• Transactions of the Korean Society of Automotive Engineers
• /
• v.18 no.5
• /
• pp.25-30
• /
• 2010

The authors have studied on the corrosion resistance of the hot stamped steel sheets for the application to automotive parts. Recently automotive companies have focused on the hot stamped parts to meet the light weighting needs and the safe reason. Because of the cost reduction of the hot stamped parts, automotive companies increase the usage of the coated steel sheets, especially Al-Si coated steel sheets. The coated layer of Al-Si coated steel sheets contains up to 50% of Fe, which was diffused from the steel sheet, after hot stamping. The hot stamped steel sheet was not phosphated due to the oxidation layer of the coating, however, the result of the water resistance test is similar to that of the conventional GA steel sheets. The pitting depth and the weight reduction of the coated layer of hot stamped steel sheets are less than those of GA steel.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.05a
• /
• pp.240-247
• /
• 2002

The rolling wear behavior of SM55C is investigated under lubrication. This is a comparative tribological behavior of heat treatment effect for SM55C. Rolling wear test method is used for Ball-on-disk type. Specimens can be classified into two main groups: as-annealing and non-annealing. As result of wear behavior, flanking initial time of non-annealing specimen keep at retard but it have not under high normal load. One of the notable features of annealing specimen is steady flanking initial time for a normal load in this experiment. Failure mechanism of SM55C is due to the fatigue wear such like flanking, pitting etc.. Flanking leads to abruptly fracture of worn surface. Fracture mechanism has a connection with normal load and polishing direction of specimens.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.15 no.5
• /
• pp.133-138
• /
• 2007

Surface pitting is a major failure mode for gears. The contact fatigue life analysis of transmission gear considering running-in process is presented in this paper. Surface roughness change of rolling test is used in a life analysis. Contact stresses are obtained by contact analysis of a semi-infinite solid based on the use of influence functions; the subsurface stress field is obtained using rectangular patch solutions. Mesoscopic multiaxial fatigue criterion which can yield satisfactory results for non-proportional loading is then applied to predict fatigue damage. Suitable counting method and damage rule were used to calculate the fatigue life of random loading caused by rough surface. The life analysis considering running-in is in good agreement with the experimental results.

• Corrosion Science and Technology
• /
• v.3 no.3
• /
• pp.102-106
• /
• 2004

Al foil used was 99.9 and 99.99 %. Test solution used was NaCl solution. The noise was determined using controlled potential electrolysis at -200 and -700 mV vs. NHE. The current fluctuation was caused by breakdown and repaired process of aluminum oxide film. The current fluctuation value of noise was proportion to degree of growth. The number of noise was proportion to the number of pit. The examining of current flutulation value and number of noise could be evaluated corrosion. A 99.99 % Al foil was the mostly crystal of {100} plane, and showed three-dimensional, as azimuth pit with along the direction of this place piled up. A 99.9 % Al foil was polycrystal, and in order of (311) >(222) >(200) >(111) plane. The azimuth pit did not occurred as the dissolution was occurred from each plane.

• Journal of Power System Engineering
• /
• v.9 no.1
• /
• pp.50-56
• /
• 2005

The corrosion experiment was performed for 120 hours on the specimens in the natural seawater tank with four steps of the loaded torsional stress. The surface corrosion pattern of SCM440 area was showed global corrosion and narrow pitting, that was cause by galvanic corrosion between friction welded IN713LC and SCM440. But corrosion does not proceeded from IN713LC area. Initially, the average relative electrode potential and corrosion current were decreased suddenly, by and large, it was stabilized gradually tend to decreasing with the elapse of the immersion time. The corrosion rate was decreased by increasing the load stress, but 200 MPa specimen was showed most large value.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.7 no.5
• /
• pp.89-95
• /
• 1999

In this study, the corrosion resistance of the aluminum casting commercial materials used in the automotive engine parts with respect to the anti-freeze coolant environment has been tested by the potentio dynamic method. especially, the effect of borax additive in engine coolant on the corrosion resistance of the aluminum casting materials has been evaluated. It was found that the borax in commercial engine coolant, used to prevent the corrosion in cast iron engine, causes a pit corrosion of aluminum casting materials at high temperature. During the engine endurance test with the coolant containing borax, the aluminum cylinder head was failed by the pitting corrosion near the exhaust port. Conclusively, it was suggested that the use of borax in the anti-freeze coolant be restricted for the automotive with aluminum cylinder head.

• Corrosion Science and Technology
• /
• v.3 no.5
• /
• pp.179-186
• /
• 2004

Recently the alloy development of duplex stainless steel has been done. On this study we studied the effect of the corrosion resistance according to the composition variety of C, Cr, N in the alloy elements of duplex stainless steel. materials which have below 0.1[mm/year] corrosion rate enable to use for corrosion-resisting materials, generally. On this experiment we inspected the effect of the composition variety of C, Cr, N in duplex stainless steel and the heat treatment, which the condition was the water quenching after the heat treatment for 1hr. The experiment was done on the basis of the ASTM G48A test, Critical pitting temperature(CPT), and ASTM G-61(Electrochemical tests for cyclic polarization).

• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.432-438
• /
• 2017

AZ91D casting alloy requires an advanced plasma anodizing processing because large amount of defects are liable to generate during anodization. In this study, plasma electrolytic oxidation (PEO) of AZ91D Mg alloy was conducted by the application of either constant voltage or current using a pulse mode and its effects on pore formation, surface roughness and corrosion resistance were investigated. The PEO films showed a three-layer structure. The PEO film thickness was found to increase linearly with voltage. The surface roughness, Ra, ranged between $0.2{\mu}m$ and $0.3{\mu}m$. The corrosion resistance increased from RN 3.5 to 9.5 by the PEO treatment when evaluated according to the 72 hour salt spray test. The PEO-treated surface exhibited higher pitting potential than the raw material.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.6
• /
• pp.280-286
• /
• 2009

In this study, the corrosion property of copper alloy tubes in seawater has been investigated. Three copper alloys of nominal composition Cu-20Zn-2Al(Al-Brass), Cu-30Ni(CN70/30) and Cu-10Ni(CN90/10) were considered. The samples were immersed in 3%NaCl flowing solution at $90^{\circ}C$ for 30, 50 and 80 days. Corrosion rate of copper alloy tubes in 3%NaCl flowing solution was investigated by weight-loss measurements and electrochemical test. The CN70/30 showed lowest corrosion rate among three copper alloy tubes. Because of passive films formation, corrosion rates of three types of copper tubes were decrease with time. Surface characteristics of copper alloy tubes were analyzed by optical micrograph(OM), scanning electronic microscopy (SEM), energy dispersive X-ray analysis(EDAX) and X-ray diffraction patterns(XRD). CN70/30 showed partly pitting problem on the surface owing to high Fe content, even though having high resistant against corrosion. Cracks appeared on the surface of CN90/10 and CN70/30 after more than 50 days immersion, which could be derived from high nickel contents.

• Journal of Power System Engineering
• /
• v.8 no.3
• /
• pp.44-51
• /
• 2004

Effect of corrosion characteristics in relation to loaded stress in the welded zone of A5083-H116 aluminum alloy, in the seawater was studied. The corrosion experiment was performed for 120 hours on the specimens in the natural seawater tank with four steps of the loaded stress. The corrosion crack, corrosion rate, electrode potential, current, and corrosion pattern, etc. were examined for the specimens with the elapse of the immersion time. The main result derived from this study is the crack growth length is increased with the increasing loaded stress. The electrode potential and the corrosion current are decreased rapidly in the early stage of the corrosion, and then decreased gradually and stabilized eventually with the elapse of the immersion time. The test condition of the longer crack growth tends to show the higher corrosion rate. Corrosion pattern of the welded zone indicates that the depth and width of the pitting become increasing with the increasing loaded stress.