• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.41 no.5
• /
• pp.483-491
• /
• 1992

Plasma silicon oxynitride film has been applied as a final passivation layer for semiconductor devices, because it has high resistance to humidity and prevents from alkali ion's penetration, and has low film stress. Structure properties of plasma silicon oxynitride film have been studied experimentally by the use of FT-IR, AES, stress gauge and ellipsometry. In this experiment,Si-N bonds increase as NS12TO/(NS12TO+NHS13T) gas ratio increases. Peaks of Si-N bond, Si-H bond and N-H bond were shifted to high wavenumber according to NS12TO/(NS12TO+NHS13T) gas ratio increase. Absorption peaks of Si-H bond were decreased by furnace anneal at 90$0^{\circ}C$. The atomic composition of film represents that oxygen atoms increase as NS12TO/(NS12TO+NHS13T) gas ratio increases, to the contrary, nitrogen atoms decrease.

• Journal of the Korean Ceramic Society
• /
• v.38 no.8
• /
• pp.687-692
• /
• 2001

Silicon nitride-La-silicon oxynitride ceramics were fabricated by Spark Plasma Sintering (SPS). The density, crystalline phase and microstructure were compared with those obtained by Hot Pressing (HP). The full density was achieved within 40 min by spark plasma sintering at 1$650^{\circ}C$, whereas the same result was required by hot pressing with a dwell time of 500 min at higher temperature. There were some differences in the microstructure and second phases in the sintered ceramics, which are attributed to the rapid densification in the spark plasma sintering. The fine and acicular grain microstructure appeared in spark plasma sintering.

• Journal of the Semiconductor & Display Technology
• /
• v.4 no.3 s.12
• /
• pp.1-4
• /
• 2005

Silicon oxynitride films were deposited using ammonia as a nitrogen source via PECVD (plasma enhanced chemical vapor deposition) to study the physical properties of the films. Silane and nitrous oxide were used as silicon and oxygen sources, respectively. The composition of the silicon oxynitride films was well controlled by changing the ratios of the sources and confirmed by XPS. The silicon oxynitride films with high oxygen content showed bigger compressive stress and less refractive index, while the values of surface roughness were around 1 nm, irrespective of the variation of the source ratios.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.38.1-38.1
• /
• 2009

Plasma etching is an essential process for electronic device industries and the particulate contamination during plasma etching has been interested as a big issue for the yield of productivity. The oxynitride glasses have a merit to prevent particulate contamination due to their amorphous structure and plasma etching resistance. The YSiAlON oxynitride glasses with increasing nitrogen content were manufactured. Each oxynitride glasses were fluorine-plasma etched and their plasma etching rate and surface roughness were compared with reference materials such as sapphire, alumina and quartz. The reinforcement mechanism of plasma etching resistance of the YSiAlON glasses studied by depth profiling at plasma etched surface using electron spectroscopy for chemical analysis. The plasma etching rate decreased with nitrogen content and there was no selective etching at the plasma etched surface of the oxynitride glasses. The concentration of silicon was very low due to the generation of SiF4 very volatile byproduct and the concentration of aluminum and yttrium was relatively constant. The elimination of silicon atoms during plasma etching was reduced with increasing nitrogen content because the content of the nitrogen was constant. And besides, the concentration of oxygen was very low on the plasma etched surface. From the study, the plasma etching resistance of the glasses may be improved by the generation of nitrogen related structural groups and those are proved by chemical composition analysis at plasma etched surface of the YSiAlON oxynitride glasses.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.44.2-44.2
• /
• 2009

Polycrystalline materials suchas yttria and alumina have been applied as a plasma resisting material for the plasma processing chamber. However, polycrystal line material may easily generate particles and the particles are sources of contamination during the plasma enhanced process. Amorphous material can be suitable to prevent particle generation due to absence of grain-boundaries. We manufactured nitrogen-containing $SiO_2-Al_2O_3-Y_2O_3$ based glasses with various contents of silicon and fixed nitrogen content. The thermal properties, mechanical properties and plasma etching rate were evaluated and compared for the different composition samples. The plasma etching behavior was estimated using XPS with depth profiling. From the result, the plasma etching rate highly depends on the silicon content and it may results from very low volatile temperature of SiF4 generated during plasma etching. The silicon concentration at the plasma etched surface was very low besides the concentration of yttrium and aluminum was relatively high than that of silicon due to high volatile temperature of fluorine compounds which consisted with aluminum and yttrium. Therefore, we conclude that the samples having low silicon content should be considered to obtain low plasma etching rate for the plasma resisting material.

• Journal of the Korean Ceramic Society
• /
• v.39 no.6
• /
• pp.594-597
• /
• 2002

Silicon Oxynitride(SiON) thick films on p-type silicon(100) wafers have obtained by using plasma-enhanced chemical vapor deposition from SiH$_4$ , N$_2$O and N$_2$. Prism coupler measurements show that the refractive indices of SiON layers range from 1.4620 to 1.5312. A high deposition power of 180 W leads to deposition rates of up to 5.92${\mu}$m/h. The influence of the deposition condition on the chemical composition was investigated using X-ray photoelectron spectroscopy. After deposition of the SiON thick films, the films were annealed at 1050$^{\circ}C$ in a nitrogen atmosphere for 2 h to remove absorption band near 1.5${\mu}$m.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.161-162
• /
• 2006

Scaling rules for TFT application devices have led to the necessity of ultra thin dielectric films and high-k dielectric layers. In this paper, The advantages of high concentration of nitrogen in silicon oxide layer deposited by using $N_2O$ in Inductively Coupled Plasma Chemical Vapor Deposition (ICP-CVD) reported about Ellipsometric measurement, Capacitance-Voltage characterization and processing conditions.

• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1327-1329
• /
• 1998

It is very important to select superior inter-layer PMD(Pre Metal Dielectric) materials which can act as penetration barrier to various impurities created by CMP processes. In this paper, hot carrier degradation and device characteristics were studied with material variation of PMD-1 layers, which were split by LP-TEOS, SR-Oxide, PE-Oxynitride, PE-Nitride, PE-TEOS films. It was observed that the oxynitride and nitride using plasma was greatly decreased in hot carrier effect in comparison with silicon oxide. Consequently, silicon oxide turned out to be a better PMD-1 material than PE-oxynitride and PE-nitride. Also, LP-TEOS film was the best PMD-1 material Among the silicon oxides.

• Korean Journal of Materials Research
• /
• v.25 no.5
• /
• pp.233-237
• /
• 2015

Silicon oxynitride that can be deposited two times faster than general SiNx:H layer was applied to fabricate the passivation protection layer of atomic layer deposition (ALD) $Al_2O_3$. The protection layer is deposited by plasma-enhanced chemical vapor deposition to protect $Al_2O_3$ passivation layer from a high temperature metallization process for contact firing in screen-printed silicon solar cell. In this study, we studied passivation performance of ALD $Al_2O_3$ film as functions of process temperature and RF plasma effect in plasma-enhanced chemical vapor deposition system. $Al_2O_3$/SiON stacks coated at $400^{\circ}C$ showed higher lifetime values in the as-stacked state. In contrast, a high quality $Al_2O_3$/SiON stack was obtained with a plasma power of 400 W and a capping-deposition temperature of $200^{\circ}C$ after the firing process. The best lifetime was achieved with stack films fired at $850^{\circ}C$. These results demonstrated the potential of the $Al_2O_3/SiON$ passivated layer for crystalline silicon solar cells.

• Proceedings of the KIEE Conference
• /
• 2006.04a
• /
• pp.138-140
• /
• 2006

A new diagnosis model was constructed by combining atomic force microscopy (AFM), wavelet, and neural network. Plasma faults were characterized by filtering AFM-measured etch surface roughness with wavelet. The presented technique was evaluated with the data collected during the etching of silicon oxynitride thin film. A total of 17 etch experiments were conducted. Applying wavelet to AFM, surface roughness was detailed into vertical, horizon%at, and diagonal components. For each component, neural network recognition models were constructed and evaluated. Comparisons revealed that the vertical component-based model yielded about 30% improvement in the recognition accuracy over others. The presented technique was evaluated with the data collected during the etching of silicon oxynitride thin film. A total of 17 etch experiments were conducted