• 대한의용생체공학회:의공학회지
• /
• 제25권5호
• /
• pp.383-389
• /
• 2004

본 연구에서는 치과용 티타늄(CP-Ti)과 Ti-25wt%Pd를 인산염계 실리카$.$알루미나 주형재로 주조 후 SEM/EDS, XRD, XPS를 이용하여 주조시 생성되는 표면반응생성물을 조사하였다. Ti-25wt%Pd는 CP-Ti에 비하여 융점이 현저이 감소하여 주조체의 표면반응이 상대적으로 적게 발생하였다. 또한 인산염계 실리카$.$알루미나 주형재를 소성한 결과 주형재는 $SiO_2$, $Al_2$ $O_3$, P$_2$ $O_{5}$, $Mg_3$(P $O_4$)$_2$, AlP $O_4$, $Mg_2$ $SiO_4$, MgAl$_2$ $O_4$의 성분들로 구성되어 있었으며, 표면반응생성물은 CP-Ti 주조체의 경우 $Ti_{5}$Si$_3$ 와 Ti $O_2$로, Ti-25wt%Pd 주조체의 경우 Ti $O_2$ 와 $SiO_{x}$ 로 구성되어 있었다.

• Bulletin of the Korean Chemical Society
• /
• 제34권12호
• /
• pp.3635-3640
• /
• 2013

We prepared Ni and Pd-modified $TiO_2@SiO_2$ core-shell nanostructures and then analyzed them by scanning electron microscopy, optical microscopy, X-ray diffraction crystallography, FT-IR and UV-Visible absorption spectroscopy. In addition, their CO oxidation performance was tested by temperature-programmed mass spectrometry. The CO oxidation activity showed an order of Ni-$TiO_2@SiO_2$ ($900^{\circ}C$) < Ni-$TiO_2@SiO_2$ ($90^{\circ}C$) < Ni-$TiO_2@SiO_2$ ($450^{\circ}C$) in the first CO oxidation run, and greatly improved activity in the same order in the second run. The $T_{10%}$ (the temperature at 10% CO conversion) corresponds to the CO oxidation rate of $2.8{\times}10^{-5}$ molCO $g{_{cat}}^{-1}s^{-1}$. For Ni-$TiO_2@SiO_2$ ($450^{\circ}C$), the $T_{10%}$ was observed at $365^{\circ}C$ in the first run and at $335^{\circ}C$ in the second run. For the Pd-$TiO_2@SiO_2$ ($450^{\circ}C$), the $T_{10%}$ was observed at a much lower temperature of $263^{\circ}C$ in the first CO oxidation run, and at $247^{\circ}C$ in the second run. The CO oxidation activities of transition metal modified $TiO_2@SiO_2$ core-shell nanostructures presented herein provide new insights that will be useful in developing catalysts for various environments.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제44회 동계 정기학술대회 초록집
• /
• pp.663-663
• /
• 2013

We prepared Cu oxides, and Ni and Pd-TiO2@SiO2 core-shellnanostructures, and tested their CO oxidation performances by temperature-programmed mass spectrometry. We found the starting temperatures of CO oxidation are around $200^{\circ}C$ and $300^{\circ}C$ for Ni and Pd-TiO2@SiO2 nanostructures, respectively. Cu oxides are cubes with 50~200 nm with, prepared with different concentrations of NaOH and ascorbic acid. For the core-shell structures, we prepared 100 nm SiO2 spheres, first coated the surface with TiO2 precursor, and then coated with Ni and Pd. Their characteristics are further examined by scanning electron microscopy, optical microscope, FT-IR, and UV-Vis absorption spectroscopy.

• 한국자기학회지
• /
• 제23권1호
• /
• pp.7-11
• /
• 2013

본 연구에서는 $TiO_2$/Co/Pd 구조의 다층박막을 마그네트론 스퍼터링으로 GaAs(100), MgO(100), MgO(111), Si(100), glass와 같은 다양한 종류의 기판에 대해 제작하여 수직 자기 이방성에 대해서 연구하였다. 산소 분압 등의 $TiO_2$ 층의 증착 조건과 기판의 종류에 따른 Co/Pd 층의 수직 자기 이방성을 측정하였다. 그 결과, $TiO_2$ 층이 5 nm 이하 일 때는 기판의 종류에 영향을 받지만, 그 이상의 두께에 대해서는 MgO(111)을 제외한 기판의 영향이 크지 않음을 확인하였고, 이는 $TiO_2$ 씨앗층의 성장조건과 계면의 거칠기, 결정방향 등과 관련이 있음을 발견하였다.

• Bulletin of the Korean Chemical Society
• /
• 제22권1호
• /
• pp.30-36
• /
• 2001

The crystal structures of fully dehydrated $Pd^{2+}$ - and $TI^{+}$ -exchanged zeolite X, $Pd_{18}TI_{56}Si_{100}Al_{92}O_{384}(Pd_{18}TI_{50-}X$, a = $24.935(4)\AA$ and $Pd_{21}TI_{50}Si_{100}Al_{92}O_{384}(Pd_{21}TI_{50-}X$ a = $24.914(4)\AA)$, have been determined by single-crystal X-ray diffraction methods in the cubic space group Fd3 at $21(1)^{\circ}C.$ The crystals were prepared using an exchange solution that had a $Pd(NH_3)_4Cl_2\;:TINO_3$ mole ratio of 50 : 1 and 200 : 1, respectively, with a total concentration of 0.05M for 4 days. After dehydration at $360^{\circ}C$ and 2 ${\times}$$10^{-6}$ Torr in flowing oxygen for 2 days, the crystals were evacuated at $21(1)^{\circ}C$ for 2 hours. They were refined to the final error indices $R_1$ = 0.045 and $R_2$ = 0.038 with 344 reflections for $Pd_{18}Tl_{56-}X$, and $R_1$ = 0.043 and $R_2$ = 0.045 with 280 reflections for $Pd_{21}Tl_{50-}X$; I > $3\sigma(I).$ In the structure of dehydrated $Pd_{18}Tl_{56-}X$, eighteen $Pd^{2+}$ ions and fourteen $TI^{+}$ ions are located at site I'. About twenty-seven $TI^{+}$ ions occupy site II recessed $1.74\AA$ into a supercage from the plane of three oxygens. The remaining fifteen $TI^{+}$ ions are distributed over two non-equivalent III' sites, with occupancies of 11 and 4, respectively. In the structure of $Pd_{21}Tl_{50-}X$, twenty $Pd^{2+}$ and ten $TI^{+}$ ions occupy site I', and one $Pd^{2+}$ ion is at site I. About twenty-three $TI^{+}$ ions occupy site II, and the remaining seventeen $TI^{+}$ ions are distributed over two different III' sites. $Pd^{2+}$ ions show a limit of exchange (ca. 39% and 46%), though their concentration of exchange was much higher than that of $TI^{+}$ ions. $Pd^{2+}$ ions tend to occupy site I', where they fit the double six-ring plane as nearly ideal trigonal planar. $TI^{+}$ ions fill the remaining I' sites, then occupy site II and two different III' sites. The two crystal structures show that approximately two and one-half I' sites per sodalite cage may be occupied by $Pd^{2+}$ ions. The remaining I' sites are occupied by $TI^{+}$ ions with Tl-O bond distance that is shorter than the sum of their ionic radii. The electrostatic repulsion between two large $TI^{+}$ ions and between $TI^{+}$ and $Pd^{2+}$ ions in the same $\beta-cage$ pushes each other to the charged six-ring planes. It causes the Tl-O bond to have some covalent character. However, $TI^{+}$ ions at site II form ionic bonds with three oxygens because the super-cage has the available space to obtain the reliable ionic bonds.

• 한국전기전자재료학회논문지
• /
• 제29권12호
• /
• pp.809-813
• /
• 2016

We investigated a SiC-based hydrogen gas sensor with MIS (metal-insulator-semiconductor) structure for high temperature applications. The sensor was fabricated by $Pd/TiO_2/SiC$ structure, and a thin titanium dioxide ($TiO_2$) layer was exploited for sensitivity improvement. In the experiment, dependences of I-V characteristics and capacitance response properties on hydrogen gas concentrations from 0 to 2,000 ppm were analyzed at room temperature to $400^{\circ}C$. As the result, our sensor using $TiO_2$ dielectric layer showed possibilities with regard to use in hydrogen gas sensors for high-temperature applications.

• 공업화학
• /
• 제21권6호
• /
• pp.648-652
• /
• 2010

고정층 상압 흐름 반응기에서 메탄의 부분산화반응를 수행하여 메탄으로부터 수소제조 위한 촉매의 활성도를 평가하였고, BET, XPS, XRD를 사용하여 촉매의 특성을 분석하였다. Pd(5)/Ti-SPK과 Pd(5)/Zr-SPK 촉매의 BET 표면적, Horvath-Kawaze의 기공부피와 기공폭, t-플롯 미세기공 면적과 부피는 각각 $284m^2/g$, $0.233cm^3/g$, 3.9 nm, $30m^2/g$ $0.015cm^3/g$과 $396m^2/g$, $0.324cm^3/g$, 3.7 nm, $119m^2/g$, $0.055cm^3/g$이었다. 촉매는 히스테리시스가 잘 발달된 IV형 임을 $N_2$-흡착등온선으로부터 확인할 수 있었다. XPS분석으로부터 SPK에 Ti와 Zr이 부분 치환된 Ti-SPK과 Zr-SPK의 Si 2p과 O 1s 피크는 SPK의 Si 2p와 O 1s 피크 보다 낮은 결합에너지 쪽으로 화학 이동함을 알 수 있었고, 촉매표면의 Pd의 산화상태는 $Pd^0$와 $Pd^{+2}$이었다. XRD의 결정 피크는 반응 전에 무정형인 촉매가 반응 후에는 결정상으로 변함을 보여주었다. Pd(5)/Ti-SPK과 Pd(5)/Zr-SPK 촉매의 메탄의 전화율과 수소의 선택도는 973 K, $CH_4/O_2$ = 2, GHSV = $8.4{\times}10^4mL/g_{cat}{\cdot}h$. 반응조건에서 각각 77, 84%와 78, 72%이었고, 반응 시작 후 3일까지도 촉매의 활성이 거의 일정하게 유지되었다. Pd(5)/Ti-SPK과 Pd(5)/Zr-SPK 촉매는 메탄의 부분산화반응에서 활성도와 열 안정성 및 물리화학적 성질이 우수하였다.

• Korean Chemical Engineering Research
• /
• 제55권1호
• /
• pp.121-129
• /
• 2017

$TiO_2$, $Al_2O_3$, $ZrO_2$, $SiO_2$와 같은 다양한 담체에 습식함침법을 이용하여 Pd 기반 촉매를 제조하여 일산화탄소 존재하에 수소의 선택적 산화반응에 적용하였다. 제조된 촉매는 물리화학적 특성을 알아보기 위하여 XRD, $N_2$ 흡착, CO-, (CO+$H_2O$)-TPD, CO-TPR, XPS등의 특성분석을 수행하였다. CO-TPD와 (CO+$H_2O$)-TPD를 통해 $CO_2$ 탈착에 대한 $H_2O$의 영향을 알아보았으며 이러한 TPD 결과는 $H_2/CO$ 전환율과 상관관계가 있음을 확인하였다. 사용된 촉매 중에서 $Pd/ZrO_2$가 $H_2$ 전환율 측면에서 가장 활성이 좋은 것으로 나타났다. $H_2O$가 첨가된 선택적 $H_2$ 산화반응에서는 $H_2O$, CO, $H_2$가 경쟁흡착을 하였으며, 첨가된 $H_2O$가 CO 및 $H_2$의 반응을 촉진시켰다.

• 한국재료학회지
• /
• 제6권1호
• /
• pp.124-129
• /
• 1996

TiN 기판상에 CVD와 무전해 도금을 이용하여 구리막을 성장시킬 때 여러 가지 전처리에 따른 증착 양상의 변화에 관하여 조사하였다. Cu(hfac)2를 선재(precursor)로 사용하여 CVD 증착을 실시할 때 각 전처리에 따른 TiN상의 구리막의 덮힘성(coverage)향상은 Pd-HF 활성화 처리>>HF dip> RF remote plasma의 순이었다. 특히 Pd-HF 활성화 처리를 해줄 경우 거의 완전한 연속막을 얻을수 있었으며 scotch tape peel test 결과 매우 양호한 부착특성을 보였으나, 이에 비해 전처리를 해주지 않은 경우에는 오랜 시간이 경과되어도 연속막으로 성장하지 못하고 섬모양의 큰 결정립을 이룰 뿐이었다. 이러한 차이는 Pd-HF 활성화 처리에 의해 표면에 미세하게 형성된 Pd층이 구리의 핵생성과 부착특성을 크게 향상시켰기 때문인 것으로 사료되며 이러한 효과는 무전해 도금의 경우에도 마찬가지였다. 그리고 기판과 증착온도에 따른 선택성을 보면 35$0^{\circ}C$이하에서는 pd-HF 활성화 처리에 의해서 SiO2에 대하여 TiN으로의 선택성을 가지나 그 이상의 온도에서는 선택성이 상실되었다.

• 청정기술
• /
• 제17권3호
• /
• pp.225-230
• /
• 2011

다양한 귀금속 촉매를 이용한 hydrocarbon selective catalytic reduction 반응특성을 조사하였다. 가장 우수한 활성금속은 Pt, 지지체는 활성금속과 지지체간 강한 상호작용에 의하여 $CeO_2$, $TiO_2$였으며, NOx 전환율은 약 55%를 나타내었다. 활성금속으로서 Pd, Rh, Ag 촉매들은 20% 미만의 전환율을 보였으며, 지지체로서 $SiO_2$, $ZrO_2$ 또한 다른 지지체들보다 저조한 활성을 나타내었다. 조업조건에 따른 촉매의 성능을 조사하기 위하여 환원제의 종류, 양, 산소농도, 공간속도에 따른 실험을 수행하였다. 환원제로서 메탄이 프로판보다 우수함을 확인하였고, 메탄/질소 산화물 비가 증가할수록 성능이 우수하였으며, 산소농도가 증가할수록, 그리고 공간속도가 감소할수록 촉매의 성능은 증가함을 확인할 수 있었다.