• 한국농공학회논문집
• /
• 제57권4호
• /
• pp.11-19
• /
• 2015

The important properties of EVA (ethylene vinyl acetate) redispersible polymer was waterproof, densification of internal pore space of concrete and ball bearing and micro filler. Also, the significant role of polypropylene(PP) fiber was crack control and blockade of movement for deterioration factors. The most studies for EVA were limited in the field of mortar and PP fiber reinforced concrete had been studied in the state of being restricted unit water content, rich mix and mixing much of the fiber without considering construction site. Therefore, the control mix design were applied in ready mixed concrete using 10 % fly ash of total cement weight used in batch plant. On the basis of control mix design, EVA contents ranging from 0 % to 10 % of total cement weight and PP fiber contents ranging from 0 % to 0.5 % of EVA concrete volume were used in the mix designs. The results showed the maximum compressive strength value was measured at EVA 5.0 % and PP fiber 0.1 %, the minimum water absorption ratio was at EVA 10 % and PP fiber 0 %, the durability factor for freezing and thawing resistance was at EVA 5.0 % and PP fiber 0.3 % and the minimum weight reduction ratio of resistance to sulfuric acid attack was at EVA 10 % and PP fiber 0.5 % after curing age 42days. Meanwhile, From these results, PP fiber reinforced EVA concrete would be very benefit, if each optimal mix types were used in hydraulic structures, underground utilities and agricultural structures.

• 한국잠사곤충학회지
• /
• 제27권2호
• /
• pp.28-39
• /
• 1985

견직물의 실용성능(방추도, 세탁성)을 개선할 목적으로 실크하브다이(silk habutae)에 실리콘수지를 유화 가공법으로 처리하였다. 실리콘가공 하브다이의 방추도, 발수도, 유연도, 강신도, 수분율 등은 직물검사 방법에 따라서 검사하였고 가공 후 견피브로인의 구조적인 변화를 구명하기 위하여 주사전자현미경, 아미노산분석, X-선 회절강도, FT-IR 흡수분석에 의하여 검토한 결과 아래와 같은 결과를 얻었다. 1) 견하브다이 직물의 방추도는 soaping 처리오 큐어링 조건에 의하여 현저히 개선되었다. 2) 실리콘 수지 가공에 의하여 견하브다이의 발수도와 유연도가 향상되었고, 가공 후 silk fibroin을 주사전자현미경으로 관찰한 결과 견섬유 특유의 불규칙한 섬유표면은 평활하게 관찰되었다. 3) 실리콘 수지와 silk fibroin의 반응에 따라서 피브로인 조성 아미노산 중 극성기를 가지고 있는 아미노산의 감소비율이 현저하였다. 4) 실리콘 수지가공 silk habutae는 soaping에 의하여 X-선 회절강도가 높아지는 경향이었다. 5) 가공 후 견하브다이의 FT-IR 흡수곡선에 실록산등의 peak가 검출된 것으로 미루어 fibroin의 개질이 가능하다고 생각된다.

• 한국응용과학기술학회지
• /
• 제22권3호
• /
• pp.270-280
• /
• 2005

To maximize a synergy effect in flame-retardancy of flame-retardant coatings, phosphorus and chlorine were introduced in polymer chains. Two-components PU flame-retardant modified polyesters (ABTTC-10C, -20C, -30C) were prepared by curing, at room temperature, of isocyanate (allophanate-trimer) and prepared modified polyesters which contain phosphorus and chlorine. To examine the film properties of the prepared flame-retardant coatings, film specimens were prepared with the prepared coatings. The film properties of ABTTC, ABTTC-10C and ABTTC-20C, which contain 0, 10 and 20wt%, 2,4-dichlorobenzoic acid (2,4-DCBA), respectively, were proved to be good, whereas the film properties of ABTTC-30C, which contains 30wt% 2,4-DCBA, were proved to be a little bit poor. Two kinds of flame retardancy tests, $45^{\circ}$Meckel burner method and LOI method, were performed. With the $45^{\circ}$Meckel burner method, three flame-retardant coatings except ABTTC showed less than 3.4 cm of char length, and showed less than 2 seconds of afterflaming and afterglow. From this result, the prepared flame-retardant coatings were proved to have the 1st grade flame retardancy. With the LOI method, the LOI values of the coatings containing more than 10wt% 2,4-DCBA were higher than 30wt%, which means that the coatings possess good flame-retardancy. From these results, it was found that synergistic effect in flame-retardancy was taken place by the introduced phosphorus and chlorine.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2011년도 제37회 추계학술대회논문집
• /
• pp.441-444
• /
• 2011

폴리우레탄 계열 바인더용 Prepolymer로 많이 사용되고 있는 HTPB의 상용모델에는 Type A와 Type B 2종류의 모델이 있다. 이에 국내외에서 생산되고 있는 이 2가지 모델에 대해 이화학적 특성과 주장약 PBX-A에 적용하여 점도 및 기계적 특성 등을 연구하였다. Type A는 Hydroxy value가 낮아 주장약에는 적용하기 힘들다고 판단되어 시험에서 제외하였으며, Type B의 경우 Type B-3 대비 Type B-1, 2를 공정에 적용하기에는 불리한 기계적 특성을 보였다. 하지만 Type B-2, 3의 공정조건(당량비/경화조건)을 규격 내에서 변경 적용한다면 이상은 없을 듯하나 Type B-3와 같은 공정조건으로 적용하기 위해서는 높은 Hydroxyl Value와 Functionality의 HTPB를 적용할 필요가 있다.

• 접착 및 계면
• /
• 제21권2호
• /
• pp.58-64
• /
• 2020

본 연구에서는 UV 경화형 폴리우레탄 아크릴레이트와 실리카 나노입자를 용매에 분산하여 간편한 스프레이 코팅을 통해 초발수 및 초발유 표면을 제작하였다. 용매의 종류, 고분자의 농도, 분사량 조절에 따른 코팅 표면 구조의 변화를 확인하였으며, 물과 오일의 접촉각 측정을 통해 초발수 및 초발유 특성을 정량화 하였다. 스프레이 코팅 표면의 re-entrant 구조를 분석하여 초발수 및 초발유 특성이 극대화된 스프레이 코팅의 메커니즘을 제시하였다. 최적화된 스프레이 코팅 조건을 적용하여 제조된 표면의 물과 오일의 접촉각 hysteresis는 각각 2°, 30° 이하이며 오일 방울이 표면에서 튈 정도로 우수한 초발수 및 초발유 특성을 보였다.

• 마이크로전자및패키징학회지
• /
• 제22권1호
• /
• pp.35-41
• /
• 2015

In this study, in order to improve the reliability of ACF interconnections, solder ACF joints were investigated interms of solder joint morphology and solder wetting areas, and evaluated the electrical properties of Flex-on-Board (FOB) interconncections. Solder ACF joints with the ultrasonic bonding method showed excellent solder wetting by broken solder oxide layers on solder surfaces compared with solder joints with remaining solder oxide layer bonded by the conventional thermo-compression (TC) bonding method. When higher target temperature was used, Sn58Bi solder joints showed concave shape due to lower degree of cure of resin at solder MP by higher heating rate. ACFs with epoxy resins and SAC305 solders showed lower degree of resin cure at solder MP due to the slow curing rate resulting in concave shaped solder joints. In terms of solder wetting area, solder ACFs with $25-32{\mu}m$ diameters and 30-40 wt% showed highest wetted solder areas. Solder ACF joints with the concave shape and the highest wetting area showed lower contact resistances and higher reliability in PCT results than conventional ACF joints. These results indicate that solder morphologies and wetting areas of solder ACF joints can be controlled by adjustment of bonding conditions and material properties of solder and polymer resin to improve reliability of ACF joints.

• The Journal of Advanced Prosthodontics
• /
• 제5권4호
• /
• pp.396-401
• /
• 2013

PURPOSE. The purpose of this in vitro study was to investigate the flexural properties of a recently introduced urethane dimethacrylate denture base material (Eclipse) after being repaired with two different materials. MATERIALS AND METHODS. Two repair groups and a control group consisting of 10 specimens each were generated. The ES group was repaired with auto-polymerizing polymer. The EE group was repaired with the Eclipse. The E group was left intact as a control group. A 3-point bending test device which was set to travel at a crosshead speed of 5 mm/min was used. Specimens were loaded until fracture occurred and the mean displacement, maximum load, flexural modulus and flexural strength values and standard deviations were calculated for each group and the data were statistically analyzed. The results were assessed at a significance level of P<.05. RESULTS. The mean "displacement", "maximum load before fracture", flexural strength" and "flexural modulus" rates of Group E were statistically significant higher than those of Groups ES and EE, but no significant difference (P>.05) was found between the mean values of Group ES and EE. There was a statistically significant positive relation (P<.01) between the displacement and maximum load of Group ES (99.5%), Group EE (94.3%) and Group E (84.4%). CONCLUSION. The more economic and commonly used self-curing acrylic resin can be recommended as an alternative repair material for Eclipse denture bases.

• 대한치과보철학회지
• /
• 제44권6호
• /
• pp.712-721
• /
• 2006

Statement of problem. Acrylic resin is most commonly used for denture bases. However, acrylic resin has week points of volumetric shrinkage during polymerization that reduces denture fit. The expandability of POSS (Polyhedral Oligomeric Silsesquioxane) containing polymer could be expected to reduce the polymerization shrinkage of denture bases and would increase the adaptability of the denture to the tissue. Purpose. The purpose of this study was to compare the dimensional stability in the conventional acrylic resin base, POSS-containing acrylic resin base, and metal bases. Materials and methods. Thirty six maxillary edentulous casts and dentures of different base were fabricated. Tooth movement and tissue contour change of denture after processing (resin curing, deflasking, decasting and finishing without polishing) and immersion in artificial saliva at $37^{\circ}C$ for 1 week and 4 weeks were measured using digital measuring microscope and threedimensional laser scanner. Results. The results were as follows: 1. The conventional resin group showed significant (p<0.01) dimensional change throughout the procedure (processing and immersion in artificial saliva). 2. After processing, the metal group and POSS resin group showed lower linear and 3-dimensional change than conventional resin group (p<0.01). 3. There was no statistically significant linear and 3-dimensional change after immersion for 1 week and 4 weeks in metal and POSS resin group. 4. In all groups, the midline and alveolar ridge crest area presented smaller 3-dimensional change compared with vestibule and posterior palatal seal area after processing and soaking in artificial saliva for 1 week and 4 weeks (p<0.01). Conclusion. In this study, a reinforced acrylic-based resin with POSS showed good dimensional stability.

• The Journal of Advanced Prosthodontics
• /
• 제9권6호
• /
• pp.439-446
• /
• 2017

PURPOSE. To evaluate the effects of different surface treatments on the bond strength of novel CAD/CAM restorative materials to resin cement by four point bending test. MATERIALS AND METHODS. The CAD/CAM materials under investigation were e.max CAD, Mark II, Lava Ultimate, and Enamic. A total of 400 bar specimens ($4{\times}1.2{\times}12mm$) (n=10) milled from the CAD/CAM blocks underwent various pretreatments (no pretreatment (C), hydrofluoric acid (A), hydrofluoric acid + universal adhesive (Scotchbond) (AS), sandblasting (Sb), and sandblasting + universal adhesive (SbS)). The bars were luted end-to-end on the prepared surfaces with a dual curing adhesive resin cement (Variolink N, Ivoclar Vivadent) on the custom-made stainless steel mold. Ten test specimens for each treatment and material combination were performed with four point bending test method. Data were analyzed using ANOVA and Tukey's test. RESULTS. The surface treatment and type of CAD/CAM restorative material showed a significant effect on the four point bending strength (FPBS) (P<.001). For LDC, AS surface treatment showed the highest FPBS results ($100.31{\pm}10.7MPa$) and the lowest values were obtained in RNC ($23.63{\pm}9.0MPa$) for control group. SEM analyses showed that the surface topography of CAD/CAM restorative materials was modified after treatments. CONCLUSION. The surface treatment of sandblasting or HF acid etching in combination with a universal adhesive containing MDP can be suggested for the adhesive cementation of the novel CAD/CAM restorative materials.

• Composites Research
• /
• 제17권6호
• /
• pp.28-36
• /
• 2004

복합재료의 성형조건과 재료의 변형간의 관계를 규명하기 위해 PVC 포움-직물 복합재료 샌드위치 구조의 성형공정 중 토우 구조의 미소 변형을 고찰하였다. 실험에 사용한 포움은 4가지 밀도를 가지는 PVC 포움이며, 면재로는 탄소섬유게폭시 프리프레그(3k)를 사용하였다. 디지털 현미경과 이미지 분석 도구를 사용하여 직물 복합재료의 굴곡 각과 토우 진폭 등의 토우 파라메터를 측정하여 서로 비교하였다. 성형 중 포움의 변화가 직물 복합재료 구조의 변형에 미치는 영향을 파악하기 위해 세 가지 온도 조건($25^{\circ}C$, $80{\circ}C$, $125^{\circ}C$)에서 포움의 압축 실험을 수행하였다. 복합재료 토우 구조의 현미경 관찰 결과 토우의 미소 변형은 포움의 밀도와 성형 압력에 따라 서로 다른 경향을 나타내었으며. 특히 포움의 변형 거동에 큰 영향을 받는 것을 확인하였다.