• Proceedings of the Korean Geotechical Society Conference
• /
• 2006.03a
• /
• pp.1083-1089
• /
• 2006

Acid drainage occurs when sulfide minerals are exposed to an oxidizing environment. The objective of this study was to examine the optimum condition for creating a phosphate coating on standard pyrite surfaces for reduction of pyrite oxidation. The solution of $10^{-2}M\;KH_2PO_4\;10^{-2}M\;H_2O_2$ pH 6 was identified as the best phosphate coating agent for the reduction of pyrite oxidation. The formation of an iron phosphate coating on pyrite surfaces was confirmed with ore microscope and scanning electron microscope equipped with energy dispersive spectroscopy. The temperature did not significantly affect on the formation of phosphate coating on the surface of pyrite. However, the phosphate coating was less stable at higher temperature than at lower temperature. The phosphate coating was quitely stable at wide range of pH and $H_2O_2$ concentration. The less than 3.4% of phosphate was dissolved at pH 2.79 and 10.64 and less than 1.0% of phosphate was dissolved at 0.1M $H_2O_2$. On the basis of these results, the phosphate coating can effectively reduce the negative environmental of acid rock drainage.

• Corrosion Science and Technology
• /
• v.22 no.6
• /
• pp.429-434
• /
• 2023

This study investigated the localized corrosion behavior of a UNS G41400 steel surface treated with manganese phosphate. The phosphate coating, primarily composed of oxygen (O), phosphorus (P), and manganese (Mn) elements, had an approximate thickness of 6 ㎛. The particles comprising the coating varied in size by several micrometers; smaller particles were mainly composed of O, P, Mn, and iron (Fe) elements, indicating incomplete formation of the manganese phosphate film. Potentiodynamic polarization curves revealed a decrease in anodic current after surface treatment and a shift in corrosion potential toward the noble direction after treatment. After immersion in a 3.5 wt% NaCl solution for 96 hours, localized corrosion was observed, with some regions retaining residual phosphate film. Even though localized corrosion occurred on the treated surface, it was less severe than that on the untreated UNS G41400 steel surface. These findings suggest that manganese phosphate coating improved resistance to localized corrosion.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.6
• /
• pp.350-356
• /
• 2019

In this study, the effect of mechanical polishing of carbon steel on the tribological properties of manganese phosphate coating on carbon steel has investigated. The microstructure, surface morphology and chemical composition were analyzed by SEM, EDS, and XRD. The surface roughness test was carried out in order to calculate Rvk value by 3D laser microscopy. Also, the tribology property of manganese phosphate coating was tested by ball-on disk. In the results of EDS analysis, coating layer consists of elements such in Mn, P, Fe, and O. XRD showed that (Mn,Fe)₅H₂(PO₄)₄·4H₂O in manganese phosphate coating layer was formed by the chemical reaction between manganese phosphate and elements in carbon steel. As the mechanical polishing degree increased, the friction coefficient was reduced. The rougher the mechanical polishing degree, the better corrosion resistance was obtained.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.2
• /
• pp.56-61
• /
• 2015

In this study, the wear performance of manganese phosphate coating on SM45C with addition agent of Tartaric acid and Citric acid were investigated. The Surface morphology of manganese phosphate coating was examined by Scanning Electron Microscope (SEM) and Energy Dispersive X-ray spectroscopy (EDS). It is found that Mn, P, Fe, O and C. The crystal structure and thee composition was analysis and determined by using XRD. The XRD results indicated that manganese phosphate coatings are mainly composed of $(Mn,Fe)_5H_2(PO_4)_44H_2O$ and consists of a lot of close packed lump crystalline. Based on the time dependence of morphology and the weight of manganese phosphate coating, it shows that the phosphating process mainly includes three stages: corrosion of the substrate, creation and growth of phosphate crystal nucleus and thickening of manganese phosphate coating. The wear tests were performed in a ball on disc apparatus as per ASTM G-99 Standard. It was showed that the initial wear was quite high followed by low sludge.

• Economic and Environmental Geology
• /
• v.39 no.1 s.176
• /
• pp.75-82
• /
• 2006

Acid drainage occurs when sulfide minerals are exposed to an oxidizing environment. The objective of this study was to examine the optimum condition for creating a phosphate coating on standard pyrite surfaces for reduction of pyrite oxidation. The solution of $10^{-2}M\;KH_2PO_4,\;10^{-2}M\;H_2O_2$ was identified as the best phosphate coating agent for the reduction of pyrite oxidation. The formation of an iron phosphate coating on pyrite surfaces was confirmed with ore microscope and scanning electron microscope equipped with energy dispersive spectroscopy. The temperature did not significantly affect the formation of phosphate coating on the surface of pyrite. However, the phosphate coating was less stable at higher temperature than at lower temperature. The phosphate coating was quitely stable at wide range of pH and $H_2O_2$ concentration. The less than $3.4\%$ of phosphate was dissolved at pH 2.79 and 10.64 and less than $1.0\%$ of phosphate was dissolved at 0.1M $H_2O_2$. On the basis of these results, the phosphate coating can effectively reduce the negative environmental impact of acid rock drainage.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.10
• /
• pp.603-610
• /
• 2017

Steel used for various industrial fields including ammunition is vulnerable to corrosion so surface treatments are required such as plating, painting and chemical conversion coating. Zinc phosphate, used for ammunition manufacturing, is used to stick the stable compound on the surface by chemical conversion of metal. The quality of phosphate coating depends on many factors such as total acidity and iron content. In this study, we studied the influence of total acidity and iron content on coating weight and corrosion resistance of phosphate coating. The surface structure of the coating becomes dense and corrosion resistance is improved with increasing iron content. However, total acidity influences only the thickness and phosphate coating weight. In conclusion, this study suggests the optimal range of total acidity and iron content to manufacture the ammunition.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.3
• /
• pp.82-88
• /
• 2011

A uniform chromium-free conversion coating treated with an alkaline phosphate- permanganate solution was formed on the AZ 31 magnesium alloy. The effect of acid pickling on the morphology and on the corrosion resistance of the alkaline phosphate-permanganate conversion coating was investigated. The chemical composition and phase structure of conversion coating layer were determined via optical microscopy, SEM, EDS, XPS and XRD. Results show that the conversion coatings are relatively uniform and continuous, with thickness 1.8 to $2.4\;{\mu}m$. The alkaline phosphate-permanganate conversion coating was mainly composed of elements Mg, O, P, Al and Mn. The conversion-coated layers were stable compounds of magnesium oxide and spinel ($MgAl_2O_4$). These compounds were excellent inhibitors to corrosion. The electrochemical corrosion behaviors of coatings in 3.5 wt.% NaCl solutions were evaluated by electrochemical impedance spectroscopy, potentiodynamic polarization technique. EIS results showed a polarization resistance of $0.1\;k{\Omega}$ for the untreated Mg and $16\;k{\Omega}$ for the alkaline phosphate-permanganate conversion treatment sample, giving an improvement of about 160 times. The results of the electrochemical measurements demonstrated that the corrosion resistance of the AZ 31 magnesium alloy was improved by the alkaline phosphate-permanganate conversion treatment.

• Journal of the Korean institute of surface engineering
• /
• v.28 no.5
• /
• pp.289-299
• /
• 1995

The effects of phosphate coating have been studied on physical properties and corrosion resistance of painted aluminum alloy sheet for automobile body. The physical properties (surface roughness, paint adhesion, impact resistance and pencil hardness) and corrosion resistance(cyclic corrosion and filiform corrosion) were investigated. Phosphate coatings enhanced the physical properties of painted Al alloy sheet, especially paint adhesion after the 240hours water immersion test. Phosphate coating also markedly improved the resistance for cyclic corrosion and filiform corrosion of painted cold rolled steel and Zn-Ni plated steel sheet as well as painted Al alloy sheet. The corrosion resistance of painted Al sheets was varied with the concentration of free fluoride ion and metal additives like Ni and Mn in the phosphating bath. A maximum corrosion resistance was obtained at about 300ppm of fluoride ion and additives of Ni and Mn obviously increased the corrosion resistance of painted specimens.

• Journal of Magnetics
• /
• v.11 no.3
• /
• pp.126-129
• /
• 2006

The phosphate coating on the $(Fe_{0.97}Cr_{0.03})_{76}(Si_{0.5}B_{0.5})_{22}C_2$ amorphous powders with an average size of 10 ${\mu}m$ in diameter has been carried out in aqueous 1.0-2.0 wt% $H_3PO_4$ solutions, and the consolidation behavior and magnetic properties of their compressed powder cores has been investigated. The phosphate coating could provide efficient electrical insulation between amorphous powders and improved consolidation ability at room temperature. Especially when the powders were treated in more concentrated phosphoric acid solution, enhanced phosphate covering and higher frequency/dc-bias stability were achieved. The powder cores phosphate-coated in 2.0 wt% $H_3PO_4$ solution exhibited constant permeability of 21 up to 10 MHz, 110 of the quality factor at 0.9 MHz, 610 mW/cm3 core loss at 100 kHz/0.1 T and 89 of percent permeability at 100 kHz.

• Corrosion Science and Technology
• /
• v.17 no.1
• /
• pp.30-36
• /
• 2018

The high rate of corrosion of magnesium alloys makes it limited for industrial applications. Therefore, surface treatment is required to enhance their corrosion resistance. In our study, a chemical conversion coating for protecting the corrosion of the magnesium alloy, AZ31B, was prepared by using a phosphate-permanganate solution. The chemical conversion coating had a limited protection ability due to defects arising from cracks and pores in the coating layer. The sol-gel coating was prepared by using trimethoxymethylsilane (MTMS) and 3-glycidoxypropyltrimethoxysilane (GPTMS) as precursors, and aluminum acetyl acetonate as a ring opening agent. The corrosion protection properties of sol-gel and conversion coatings in 0.35wt% NaCl solution were measured by the electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization test. The EIS results indicated that the resistance of the chemical conversion coating with the sol-gel coating was significantly improved through the sol-gel sealed phosphate-permanganate conversion coating. The results of the potentiodynamic polarization test revealed that the sol-gel coating decreased the corrosion current density ($I_{corr}$). The SEM image showed that the sol-gel coating sealed conversion coating and improved corrosion protection.