphological properties and deposition rate of the film, was studied experimentally. The results showed that the contact angle of water on PET film was reduced significantly from $62^{\circ}$ to $43^{\circ}$ by DBD surface treatment at 20 min. of treatment time. The plasma treatment also improved the deposition rate and electrical properties. The deposition rate was increased almost linearly with surface treatment time. The lowest electrical resistivity as low as $4.97{\times}10^{-3}[\Omega-cm]$ and the highest deposition rate of 234[${\AA}m$/min] were obtained in ZnO:Al film with surface treatment time of 5min. and 20min., respectively.

• Journal of the Korean Ceramic Society
• /
• v.42 no.9 s.280
• /
• pp.624-630
• /
• 2005

To investigate the possibility of the $ZrO_2$ buffer layer as the insulator for the Metal-Ferroelectric-Insulator-semiconductor (MFIS) structure, $ZrO_2$ and $SrBi_2Ta_2O_9$ (SBT) thin films were deposited on the P-type Si(111) wafer by the R.F. magnetron-sputtering method. According to the process with and without the post-annealing of the $ZrO_2$ buffer layer and SBT thin film, the diffusion amount of Sr, Bi, Ta elements show slight difference through the Glow Discharge Spectrometer (GDS) analysis. From X-ray Photoelectron Spectroscopy (XPS) results, we could confirm that the post-annealing process affects the chemical binding condition of the interface between the $ZrO_2$ thin film and the Si substrate. Compared to the MFIS structure without the post-annealing of the $ZrO_2$ buffer layer, memory window value of MFlS structure with post-annealing of the $ZrO_2$ buffer layer were considerably improved. The window memory of the Pt/SBT (260 nm, $800^{\circ}C)/ZrO_2$ (20 nm) structure increases from 0.75 to 2.2 V under the applied voltage of 9 V after post-annealing.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1096_1097
• /
• 2009

Aluminium doped zinc oxide(ZnO:Al) thin film, which is mainly used as a transparent conducting electrode in electronic devices, has many advantages compared with conventional indium tin oxide(ITO). In this paper in order to investigate the possible application of ZnO:Al thin films as a transparent conducting electrode for flexible film-typed dye sensitized solar cell (FT-DSCs), ZnO:Al and ITO thin films were prepared on the polyethylene terephthalate (PET) substrate by r. f. magnetron sputtering method. Specially one-inched FT-DSCs using either a ZnO:Al or ITO electrode were also fabricated separately under the same manufacturing conditions. Some properties of both the FT-DSCs with ZnO:Al and ITO transparent electrodes, such as conversion efficiency, fill factor, and photocurrent were measured and compared with each other. The results showed that by doping the ZnO target with 2 wt% of $Al_2O_3$, the film deposited at discharge power of 200W resulted in the minimum resistivity of $2.2\times10^{-3}\Omega/cm$ and at ransmittance of 91.7%, which are comparable with those of commercially available ITO. Two types of FT-DSCs showed nearly the same tendency of I-V characteristics and the same value of conversion efficiencies. Efficiency of FT-DSCs using ZnO:Al electrode was around 2.6% and that of fabricated FT-DSCs using ITO was 2.5%. This means that ZnO:Al thin film can be used in FT-DSCs as a transparent conducting layer.

• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.276-279
• /
• 2000

Ferroelectric properties of $SrBi_2TaNbO_9$ (SBTN) thin films were changed by the amount of Bi content in SBTN. We suggested that the addition of excess Bi into the films could be accomplished by heat-treating $SBTN/Bi_2O_3/SBTN$ heterostructure fabricated by r.f. magnetron sputtering method. Excess Bi composition was controlled by the thickness of the sandwiched $Bi_2O_3$ from 0 to $400\;\AA$. When the SBTN thin films were inserted by $400\;{\AA}\;Bi_2O_3$ layer, $Bi_2Pt$ phase was formed as a second phase in SBTN films, resulting in poor ferroelectric properties. The onset temperature for hysteresis loop can be reduced by heat treating $SBTN/Bi_2O_3/SBTN$ heterostructure. The films with $SBTN/Bi_2O_3(100\;{\AA})/SBTN$ hetero-structure followed by annealing at $650^{\circ}C$ for 30 min show 2Pr and Ec of $5.66\;{\mu}C/\textrm{cm}^2$ and 54 kV/cm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.200-201
• /
• 2007

The SBT($SrBi_2Ta_2O_9$) thin films with $Bi_2O_3$ buffer layer were deposited on Pt/Ti/$SiO_2$/Si substrate by R.F. magnetron sputtering method in order to improve the ferroelectric characteristics. In SBT thin films, the deficiency of bismuth during the process due to its volatility results in an obvious non stoichiometry of the films and the presence of secondary phases. $Bi_2O_3$ buffer layer was found to be effective to achieve the low temperature crystallization and improve the ferroelectric properties of SBT thin films. Ferroelectric properties and crystallinities of SBT thin films with various post annealing of $Bi_2O_3$ buffer layer were observed as various annealing temperature, using X-Ray Diffraction (XRD), scanning electron microscopy (SEM), Keithley 237 and HP 4192A Impedance Analyzer.