• Journal of the Korean Applied Science and Technology
• /
• v.26 no.4
• /
• pp.400-406
• /
• 2009

We investigated the electrochemical properties for Langmuir-Blodgett (LB) films of functionalized polyimide. LB films of polyimide monolayer were deposited by the Langmuir-Blodgett method on the indium tin oxide(ITO) glass. The electrochemical properties measured by cyclic voltammetry with a three-electrode system(an Ag/AgCl reference electrode, a platinum wire counter electrode and LB film-coated ITO working electrode) at various concentrations(0.5, 1.0, and 1.5 N) of $NaClO_4$ solution. The current of reduction and oxidation range was measured from 1650 mV to -1350 mV, continuously. The scan rates were 50, 100 and 150 mV/s, respectively. As a result, monolayer and multilayer LB films of polyimide are appeared on irreversible process caused by the oxidation current from the cyclic voltammogram.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.1
• /
• pp.56-60
• /
• 2014

The polyimide composite membranes were prepared with polyimide composite solutions including graphenes by using the phase inversion method. The morphologies of these membranes were significantly changed according to the graphene loadings in composite solutions and the solvent systems of the composite solutions. The finger-like macro-voids were formed in the hollow fiber membranes which were prepared in the NMP solvent system with a small amount of ethanol. As increasing the content of the viscous alcohols such as glycerol or 1,3-propanediol in the composite solution, however, the morphologies of the hollow fiber membranes were changed to sponge-like types. In case of flat membranes, the increase of graphene content in polyimide composites causes that their membranes change from the finger-like macro-porous to sponge-like morphologies.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.199-202
• /
• 2003

We have investigated the generation of pretilt angle for a nematic liquid crystal (NLC) alignment with rubbing alignment method on two kinds of polyimide (PI) surfaces using thin plastic substrates. The generated NLC pretilt angles on the pre-imidized type PI are about $3.8^{\circ}$ by the rubbing alignment method with thin plastic substrates, However, the pretilt angle measured at about $2.8^{\circ}$ lower on the polyamic acid type PI than by pre-imidized type PI surface with thin polymer film. The tilt angle increases as increasing curring temperature for making polyimide layer using polyamic acid type PI. It was concluded that pretilt angle in the polyimide surface is attributable to the increasing of imide rato.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.209-212
• /
• 2001

Polyimide(PI) films have been considered as the interlayer dielectric materials due to low dielectric constant, low water absorption, high gap-fill and planarization capability. The PI mm Was etched with using inductively coupled plasma (ICP). The etching characteristics such as etch rate and selectivity were evaluated to gas mixing ratio. High etch rate was $8300{\AA}/min$ and vertical profile was approximately acquired $90^{\circ}$ at $CF_{4}/(CF_{4}+O_{2})$ of 0.2. The selectivies of polyimide to PR and $SiO_{2}$ were 1.2, 5.9, respectively. The etching profiles of PI films with an aluminum pattern were measured by a scanning electron microscope (SEM). The chemical states on the PI film surface were investigated by x-ray photoelectron spectroscopy (XPS). Radical densities of oxygen and fluorine in different gas mixing ratio of $O_{2}/CF_{4}$ were investigated by optical emission spectrometer (OES).

• Korean Membrane Journal
• /
• v.4 no.1
• /
• pp.25-35
• /
• 2002

The gas permeation properties have been studied on carbon molecular sieve (CMS) membranes prepared by pyrolysis of P84 polyimide under various conditions. P84 polyimide shows high permselectivities (O$_2$/N$_2$= 9.17 and CO$_2$/N$_2$= 35) for various gas pairs and has a good processibility because it is easily soluble in high polar solvents such as N-methylpyrrolidinone (NMP), dimethylformamide (DMF), and N,N-dimethylacetamide (DMAc). After pyrolysis under Ar flow, the change in the heating rate was found to affect the gas permeation properties to some extent. The permeabilities of the selected gases were shown to be in the order He ＞ CO$_2$＞ O$_2$＞ N$_2$for all the CMS membranes, whose order was in accordance with the order of kinetic gas diameters. It also revealed that the pyrolysis temperature considerably influenced the gas permeation properties of the CMS membranes derived from P84 polyimide. The CMS membranes pyrolized at 700$\^{C}$ temperature exhibited the highest permeability with relatively targe loss in permselectivity. This means that the pyrolysis temperature should be varied in accordance with target gases to be separated.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.56 no.11
• /
• pp.1998-2003
• /
• 2007

A flexible but implantable polyimide-based neural implant was fabricated for reliable and stable long-term monitoring of neural activities from brain. The developed neural implant provides 3-dimensional (3D) $3{\times}3$ structure, avoids any hand handling, and makes the insertion more efficient and reliable. Any film curvature caused by residual stress was not observed in the electrode. The 3D flexible polyimide electrode penetrated a dense gel whose stiffness is close to live brain tissue, because a ${\sim}1{\mu}m$ thick nickel was electroplated along the edge of the shank in order to improve the stiffness. The recording sites were positioned at both side of the shank to increase the probability of recording neural signals from a target volume of tissue. Impedance remained stable over 72 hours because of extremely low moisture uptake in the polyimide dielectric layers. At electrical recording test in vitro, the fabricated electrode showed excellent recording performance, suggesting that this electrode has the potential for great recording from neuron firing and long-term implant performance.

• Macromolecular Research
• /
• v.12 no.3
• /
• pp.263-268
• /
• 2004

We have synthesized a water-soluble polyimide precursor, poly(amic acid) amine salt (PAD), from pyromellitic dianhydride (PMDA), 4,4'-oxydianiline, and N,N -dimethylethanolamine (DMEA) and have investigated in detail its properties with respect to the degree of salt formation (D$\_$sf/). The maximum value of D$\_$sf/ we obtained upon precipitation of the precursor solution into acetone was 79%. We synthesized a PAD having a D$\_$sf/ of 100% (PAD100) by the solid state drying of an organic solution. The precursors showed different solubility depending on the D$\_$sf/ to make up to 4 wt% solutions in water containing a small amount of DMEA. PAD100 is completely soluble in pure water. We investigated the imidization behavior of PAD in aqueous solution using various spectroscopic methods, which revealed that PAD 100 has faster imidization kinetics relative to that of the poly(amic acid)-type precursors. The resulting polyimide films prepared from an aqueous precursor solution possess almost similar physical and thermal properties as those prepared from N-methyl-2-pyrrolidone(NMP) solution. Therefore, we have demonstrated that PAD can be used as a water-based precursor of polyimide; this procedure avoids the use of toxic organic solvents, such as NMP.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.400-400
• /
• 2007

In this study, we investigated liquid crystal (LC) alignment with ion beam (IB) that non contact alignment technique on polyimide and electro-optical characteristics of twisted nematic (TN)-liquid crystal display (LCD) on the polyimide under various ion beam angles. In this experiment, polyimide layer was coated on glass by spin-coating and Voltage-transmittance(VT) and response time characteristics of the TN cell were measured by a LCD evaluation system. The good characteristics of the nematic liquid crystal (NLC) alignment with the ion beam exposured polyimide surface was observed. In addition, it can be achieved the good EO properties, and residual DC property of the ion beam aligned TN cell on polyimide surface.

• Transactions of the Korean hydrogen and new energy society
• /
• v.32 no.5
• /
• pp.308-314
• /
• 2021

Chemical durability issue in polymer electrolyte membranes has been a challenge for the commercialization of polymer electrolyte membrane fuel cells (PEMFCs). In this study, we proposed a manufacturing method of Nafion composite membrane containing a stable polyimide antioxidant to improve the chemical durability of the membrane. The thermal casting of the Nafion solution with poly (amic acid) induced polyimide reaction. We evaluated proton conductivity, oxidative stability with ex-situ Fenton's test, and fluoride ion emission to analyze the effect of polyimide antioxidants. We confirmed that incorporating the polyimide antioxidant improves the chemical durability of the Nafion membrane while maintaining inherent proton conductivity.

• Textile Coloration and Finishing
• /
• v.31 no.2
• /
• pp.65-76
• /
• 2019

A multi-point touch input sensor having different sizes or different capacitance touch points connected by only one pair of signal transmission lines was fabricated using a polyimide film coated with a thin copper plate. The capacitance increases with the decrease in the number of sheets of fabric spacers placed between the two sheets of the polyimide film. Therefore, the touch input sensor could be manufactured without fabric spacers, which was possible by the action of the polyimide film as a dielectric material in the capacitor. On the multi-point touch sensor, higher capacitance was obtained when pressing wider-area touch points with 10mm to 25mm diameter on average. However, the capacitance of a system comprising two sheets of touch sensors was considerably low, causing a serious overlap of the capacitance values according to the data collected from the reliability test. Although the capacitance values could be increased by stacking several sheets of touch sensors, the overlap of data was still observed. After reducing the size of all touch points to 10mm and stacking up to eight sheets of sensors, reliable and consistent capacitance data was obtained. Five different capacitance signals could be induced in the sensors by pushing touch points simultaneously.