• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.6
• /
• pp.272-279
• /
• 2015

$Y_2O_3:Eu^{3+}$ is an excellent red-emitting phosphor, which has been widely used for display devices due to highly luminescent property and chemical stability. In this study, $Y_2O_3:Eu^{3+}$ red phosphors were prepared using the solid state reaction and RF thermal plasma synthesis. The particle size of $Y_2O_3:Eu^{3+}$ phosphors obtained by the solid state reaction varied from 10 to $20{\mu}m$, and 30~100 nanometer sized $Y_2O_3:Eu^{3+}$ particles were obtained from a liquid form of raw material through RF thermal plasma synthesis without an additional heat treatment. Photoluminescence measurements of the obtained $Y_2O_3:Eu^{3+}$ particles showed a red emission peak at 611 nm ($^5D_0{\rightarrow}^7F_2$). PL intensity of red nano phosphors prepared by RF thermal plasma synthesis was comparable to that of red phosphors prepared by the solid state reaction, indicating that nano-sized $Y_2O_3:Eu^{3+}$ red phosphors could be successfully synthesized using one-step process of RF thermal plasma.

• Journal of Powder Materials
• /
• v.12 no.4 s.51
• /
• pp.279-283
• /
• 2005

In this study, the ZnS composite powders for host material in phosphor was synthesized in situ by mechanical alloying. As the mechanical alloying time increases, particle size of ZnS decreases. ZnS powders of $1.85\;\mu{m}$ in a mean size was fabricated by mechanical alloying for 10h. The crystal structures of ZnS powders were investigated by X-ray diffraction and the photo-luminescence properties was evaluated with the optical spectra analyzer. The steady state condition of mechanically alloyed ZnS was obtained as a mean particle size of $2\;\mu{m}$ in 5h milling. The sphalerite and wurtize structures coexist in the ZnS mechanically alloyed for 5h. The ZnS powder mechanically alloyed for 10h grows to the sphalerite structure. And the strong emission peaks of ZnS are observed at 480 nm wave length at the powders of mechanically alloyed for 10h, but the sphalerite and wurtize structures in ZnS coexist and emission peaks are not appeared at the powders of mechanically alloyed for 10h.

• Korean Journal of Materials Research
• /
• v.26 no.10
• /
• pp.561-569
• /
• 2016

$SrAl_2O_4$: $Eu^{2+}$ and $Dy^{3+}$ phosphorescent phosphors were synthesized using the polymerized complex method. Generally, phosphorescent phosphors synthesized by conventional solid state reaction show a micro-sized particle diameter; thus, this process is restricted to applications such as phosphorescent ink and paint. However, it is possible to synthesize homogeneous multi-component powders with fine particle diameter by wet process such as the polymerized complex method. The characteristics of $SrAl_2O_4$: $Eu^{2+}$ and $Dy^{3+}$ powders prepared by polymerized complex method with one and two step calcination processes were comparatively analyzed. Temperatures of organic material removal and crystallization were observed through TG-DTA analysis. The crystalline phase and crystallite size of the $SrAl_2O_4$: $Eu^{2+}$ and $Dy^{3+}$ phosphorescent phosphors were analyzed by XRD. Microstructures and afterglow characteristics of the $SrAl_2O_4$: $Eu^{2+}$ and $Dy^{3+}$ phosphors were measured by SEM and spectrofluorometry, respectively.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1520-1522
• /
• 1999

저 전압용 형광체는 최근에 활발히 연구가 진행되고 있으며 가장 대표적인 형광체가 ZnO : Zn 녹색 형광체이다. ZnO : Zn 형광체는 자체발광형 형광체로써 ZnO을 환원분위기 하에서 열처리를 함으로써 얻을 수 있다. 본 연구에서는 자발착화 연소반응법(Glycine Nitrate Process)을 이용하여 ZnO : Zn 분말을 합성하고 형광특성 및 분말특성을 알아보았다. 출발물질로는 Zn Nitrate와 Glycine을 이용하였고 자발연소 반응이 발생하는데 적절한 글리신의 양을 확인하기 위해서 글리신과 양이온의 비를 변화시키며 ZnO를 합성하였다. 그리고 Zn Excess가 생겨난 양과 그에 따른 형광특성을 관찰하기 위해 $N_2$ 분위기에서 각기 $500^{\circ}C,\;750^{\circ}C,\;950^{\circ}C$의 온도에서 열처리를 행하였다. 제조된 ZnO 분말의 입자형태와 결정상태는 SEM과 XRD를 이용하여 분석하였고 TG-DTA를 측정하여 열처리 온도에 따른 질량감소(ZR excess)를 관찰하였다. 또 Particle size analyzer로 분말의 크기를 알아보았고 형광체로써의 발광특성을 살펴보기 위해 PL을 이용하여 발광피크를 관찰하였다.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2003.10a
• /
• pp.24-29
• /
• 2003

Deep sea water has cold temperature, abundant nutrients and minerals, and good water quality that is pathogen-free and stable. Compared with surface water, deep sea water contains more nutrition salt, such as nitrogen and phosphor. Moreover, if has the good balance of minerals. Because of the ability of the spray drying process to produce a free-flowing power considering of spherical particles with a well-defined size distribution and the rapid drying times for heat-sensitive material, spray drying is attractive for a wide range of applications spray drying is a unique unit operation in which powders are produced from a liquid feed in a single processing step. Key component of the process are atomizer, spray chamber. Design of spray chamber should be based on the atomizer type, the production rate, and the particle size required. Because of the complex processes taking place during spray drying, traditional design method are based on pilot-plant tests and empirical scale-up rules. Modern technique such as CFD have a role to play in design and troubleshooting.

• Korean Journal of Materials Research
• /
• v.26 no.1
• /
• pp.29-34
• /
• 2016

$NaLa_{1-x}{(MoO_4)}_2$:$Ho^{3+}/Yb^{3+}$ phosphors with the correct doping concentrations of $Ho^{3+}$ and $Yb^{3+}$ ($x=Ho^{3+}+Yb^{3+}$, $Ho^{3+}=0.05$ and $Yb^{3+}=0.35$, 0.40, 0.45 and 0.50) were successfully synthesized by the microwave-modified sol-gel method. Well-crystallized particles formed after heat-treatment at $900^{\circ}C$ for 16 h showed a fine and homogeneous morphology with particle sizes of $3-5{\mu}m$. The optical properties were examined using photoluminescence emission and Raman spectroscopy. Under excitation at 980 nm, the UC intensities of the doped samples exhibited strong yellow emissions based on the combination of strong emission bands at 545-nm and 655-nm emission bands in green and red spectral regions, respectively. The strong 545-nm emission band in the green region corresponds to the $^5S_2/^5F_4{\rightarrow}^5I_8$ transition in $Ho^{3+}$ ions, while the strong emission 655-nm band in the red region appears due to the $^5F_5{\rightarrow}^5I_8$ transition in $Ho^{3+}$ ions. Pump power dependence and Commission Internationale de L'Eclairage chromaticity of the upconversion emission intensity were evaluated in detail.

• Korean Journal of Materials Research
• /
• v.27 no.5
• /
• pp.270-275
• /
• 2017

Inorganic phosphors based on $ZrO_2:Eu^{3+}$ nanoparticles were synthesized by a salt-assisted ultrasonic spray pyrolysis process that is suitable for industrially-scalable production because of its continuous nature and because it does not require expensive precursors, long reaction time, physical templates or surfactant. This facile process results in the formation of tiny, highly crystalline spherical nanoparticles without hard agglomeration. The powder X-ray diffraction patterns of the $ZrO_2:Eu^{3+}$ (1-20 mol%) confirmed the body centered tetragonal phase. The average particle size, estimated from the Scherrer equation and from TEM images, was found to be approximately 11 nm. Photoluminescence (PL) emission was recorded under 266 nm excitation and shows an intense emission peak at 607 nm, along with other emission peaks at 580, 592 and 632 nm which are indicated in red.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.461-462
• /
• 2008

$BaMgAl_{10}O_{17}$:Mn, $Eu^{2+}$ green phosphors has been synthesized by the solid state reaction. Green phosphors of nano-size were manufactured in short time by shake method. which were easily manufactured respectively general method. Green phosphors of nano size were control additive, size of $ZrO_3$ ball, shake time and weight of ball in toluene. In result that green phosphors were obtained particle size of 140nm~150nm. The characteristics of fired samples were obtained by 365nm and 380nm excitation source under ultraviolet. In result that the highest PL intensity were observed in wavelength of 365nm.

• Journal of the Korean Society of Radiology
• /
• v.2 no.3
• /
• pp.11-18
• /
• 2008

In this study, the particle properties and luminescence properties of Gd2O3 nano powder with various Eu content were studied. Gd2O3:Eu nano powder was fabricated using special solvent which mixed the alcohol and the distilled water at specific ratio. This solvent by the solution method showed short fabrication time because solution time of Gd and Eu was reduced. From this experiment with Gd2O3:Eu, the particle properties og nano powder phosphor way analysed using SEM (scanning electron microscope) and EDX(Energy Dispersive X-ray). Also the luminescence properties of nano powder was measured using PL(Photoluminescence) and CL (CathodeLuminescence). The size of powder was 30nm~40nm. The magnitude of powder showed the best peak at 620nm. Among 1,3,5wt% of Eu content, the more Eu content was added in powder, the more photons wre generated. Also it shows luminescence efficiency was improved adding 5% of Eu content.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.386-386
• /
• 2012

For white light emitting diode (LED) applications, it has been reported that Y3Al5O12:Ce3+ (YAG:Ce) in nano-sized phosphor performs better than it does in micro-sized particles. This is because nano-sized YAG:Ce can reduce internal light scattering when coated onto a blue LED surface. Recently, there have been many reports on the synthesis of nano-sized YAG particles using bottom-up method, such as co-precipitation method, sol-gel process, hydrothermal method, solvothermal method, and glycothermal method. However, there has been no report using top-down method. Top-down method has advantages than bottom-up method, such as large scale production and easy control of doping concentration and particle size. Therefore, in this study, nano-sized YAG:Ce phosphors were synthesized by a high energy beads milling process with varying beads size, milling time and milling steps. The beads milling process was performed by Laboratory Mill MINICER with ZrO2 beads. The phase identity and morphology of nano-sized YAG:Ce were characterized by X-ray powder diffraction (XRD) and field-emission scanning electron microscopy (FESEM), respectively. By controlling beads size, milling time and milling steps, we synthesized a size-tunable and uniform nano-sized YAG:Ce phosphors which average diameters were 100, 85 and 40 nm, respectively. After milling, there was no impurity and all of the peaks were in good agreement with YAG (JCPDS No. 33-0040). Luminescence and quantum efficiency (QE) of nano-sized YAG:Ce phosphors were measured by fluorescence spectrometer and QE measuring instrument, respectively. The synthesized YAG:Ce absorbed light efficiently in the visible region of 400-500 nm, and showed single broadband emission peaked at 550 nm with 50% of QE. As a result, by considering above results, high energy beads milling process could be a facile and reproducible synthesis method for nano-sized YAG:Ce phosphors.