• Journal of the Korean institute of surface engineering
• /
• v.55 no.4
• /
• pp.215-221
• /
• 2022

In the present work, copper oxide thin films were formed by heat-treatment method with different temperatures and atmosphere, e.g., at 200 ~ 400 ℃; in air and Ar atmosphere. The morphological, electrical and optical properties of the thermally fabricated Cu oxide films were analyzed by SEM, XRD, and UV-VIS spectrometer. Thereafter, photoelectrochemical properties of the thermal copper oxide films were analyzed under solar light (AM 1.5, 100 mW/cm²). Conclusively, the highest photocurrent was obtained with Cu₂O formed under the optimum annealing condition at 300 ℃ in air atmosphere. In addition, EIS results of Cu oxide formed in air atmosphere showed relatively low resistance and long electron life-time compared with Cu Oxide fabricated in Ar atmosphere at the same temperature. This is because heat-treatment in Ar atmosphere could not form Cu₂O due to lack of oxygen, and thermally formed CuO at high temperature suppressed stability and conductivity of the Cu oxide.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1795-1796
• /
• 1999

ITO thin films have been deposited on PET substrate by reactive dc magnetron sputtering without substrate heater and post heat treatment. The electrical and optical properties of as-deposited films are dominated by oxygen gas ratio. As the experimental results, the excellent ITO films are prepared on PET substrate at the operating conditions as follows: operating pressure of 5 mTorr, target-substrate distance of 4.5 cm, dc power of $20{\sim}30W$, and oxygen gas ratio of 10 %. The optical transmittance is above 80 % at 550 nm, and the sheet resistance and resistivity of films are $24{\Omega}$/square and $1.5{\times}10^{-3}{\Omega}cm$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.28 no.6
• /
• pp.495-501
• /
• 1991

This study is intended to make defect-free region, denuded zone at the silicon wafer surface for semiconductor device substrates. In this experiment, initial oxygen concentration of starting material CZ-grown silicon wafer, various heat treatment combinations, denuding ambient and the amounts of oxygen reduction were measured, and then denuded zone (DZ) formation and depth were investigated. In Low/High anneal (DZ formation could be achieved), the optimum temperature for Low anneal was 700$^{\circ}C$∼750$^{\circ}C$. In case of High anneal, with the time increased, DZ depth was increased at 1000$^{\circ}C$, 1150$^{\circ}C$ respectively, but on the contrary, DZ depth was decreased at low temperature 900$^{\circ}C$. As well, out-diffusion time below 2 hours was unsuitable for effective Gettering technique even though the temperature was high, and DZ formation could be achieved when initial oxygen concentration was only above 14 ppm in silicon wafer.

• Journal of the Korean Electrochemical Society
• /
• v.14 no.2
• /
• pp.71-76
• /
• 2011

Fe-tetramethoxyphenylporphyrin on carbon black (Fe-TMPP/C) is examined and compared with carbon (C) and Pt-coated carbon (Pt/C) for oxygen reduction reaction in a two chambered microbial fuel cell (MFC). The Fe-TMPP/C is prepared by heat treatment and characterized using SEM, TEM, and XPS. The electrochemical properties of catalysts are characterized by voltammerty and single cell measurements. It is found that the power generation in the MFC with Fe-TMPP/C as the cathode is higher than that with Pt/C. The maximum power of the Fe-TMPP/C is 0.12 mW compared with 0.10 mW (Pt/C) and 0.02 mW (C). This high output with the Fe-TMPP/C indicates that MFCs are promising in further practical applications with low cost macrocycles catalysts.

• Korean Journal of Microbiology
• /
• v.18 no.3
• /
• pp.148-152
• /
• 1980

The microwave of 2450 MHz, generated by a household cooking oven, was evaluated for its applicability to melt various rehydrated media and to remove dissolved oxygen from tubed media for anaerobic culture. The effect on the sterilization of E. coli in selective media was also evaluated. The following results were obtained. 10 The microwave oven was useful in saving time for melting media and in eliminating heat and combustion gas from the laboratory, which were inevitable by-products in the conventional flame method. 2) Dissolved oxygen could be removed without boiling over by exposing the tubes of anaerobic culture medium after putting them in a wire basket in a beaker with water. 30 The count of E. coli during the melting of MacConkey and EMB agar were similar to those treated with open flame. The microwave treatment was not considered a possible mean to replace autoclaving even in these selective media.

• Journal of Ceramic Processing Research
• /
• v.19 no.6
• /
• pp.499-503
• /
• 2018

In this paper, cobalt embedded in nitrogen and sulfur co-doped carbon nanotubes (CoNSTs) were synthesized for oxygen reduction reaction (ORR) catalysts. The CoNSTs were prepared through a facile heat treatment method without any templates. Different amounts of the metal salt were employed to examine the physicochemical and electrochemical properties of the CoNSTs. The CoNSTs showed the bamboo-like tube morphology with the encased Co nanoparticles in the tubes. Through the x-ray photoelectron spectroscopy analysis, the catalysts exhibited different chemical states of the nitrogen and sulfur species. As a result, the CoNST performed high activity toward the ORR in an acidic condition with the onset potential of 0.863 V (vs. reversible hydrogen electrode). It was clearly demonstrated from the electrochemical characterizations that the quality of the nitrogen and sulfur species significantly influences the ORR activity rather than the total amount of the dopants.

• Applied Chemistry
• /
• v.15 no.1
• /
• pp.81-84
• /
• 2011

Platinum catalyst activity and stability is excellent in terms of fuel cells as a catalyst here. Although it is widely used, to compensate for the high price issue non-precious fuel cell catalysts are being developed. In this study, Co/PANi/CNT composite and non-precious as a catalyst for oxygen reduction was applied. Polyaniline on the interaction between cobalt and the oxygen reduction reaction and the structural characteristics observed in the impact and heat treatment was carried out according to the improved catalytic performance. Potential range is oxygen reduction reaction 0.55 V to 0.78 V(vs. NHE) after pyrolysis. Through this study, Co /PANi/CNT composites as a potential catalyst for fuel cells were non-precious.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.360-365
• /
• 1996

The purpose of this study was to evaluate the changes in the degree of conversion on a composite resin surface following heat treatment and mylar strip finishing. The effects of the time interval between the light-curing and heat-curing process were also evaluated. The composite resin surface which had been covered with a coverglass showed a lower conversion rate than the surface from which a layer of $500{\mu}m$ was ground away. The composite resin surface was definitely affected by oxygen during the heat curing process when it had not been insulated. When the composite resins were heat cured after 3 days of storage following the light curing process, the increased in the degree of conversion through heatcuring was limited.

• Journal of the Korean Ceramic Society
• /
• v.30 no.1
• /
• pp.17-24
• /
• 1993

Sol-gel spin-coating technique was used to produce Nb2O5 thin films on silicon substrates from Nb(OC2H5)5 precursor. The films were heat-treated at temperatures between $600^{\circ}C$ and 100$0^{\circ}C$ in oxygen atmosphere and their crystalline phases, chemical states, and dielectric characteristics were investigated by X-ray diffractometry (XRD), Auger electron spectroscopy (AES), and C-V measurements, respectively. After 1 hour heat-treatment at 80$0^{\circ}C$, T-type Nb2O5 was formed, and its chemical composition was homogeneous with no appreciable SiO2 oxide at interfaces between the films and substrates. The films heat-treated at temperatures between $600^{\circ}C$ and 80$0^{\circ}C$ exhibit dielectric constant of less than 20 while the films heat treated at 100$0^{\circ}C$ show dielectric constant of 28.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.18 no.1
• /
• pp.81-88
• /
• 2010

Characteristic of hydrogen production was investigated to find the optimum heat pretreatment conditions for the anaerobic fermentation of food waste. The heat pretreatment of food waste enhanced the hydrogen yield due to the increase of soluble chemical oxygen demand (SCOD) and carbohydrate content. This result revealed that the maximum degrees of disintegration of SCOD and carbohydrate content were 55.1% and 223.6%, respectively. On the other hand, the improvement of hydrogen yield was insignificantly affected by heating reaction time at longer than 20 min; the increase of hydrogen yield was only about 7% between 20min and 1 hour. Therefore, the increase of reaction time more than 20min was not necessary.