• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.1
• /
• pp.27-31
• /
• 2007

The cpapcitors with MIM(metal-insulator-metal) structures using PVP gate insulation films were prepared for the application of flexible organic thin film transistors (OTFT). The co-polymer organic insulation films were synthesized by using PVP(poly-4-vinylphenol) as a solute and PGMEA(propylene glycol monomethyl ether acetate) as a solvent. The cross-linked PVP insulation films were also prepared by addition of poly(melamine-co-formaldehyde) as thermal hardener. The leakage current of the cross- linked PVP films was found to be about 1.3 nA on Al/PES(polyethersulfone) substrate, whereas, on ITO/ glass substrate was about 27.5 nA indicating improvement of the leakage current at Al/PES substrates. Also, the capacitances of all prepared samples on ITO/glass and Al/PES substrates w ere ranged from 1.0 to $1.2nF/cm^2$, showing very similar result with the calculated capacitance values.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.15 no.7
• /
• pp.1559-1563
• /
• 2011

We fabricated gallium doped ZnO (GZO, 5 wt% Ga) thin films on PES (polyethersulfon) substrate with RF magnetron sputtering and investigated optical and electrical properties for various substrate temperatures ($50{\sim}200^{\circ}C$). All GZO thin film has c-axis preferred orientation without reference to deposition conditions. As a result of AFM analysis, the GZO thin film deposited at $200^{\circ}C$ exhibited the lowest surface roughness of 0.196nm. The transmittance of GZO thin films were above 80% and Burstein-Moss effect was observed. In the analysis of Hall measurement, we confirmed that the GZO thin film deposited at $200^{\circ}C$ showed the lowest resistivity of $6.93{\times}10-4{\Omega}{\cdot}cm$ and the highest carrier concentration of $7.04{\times}1020/cm^3$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.211-211
• /
• 2010

본 논문에서는 ZnO 박막을 휘어지기 쉬운 PES(polyethersulfone) 기판위에 PLD(pusled laser deposition)법을 사용하여 다양한 조건에서 성장시켰다. 성장된 ZnO 박막의 표면 형상과 광특성을 SEM과 PL을 사용하여 측정하였고, 레이저 밀도 0.3 J/$cm^2$, 기판 온도 $200^{\circ}C$에서 가장 좋은 광특성을 보였다.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1341-1342
• /
• 2007

Poly-ether-sulphone (PES) 기판위에 열처리 공정을 거친 HgTe 나노입자를 이용하여 플렉시블 투명 박막 트랜지스터를 제작하였다. 활성층으로 사용된 HgTe 나노입자층은 UV/ozone 처리로 친수성화 된 PES 기판위에 스핀코팅으로 형성되었다. 제작된 박막 트랜지스터는 전형적인 p형 트랜지스터 특성을 보여주었으며, PES 기판에 스트레인을 가하지 않은 상태에서는 164의 전류점멸비와 1.6 $cm^{2}/Vs$ 의 전하 이동도가 계산되었고, PES 기판에 2.0%의 스트레인을 인가하였을 때에는 266의 전류점멸비와 1.0 $cm^2/Vs$ 의 전하 이동도가 계산되었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.283.2-283.2
• /
• 2016

최근 ZnO는 무독성, 저가격, 수소 플라즈마에 대한 내구성 및 열적 안정성 등의 활발히 연구되고 있으며, III족 원소(Al, Ga, In) 불순물을 도핑하여 전기적 성질의 열적 불안정성을 해결하고 전기적 성질을 향상 시키고 또한 밴드갭 에너지가 3.3 eV 이상으로 증가하여 가시광선 영역에서 광투과율이 높은 투명도 전성 재료를 제공할 수 있다. 본 연구에서는 RF Magnetron Sputtering을 이용하여 내열성과 광학적 측면에서 우수한 성능을 가지는 PES 기판에 표면 에너지를 높이고 치밀한 구조의 박막을 증착하기 위해서 $O_2$ 플라즈마 처리를 하여 ZnO계 투명 전도막을 제작함으로써 투명전극에서 요구하는 $10^{-3}{\Omega}{\cdot}cm$ 이하의 낮은 비저항과 80% 이상의 광투과율을 가지는 방안에 대하여 연구하였다. PES 기판 위에 고밀도 $O_2$ 플라즈마를 이용하여 전 처리를 실시한 후 4인치의 Al-doped ZnO(ZnO 98 wt% : $Al_2O_3$ 2 wt%), AZO의 타겟을 이용하여 상온에서 RF Magnetron Sputtering 법으로 AZO 박막을 증착하였다. PES 기판상의 AZO 박막 두께가(100~400nm) 증가함에 따라 캐리어 농도와 홀 이동도가 점차 증가하는 경향을 보였다. 이는 박막 두께가 증가할수록 면저항과 비저항은 감소하며 결정립 크기가 커지고 결정입계에서 산란이 줄어들기 때문에 전기적 특성이 개선된 것으로 판단된다. 고밀도 $O_2$ 플라즈마 표면처리 시간이 증가함에 따라 플라스틱 기판의 결합에너지와 부착력이 증가하여 AZO 박막의 결정립 크기를 증가시키며, 접촉각은 감소하였다. 또한 급속열처리 온도가 증가함에 따라 전기적 특성과 광학적 특성이 향상됨을 확인할 수 있었다. 제작된 AZO 박막은 급속열처리 시간 10분에서 온도 $200^{\circ}C$일 때, 캐리어 농도 $2.32{\times}10^{21}cm^{-3}$, 홀 이동도 $4.3cm^{-2}/V$로 가장 높은 것을 확인할 수 있었고, 가장 낮은 비저항 $1.07{\times}10^{-3}{\Omega}{\cdot}cm$과 가시광 영역(300 nm ~ 1100 nm)에서의 AZO 박막의 광 투과율은 약 86%를 얻을 수 있었다.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.19 no.6
• /
• pp.1393-1398
• /
• 2015

In this study, the electrical and optical properties of GZO (Ga-doped ZnO) thin films prepared on PES substrates by RF magnetron sputtering method with various working pressures (5 to 20 mTorr) were investigated. All GZO thin films exhibited c-axis preferential growth regardless of working pressure, the GZO thin film deposited at 5 mTorr showed the most excellent crystallinity having 0.44˚ of FWHM. In AFM observations, surface roughness exhibited the lowest value of 0.20 nm in a thin film produced by the working pressure 5 mTorr. Figure of merits of GZO thin film deposited at 5 mTorr showed the highest value of 6652, in this case resistivity and average transmittance in the visible light region were 6.93×10^-4Ω-cm and 81.4%, respectively. We could observed the Burstein-Moss effect that carrier concentration decrease with the increase of working pressure and thus the energy band gap is narrowed.

• Polymer(Korea)
• /
• v.36 no.3
• /
• pp.393-400
• /
• 2012

The characteristics of indium tin oxide (ITO) thin film deposited on polyethersulfone (PES) film by low temperature E beam has been studied for the flexible photovoltaic devices. It was found that the substrate temperature in the deposition process affected the crystallization behavior of ITO during the post low temperature annealing process. Higher substrate temperature resulted in the increase of crystallinity of annealed ITO. Consequently, the lowering of sheet resistivity and better transmittance were obtained. Crystallization of ITO during the annealing process was facilitated by using oxygen gas in the deposition process and resulted in the enhancement on sheet resistivity and transmittance of ITO. The surface roughness of PES film prohibited the crystallization of ITO during the annealing process and it caused the increase of sheet resistivity and the decrease of transmittance of ITO.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.59 no.1
• /
• pp.113-115
• /
• 2010

In this study, ZnO films have been grown on PES(polyethersu]fone) substrate by PLD(pulsed laser deposition) and characterized as a change of laser density and substrate temperature. Growing conditions were changed with substrate temperatures ranging from 50 to $200^{\circ}C$ and laser densities ranging from $0.2\sim0.4 J/cm^2$. Optical and structural properties were measured by XRD, SEM, AFM, PL measurement.

• The Journal of the Korea institute of electronic communication sciences
• /
• v.14 no.5
• /
• pp.887-892
• /
• 2019

In this study, after 20nm-thick $SiO_2$ thin film was deposited by PECVD method on the PES substrate, which is known to have the highest heat resistance among plastic substrates, as a buffer layer, ITZO thin films were deposited by RF magnetron sputtering method to investigate the electrical and optical properties according to the working pressure. The ITZO thin film deposited at the working pressure of 3mTorr showed the best electrical properties with a resistivity of $8.02{\times}10^{-4}{\Omega}-cm$ and a sheet resistance of $50.13{\Omega}/sq.$. The average transmittance in the visible region (400-800nm) of all ITZO films was over 80% regardless of working pressure. The Figure of merit showed the largest value of $23.90{\times}10^{-4}{\Omega}^{-1}$ in the ITZO thin film deposited at 3mTorr. This study found that ITZO thin films are very promising materials to replace ITO thin films in next-generation flexible display devices.

• The Journal of the Korea institute of electronic communication sciences
• /
• v.16 no.3
• /
• pp.443-450
• /
• 2021

After selecting a PES substrate with excellent thermal stability and optical properties among plastic substrates, a SiO₂ thin film was deposited as a buffer layer to a thickness of 20nm by plasma-enhanced chemical vapor deposition to compensate for the high moisture absorption. Then, the ITZO thin film was deposited by a RF magnetron sputtering method to investigate electrical and optical properties according to RF power. The ITZO thin film deposited at 50W showed the best electrical properties such as a resistivity of 8.02×10^-4 Ω-cm and a sheet resistance of 50.13Ω/sq.. The average transmittance of the ITZO thin film in the visible light region(400-800nm) was relatively high as 80% or more when the RF power was 40 and 50W. Figure of Merits (Φ_TC and FOM) showed the largest values of 23.90×10^-4 Ω^-1 and 5883 Ω^-1cm^-1, respectively, in the ITZO thin film deposited at 50W.