• 멤브레인
• /
• 제29권6호
• /
• pp.308-313
• /
• 2019

본 연구에서는 구리 이온(Cu²⁺ ion) 제거를 위한 산화철(Fe₃O₄)/다공성 탄소 복합체를 합성하였으며, 이를 바탕으로 구리 이온 제거에 대한 특성 평가를 실시하였다. SEM, XRD 분석을 진행하여 수열합성(hydrothermal) 반응을 이용한 산화철/다공성 탄소 복합체의 형태와 구조를 확인하였다. BET 분석을 통해 비표면적과 기공 크기를 확인하였으며, UV-vis 장비를 통해 성능 평가를 실시하여 자성이 있는 Fe₃O₄와 다공성 탄소와의 시너지효과를 통해 액체 상태에서 존재하는 구리 이온을 제거할 수 있는 가능성을 제시하였다.

• 한국분말재료학회지
• /
• 제11권2호
• /
• pp.158-164
• /
• 2004

W-Cu composite has been used for the applications requiring both high strength, good thermal and electrical conductivity. A graded combination of W and Cu will reduce thermal stress concerned with heat conduction, maintaining good thermal conductivity and high mechanical strength. In the present work, an attempt was made to fabricate continuous W-Cu FGM by preparing the graded porous structure of W skeleton using spark plasma sintering (SPS) process followed by infiltrating Cu. The graded porous structure was prepared at 150$0^{\circ}C$ for 60s under pressure of 15MPa by SPS process using a graphite mold with varying crr)ss section in the longitudinal direction. Infiltration of Cu was performed at 115$0^{\circ}C$ for 1 hour under $H_2$. W-Cu composite with graded Cu composition of 14 to 27 wt％ was finally prepared. In this process the gradient of composition could be conveniently controlled by varying the gradient of cross sectional area of graphite mold, temperature and pressure.

• Journal of Welding and Joining
• /
• 제10권4호
• /
• pp.213-221
• /
• 1992

Al$_{2}$O$_{3}$ ceramic coating layer by gas flame spraying was very porous, therefore it could not have wear and corrosion resistance at all. To get a dense and strong coating layer, a method to infiltrate an alloy into the pores of $Al_{2}$O$_{3}$ ceramic coating was investigated. Cu-Ti alloys, which had good wettability and reactivity with $Al_{2}$O$_{3}$ ceramic, were examined for infiltration. Infiltration of the alloys was performed in vacuum at 1100.deg.C. The melt of Cu-50 at % Ti alloy was well penetrated through the porous $Al_{2}$O$_{3}$ coating and tightly sealed the pores, unbounded area and microcracks in the coating. The alloy melt in the pores reacted with $Al_{2}$O$_{3}$ ceramic to produce a suboxide phase, Cu$_{2}$Ti$_{4}$O. This composite layer which was composed of $Al_{2}$O$_{3}$ and Cu$_{2}$Ti$_{4}$O phase had good microstructure and wear and corrosion resistance. Additionally, microstructures at interfaces between coating layers were greatly improved owing to the effect of vacuum heat treating.

• 한국분말재료학회지
• /
• 제25권1호
• /
• pp.25-29
• /
• 2018

Porous Cu with a dispersion of nanoscale $Al_2O_3$ particles is fabricated by freeze-drying $CuO-Al_2O_3$/camphene slurry and sintering. Camphene slurries with $CuO-Al_2O_3$ contents of 5 and 10 vol% are unidirectionally frozen at $-30^{\circ}C$, and pores are generated in the frozen specimens by camphene sublimation during air drying. The green bodies are sintered for 1 h at $700^{\circ}C$ and $800^{\circ}C$ in $H_2$ atmosphere. The sintered samples show large pores of $100{\mu}m$ in average size aligned parallel to the camphene growth direction. The internal walls of the large pores feature relatively small pores of ${\sim}10{\mu}m$ in size. The size of the large pores decreases with increasing $CuO-Al_2O_3$ content by the changing degree of powder rearrangement in the slurry. The size of the small pores decreases with increasing sintering temperature. Microstructural analysis reveals that 100-nm $Al_2O_3$ particles are homogeneously dispersed in the Cu matrix. These results suggest that a porous composite body with aligned large pores could be fabricated by a freeze-drying and $H_2$ reducing process.

• 한국재료학회지
• /
• 제23권12호
• /
• pp.722-726
• /
• 2013

Freeze drying of a porous Cu-Sn alloy with unidirectionally aligned pore channels was accomplished by using a composite powder of CuO-$SnO_2$ and camphene. Camphene slurries with CuO-$SnO_2$ content of 3, 5 and 10 vol% were prepared by mixing with a small amount of dispersant at $50^{\circ}C$. Freezing of a slurry was done at $-25^{\circ}C$ while the growth direction of the camphene was unidirectionally controlled. Pores were generated subsequently by sublimation of the camphene during drying in air for 48 h. The green bodies were hydrogen-reduced at $650^{\circ}C$ and then were sintered at $650^{\circ}C$ and $750^{\circ}C$ for 1 h. XRD analysis revealed that the CuO-$SnO_2$ powder was completely converted to Cu-Sn alloy without any reaction phases. The sintered samples showed large pores with an average size of above $100{\mu}m$ which were aligned parallel to the camphene growth direction. Also, the internal walls of the large pores had relatively small pores. The size of the large pores decreased with increasing CuO-$SnO_2$ content due to the change of the degree of powder rearrangement in the slurry. The size of the small pores decreased with increase of the sintering temperature from $650^{\circ}C$ to $750^{\circ}C$, while that of the large pores was unchanged. These results suggest that a porous alloy body with aligned large pores can be fabricated by a freeze-drying and hydrogen reduction process using oxide powders.

• Corrosion Science and Technology
• /
• 제6권3호
• /
• pp.133-139
• /
• 2007

Nickel powder was coated with aluminum nitrate solution to increase the thermal stability of a porous nickel support and control the nickel content in the Pd-Cu-Ni ternary alloyed membrane. Raw nickel powder and alumina coated nickel powder were uniaxialy pressed by home made press with metal cylindrical mold. Though the used nickel powder prepared by pulsed wire evaporation (PWE) method has a good thermal stability, the porous nickel support was too much sintered and the pores of porous nickel support was plugged at high temperature (over $800^{\circ}C$) making it not suitable for the porous support of a palladium based composite membrane. In order to overcome this problem, the nickel powder was coated by alumina and alumina modified porous nickel support resists up to $1000^{\circ}C$ without pore destruction. Furthermore, the compositions of Pd-Cu-Ni ternary alloy membrane prepared by magnetron sputtering and Cu-reflow could be controlled by not only Cu-reflow temperature but also alumina coating amount. SEM analysis and mercury porosimeter analysis evidenced that the alumina coated on the surface of nickel powder interrupted nickel sintering.

• 한국수소및신에너지학회논문집
• /
• 제23권4호
• /
• pp.353-363
• /
• 2012

The relationship between the diffusivity and electrochemical characteristics of lithium secondary battery with the modified Si anode material prepared in HF/$AgNO_3$ solution was investigated. The crystallographic structure and images of the modified porous Si and modified Si/Cu was examined using the X-ray diffraction, BET and SEM. To examine the effect of metal composite and pore size distribution according to chemical etching on the electrochemical characterization, the electrodes for half cells were prepared with the modified Si, modified Si/Cu, and modified Si/Cu annealed with $600^{\circ}C$. Our results showed that the chemical diffusivity of lithium ions was related to structure and resistance of Si/Cu composite anode material. The lithium diffusivity in modified silicon compound calculated from the CV was at the range of $1{\times}10^{-12}$ to $9{\times}10^{-16}cm^2/s$. The effects of modified silicon structure and resistance on the cycling efficiency were significant.

• 공업화학
• /
• 제21권3호
• /
• pp.328-332
• /
• 2010

본 연구에서는 다이에틸렌글리콜 용매 상에서 공침법을 이용하여 기공성 아연 구형 산화물과 구리-아연 복합 산화물을 합성하였다. 합성된 물질들의 물리화학적 특성은 전자현미경, X-선 회절분석, $N_2$ 흡착, $H_2$-TPR 방법을 통하여 분석되었고, 다양한 Cu 함량(0, 6.6, 21.3 36.4, 54.6, 77.8 wt%)을 포함한 Cu-ZnO 복합 산화물을 고정층 반응 장치에서 일산화탄소 산화 반응성을 고찰하였다. 합성된 산화물 중에서 Cu 함량이 증가할수록 Cu-ZnO의 비표면적과 미세 기공 부피는 감소하였으며, Cu (36.4 wt%)-ZnO이 가장 좋은 일산화탄소 산화 반응성을 나타내었다.

• 한국주조공학회지
• /
• 제23권5호
• /
• pp.244-250
• /
• 2003

The aim of this study is fabricating of composite filler metal (CFM) by a combination of selective laser sintering (SLS) of stainless steel powders (RapidSteel $2.0^{TM}$ and liquid phase infiltration of Ag-28 wt.%Cu alloy. Porous stainless steel body with inter-connected pore channels was fabricated by SLS, binder decomposing and densification processes. By the direct contact infiltration, the narrow inter-particle channels of the porous body were completely filled with the Ag-28 wt.%Cu alloy infiltrant. During infiltration, the dissolved elements of Fe, Ni and Cr from the porous body were solved into copper solid solution phases, which consist of eutectic structure of composite metal matrix. The S10C/CFM/S10C joints, which have narrow clearance gaps between them up to 10 micrometers, were joined successfully by self-feeding of filler metal from the matrix of CFM. The CFM kept its original thickness and microstructure after brazing. The tensile strength of brazed specimen was higher than 30 kgf/$mm^2$ and showed a typical ductile fracture mode in the CFM.

• 한국분말재료학회지
• /
• 제26권1호
• /
• pp.1-5
• /
• 2019

In this study, porous Mo-5 wt% Cu with unidirectionally aligned pores is prepared by freeze drying of camphene slurry with $MoO_3-CuO$ powders. Unidirectional freezing of camphene slurry with dispersion stability is conducted at $-25^{\circ}C$, and pores in the frozen specimens are generated by sublimation of the camphene crystals. The green bodies are hydrogen-reduced at $750^{\circ}C$ and sintered at $1000^{\circ}C$ for 1 h. X-ray diffraction analysis reveals that $MoO_3-CuO$ composite powders are completely converted to a Mo-and-Cu phase without any reaction phases by hydrogen reduction. The sintered bodies with the Mo-Cu phase show large and aligned parallel pores to the camphene growth direction as well as small pores in the internal walls of large pores. The pore size and porosity decrease with increasing composite powder content from 5 to 10 vol%. The change of pore characteristics is explained by the degree of powder rearrangement in slurry and the accumulation behavior of powders in the interdendritic spaces of solidified camphene.