• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.582-586
• /
• 2001

방전 플라즈마 소결법을 이용하여 ZrB$_2$-ZrC 복합체를 소결하여 소결 거동과 미세구조에 대하여 조사하였다. 소결 조제로서 란타늄을 첨가하였을 경우에 첨가하지 않았을 경우보다 더 낮은 온도에서 소결 수축이 시작되었으며, 180$0^{\circ}C$에서 거의 치밀화가 완성되었다. 란타늄은 방전플라즈마 소결시 초기 분말 간 액상 형성으로 물질이동을 가속화하여 ZrB$_2$-ZrC 복합체의 치밀화에 커다란 기여를 하며, 냉각 시에 재결정화하여 결정립계와 결정립 삼중점에 란타늄이 포함된 이차상을 형성하는 것으로 확인되었다. 또한 ZrB$_2$-ZrC는 강한 공유결합성 재료임에도 불구하고 미세 구조 내에 잘 발달된 전위 구조를 형성하고 있음을 확인하였다.

• Journal of Powder Materials
• /
• v.13 no.5 s.58
• /
• pp.351-359
• /
• 2006

Ni based($Ni_{57}Zr_{20}Ti_{18}Si_2Sn_3$) bulk metallic glass(BMG) powders were produced by a gas atomization process, and ductile Cu powders were mixed using a spray drying process. The Ni-based amorphous powder and Cu mixed Ni composite powders were compacted by a spark plasma sintering (SPS) processes into cylindrical shape. The relative density varied with the used SPS mold materials such as graphite, hardened steel and WC-Co hard metal. The relative density increased from 87% to 98% when the sintering temperature increased up to $460^{\circ}C$ in the WC-Co hard metal mold.

• Journal of Powder Materials
• /
• v.21 no.2
• /
• pp.97-101
• /
• 2014

The 304 stainless steel powders were prepared by high energy ball milling and subsequently sintered by spark plasma sintering, and the microstructural characteristics and micro-hardness were investigated. The initial size of the irregular shaped 304 stainless steel powders was approximately 42 ${\mu}m$. After high energy ball milling at 800 rpm for 5h, the powders became spherical with a size of approximately 2 ${\mu}m$, and without formation of reaction compounds. From TEM analysis, it was confirmed that the as-milled powders consisted of the aggregates of the nano-sized particles. As the sintering temperature increased from 1073K to 1573K, the relative density and micro-hardness of sintered sample increased. The sample sintered at 1573K showed the highest relative density of approximately 95% and a micro-hardness of 550 Hv.

• Journal of Powder Materials
• /
• v.22 no.3
• /
• pp.157-162
• /
• 2015

SKD11(ASTM D2) tool steel is a versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium rich alloy carbide in the microstructure. SKD11 tool steel provides an effective combination of wear resistance and toughness, tool performance, price, and a wide variety of product forms. Adding of CNTs increased the performance of mechanical properties more. 1, 3 vol.% CNTs was dispersed in SKD11 matrix by mechanical alloying. SKD11 carbon nanocomposite powder was sintered by spark plasma sintering process. FE-SEM, HR-TEM and Raman analysis were carried out SKD11 carbon nanocomposites.

• Korean Journal of Materials Research
• /
• v.17 no.6
• /
• pp.337-341
• /
• 2007

[ $Mg_{97}Zn_1Y_2$ ] alloy powders were prepared from gas atomization process, followed by consolidation using spark plasma sintering (SPS) process. The atomized $Mg_{97}Zn_1Y_2$ alloy particles were entirely spherical in shape and dendritic microstructure. The compacts sintered by SPS process had theoretical density more than 99%. The compressive yield strength was decreased as sintering temperature increased. It was found that the compressive strength showed the maximum value of 303MPa at the $Mg_{97}Y_2Zn_1$ specimen sintered under load of 255 MPa at $350^{\circ}C$.

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.176-180
• /
• 2003

Pure WC powders which does not include a binder phase were consolidated by spark plasma sintering (SPS) process at 1600~185$0^{\circ}C$ for 0~30 min under 50 MPa. Microstructure alid mechanical properties of binderless WC prepared by SPS were investigated. With increasing sintering temperature, sintered density and Vickers hardness of binderless WC increased. The fracture toughness of binderless WC was 7~15 MPa $m^{1/2}$ depending on the sintered density and decreased with increasing the Vickers hardness. It is found that the binderless WC prepared by SPS at 175$0^{\circ}C$ for 10 min under 50 MPa showed nearly full densification with fine-grained structure and revealed excellent mechanical properties of high hardness (~HV 2400) and considerably high fracture toughness (~7 MPa $m^{1/2}$).

• Journal of the Korean Ceramic Society
• /
• v.46 no.5
• /
• pp.467-471
• /
• 2009

Effects of boron and carbon on the densification and thermal decomposition of an AlN-SiC-$TiB_2$ system were investigated. $SiO_2$ was mostly removed by the addition of carbon, while $Al_2O_3$ formed $Al_4O_4C$ and promoted the densification of the systems above $1850^{\circ}C$. Rather porous specimens were obtained without the additives after hot pressing at $2100^{\circ}C$, while densification was mostly completed at $2000^{\circ}C$ by using the additives. The sintering temperature decreased further to $1950^{\circ}C$ by applying spark plasma sintering. The additives promoted the shrinkage of AlN by forming a liquid phase which was originated from the carbo- and boro-thermal reduction of $Al_2O_3$ and AlN.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.1
• /
• pp.43-48
• /
• 2006

In this Part 2, the grain growth processes of $Al_2O_3$ ceramics is numerically simulated using Monte Carlo method (MCM) and finite element method (FEM) and the pore sizes are analyzed. As the green ceramics whose thermal conductivities in high temperatures are generally low are sintered by the plasma heat and are rapidly cooled, the grain growth of the sintered body in the center is different from that in the outer. Also, even in the same sintering temperature, the pore size differs according to the pressing pressure. In order to prove the difference, the temperature distribution of the sintered body was analyzed using the finite element method and then the grain growth process associated with pressing pressures and relative densities was simulated using Monte Carlo method.

• Journal of Powder Materials
• /
• v.12 no.5 s.52
• /
• pp.345-350
• /
• 2005

In this study the nanostructured ${\alpha}-Al_{2}O_3$ ceramics have been fabricated by the combined application of magnetic pulsed compaction (MPC) and subsequent spark plasma sintering (SPS), and their density and hardness properties were investigated. The ${\alpha}-Al_{2}O_3$ prepared by the combined processes showed an increase by $8.4\%$ in density, approaching the value close to the true density, and an enhancement by $210\~400\;Hv$ in hardness, compared to those fabricated by MPC or static compaction method followed by sintering treatment.

• Korean Journal of Metals and Materials
• /
• v.49 no.1
• /
• pp.40-45
• /
• 2011

Using the spark plasma sintering process (SPS process), the WC-6wt.%Co hard materials were densified using an ultra fine WC-Co powder. The WC-Co was almost completely dense with a relative density of up to 100% after the simultaneous application of a pressure of 60 MPa and the DC pulse current for 3 min without any significant change in the grain size. The average grain size of WC that was produced through this experiment was about $0.2{\sim}0.8{\mu}m$. The hardness and fracture toughness were about $1816kg/mm^2$ and $15.1MPa{\cdot}m^{1/2}$, respectively, for 60 MPa at $1200^{\circ}C$.