• Journal of the Korean Ceramic Society
• /
• v.53 no.6
• /
• pp.597-603
• /
• 2016

Tantalum carbide, which is one of the ultra-high temperature ceramics, was deposited on graphite by low pressure chemical vapor deposition from a $TaCl_5-C_3H_6-Ar-H_2$ mixture. To maintain a constant $TaCl_5/C_3H_6$ ratio during the deposition process, $TaCl_5$ powders were continuously fed into the sublimation chamber using a screw-driven feeder. Sublimation behavior of $TaCl_5$ powder was measured by thermogravimetric analysis. TaC coatings have various phases such as $Ta+{\alpha}-Ta_2C$, ${\alpha}-Ta_2C+TaC_{1-x}$, and $TaC_{1-x}$ depending on the powder feeding methods, the $C_3H_6/TaCl_5$ ratio, and the deposition temperatures. Near-stoichiometric TaC was obtained by optimizing the deposition parameters. Phase compositions were analyzed by XRD, XPS, and Raman analysis.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.11-12
• /
• 2008

Micron-sized Co-alloy T800 powder was coated on Inconel718 (IN718) using high velocity oxygen fuel (HVOF) thermal spraying by the optimal coating process (OCP) determined from the best surface hardness of 16 coatings prepared by Taguchi program. The surface hardness improved 140-160 % from 399 Hv of IN718 to 560-630 Hv by the coating. Porosity of the coating was 1.0-2.7 %, strongly depending on spray parameters. Both friction coefficients (FC) and wear traces (WT) of the coating were smaller than those of IN718 substrate at both $25^{\circ}C$ and $538^{\circ}C$. FC and WT of IN718 and coating decreased with increasing the surface temperature. Tensile bond strength (TBS) and fracture location (FL) of Ti64/T800 were 8,770 psi and near middle of T800 coating respectively. TBS and FL of Ti64/NiCr/T800 were 8,740 psi and near middle of T800 coating respectively. This showed that cohesion of T800 coating was 8,740-8,770 psi, and adhesion of T800 on Ti64 and NiCr was stronger than the cohesion of T800.

• Journal of Powder Materials
• /
• v.17 no.6
• /
• pp.456-463
• /
• 2010

This paper describes the results of the application of Cr-Diamond-like carbon (DLC) films for efficiency improvement through surface modification of spur gear parts in the hydraulic gear pump. Cr-DLC films were successfully deposited on SCM 415 substrates by a hybrid coating process using linear ion source (LIS) and magnetron sputtering method. The characteristics of the films were systematically investigated using FE-SEM, nano-indentation, sliding tester and AFM instrument. The microstructure of Cr-DLC films turned into the dense and fine grains with relatively preferred orientation. The thickness formed in our Cr buffer layer and DLC coating layer were obtained the 487 nm and $1.14\;{\mu}m$. The average friction coefficient of Cr-DLC films considerably decreased to 0.15 for 0.50 of uncoated SCM415 material. The hardness and surface roughness of Cr-DLC films were measured 20 GPa and 10.76 nm, respectively. And then, efficiency tests were performed on the hydraulic gear pump to investigate the efficiency performance of the Cr-DLC coated spur gear. The experimental results show that the volumetric and mechanical efficiency of hydraulic gear pump using the Cr-DLC spur gear were improved up to 2~5% and better efficiency improvement could be attributed to its excellent microstructure, higher hardness, and lower friction coefficient. This conclusion proves the feasibility in the efficiency improvement of hydraulic gear pump for industrial applications.

• Korean Journal of Materials Research
• /
• v.30 no.7
• /
• pp.350-358
• /
• 2020

A variety of composite powders having different aluminum and carbon contents are prepared using various organic solvents having different amounts of carbon atoms in unit volume as ball milling agents for titanium and aluminum ball milling. The effects of substrate temperature and post-heat treatment on the texture and hardness of the coating are investigated by spraying with this reduced pressure plasma spray. The aluminum part of the composite powder evaporates during spraying, so that the film aluminum content is 30.9 mass%~37.4 mass% and the carbon content is 0.64 mass%~1.69 mass%. The main constituent phase of the coating formed on the water-cooled substrate is a non-planar α₂ phase, obtained by supersaturated carbon regardless of the alloy composition. When these films are heat-treated at 1123 K, the main constituent phase becomes γ phase, and fine Ti₂AlC precipitates to increase the film hardness. However, when heat treatment is performed at a higher temperature, the hardness is lowered. The main constitutional phase of the coating formed on the preheated substrate is an equilibrium gamma phase, and fine Ti₂AlC precipitates. The hardness of this coating is much higher than the hardness of the coating in the sprayed state formed on the water-cooled substrate. When hot pressing is applied to the coating, the porosity decreases but hardness also decreases because Ti₂AlC grows. The amount of Ti₂AlC in the hot-pressed film is 4.9 vol% to 15.3 vol%, depending on the carbon content of the film.

• Korean Journal of Metals and Materials
• /
• v.46 no.3
• /
• pp.182-188
• /
• 2008

Carbon nanotubes(CNTs) have outstanding mechanical, thermal, and electrical properties. Thus, by placing nanotubes into appropriate matrix, it is postulated that the resulting composites will have enhanced properties. Cold spray can produce thick metal-based composite coatings with very high density, low oxygen content, and phase purity, which leads to excellent physical properties. In this study, we applied cold spray coating process for the consolidation of Cu/CNT composite powder. The precursor powder mixture, in which CNTs were filled into copper particles, was prepared to improve the distribution of the CNT in copper matrix. Pure copper coating was also conducted by cold spraying as a reference. Annealing heat treatment was applied to the coating to examine its effect on the properties of the composite coating. The hardness of Cu/CNT composite coating represented similar value to that of pure copper coating. It was importantly found that the electrical conductivity of the Cu/CNT composite coating significantly increased from 53% for the standard condition to almost 55% in the optimized condition, taking annealed ($500^{\circ}C/1hr$.) copper coating as a reference (100%). The thermal conductivity of Cu/CNT composite coating layer was higher than that of pure Cu coating. It was also found that the electrical and thermal conductivities of Cu/CNT composite could be improved through annealing heat treatment. The microstructural evolution of Cu/CNT coating was also investigated and related to the macroscopic properties.

• Journal of Powder Materials
• /
• v.29 no.3
• /
• pp.207-212
• /
• 2022

Nanosized rutile titanium dioxide (TiO₂) is used in inorganic pigments and cosmetics because of its high whiteness and duality. The high quality of the white pigments depends on their surface coating technique via the solgel process. SiO₂ coatings are required to improve the dispersibility, UV-blocking, and whiteness of TiO₂. Tetraethyl orthosilicate (TEOS) is an important coating precursor owing to its ability to control various thicknesses and densities. In addition, we use Na₂SiO₃ (sodium silicate) as a precursor because of its low cost. Compared to TEOS, which controls the pH using a basic catalyst, Na₂SiO₃ controls the pH using an acid catalyst, giving a uniform coating. The coating thickness of TiO₂ is controlled using a surface modifier, cetrimonium bromide, which is used in various applications. The shape and thickness of the nanosized coating layer on TiO₂ are analyzed using transmission electron microscopy, and the SiO₂ nanoparticle behavior in terms of the before-and-after size distribution is measured using a particle size analyzer. The color measurements of the SiO₂ pigment are performed using UV-visible spectroscopy.

• Journal of Powder Materials
• /
• v.30 no.5
• /
• pp.402-408
• /
• 2023

This study focused on improving the phase stability and mechanical properties of yttria-stabilized zirconia (YSZ), commonly utilized in gas turbine engine thermal barrier coatings, by incorporating Gd₂O₃, Er₂O₃, and TiO₂. The addition of 3-valent rare earth elements to YSZ can reduce thermal conductivity and enhance phase stability while adding the 4-valent element TiO₂ can improve phase stability and mechanical properties. Sintered specimens were prepared with hot-press equipment. Phase analysis was conducted with X-ray diffraction (XRD), and mechanical properties were assessed with Vickers hardness equipment. The research results revealed that, except for Z10YGE10T, most compositions predominantly exhibited the t-phase. Increasing the content of 3-valent rare earth oxides resulted in a decrease in the monoclinic phase and an increase in the tetragonal phase. In addition, the t(400) angle decreased while the t(004) angle increased. The addition of 10 mol% of 3-valent rare-earth oxides discarded the t-phase and led to the complete development of the c-phase. Adding 10 mol% TiO₂ increased hardness than YSZ.

• Journal of Powder Materials
• /
• v.30 no.5
• /
• pp.415-423
• /
• 2023

With the increasing attention to environmental pollution caused by particulate matter globally, the automotive industry has also become increasingly interested in particulate matter, especially particulate matter generated by automobile brake systems. Here, we designed a coating composition and analyzed its mechanical properties to reduce particulate matter generated by brake systems during braking of vehicles. We designed a composition to check the mechanical properties change by adding Cr₃C₂ and YSZ to the WC-Ni-Cr composite composition. Based on the designed composition, coating samples were manufactured, and the coating properties were analyzed by Vickers hardness and ball-on-disk tests. As a result of the experiments, we found that the hardness and friction coefficient of the coating increased as the amount of Cr₃C₂ added decreased. Furthermore, we found that the hardness of the coating layer decreased when YSZ was added at 20vol%, but the friction coefficient was higher than the composition with Cr₃C₂ addition.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.465-472
• /
• 2017

The ingot fabrication conditions related with the thermal shock bearing phase and microstructure have investigated for the rare earth zirconate ceramic material, lanthanum gadolinium zirconate, as a thermal barrier coating using electron beam evaporation method. The thermal shock resistance of the prepared ingot was evaluated by high energy electron beam irradiation. The rare earth zirconate ceramic powder was prepared by controlling the raw material powder composition of $La_2O_3$, $Gd_2O_3$ and $ZrO_2$ so as to have a composition of $(La_{0.3}Gd_{0.7})_2Zr_2O_7$ which was selected from the former study. Ingot samples were prepared under two conditions. The first condition is prepared by sintering the prepared powder mixture to form an ingot. The second condition is prepared by calcining the prepared powder mixture to form a composite phase and then sintering to form an ingot. X-ray diffraction(XRD) and Scanning Electron Microscope(SEM) were used to analyze phase forming behavior and microstructure of ingot samples. Nanoindentation method used to obtain elastic modulus and hardness of each ingot specimen. Also the stress distribution of ingot was simulated by using FEM method assuming the ingot surface was exposed to electron beam. As a results, in the case of an ingot having a network-shaped microstructure in which relatively coarse pores are included, it seems that the thermal shock resistance was higher than in the case of an ingot having a microstructure composed of relatively fine grains only or particles with the similar level size when the high energy electron beam irradiation.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.2
• /
• pp.153-164
• /
• 2023

The objective of this study is to examine the removal rate of air pollutants, specifically sulfur oxides (SO_x) and nitrogen oxides(NO_x), using concrete permeable blocks containing zeolite beads coated with materials capable of eliminating these pollutants. Titanium dioxide(TiO₂) powder and coconut shell powder were utilized for the removal of SO_x and NO_x and were applied as coatings on the zeolite beads. Concrete permeable block specimens embedded with the coated zeolite beads were produced using an actual factory production line. Test results demonstrated that the concrete permeable block containing zeolite beads coated with coconut shell powder in the surface layer achieved SO_x and NO_x removal rates of 12.5% and 99%, respectively, exhibiting superior performance compared to other blocks. Additionally, the flexural strength and slip resistance were 5.3MPa and 65BPN or higher, respectively, satisfying the requirements specified in KS F 4419 and KS F 4561. Conversely, the permeability coefficient exhibited low permeability, with grades 2 and 3 before and after contaminant pollution, according to the standard for 'design, construction, and maintenance of pavement using permeable block'. In conclusion, incorporating zeolite beads coated with coconut shell powder in the surface layer enables simultaneous removal of SO_x and NO_x, irrespective of ultraviolet rays, while maintaining adequate flexural strength and slip resistance. However, the permeability is significantly reduced, necessitating further improvements.