• Design & Manufacturing
• /
• v.14 no.1
• /
• pp.1-7
• /
• 2020

In this study, the variation of the shrinkage in the thickness direction of the molded parts according to the gate size of the polymer core fabricated through the 3D printer using the SLS method was studied. The polymer cores are laser sintered and the powder material is nylon base PA2200. The polymer cores have lower heat transfer rate and rigidity than the metal core due to the characteristics of the material. Therefore, the injection molding test conditions are set to minimize the deformation of the core during the injection process. The resin used in the injection molding test is a PP material. The packing condition was set to 80, 90 and 100% of the maximum injection pressure for each gate size. The runner diameter used was ∅3mm, and the gates were fabricated in semicircle shapes with cross sections 1, 2, and 3 ㎟, respectively. Thickness measurement was performed for 10 points at 2.5 mm intervals from the point 2.5 mm away from the gate, and the shrinkage to thickness was measured for each point. The shrinkage rate according to the gate size tends to decrease as the cross-sectional area decreases as the maximum injection pressure increases. The average thickness shrinkage rate was close to 0% when the packing pressure was 90% for the gate area of 1mm2. When the holding pressure was set to 100%, the shrinkage was found to decrease by 3% from the standard dimension due to the over-packing phenomenon. Therefore, the smaller the gate, the more closely the molded dimensions can be molded due to the high pressure generation. It was confirmed that precise packing process control is necessary because over-packing phenomenon may occur.

• Journal of Powder Materials
• /
• v.9 no.4
• /
• pp.251-260
• /
• 2002

In the viscosity measurement of PIM feedstock, slip correction methods require a number of experiments and produce a high level of error. In this study, a rotational rheometer with a parallel-discs configuration having different surface roughness was tried to minimize the effect of the slip phenomenon. Disc surface was prepared in 3 different roughness conditions - a smooth and 2 roughened surfaces. Results with the roughened surfaces were compared with the results obtained with a slip correction method. Relationship between powder characteristics such as size and shape and a surface roughness of the disc was examined for feedstock of 4 different powders with a same binder. As results, the effect of the slip phenomenon could be sufficiently minimized on the roughened surface in most cases. However, the effect of the slip phenomenon could not be sufficiently minimized for feedstock of a round-particular-shape powder and in the case of very narrow gap size.

• Design & Manufacturing
• /
• v.13 no.3
• /
• pp.24-28
• /
• 2019

In this study, a study was carried out that could effectively produce a heat dissipation effect on plastic materials. Using carbon nanotube (CNT), aluminum powder and plastic, the material properties were tested in 2 cases of compounding ratio. The test sample mold was designed and constructed prior to the experiment. The experiments include tensile strength, elongation rate, flexural strength, flexural elasticity rate, eye-jaw impact strength, gravity and thermal conductivity. Results from 60% and 70% mixture of aluminium to plastic were tested, and a 10% less combined result was a relatively good property. For research purposes, the heat dissipation effect and light weighting obtained a good measure when the combined amount of Al was 60%.

• Design & Manufacturing
• /
• v.13 no.3
• /
• pp.6-10
• /
• 2019

In this study, a study was carried out that could effectively produce a heat dissipation effect on plastic materials. Using carbon nanotube (CNT), aluminum powder and plastic, the material properties were tested in 2 cases of compounding ratio. The test sample mold was designed and constructed prior to the experiment. The experiments include tensile strength, elongation rate, flexural strength, flexural elasticity rate, eye-jaw impact strength, gravity and thermal conductivity. Results from 60% and 70% mixture of aluminium to plastic were tested, and a 10% less combined result was a relatively good property. For research purposes, the heat dissipation effect and light weighting obtained a good measure when the combined amount of Al was 60%.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.6
• /
• pp.3396-3402
• /
• 2014

The importance of shape design for strength is highly regarded when applied to thin plate products in Ceramic Injection Molding (CIM), such as cases for electronic goods. This study analyzed the characteristics of the mechanical strength of CIM product by measuring the flexural strength and elastic modulus through a 3-point bending test according to the thickness of a thin plate test piece prepared by CIM. The specimen with a thickness of 0.48mm required a 82.9~94.5N fracture load, whereas a 1.0mm thick test piece required 233.6~345.8N. The increase in thickness by 0.5mm resulted in a 3-fold increase in the fracture load, whereas the elastic modulus decreased by 20%. The thicker the specimen, the lower relative density and surface hardness of the specimen. This is because the thicker the specimen, the lower the powder fraction of the ceramic mixture, and the material properties partially change after sintering.

• Design & Manufacturing
• /
• v.12 no.3
• /
• pp.36-41
• /
• 2018

Metal 3D printing is very useful for making the injection molds containing complex conformal cooling channels. The most important issue of the 3D printed molds is cost and life cycle. However, powder bed fusion (PBF) methods are vulnerable to fatigue loading because of the presence of pores and rough surfaces. In the present study, the fatigue test was performed to obtain fatigue analysis input data for predicting the durability of a 3D printed injection mold core. The metal 3D printer used to manufacture the specimen was OPM250L from Sodick, and the metal powder material was maraging steel. The ultrasonic fatigue testing method was adopted for the fatigue test. A key advantage of the ultrasonic fatigue method is that $10^8{\sim}10^9$ long cycle test data or more could be obtained within a relatively short period. Based on the results of the experiment, the effect of heat treatment was negligible. However, there was an apparent difference in durability depending on the presence or absence of the surface treatment.

• Journal of Powder Materials
• /
• v.8 no.1
• /
• pp.49-54
• /
• 2001

The synthesis and characteristics of W-Ni-Fe nanocomposite powder by hydrogen reduction of ball milled W-Ni-Fe oxide mixture were investigated. The ball milled oxide mixture was prepared by high energy attrition milling of W blue powder, NiO and $Fe_2O_3$ for 1 h. The structure of the oxide mixture was characteristic of nano porous agglomerate composite powder consisting of nanoscale particles and pores which act as effective removal path of water vapor during hydrogen reduction process. The reduction experiment showed that the reduction reaction starts from NiO, followed by $Fe_2O_3$ and finally W oxide. It was also found that during the reduction process rapid alloying of Ni-Fe yielded the formation of $\gamma$-Ni-Fe. After reduction at 80$0^{\circ}C$ for 1 h, the nano-composite powder of W-4.57Ni-2.34Fe comprising W and $\gamma$-Ni-Fe phases was produced, of which grain size was35nm for W and 87 nm for $\gamma$-Ni-Fe, respectively. Sinterability of the W heavy alloy nanopowder showing full density and sound microstructure under the condition of 147$0^{\circ}C$/20 min is thought to be suitable for raw material for powder injection molding of tungsten heavy alloy.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.1531-1532
• /
• 2013

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2009.06a
• /
• pp.13-14
• /
• 2009

• Journal of Powder Materials
• /
• v.14 no.6
• /
• pp.410-414
• /
• 2007

Carbon contamination from the binder resin is an inherent problem with the metal powder injection molding process. Residual carbon in the W-Cu compacts has a strong impact on the thermal and electric properties. In this study, uncertainty was quantified to evaluate determination of carbon in a W-15%Cu MIM body by the combustition method. For a valid generalization about this evaluation, uncertainty scheme applied even to the repeatability as well as the uncertainty sources of each analyse step and quality appraisal sources. As a result, the concentration of carbon in the W-Cu part were measured as 0.062% with expanded uncertainty of 0.003% at 95% level. This evaluation example may be useful to uncertainty evaluation for other MIM products.