Effect of Deposition Temperature on the Property of Pyrolytic SiC Fabricated by the FBCVD Method  

Kim, Yeon-Ku (Advanced Fuel Technology Development Division, KAERI)
Kim, Weon-Ju (Advanced Fuel Technology Development Division, KAERI)
Yeo, SungHwan (Advanced Fuel Technology Development Division, KAERI)
Cho, Moon-Sung (Advanced Fuel Technology Development Division, KAERI)
Publication Information
Journal of Powder Materials / v.21, no.6, 2014 , pp. 434-440 More about this Journal
Abstract
Silicon carbide(SiC) layer is particularly important tri-isotropic (TRISO) coating layers because it acts as a miniature pressure vessel and a diffusion barrier to gaseous and metallic fission products in the TRISO coated particle. The high temperature deposition of SiC layer normally performed at $1500-1650^{\circ}C$ has a negative effect on the property of IPyC layer by increasing its anisotropy. To investigate the feasibility of lower temperature SiC deposition, the influence of deposition temperature on the property of SiC layer are examined in this study. While the SiC layer coated at $1500^{\circ}C$ obtains nearly stoichiometric composition, the composition of the SiC layer coated at $1300-1400^{\circ}C$ shows discrepancy from stoichiometric ratio(1:1). $3-7{\mu}m$ grain size of SiC layer coated at $1500^{\circ}C$ is decreased to sub-micrometer (< $1{\mu}m$) $-2{\mu}m$ grain size when coated at $1400^{\circ}C$, and further decreased to nano grain size when coated at $1300-1350^{\circ}C$. Moreover, the high density of SiC layer (${\geq}3.19g/cm^3$) which is easily obtained at $1500^{\circ}C$ coating is difficult to achieve at lower temperature owing to nano size pores. the density is remarkably decreased with decreasing SiC deposition temperature.
Keywords
Pyrolytic SiC; Fluidize-bed chemical vapor deposition; Deposition temperature; TRISO coated particle;
Citations & Related Records
연도 인용수 순위
  • Reference
1 C. W. Forsberg: Int. J. Hydrogen Energy, 28 (2003) 1073.
2 H. D. Ringel and E. Zimmer: Nucl. Tech., 45 (1979) 287.
3 P. Naefe and E. Zimmer: Nucl. Tech., 42 (1979) 163.
4 J. Schlichting: Powder Metall. Int., 12 (1980) 196.
5 W. Von Muench: J. Electrochem. Soc., 125 (1978) 294.   DOI
6 D. P. Stinton and W. J. Lackey: Ceram. Bull., 57 (1978) 568.
7 K. Minato and K. Fukuda: J. Nuclear Mater., 149 (1987) 233.   DOI   ScienceOn
8 Fukuda, E. Lopez-Honorato: J. Tan and P.J Meadows: J. Nuclear Mater., 392 (2009) 219.   DOI   ScienceOn
9 Y. J. Lee, D. J. Choi, J. Y. Park and W. Hong: J. Mater. Sci., 35 (2000) 4519.   DOI   ScienceOn
10 S. Nakashima and H. Harima: Phys. Status Solidi., 39 (1997) 162.
11 E. Lopez-Honorato, P. J. Meadows, J. Tan and P. Xiao: J. Mater. Res., 23 (2009) 1785.
12 J. W. Chang: KAERI/AR-600, (2001).
13 M. D. Allendorf and R. J. Kee: J. Electrochem. Soc. 138 (1991) 841.   DOI