• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.3
• /
• pp.51-56
• /
• 2016

To fabricate a copper (Cu)-based fine conductive filler having antioxidation property, submicron silver (Ag)-coated Cu particles were fabricated and their antioxidation property was evaluated. After synthesizing the Cu particles of $0.705{\mu}m$ in average diameter by a wet-reduction process, Ag-coated Cu particles were fabricated by successive Ag plating using ethylene grycol solvent. Main process parameters in the Ag plating were the concentration of reductant (ascorbic acid), the injection rate of Ag precursor solution, and the stirring rate in mixed solution. Thus, Ag plating characteristics and the formation of separate fine pure Ag phase were observed with different combinations of process parameters. As a result, formation of the separate pure Ag phase and aggregation between Ag-coated Cu particles could be suppressed by optimization of the process parameters. The Ag-coated Cu particles which were fabricated using optimal conditions showed slight aggregation, but excellent antioxidation property. For example, the particles indicated the weight gain not exceeding 0.1% until $225^{\circ}C$ when they were heated in air at the rate of $10^{\circ}C/min$ and no weight gain until 75 min when they were heated in air at $150^{\circ}C$.

• Journal of the Korea Convergence Society
• /
• v.9 no.10
• /
• pp.271-276
• /
• 2018

In the industry, Zn galvanizing on the steel using the principle of sacrificial anode is used. The steel have some problem, specially corrosion problem. To solve corrosion problem, Zn-Mn alloy plating has been studied as one of the measures to increase the corrosion resistance rather than pure zinc plating. It is possible to be applied to automotive parts requiring high corrosion resistance even though the plating cost is high. In this study, Zn-Mn alloys were electrodeposited from an acidic chloride bath. The influence of the electrolytic conditions on the composition of the alloy plating in the chloride bath was investigated. As the current density of the cathode increases, Zn content of electrodeposit decrease and Mn content of electrodeposit increase. As the temperature of the electrolyte increases, Zn content of electrodeposit decrease and Mn content of electrodeposit increase. The results are explained by the cathode overvoltage curve of Mn and Zn.

• Polymer(Korea)
• /
• v.31 no.5
• /
• pp.410-416
• /
• 2007

Monodisperse polymer particles were prepared via one- step seeded polymerization using PMMA as seed particles, and HDDA, triEGDMA or EGDMA as crosslinking monomer. For the study, the effects of 1) the ratio of the absorbed monomer to the seed polymer particles (swelling ratio), 2) the characteristics of crosslinking monomer, 3) electroless Ni plating, and 4) electroless Au Plating on the variation of mechanical properties of polymer particles, such as recovery rate, K-values, breaking strength and breaking displacement were investigated by using MCT (micro compression test). It was observed that swelling ratio of polymer particles influenced only on breaking strength of polymer Particles, while electroless plating did on recovery rate, K-values ($K_{10}\;and\;K_{20}$) and breaking strength of electroless plated polymer particles. However, breaking displacement and K-values ($K_{30}{\sim}K_{50}$) were more or less insensitive to electroless plating.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.4
• /
• pp.57-63
• /
• 2015

In order to prepare a low-cost conductive filler material possessing improved anti-oxidation property, Ag-coated Cu flakes were fabricated and the effects of an applying method of ammonium-based pretreatment solution on the Cu flakes were analyzed. The pretreatment solution was used to remove the surface oxide layer on Cu flake. During a single-stage pretreatment process, hole-shaped defects were formed on the flake surface during the pretreatment after 2 min, and the number and size increased in proportion to the pretreatment time. In the case that Ag plating solution was injected in the pretreatment solution after the pretreatment for 2 min, the defects were also formed during Ag plating. In contrast, the defects tremendous decreased in the case that the pretreatment solution was removed after the first pretreatment for 2 min and the Ag plating proceeded after the second pretratment using a low concentration pretreatment solution. As the final result, the 15 wt% Ag-coated Cu flake sample which was fabricated using the single-stage pretreatment oxidized at $166^{\circ}C$, but the sample fabricated by the double-stage pretreatment oxidized at $224^{\circ}C$, indicating definitely improved anti-oxidation property.

• The korean journal of orthodontics
• /
• v.36 no.2 s.115
• /
• pp.145-152
• /
• 2006

The purpose of this study was to evaluate electroless plating as a method of increasing the diameter of an orthodontic wire in comparison with eletroplating. After pretreatment plating of the 0.016 inch stainless steel orthodontic wire, electroless plating was performed at $90^{\circ}C$ until the diameter of the wire was increased to 0.018 inch. During the process of electroless plating, the diameter of the wire was measured every 5 minutes to examine the increasing ratio of the wire's diameter per time unit. And to examine the uniformity, the diameter at 3 points on the electroless-plated orthodontic wire was measured. An X-ray diffraction test for analyzing the nature of the plated metal and a 3-point bending test for analyzing the physical property were performed. The electroless-plated wire group showed a increased tendency for stiffness, yield strength, and ultimate strength than the electroplated wire group. And there was a statistically significant difference between the two groups for stiffness and ultimate strength. In the electroless-plated wire group, the increasing ratio of the diameter was $0.00461{\pm}0.00003mm/5min$ (0.00092 mm/min). In the electroplated wire group, it was $0.00821{\pm}0.00015mm/min$. The results of the uniformity test showed a tendency for uniformity in both the plating methods. The results of this study suggest that electroless plating of the wire is closer to the ready-made wire than electroplating wire in terms of the physical property. However, the length of plating time needs further consideration for the clinical application of electroless plating.

• Korean Journal of Materials Research
• /
• v.24 no.11
• /
• pp.617-624
• /
• 2014

To elucidate the effects of a pretreatment process on the uniformity of Ag electroless plating on Cu flakes, pretreatment time was mainly considered with a mixed solution of 0.15 M ammonium hydroxide and 0.0375 M ammonium sulphate. Optical inspection of Ag-coated Cu flakes determined that the optimal pretreatment time is 120 s. Repetition of the sequence in which Ag plating was done immediately after the pretreatment of 120 s clearly enhanced the plating uniformity. Scanning electron microscopy revealed that holes were formed irregularly on some Cu flakes during the period from the asdropping of an Ag precursor solution to 5 min. The hole formation was judged to be due to continuous removal of Cu on the local surfaces by the repetitive formation and elimination of $Cu_2O$ or $Cu(OH)_2$ layers. However, the increase of the amount of Ag coating suppressed the hole creation and increasingly enhanced the antioxidant property.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.3
• /
• pp.144-149
• /
• 2008

It has been reported that copper and copper alloys have a large anisotropy of functional properties such as electrical, thermal and mechanical properties, which means that the texture of polycrystalline alloy should be considered to achieve better properties. In this study, the determination of grain growth orientation and texture formation in the cold-rolled, heat-treated and Ni-plated hybrid copper sheets was investigated. Grain growth direction and texture formation were analyzed by the X-ray pole figure. The influence of texture on the mechanical properties could be quantitatively confirmed by the results from the orientation distribution function and the tensile test. The heat-treated texture in the cold-rolled hybrid copper sheet is also investigated and discussed.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.3
• /
• pp.165-171
• /
• 2002

TiN coating were deposited onto different WC-Co substrates using arc ion plating (AIP) technique. The structure and morphology for the deposited coating were characterized by x-ray diffraction (XRD) and scanning electron microscopy (SEM). The adhesion behavior of the deposited TiN coating was investigated with a conventional scratch test. Effects of WC particle size and Co content on the adhesion strength between the deposited TiN coating and substrate were studied. During the scratch test, the value of critical load was dependent of WC particle size and Co content on substrate. As the WC particle size and Co content on substrate decreased, the critical load increased. The highest critical load, approximately 110N, was obtained at WC particle size of 1$\mu\textrm{m}$ and Co content of 10wt.%.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1889-1892
• /
• 2003

The fabrication of micro-size patterning on alumina substrate is generated by laser direct writing, which has high precision and selectivity of various laser beam energies. The depth and width of patterns is affected by laser parameter such as laser power, scan rate. Through the chemical and mechanical polishing Pd seeds was effectively got rid of alumina substrate for selectivity electroless Ni plating. Thermal treatment is good method for changing electrical property of conductor line, because the treatment can control of the grain size.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.9
• /
• pp.832-837
• /
• 2006

Antennas were fabricated by physical(adhesive) and chemical(deposition+plating) method on organic-inorganic composite material. And antennas were measured dielectric constant and gain. Dielectric constant of antennas were fabricated by physical method was decreased with increase of adhesive tape thickness and number of conduction material composition. But antennas were fabricated by chemical method was reached to 90 % of dielectric material. Gain of antennas were fabricated by physical method was decreased with increase of adhesive tape thickness. But they were unrelated with conduction material composition. The other side antennas were fabricated by chemical method excelled more 0.8 dBic than antennas were fabricated by physical method in gain of antenna. Finally, chemical method can expect excellent product process because it can produce smaller size, higher gain and elimination of many handworks.