• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.641-643
• /
• 2003

The ferroelectric properties of PZT(53/47) thin film was investigated by methoxy enthanol solution based on sol-gel method. The thickness of each layer by spincoating 0.25M sol at one time was $0.1{\mu}m$ and crack-free film was formed. $LaNiO_3/Si(100)$ electrode and $Pt/Ti/SiO_2/Si(100)$ electrode was coated by PZT sol at several times. PZT orientation was confirmed as a method of XRD and coercive field(Ec) as well as remnant polarization(Pr) was investigated from hysterisis curve. As a result of XRD analysis, we can know that the orientation of on PZT/LNO/Si(100) is better than on $Pt/Ti/SiO_2/Si(100)$. The remnant polarization(Pr) in LNO electrode was $87.5{\mu}C/cm^2$ and $39.8{\mu}C/cm^2$ in Pt. From this figures, it is investigated that the Pr in LNO electrode was better than in Pt.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.3
• /
• pp.188-192
• /
• 2000

In this study PZT etching was performed using planar inductively coupled Ar/Cl$_2$/BCI$_3$ plasma. The etch rate of PZT film was 2450 $\AA$/min at Ar(20)/BCl$_3$(80) gas mixing ratio and substrate temperature of 8$0^{\circ}C$. X-ray photoelectron spectroscopy(XPS) analysis for films composition of etched PZT surface was utilized. The chemical bond of PbO is broken by ion bombardment and Cl radical, and the peak of metal Pb in a Pb 4f narrow scan begins to appear upon etching. As increasing additive BCl$_3$content the relative content of oxygen decreases rapidly in contrast with etch rate of PZT thin film. So we though that the etch rate of PZT thin film increased because abundant B and BCl radicals made volatile oxy-compound such as B$_{x}$/O$_{y}$ and/or BClO$_{x}$ bond. We achieved etch profile of about 80$^{\circ}$ at Ar(20)/BCl$_3$(80) gas mixing condition and substrate temperature of 8$0^{\circ}C$TEX>X>.

• Journal of Sensor Science and Technology
• /
• v.19 no.3
• /
• pp.202-208
• /
• 2010

This study examined the dependency of crystalline orientation and electric properties of sol-gel PZT film on hydrolysis, a $PbTiO_3$ seed layer and a concentration of sol-gel solution. The PZT thin films were prepared by using 2-Methoxyethanol-based sol-gel method and spin-coating on Pt/Ti/$SiO_2$/Si substrates. The 1-${\mu}m$-thick PZT films were coated and then fired in a furnace by direct insert method. The highly (111) oriented PZT film of pure perovskite structure could be obtained. We could control the degree of orientation by various parameters such as hydrolysis, a $PbTiO_3$ seed layer and a concentration of sol-gel solution. The highest measured remanent polarization, dielectric constant and piezoelectric coefficient are $24.16\;{\mu}C/cm^2$, 2808, and 159 pC/N, respectively.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2003.05a
• /
• pp.1004-1008
• /
• 2003

Near-filed optical storage using cantilever aperture tip is a promising way fer next generation optical data storage. To enhance the speed of reading and writing data, gap between tip and media should be controlled fast and precisely within near field region. In this paper, several PZT actuators are analyzed far constructing dual servo control algorithm: coarse actuators(stact. PZT, bimorph PZI) for media surface inclination and One actuator(film PZT) for media surface roughness. Dynamic analysis of stack PZT, bimorph PZT, and film PZT are performed through the frequency response. Based on the frequency response and mathematical model, fast analog controller is designed.

• Transactions on Electrical and Electronic Materials
• /
• v.4 no.2
• /
• pp.20-23
• /
• 2003

Piezoelectric powder with the composition of PbTiO$_3$-PbZrO$_3$-Pb(Mn$\_$1/3/Nb$\_$2/3/)O$_3$ and small particle size of 0.3 $\mu\textrm{m}$ was investigated for low-temperature firing of PZT thick films. PbTiO$_3$-PbZrO$_3$-Pb(Mn$\_$1/3/Nb$\_$2/3)O$_3$ ceramics showed dense microstructure and superior piezoelectric properties, electromechanical coupling factor (k$\_$p/) of 0.501 and piezoelectric constant (d$\_$33/) of 224. The PZT paste was made of the powder and organic vehicles, and screen-printed on Pt(450nm)/YSZ(110nm)/SiO$_2$(300nm)/Si substrates and fired at 800∼900$^{\circ}C$. Any interface reaction between the PZT thick film and the bottom electrode was not observed in the PZT thick films. The PZT thick film fired at 800$^{\circ}C$ showed moderate electrical properties, the remanent polarization(p$\_$r/) of 16.0 ${\mu}$C/$\textrm{cm}^2$, the coercive field(E$\_$c/) of 36.7 ㎸/cm, and dielectric constant ($\varepsilon$$\_$r/) of 531. Low-temperature sinterable piezoelectric composition and high activity of fine particles reduced the sintering temperature of the thick film. This PZT thick film could be utilized for piezoelectric microactuators or microsensors that require Si micromachining technology.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1240_1241
• /
• 2009

In this paper, sol-gel-spin coated $Pb(ZrTi)O_3$ thin film with $ZrO_2$ buffer-layer and $PbTiO_3$ seed-layer was investigated for vibration MEMS energy harvester to scavenge power from ambient vibration via d33 piezoelectric mode. Piezoelectric thin film deposition techniques on insulating layer is the important key for $d_{33}$ mode of piezoelectric vibration energy harvester. $ZrO_2$ buff-layer was utilized as an insulating layer. $PbTIO_3$ seed-layer was applied as an inter-layer between PZT and $ZrO_2$ layer to improve the crystalline of PZT thin film. The fabricated PZT thin film had a remanent polarization of 5.3uC/$cm^2$ and the coercive field of 60kV/cm. The fabricated energy harvester using PZT thin film with PTO seed-layer generated 1.1uW of electrical power to $2.2M{\Omega}$ of load with $4.4V_{pvp}$ from vibration of 0.39g at 528Hz.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.6
• /
• pp.436-441
• /
• 1998

$Pt/SrTiO_3/Pb_x(Zr_{0.52}, Ti_{0.48})O_3/SrTiO_3/Si$ structure was prepared by rf-magnetron sputtering method for use in nondestructive read out ferroelectric RAM(NDRO-FEAM). PBx(Zr_{0.52}Ti_{0.48})O_3}$(PZT) and $SrTiO_3$(STO) films were deposited respectively at the temperatures of $300^{\circ}C and 500^{\circ}C$on p-Si(100) substrate. The role of the STO film as a buffer layer between the PZT film and the Si substrate was studied using X-ray diffraction (XRD), Auger electron spectroscopy (ASE), and scanning electron microscope(SEM). Structural analysis on the interfaces was carried out using a cross sectional transmission electron microscope(TEM). For PZT/Si structure, mostly Pb deficient pyrochlore phase was formed due to the serious diffusion of Pb into the Si substrate. On the other hand, for STO/PZT/STO/Si structure, the PZT film had perovskite phase and larger grain size with a little Pb interdiffusion. the interfaces of the PZT and the STO film, of the STO film and the interface layer and $SiO_2$, and of the $SiO_2$ and the Si substate had a good flatness. Across sectional TEM image showed the existence of an amorphous layer and $SiO_2$ with 7nm thickness between the STO film and the Si substrate. The electrical properties of MIFIS structure was characterized by C-V and I-V measurements. By 1MHz C-V characteristics Pt/STO(25nm)/PZT(160nm)/STO(25nm)/Si structure, memory window was about 1.2 V for and applied voltage of 5 V. Memory window increased by increasing the applied voltage and maximum voltage of memory window was 2 V for V applied. Memory window decreased by decreasing PZT film thickness to 110nm. Typical leakage current was abour $10{-8}$ A/cm for an applied voltage of 5 V.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.7
• /
• pp.551-556
• /
• 2001

In this work, the recovery of etching damage in the etched PZT thin film with $O_2$ annealing has been studied. The PZT thin films were etched as a function of Cl$_2$/Ar and additive CF$_4$ into Cl$_2$(80%) /Ar(20%). the etch rates of PZT thin films were 1600$\AA$/min at Cl$_2$(80%)/Ar(20%) and 1970 $\AA$/min at 30% additive Cf$_4$ into Cl$_2$(80%)/Ar(20%). In order to recover the characteristics of etched PZT thin films, the etched PZT thin films were annealed in $O_2$ atmosphere at various temperatures. From the hysteresis curves, ferroelectrical properties are improved by $O_2$ annealing process. The improvement of ferroelectric behavior is consistent with the increase of the (100) and (200) PZT phase revealed by x-ray diffraction (XRD). From x-ray photoelectron spectroscopy (XPS) analysis, intensities of Pb-O, Zr-O and Ti-O peak increase and the chemical residue peak is reduced by $O_2$ annealing. From the atomic force microscopy (AFM) images. it shows that the surface morphology of re-annealed PZT thin films after etching is improved.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.11
• /
• pp.983-989
• /
• 2005

[ $PZT(Pb(Zr,Ti)O_3)$ ] thin films were deposited by multi-target reactive sputtering method on $RuO_2$ substrates. Pure perovskite phase PZT films could be obtained by introducing Ti-oxide seed layer on the $RuO_2$ substrates prior to PZT film deposition. The PZT films deposited on the $RuO_2$ substrates showed highly voltage-shifted hysteresis loop compared with the films deposited on the Pt substrates. The surface of $RuO_2$ substrate was found to be reduced to metallic Ru in vacuum at elevated temperature, which caused the formation of oxygen vacancies at the initial stage of PZT film deposition and gave rise to the voltage shift in the P-E hysteresis loop of the PZT capacitor. The fatigue characteristics of the PZT capacitors under unipolar wane electric field were different from those under bipolar wane. The fatigue test under unipolar wane showed the increase of polarization. It was thought that the ferroelectric domains which had been pinned by charged defects such as oxygen vacancies and the charged defects were reduced in number by combining with the electrons injected from the electrode under unipolar wave, resulting in the relaxation of the ferroelectric domains and the increase of polarization.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1301-1302
• /
• 2007

The multilayered $Pb_{1.1}(Zr_{0.4}Ti_{0.6})O_{3}$/$Pb_{1.1}(Zr_{0.6}Ti_{0.4})O_{3}/Pb_{1.1}(Zr_{0.4}Ti_{0.6})O_{3}$[PZT(4060)/(6040)/(4060)] thin films were deposited by RF sputtering method on the Pt/TiO2/SiO2/Si substrate. We investigated the effects of deposition conditions on the structural and electrical properties of the multilayered PZT thin films. All the multilayered PZT thin films showed dense and homogeneous structure without the presence of the rosette structure. The dielectric properties such as dielectric constant, loss, remanent polarization of the multilayered PZT thin film were superior to those of single composition PZT(4060) and PZT(6040) films, and those values for the multilayered PZT(10/20/10) thin film were 903, 1.01% and $25.60{\mu}C/cm^2$. This study suggests that the design of the multilayered PZT thin films capacitor with tetragonal and rhombohedral phase should be an effective method to enhance the dielectric and ferroelectric performance in devices.