• 한국세라믹학회지
• /
• 제44권9호
• /
• pp.496-501
• /
• 2007

The properties of the polymer-modified mortars are influenced by the polymer film, cement hydrates and the combined structure between the organic and inorganic phases. Also, this quality of polymer modified cement strongly depend on weather condition. To overcome this problem, polymer-modified cement based on rapid setting cement mortars were prepared by varying polymer/cement mass ratio (P/C) with a constant water/cement mass ratio of 0.5. The effect of polymer on the hydration of this polymer cement is studied on different curing temperature. The results showed that the polymer mortar which is modified with rapid setting cement have superior physical strength properties on independent curing temperature. In addition the PIC ratio, the compressive strength, flexural strength, tensile strength and adhesion strength of mortar is enhances and polymer-modified cement based on rapid setting cement is more beneficial to the improvement of the mortar properties in jobsite.

• 한국건축시공학회지
• /
• 제9권5호
• /
• pp.71-77
• /
• 2009

시멘트 혼화용 폴리머 디스퍼션은 시멘트 모르타르 및 콘크리트 내부에서 폴리머 필림을 형성하여 각종 역학적성 질 및 내구성을 향상시킨다. 본 연구는 3종류의 폴리머 디스퍼션을 폴리머 시멘트비 0, 5, 10, 20%로 변환한 폴리머 시멘트 모르타르를 제작, 투수시험을 실시하여 투수성능을 실험하였으며, 더욱이 폴리머 시멘트 슬러리를 폴리머 시멘트 모르타르 표면에 도포하여 방수성능의 개선효과를 평가하였다. 또한 보통시멘트 콘크리트 표면에 폴리머 시멘트 슬러리를 도포하여 시멘트 콘크리트와 폴리머 시멘트 슬러리의 건조수축을 측정하였다. 그리고 기본적인 역학적 성상인 휨강도와 압축강도를 측정하여 보통 시멘트 모르타르와 비교 검토하였다. 연구결과, 폴리머 시멘트 모르타르는 보통 시멘트 모르타르에 비해 방수성능과 강도가 크게 개선되었으며, 폴리머 시멘트 슬러리의 건조수축은 시멘트 콘크리트에 비해 4-5배 크게 나타났다. 또한 향후 건조수축에 따른 접착성능의 영향성에 대한 연구가 진행되어야 할 것이다.

• 한국세라믹학회지
• /
• 제36권5호
• /
• pp.539-546
• /
• 1999

Absorbent polymer-cement composites were fabricated by the semi-powder mixing OPC(ordinary Portland cement) with an absorbent polymer. The effects of absorbent polymer on the mechanical properties and the hydration characteristics were observed and the polymer-cement interaction also discussed. Absorbent polymer-cement composites showed the value of total porosity of 8vol% the value of 28 days flexural strength was up to 280 Kgf/cm2 in the case of absorbent polymer-cement composite at 1 wt% absorbent polymer content and microstructure of absorbent polymer-cement composite has been observed more dense than that of OPC paste. Accordingly the permeability of compositewas improved and so the moisture resistance was also increased. Adding polymer did not retard the hydration of OPC. It was considered from the results of IR(infrared) analysis that the functional group of absorbent polymer would be changed from unidentate to bidentate during by the hydration of cement minerals.

• 한국세라믹학회지
• /
• 제45권11호
• /
• pp.744-749
• /
• 2008

The properties of the polymer-modified mortars are influenced by the polymer film, cement hydrates and the combined structure between the organic and inorganic phases. Also, this quality of polymer modified cement strongly depend on weather condition and polymer cement ratio. To overcome this problem, polymer-modified cement were prepared by varying polymer/cement mass ratio (P/C) with $0{\sim}20%$ and constant water/cement mass ratio of 0.5. The effect of polymer on the hydration of this polymer cement is studied on different polymer cement ratio. The results showed that the polymer cement paste have increased the viscosity in addition the amount of polymer dosage and the polymers is completed resulting in a reduced degree of hydration caused by different ion elution amount. Also we know that the reactants is calcium acetate as a results of chemical reaction between acetate group in EVA which is hydrolysis in water and $Ca^{2+}$ ion during hydration of cement.

• 콘크리트학회논문집
• /
• 제18권5호
• /
• pp.667-675
• /
• 2006

대분분의 콘크리트 구조물은 여러 가지 환경요인에 노출되었는데, 여러 가지 환경요인 중, 요인 한가지만의 작용이 아니라 여러 가지 요인이 복합적으로 작용하여 콘크리트의 내구성은 현격하게 저하하게 된다. 본 연구에서는 복합양생을 받는 폴리머 시멘트 모르타르에 관한 강도 및 내구성 개선효과를 실험하였다. 폴리머 종류, 폴리머 시멘트비, 시멘트-잔골재비를 변화하여 폴리머 시멘트 모르타르를 제작한 후, 5가지의 환경요인, 즉 양생조건을 달리하여, 강도성상, 중성화, 염화물이온 침투, 내동해성, 내산성을 시험하였다. 시험결과, 폴리머 시멘트 모르타르는 보통 시멘트 모르타르에 비해 우수한 강도성상을 나타냈으며, 양생조건 II와 V에서 강도가 개선되었으나, 양생조건 I와 IV에서는 강도의 발현이 낮았다. 또한 중성화 및 염화물이온 침투 깊이는 양생조건 III-C, IV-B, V-A 순으로 작아졌으며, 폴리머 시멘트비의 증가에 따라 감소하였다. 본 연구에서 폴리머 시멘트비의 적정 혼입비는 10% 또는 15%이었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회 논문집(II)
• /
• pp.1121-1126
• /
• 2000

The purpose of this study is to clarify chemical resistance of polymer-cement slurry coated reinforcing bars. Polymer cement slurry coated reinforcing bars were showed the good state to the bending resistance, impact resistance, adhesive strength, but exact data of the chemical resistance do not exist. Through the experimental, it is to certify chemical resistance of polymer cement slurry coated reinforcing bars. In this study, polymer cement slurry coated reinforcing bars are prepared with two types of polymer, polymer-cement ratios of 50%, 100%, 150%, coating thickness, curing periods of 3, 7, 28days, and tested for chemical resistance as KS(Korea Standard). From the test results, chemical resistance of polymer cement slurry coated reinforcing bars used by acrylic and St/BA emulsion were showed excellent without concerned polymer-cement ratios, curing period except for 1% aqueous solution $H_2SO_4$. But polymer cement coated reinforcing bar used by acrylic emulsion is inferior to aqueous solution NaOH.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 가을 학술논문 발표대회
• /
• pp.159-160
• /
• 2022

The purpose of this study is to evaluate the adhesion in flexure depending on the cement type, polymer type, polymer-cement ratio, and silica fume ratio of the polymer-cement composites(PCCs) for crack repair in RC structures to induce optimal mix proportions. The adhesion in flexure of PCCs for crack repair of RC structure has a significant effect on the polymer type and polymer-cement ratio, and the adhesion in flexure is generally improved with mixing of silica fume as a mixture. The adhesion in flexure according to the type of polymer is slightly higher in the order of SAE, EVA, and SBR, and it is relatively high at the polymer-cement ratio of 60% or 80%. In addition, the adhesion in flexure of PCCs with silica fume ratio of 10% or 20% to the cement weight is higher than that without silica fume. In order to improve the adhesion in flexure of PCCs for repairing cracks in RC structures, the optimal mix design is to properly adjust the cement type, polymer type, polymer-cement ratio, and silica fume ratio.

• 공업화학
• /
• 제5권5호
• /
• pp.786-794
• /
• 1994

폴리머-시멘트 모르타르의 강도와 내구성에 대하여 검토하였다. 폴리머-혼화제로서 styrene-butadiene rubber(SBR) 라텍스, ethylene-vinyl acetate(EVA) 에멀젼 및 polyacrylic ester(PAE) 에멀젼을 사용하고, 폴린머-시멘트 비를 다양하게 변화시켜(5, 10, 15, 20 wt%) 공시체를 제작하였다. 내구성의 평가시험으로는 동결융해시험, 내산성시험 및 내열성 시험을 수행하였다. 폴리머-시멘트 모르타르의 내동해성은 폴리머-시멘트비가 증가될수록 현저히 향상되었으나 내산성과 내열성은 저하되었다. SBR 폴리머-시멘트 모르타르의 강도(압축 및 휨강도)는 폴리머-시멘트비가 증가될수록 향상되었으나 EVA 및 PAE 폴리머-시멘트 모르타르는 폴리머-시멘트비 10wt%에서 최대치를 나타내었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 가을 학술발표논문집(II)
• /
• pp.356-361
• /
• 1998

Permeable polymer cement concrete in this study is one of the invironment conscious concretes that can be applied at roads, side walks, parking lots, interlocking block and river embankment, etc. In this study, permeable polymer cement concretes using polymer dispersion(St/Ac) with water-cement ratios of 25, 30, 35 and 40%, polymer-cement ratios of 0, 5, 10, 15 and 20%, and a ratio of cement to aggregate (by weight), 1 : 3.5(about 415kg/㎥), 1 : 4.0(about 375 kg/㎥), and 1 : 4.5(about 345kg/㎥) are prepared, and tested for compressive, flexural and tensile strength, and permeability. From the test results, increase in the strengths of permeable polymer cement concrete are clearly observed with increasing polymer-cement ratio, we can obtain the maximum strengths at water-cement ratio of 35%. The optimum permeable polymer cement concrete according to application and location of work can be selected in various mix proportions.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.727-730
• /
• 2004

The purpose of this study is to evaluate the fundamental properties of fine type cement grouts with redispersible polymer powders. Cement grouts with redispersible polymer powders are prepared with various polymer-cement ratios, and tested. for flow, water absorption, drying shrinkage, flexural and compressive strengths. From the test results, flow of the cement grouts with EVA and Va/VeoVa polymer powers decreased with increasing elapsed time. Regardless of polymer type, the flexural strength of the cement grouts tends to increase with increase in polymer-cement ratio. The maximum compressive strengths of the cement grouts are obtained at a polymer-cement ratio of $5\%$.