• 한국분말재료학회지
• /
• 제5권2호
• /
• pp.111-121
• /
• 1998

Thick and dense deposit of higher than 97% of theoretical density was formed by induction plasma spraying. To investigate the effects of powder morphology on the density of deposit, two different kinds of Yttria-Stabilized-Zirconia powder, METCO202NS (atomized & agglomerated) and AMDRY146 (fused & crushed), were used and compared. After plasma treatment, porous METCO202NS powder was all the more densely deposited and its density was increased. In addition to the effect of powder morphology, the process parameters such as, sheath gas composition, probe position, particle size and spraying distance, and so on, were evaluated. The result of experiment with AMDRY146 powder, particle size and spraying distance affected highly on the density of the deposit. The optimum process condition for the deposition of -75 ${\mu}m$ of 20%-Yttria-Stabilized-Zirconia powder was 120/201/min of Ar/$H_2$ gas rate, 80 kW of plasma plate power, 8 cm of probe position and 150 Torr of spraying chamber pressure, at which its density showed 97.91% of theoretical density and its deposition rate was 20 mm/min. All the results were assessed by statistical approach what is called ANOVA.

• 한국분말재료학회지
• /
• 제28권6호
• /
• pp.491-496
• /
• 2021

The process optimization of directed energy deposition (DED) has become imperative in the manufacture of reliable products. However, an energy-density-based approach without a sufficient powder feed rate hinders the attainment of an appropriate processing window for DED-processed materials. Optimizing the processing of DED-processed Ti-6Al- 4V alloys using energy per unit area (E_eff) and powder deposition density (PDD_eff) as parameters helps overcome this problem in the present work. The experimental results show a lack of fusion, complete melting, and overmelting regions, which can be differentiated using energy per unit mass as a measure. Moreover, the optimized processing window (E_eff = 44~47 J/mm² and PDD_eff = 0.002~0.0025 g/mm²) is located within the complete melting region. This result shows that the Eeff and PDDeff-based processing optimization methodology is effective for estimating the properties of DED-processed materials.

• 분석과학
• /
• 제33권3호
• /
• pp.159-166
• /
• 2020

진공금속증착법(vacuum metal deposition, 이하 VMD)는 비다공성과 반다공성 표면의 잠재지문을 현출하는데 효과적이다. VMD는 일반적인 기법으로 현출할 수 없거나 어려운 표면에 유류된 지문을 현출하는 경우에서 활용할 수 있다. VMD 기법이 권장되는 표면은 비닐, 폴리머 지폐, 마그네틱 코팅 처리가 된 티켓 등이 있다. 본 연구에서는 택배 봉투로 주로 사용되는 분홍색 고밀도 폴리에틸렌 봉투(HDPE)와 저밀도 폴리에틸렌 봉투(LDPE)에 지문을 유류한 뒤 최소 12시간부터 최대 28일이 경과한 지문을 현출하기 위한 금의 최소 투입량을 탐색하였다. 그리고 그 결과를 흑색분말, 형광분말의 효과와 비교하였다. 또한, 실제로 배송에 사용된 택배 봉투를 수거한 다음 HDPE와 LDPE로 분류하고 pseudo-operation test를 시행하였다. 그 결과, VMD는 HDPE와 LDPE 표면에서 비교적 일관된 지문 현출 결과를 보여주었다.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1998년도 춘계학술발표회논문집(2)
• /
• pp.216-221
• /
• 1998

A study on induction plasma deposition with ceramic materials, yttria-stabilized-zirconia ZrO$_2$-Y$_2$O$_3$ (m.p 264O $^{\circ}C$), was conducted with a view developing a new method for nuclear fuel fabrication Before making dense pellets more than 96％TD., the spraying condition was optimized through the process parameters, such as chamber pressure, plasma plate power powder spraying distance, sheath gas composition, probe position, particle size and powders different morphology. The results with a 5mm thick deposit on rectangular planar graphite substrates showed a 97.11％ theoretical density when the sheath gas flow rate was Ar/H$_2$120/20 l/min, probe position 8cm, particle size -75 ${\mu}{\textrm}{m}$ and spraying distance 22cm by AMDRY146 powder. The degree of influence of the main effects on density were powder morphology. particle size, sheath gas composition, plate power and spraying distance, in that order. Among the two parameter interactions, the sheath gas composition and chamber pressure affects density greatly. By using the multi-pellets mold wheel type, the pellet density did not exceed 94%T.D., owing to the spraying angle.

• Archives of Metallurgy and Materials
• /
• 제66권3호
• /
• pp.795-798
• /
• 2021

Molybdenum (Mo) is used to form a barrier layer for metal wiring in displays or semiconductor devices. Recently, researches have been continuously attempted to fabricate Mo sputtering targets through additive manufacturing. In this study, spherical Mo powders with an average particle size of about 37 um were manufactured by electrode induction melting gas atomization. Subsequently, Mo layer with a thickness of 0.25 mm was formed by direct energy deposition in which the scan speed was set as a variable. According to the change of the scan speed, pores or cracks were found in the Mo deposition layer. Mo layer deposited with scan speed of 600 mm/min has the hardness value of 324 Hv with a porosity of approximately 2%. We demonstrated that Mo layers with higher relative density and hardness can be formed with less effort through direct energy deposition compared to the conventional powder metallurgy.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.503-506
• /
• 2000

YBCO superconducting thick films were prepared on Ag wire by electrophoresis in acetone and ethanol with chemically modified suspension. The addition of organic compounds, such as PEG, EG into suspension solution for improving critical current density was investigated. Surface state, deposition condition, pore distribution and cracks were investigated by using SEM photographs. Controlling preparation conditions were studied for reducing these defects. As a results, in acetone solution, the surface crack of samples was decreased with increasing PEG. On the contrary, the surface crack of sample was increasing with increasing the amount of EG. In ethanol solution without I$_2$, which was generally used for an electrolyte, the deposition time was longer than this of acetone. For that reason the sample deposition in ethanol time was needed with enough stirring time for suspending YBCO powder and deposition time.

• 한국분말재료학회지
• /
• 제21권6호
• /
• pp.434-440
• /
• 2014

Silicon carbide(SiC) layer is particularly important tri-isotropic (TRISO) coating layers because it acts as a miniature pressure vessel and a diffusion barrier to gaseous and metallic fission products in the TRISO coated particle. The high temperature deposition of SiC layer normally performed at $1500-1650^{\circ}C$ has a negative effect on the property of IPyC layer by increasing its anisotropy. To investigate the feasibility of lower temperature SiC deposition, the influence of deposition temperature on the property of SiC layer are examined in this study. While the SiC layer coated at $1500^{\circ}C$ obtains nearly stoichiometric composition, the composition of the SiC layer coated at $1300-1400^{\circ}C$ shows discrepancy from stoichiometric ratio(1:1). $3-7{\mu}m$ grain size of SiC layer coated at $1500^{\circ}C$ is decreased to sub-micrometer (< $1{\mu}m$) $-2{\mu}m$ grain size when coated at $1400^{\circ}C$, and further decreased to nano grain size when coated at $1300-1350^{\circ}C$. Moreover, the high density of SiC layer (${\geq}3.19g/cm^3$) which is easily obtained at $1500^{\circ}C$ coating is difficult to achieve at lower temperature owing to nano size pores. the density is remarkably decreased with decreasing SiC deposition temperature.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 기술교육전문연구회
• /
• pp.82-85
• /
• 2003

This dissertation describes an optimization method for fabricating thick films with superconducting YBCO powders by electrophoresis technique. The lateral alternating applied voltage caused to shake the superconducting powder vertically to the deposition field during the process of the oriented deposition so that it was deposited along the c-axis on the silver tape with shaky-aligned EPD. As the result, the optimized thin film fabrication method was obtained to get more dense and uniform surface morphology as well as the improved critical current density. For commercial utilization and efficiency, in this dissertation, alternating voltage of 25-120 V/cm in frequency of 60Hz was proposed to apply it as a subsidiary source for shaky-flow deposition so that the fabricated thin film showed uniform surface morphology with less voids and cracks and $T_{c.zero}$ of 90 K and the critical current density of $3419A/cm^2$.

• 한국세라믹학회지
• /
• 제46권5호
• /
• pp.447-451
• /
• 2009

Continuous SiC fiber-reinforced SiC composites ($SiC_f$/SiC) were fabricated by electrophoretic deposition (EPD). Nine types of slurries with different powder contents, binder resin amounts and slurry pH were deposited on Tyranno$^{TM}$-SA fabrics by EPD at 135 V for ten minutes to determine the optimal conditions. Further EPD using the optimum slurry conditions was performed on fabrics with four different pyrolitic carbon (PyC) thicknesses. The density of the hot-pressed composites decreased with increasing PyC thickness due to the difficulty of infiltrating the slurry into the narrow gaps between the fibers. On the other hand, the mechanical strength increased with increasing PyC thickness despite the decrease in density, which was explained by the enhanced crack deflection with increasing PyC thickness. The $SiC_f$/SiC composites showed the highest density and flexural strength of 94% and 342 MPa, respectively, showing EPD as a feasible method for dense $SiC_f$/SiC fabrication.

• Archives of Metallurgy and Materials
• /
• 제64권2호
• /
• pp.607-611
• /
• 2019

Thermal/cold spray deposition were used for additive manufacture of oxide dispersion strengthened (ODS) steel layers. Mechanically alloyed F/M ODS steel powders (Fe(bal.)-10Cr-1Mo-0.25Ti-0.35Y2O3 in wt.%) were sprayed by a high velocity oxygen fuel (HVOF) and cold spray methods. HVOF, as a thermal method, was used for manufacturing a 1 mm-thick ODS steel layer with a ~95% density. The source to objective distance (SOD) and feeding rate were controlled to achieve sound manufacturing. Y₂Ti₂O₇ nano-particles were preserved in the HVOF sprayed layer; however, unexpected Cr₂O₃ phases were frequently observed at the boundary area of the powders. A cold spray was used for manufacturing the Cr₂O₃-free layer and showed great feasibility. The density and yield of the cold spray were roughly 80% and 45%, respectively. The softening of ODS powders before the cold spray was conducted using a tube furnace of up to 1200℃. Microstructural characteristics of the cold sprayed layer were investigated by electron back-scattered diffraction (EBSD), the uniformity of deformation amount inside powders was observed.