• Structural Engineering and Mechanics
• /
• v.63 no.3
• /
• pp.317-327
• /
• 2017

The addition of different types of polymers such as SBR, VAE, Acrylic, etc. in concrete and mortar leads to an increase in compressive, tensile and bond strength and decrease in permeability of polymer modified mortar (PMM) and concrete (PMC). The improvement in properties such as bond strength and impermeability makes PMM/PMC suitable for use as repair/retrofitting and water proofing material. In the present study effect of addition of fluoropolymer on the strength and permeability properties of mortar has been studied. In the cement mortar different percentages viz. 10, 20 and 30 percent of fluoropolymer by weight of cement was added. It has been observed that on addition of fluoropolymer in mortar the workability of mortar increases. In the present study all specimens were cast keeping the workability constant, i.e., flow value $105{\pm}5mm$, by changing the amount of water content in the mortar suitably. The specimens were cured for two different curing conditions. Firstly, these were cured wet for one day and then cured dry for 27 days. Secondly, specimens were cured wet for 7 days and then cured dry for 21 days. It has been observed that compressive strength and split tensile strength of specimens cured wet for 7 days and then cured dry for 21 days is 7-13 percent and 12-15 percent, respectively, higher than specimens cured one day dry and 27 days wet. The sorptivity of fluoropolymer modified mortar decreases by 88.56% and 91% for curing condtion one and two, respectively. However, It has been observed that on addition of 10 percent fluoropolymer both compressive and tensile strength decreases, but with the increase in percentage addition from 10 to 20 and 30 percent both the strengths starts increasing and becomes equal to that of the control specimen at 30 percent for both the curing conditions. It is further observed that percentage decrease in strength for second curing condition is relatively less as compared to the first curing condition. However, for both the curing conditions chloride ion permeability of polymer modified mortar becomes very low.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.58 no.3
• /
• pp.21-27
• /
• 2016

This study was performed to evaluate engineering properties of carbon and glass fiber reinforced recycled polymer concrete. Fiber reinforced recycled polymer concrete were used recycled aggregate as coarse aggregate, natural aggregate as fine aggregate, $CaCO_3$ as filler, unsaturated polyester resin as binder, and carbon and glass fiber as fibers. The compressive and flexural strength of carbon fiber reinforced recycled polymer concrete were in the range of 68~81.5 MPa and 19.1~21.5 MPa at the curing 7days. Also, the compressive and flexural strength of glass fiber reinforced recycled polymer concrete were in the range of 69.4~85.1 MPa and 19~20.1 MPa at the curing 7days. Abrasion ratio of carbon and glass fiber reinforced recycled polymer concrete were decreased 21.6 % and 11.6 % by fiber content 0.9 %, respectively. After impact resistance test, drop numbers of initial and final fracture were increased with increase of fiber contents. Accordingly, carbon fiber and glass fiber reinforced recycled polymer concrete will greatly improve the hydraulic structures, underground utilities and agricultural structures.

• Polymer(Korea)
• /
• v.25 no.1
• /
• pp.78-89
• /
• 2001

Morphological changes of unsaturated polyester/polyvinylacetate semi-IPN were studied while the phase separation and the cure reaction occurred in a competing fashion. The light scattering and thermal analysis techniques were used to investigate the phase separation rates and mechanical properties resultantly induced by molecular diffusion of thermoplastic polymer during the curing process of thermosetting polymer. The reaction activation energy was calculated by using Flynn-Wall method and the semi-IPN structure exhibited various phase-separation morphological characteristics. When PVAc composition was 10 wt%, the phase separation was not observed during the curing reaction, but the phase separation occurred in a similar fashion to nucleation and growth(NG) mechanism at room temperature. On the other hand, when PVAc composition was over 11.65 wt%, the phase separation was generated in the middle of the curing process. Consequently, the phase separation seemed to influence the curing reaction rate, which was also supported by the changing activation energy with conversion and PVAc composition. Finally, the total scattered intensity was measured at various temperature, and subsequently the diffusion rates of phase separation R(${\beta}m$) were evaluated.

• Macromolecular Research
• /
• v.16 no.2
• /
• pp.128-133
• /
• 2008

Several dual-curable acrylic pressure-sensitive adhesives (PSA) were synthesized by the radical polymerization of acrylic monomers containing benzophenone, hydroxyl, and alkyl groups. The optimum extent of UV-induced cure was determined by varying the content of the benzophenone groups (the photoinitiator) from 0.5 to 1.5 wt%. The weight average molecular weight of the polymers obtained ranged from 300,000 to 700,000 amu. The coated pressure-sensitive adhesives were cured either by short UV exposure to induce the grafting of acrylic polymers, or by heating for 6 hat $60^{\circ}C$ to promote the reactions between the polyisocyanates and hydroxyl groups. The dual-curing behavior was determined by monitoring both processes quantitatively by infrared spectroscopy. The developed dual-curable acrylic pressure-sensitive adhesives were found to compensate for the limitations in UV-induced curing of thick coatings.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.10a
• /
• pp.1-2
• /
• 2003

While aromatic polyimides and polyamides have found widespread use as high performance polymers, the present work addressed the need for organosoluble materials through the use of a hyperbranching scheme. The $AB_2$ monomers were prepared. The $AB_2$ monomers were then polymerized via aromatic fluoride-displacement and Yamazaki reactions to afford the corresponding hydroxyl-terminated hyperbranched polyimides (HT-PAEKI) and amine-terminated hyperbranched polyamides, respectively. HT-FAEKI was then functionalized with allyl and propargyl bromides as well as epichlorohydrin to afford allyl-terminated AT-PAEKI, propargyl-terminated PT-PAEKI, and epoxy (glycidyl)-terminated ET-PAEKI, in that order. All hyperbranched poly(ether-ketone-imide)s were soluble in common organic solvents. AT-PAEKI was blended with a bisphenol-A-based bismaleimide (BFA-BMI) in various weight ratios. Thermal, rheological, and mechanical properties of these blend systems were evaluated. Two characteristic hyperbranched polyamides, which the one has para-electron donating groups to the surface amine groups and the other has para-electron withdrawing groups to the surface amine groups, were selected to compare BMI curing behaviors. The electron rich polymer displayed ordinary Michael addition type exothermic reaction, while electron deficient polymer did display unusual curing behaviors. Based on analytical data, the later system provided the strong evidences to support room temperature curing of BMI by reactive intermediates instead of reactive primary amine groups on the macromolecule surface.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.5
• /
• pp.86-94
• /
• 2020

When the Superabsorbent Polymer (SAP) is added into concrete, the slump decreases rapidly, deteriorating the workability, the internal curing effect can be obtained through the water absorption and discharge process, and the internal voids of the concrete are increased. In this study, the effects of internal curing and voids were evaluated by evaluating the compressive strength, freeze-thaw resistance, and chloride penetration resistance of SAP-adding concrete that secured workability using a water reducing agent. Also, the internal curing effect of SAP was evaluated by dividing the curing conditions of concrete into water curing and sealed curing. From the result, as the SAP adding ratio increased, the amount of water reducing agent increased, and as for the compressive strength, the SAP adding ratio of 1.5% showed the greatest compressive strength. In particular, in the case of sealed curing showed higher compressive strength than the water curing. It is considered that the compressive strength increased due to the reduction of the effective water-cement ratio and the internal curing effect. Adding 1.0~1.5% of SAP improved the freeze-thaw resistance similar to the case of adding the AE agent, and the addition of more than 1.0% of SAP improved the chloride penetration resistance. The optimal adding ratio of SAP is 1.5%, and the adding ratio of 2.0% or more adversely affects the compressive strength and freeze-thaw resistance.

• Polymer(Korea)
• /
• v.38 no.4
• /
• pp.417-424
• /
• 2014

Reactivity and rheological behavior of highly concentrated polymer bonded explosives (PBX) simulant was studied. As a binder, thermosetting hydroxyl terminated polybutadiene (HTPB) was used. By using bimodal $CaCO_3$ (size ratio 10:1) and sugar particles (size ratio 25:1) as fillers, maximum 75 v% filling was possible during melt mixing. The relative viscosities of bimodal suspension were much lower than those of unimodal one and showed minimum values at 0.25 of fine particle fraction. In curing experiment, as curing temperature increased, the time of initiation and completeness of curing reaction became shortened, the torque kept low, and the change of internal temperature decreased.

• Journal of Adhesion and Interface
• /
• v.13 no.1
• /
• pp.38-44
• /
• 2012

Surface properties and curing behavior of UV-initiated photopolymerization with and without wax have been investigated by pendulum hardness, pencil hardness, gloss, photo-differential scanning calorimetry (photo-DSC) and SEM. In addition, the influence of wax type (paraffin wax, PE wax) on the various properties of UV cured films was studied. The results showed that the wax type was the significant factor affecting gloss and surface hardness of UV cured films. Specially, the photo-DSC results showed that ${\Delta}H$ for the UV cured films containing paraffin wax was higher than the corresponding values for the formulation without wax and with PE wax. The observed results clearly demonstrate that the photopolymerization of UV curing with paraffin wax in an air atmosphere is less inhibited by the oxygen compared to UV curing without wax and with PE wax.

• Polymer(Korea)
• /
• v.34 no.5
• /
• pp.469-473
• /
• 2010

The curing mechanism and characteristics of UV curable acrylate resins were studied using Photo-DSC, FTIR, and Raman spectroscopy. Effects of chemical structures of acrylate, numbers of functional group, and UV intensity on curing kinetics were investigated with Photo-DSC. FTIR and Raman spectroscopy has been used to understand curing mechanisms and reaction conversion. In order to investigate the effect of oxygen on the photo-curing reaction, the curing process was compared between the acrylate and thiol-ene resins. The reaction conversion was found to be less than 80% for acrylate resins. The photo-curing reaction of the acrylate resin could not proceed to the end because of oxygen which acts as a reaction inhibitor while the thiol-ene resin was hardly affected from oxygen during the curing process.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1394-1399
• /
• 2007

Recently, Study of 3D freeform fabrication method was working in the various applications. For example, in the powder base, it's laminated using a binding method or laser sintering method. However, these methods are not suitable in the office environments because it dust with powder that is bad for health. In this paper, we introduce a method of 3D freeform fabrication using a curing of photo-polymer resin and construct a system has multi printing head. A photo-polymer curing method has simply fabrication process and high strength of manufacturing part. However, this method has a problem on the multi print-head system. Because multi-printing system has a other printing method compare with a single printing system. Therefore, we experiment a single head 3D printing and proposed a 3D printing method using a multi-piezo head.