• Journal of the Korean Applied Science and Technology
• /
• v.29 no.1
• /
• pp.102-107
• /
• 2012

The recovery of a Pt anode in a PEMFC through 30 ppm $H_2S/H_2$ exposure was evaluated by using a cyclic voltametry(CV) scan. First, the PEMFC unit cell performanc loss was measured three times under an anode feeding with 30 ppm $H_2S/H_2$ for 1hr at $0.5A/cm^2$ of current density. The initial cell performance was $1.16A/cm^2$ at 0.6 V without $H_2S$ poisoning. After first poisoning step for 1hr the cell performance was decrease to $0.77A/cm^2$, and the further poisoning steps decreased up 0.57 V. Finally, the recovery of the cell performance of $H_2S$ poisoned PEMFC was achieved up to 90.3% by applying CV scan. Moreover, we also found out that another possible approach for over 80% recovery of the cell performance of $H_2S$ poisoned anode Pt catalyst layer was to just inject fresh hydrogen into the anode feeding stream.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2011.06a
• /
• pp.129-129
• /
• 2011

The limited understanding of the surface properties of $Pt_3Ni$ for the oxygen reduction reaction (ORR) in polymer electrolyte membrane fuel cell (PEMFC) has motivated the study of properties and electronic structures of seven layered $Pt_3Ni$ (001), (110), and (111) surfaces. The first principle method based on density functional theory (DFT) is carried out. It is found that the bulk $Pt_3Ni$ has a ferromagnetic ground state with the ordered fcc type L12 structure, which is in good agreement with other results. Non magnetic Pt has the induced magnetic moment due to the strong hybridization between 3d Ni and 5d Pt. The magnetic moment of Pt and Ni enhanced on the surface of each due to surface effect however the magnetic moment of surface Pt in the Pt-segregated Pt3Ni (111) decreased and the magnetic moment of Ni in Ni rich subsurface increased significantly. The calculated d band centers of Pt explain the possibilities for oxygen absorption and play the important roles in altering the catalytic properties. The spin polarized densities of states are presented in order to understand physical properties of Pt in different surfaces in detail.

• The Transactions of the Korean Institute of Power Electronics
• /
• v.15 no.1
• /
• pp.75-85
• /
• 2010

In this paper, a Z-source hybrid active power filter is proposed to compensate the harmonics and reactive power in power distribution system. The proposed system is composed of a 7th harmonics-tuned passive filter and an active power filter with a Z-source inverter topology, while voltage source PWM inverter or current source PWM inverter are applied as the power converter topology of conventional active power filters. The Z-source impedance network along with shoot through capability would ensure a constant DC voltage across the DC link. A polymer electrolyte membrane fuel cell is employed as an compensation DC energy source of the proposed system and its equivalent R-L-C circuit is modeled for simulation. As the compensation and control algorithm of the proposed system, the current synchronous detection algorithm is applied. The simulation analysis by PSIM is performed under the three-phase 220V/60Hz voltage source and 25A nonlinear diode loads. The effectiveness of the proposed the system is verified in the steady and transient states.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2011.12a
• /
• pp.14-14
• /
• 2011

Limited understanding of the surface properties of $Pt_3Ni$ for the oxygen reduction reaction (ORR) in polymer electrolyte membrane fuel cell (PEMFC) has motivated the study of magnetic properties and electronic structures of Pt segregated $Pt_3Ni$ (111) surface during adsorption of oxygen molecule on it. The first principle method based on density functional theory (DFT) is carried out. Nonmagnetic Pt has induced magnetic moment due to strong hybridization between Ni 3d and Pt 5d. It is found that an oxygen molecule prefers bridge site with Pt rich subsurface environment for adsorption on the surface of Pt segregated $Pt_3Ni$ (111). It is seen that there is very small charge transfer from $O_2$ to Pt. The curve of energy versus magnetic moment of the oxygen explains the magnetic moments in transition states. We found the dissociation barrier of 1.07eV significantly higher than dissociation barrier 0.77eV on Pt (111) suggesting that the dissociation is more difficult on Pt segregated $Pt_3Ni$ (111) surface. The spin polarized densities of states are presented in order to understand electronic structures of Pt and $O_2$ during the adsorption in detail.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.5
• /
• pp.579-584
• /
• 2011

Sulfonated poly (ether sulfone)s containing BFBN were prepared from 2,3-bis(4-fluorophenyl)-2-butenedinitrile , 4,4-sulfonyldiphenol and sulfonated 4,4'-difluorodiphenylsulfone sodium salt using potassium carbonate, and followed acidification reaction with 1M $H_2SO_4$. BFBN was prepared from 4-fluorobenzylcyanide, $CCl_4$, NaOH using trimethylbenzylammoniumchloride . Sulfonated poly(ether sulfone)s containing BFBN were studied by FT-IR, $^1H$-NMR spectroscopy, and thermo gravimetric analysis (TGA). The water uptake of synthesized S-PBFBN membranes exhibit 31~62% compared with 28% of Nafion 211. The S-PBFBN membranes exhibit proton conductivities ($80^{\circ}C$, RH 100) of 53.8~117.4 mS/cm compared with 137.4 mS/cm of Nafion 211.

• Journal of Energy Engineering
• /
• v.19 no.2
• /
• pp.73-80
• /
• 2010

A solid oxide fuel cells(SOFC) is a clean energy technology which directly converts chemical energy to electric energy. When the SOFC is used in cogeneration then the efficiency can reach higher than 80%. Also, it has flexibility in using various fuels like natural gases and bio gases, so it has an advantage over polymer electrolyte membrane fuel cells in terms of fuel selection. A typical cathode material of the SOFC in conjunction with yttria stabilized zirconia(YSZ) electrolyte is still Sr-doped $LaMnO_3$(LSM). Recently, application of mixed electronic and ionic conducting perovskites such as Sr-doped $LaCoO_3$(LSCo), $LaFeO_3$(LSF), and $LaFe_{0.8}Co_{0.2}O_3$(LSCF) has drawn much attention because these materials exhibit lower electrode impedance than LSM. However, chemical reaction occurs at the manufacturing temperature of the cathode when these materials directly contact with YSZ. In addition, thermal expansion coefficient(TEC) mismatch with YSZ is also a significant issue. It is important, therefore, to develop cathode materials with good chemical stability and matched TEC with the SOFC electrolyte, as well as with high electrochemical activity.

• Korean Chemical Engineering Research
• /
• v.62 no.1
• /
• pp.7-12
• /
• 2024

The durability of the catalyst support has a significant effect on the durability of proton exchange membrane fuel cells (PEMFC). The accelerated durability evaluation of the catalyst support is performed at a high voltage (1.0 to 1.5 V), and the catalyst and ionomer binder in the catalyst layer are also deteriorated, hindering the evaluation of the durability of the support. The existing protocol (DOE protocol) was improved to find conditions in which the support, which is a durability evaluation target, deteriorates further. A protocol (MDOE) was developed in which the relative humidity was lowered by 35% and the number of voltage changes was reduced. After repeating the 1.0 ↔ 1.5 V voltage change cycle, the catalyst mass activitiy (MA), electrochemical active area (ECSA), electrical double layer capacity (DLC), Pt dissolution and particle growth were analyzed. Reaching 40% reduction in mass activity, the MDOE protocol took only 500 cycles, reducing the number of voltage changes compared to the DOE method and increasing the degradation of the carbon support by 50% compared to the DOE protocol.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.2
• /
• pp.142-147
• /
• 2009

The influence of graphitization of carbon support on the electrochemical corrosion of carbon and sintering of Pt particles are investigated by measuring $CO_2$ emission at a constant potential of 1.4 V for 30 min using on-line mass spectrometry and cyclic voltammogram. In comparison to commercial Pt/C (from Johnson Matthey), highly graphitized carbon nanofiber (CNF) supported Pt catalyst exhibits lower performance degradation and $CO_2$ emission. As the more carbon corrosion occurred, the more prominent changes were detected in electrochemical characteristics of fuel cell. This indicates that the carbon corrosion affects significantly the fuel cell durability. From the observed results, CNF is considered to be more corrosion resistant material as a catalyst support. However, CNF shows higher aggregation of Pt particles under repeated cyclic voltammetry between 0 and 0.8 V where the carbon corrosion is not initiated.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.143.1-143.1
• /
• 2010

고분자 전해질막 연료전지(Polymer Electrolyte Membrane Fuel Cell; PEMFC)는 수소를 이용하여 전기를 발생시키는 친환경적이고 이상적인 발전장치로 고효율과 높은 전류밀도를 가지며 그 응용분야가 다양하다. 저온에서 작동하는 PEM fuel cell은 전극에서 효과적인 산화환원반응을 위해 그 촉매로 활성이 우수한 Pt(Platinum)을 사용하고 있으나, Pt의 높은 가격은 연료전지의 상용화에 걸림돌이 되고 있다. 본 연구에서는 연료전지의 Pt/C 촉매 층에서 Pt의 분산성을 높여 Pt의 담지량을 줄이고 작동 중 발생하는 Pt의 응집 현상을 방지하여 Pt의 수명을 연장시킬 목적으로, Au(gold) 나노입자를 첨가한 Pt-Au/C 복합나노촉매를 제조하였다. 본 발표에서는 합성된 Pt-Au/C 복합촉매 중 Au 첨가량이 Pt 촉매의 활성에 미치는 영향을 조사하기 위하여, 복합촉매 중에 금속(Pt+Au)의 총 함량이 30 wt.%와 40 wt.% 인 Pt-Au/C 촉매에 대하여 각각 Au 첨가량을 변화시켜, cyclic voltammetry 법에 의해 Au 첨가 효과를 조사한 결과에 대하여 보고하고자 한다. Au 나노입자를 제조하기 위한 출발 물질로는 $HAuCl_4{\cdot}4H_2O$를 이용하였고 trisodium citrate와 $NaBH_4$를 환원제로 하여, 입경이 5~8 nm 인 Au 콜로이드를 제조하였다. Pt-Au/C 복합나노촉매를 제조하기 위하여 먼저 Au/C 복합분체가 제조되었다. 0.03g의 carbon이 첨가된 carbon 현탁액에 합성된 Au 콜로이드 수용액을 첨가한 후 24시간 동안 교반하여 Au/C 복합분체를 제조하였다. 이 Au/C 복합분체에 $H_2PtCl_6{\cdot}6H_2O$ 수용액을 현탁하고 methanol 을 환원제로 사용해 Pt를 환원 석출시켜 Pt-Au/C 복합촉매를 제조하였다. Pt-Au/C 복합 나노촉매에서 Pt와 Au를 다양한 비율(3:1, 2.5:1.5, 2:2)로 합성하였으며 Pt-Au/C 복합촉매 중 금속(Pt+Au) 촉매의 총 함량은 30 wt.%와 40 wt.%로 각각 제조되었다. Au 나노입자 콜로이드의 분산성은 UV-visible spectrum의 흡광도에 의해 관찰되었고, Pt-Au/C 복합 나노촉매의 형상 및 분산성 분석은 transmission electron microscopy(TEM)에 의해 이루어졌다. 또한, 촉매의 전기화학적 특성평가는 cyclic voltammetry(CV)에 의해 조사되었다.

• Journal of the Korean Applied Science and Technology
• /
• v.34 no.4
• /
• pp.883-891
• /
• 2017

For the preferential oxidation of CO contained in the fuel of polymer electrolyte membrane fuel cell (PEMFC), CuO-$CeO_2$ mixed oxide catalysts were prepared by the sol-gel and co-precipitation methods to replace noble metal catalysts. In the catalyst preparation by the sol-gel method, Cu/Ce ratio and hydrolysis ratio were changed. The catalytic activity of the prepared catalysts was compared with the catalytic activity of the noble metal catalyst($Pt/{\gamma}-Al_2O_3$). Among the catalysts prepared with different Cu/Ce ratios, the catalyst whose Cu/Ce ratio was 4:16 showed the highest CO conversion (90%) and selectivity (60%) at $150^{\circ}C$. As the hydrolysis ratio was increased in the catalyst preparation, surface area increased, and catalytic activity also increased. The highest CO conversions with the CuO-$CeO_2$ mixed oxide catalyst prepared by the co-precipitation method and the noble metal catalyst (1wt% $Pt/{\gamma}-Al_2O_3$) were 82 and 81% at $150^{\circ}C$, respectively, whereas the highest CO conversion with the CuO-$CeO_2$ mixed oxide catalyst prepared by the sol-gel method was 90% at the same temperature. This indicates that the catalyst prepared by the sol-gel method shows higher catalytic activity than the catalysts prepared by the co-precipitation method and the noble metal catalyst. From the CO-TPD experiment, it was found that the catalyst having CO desorption peak at a lower temperature ($140^{\circ}C$) revealed higher catalytic activity.