• Korean Journal of Materials Research
• /
• v.32 no.2
• /
• pp.107-113
• /
• 2022

Fibrous supercapacitors (FSs), owing to their high power density, good safety characteristic, and high flexibility, have recently been in the spotlight as energy storage devices for wearable electronics. However, despite these advantages, FCs face many challenges related to their active material of carbon fiber (CF). CF has low surface area and poor wettability between electrode and electrolyte, which result in low capacitance and poor long-term stability at high current densities. To overcome these limits, fibrous supercapacitors made using surface-activated CF (FS-SACF) are here suggested; these materials have improved specific surface area and better wettability, obtained by introducing porous structure and oxygen-containing functional groups on the CF surface, respectively, through surface engineering. The FS-SACF shows an improved ion diffusion coefficient and better electrochemical performance, including high specific capacity of 223.6 mF cm^-2 at current density of 10 ㎂ cm^-2, high-rate performance of 171.2 mF cm^-2 at current density of 50.0 ㎂ cm^-2, and remarkable, ultrafast cycling stability (96.2 % after 1,000 cycles at current density of 250.0 ㎂ cm^-2). The excellent electrochemical performance is definitely due to the effects of surface functionalization on CF, leading to improved specific surface area and superior ion diffusion capability.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.6
• /
• pp.278-282
• /
• 2010

The doping effect of thulium on electrical properties and degradation behavior in barium titanate ceramics ($BaTiO_3$) was investigated in terms of generations of core-shell structure and micro-chemical changes through highly accelerated degradation test. The dielectric specimens of pellet type and multi-layered sheets were prepared by using $BaTiO_3$ with undoped and doped with 1 mol% $Tm_2O_3$. The $BaTiO_3$ ceramics doped with 1 mol% $Tm_2O_3$ had 40% higher dielectric constant (${\varepsilon}$ = 2700) than that of the undoped $BaTiO_3$ specimen at curie temperature and met X7R specification. According to the result of highly accelerated degradation test conducted at $150^{\circ}C$, 70 V, and 24 hr, the oxygen diffusion was declined in dielectrics doped with 1 mol% $Tm_2O_3$. The $Tm^{3+}$ ion substituted selectively Ba site and Ti site and contributed to the generation of the core-shell structure. Oxygen vacancies occurred by substitution for Ti site could reduce excess oxygen that reacted to the Ni electrode.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.47 no.7
• /
• pp.8-16
• /
• 2010

In this paper, we investigated the effects of $O_2$ fraction on the properties of Al-doped ZnO (AZO) thin films prepared by radio frequency (RF) magnetron sputtering. Hall, photoluminescence (PL), and X-ray photoelectron spectroscopy (XPS) measurements revealed that the p-type conductivity was exhibited for AZO films with an $O_2$ fraction of 0.9 while the n-type conductivity was observed for films with $O_2$ fractions in range of 0 - 0.6. PL and XPS also showed that the acceptor-like defects, such as zinc vacancies and oxygen interstitials, increased in films prepared by an $O_2$ fraction of 0.9, resulting in the p-type conductivity in the films. Hall results indicated that AZO films prepared by $O_2$ fractions in range of 0 - 0.6 can be used for electrode layers in the applications of transparent thin film transistor. We concluded from the X-ray diffraction analysis that worse crystallinity with a smaller grain size as well as higher tensile stress was observed in the films prepared by a higher $O_2$ fraction, which is related to incorporation of more oxygen atoms into the films during deposition. The study of atomic force microscope suggested that the smoother surface morphology was observed in films prepared by using $O_2$ fraction, which causes the higher resistivity in those films, as evidenced by Hall measurements.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.2
• /
• pp.82-87
• /
• 2005

The cathode material, $LiNi_{0.5}Mn_{1.5}O_4$, for high voltage applications of Li-ion batteries exhibits impurity phases due to oxygen deficiency during the high temperature heat treatment. The impurity phase reduces the electrochemical properties of the electrode since the deficiency spinel structure disturbs the lithium ion intercalation and deintercalation. In this study, Cr-substituted $LiNi_{0.5-x}Mn_{1.5}Cr_xO_4(0{\leq}x{\leq}0.05)$ powders are synthesized by a sol-gel method in order to reduce the amount of the impurity phases in the $LiNi_{0.5-x}Mn_{1.5}Cr_xO_4$. Thermal analysis of the cathode material shows that the $LiNi_{0.5}Mn_{1.5}O_4$ without Cr substitution looses $2\%$ of its weight due to oxygen deficiency but the amount of weight loss is diminished when Cr is substituted. XRD analysis also supports the reduction of the impurity phases in the cathode after chromium substitution, suggesting that the improvement of the electrochemical properties such as the capacity retention and electrochemical stability are attributed to the low content of impurity phases in the Cr-substituted $LiNi_{0.5-x}Mn_{1.5}Cr_xO_4.$

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.10
• /
• pp.805-810
• /
• 2012

Transparent conducting oxides (TCOs) have wide range of application areas in transparent electrode for display devices, Transparent coating for solar energy heat mirrors, and electromagnetic wave shield. $SnO_2$ is intrinsically an n-type semiconductor due to oxygen deficiencies and has a high energy-band gap more than 3.5 eV. It is known as a transparent conducting oxide because of its low resistivity of $10^{-3}{\Omega}{\cdot}cm$ and high transmittance over 90% in visible region. In this study, co-doping effects of Al and Y on the properties of $SnO_2$ were investigated. The addition of Y in $SnO_2$ was tried to create oxygen vacancies that increase the diffusivity of oxygen ions for the densification of $SnO_2$. The addition of Al was expected to increase the electron concentration. Once, we observed solubility limit of $SnO_2$ single-doped with Al and Y. $\{(x/2)Al_2O_3+(x/2)Y_2O_3\}-SnO_2$ was used for the source of Al and Y to prevent the evaporation of $Al_2O_3$ and for the charge compensation. And we observed the valence changes of aluminium oxide because generally reported of valence changes of aluminium oxide in Tin - Aluminium binary system. The electrical properties, solubility limit, densification and microstructure of $SnO_2$ co-doped with Al and Y will be discussed.

• Journal of Korean Ophthalmic Optics Society
• /
• v.14 no.1
• /
• pp.63-68
• /
• 2009

Purpose: TiN films were deposited on sus304 by unbalanced magnetron sputtering system which was designed and developed as unbalancing the strength of the magnets in the magnetron electrode. The effect of oxygen incorporation in the fabrication of deposited films was investigated. Methods: The cross sections of deposited films on Silicon wafer were observed by SEM to measure the thickness of the films, the components of the surface of the films were identified by XPS survey spectra, the compositional depth-profile of deposited films was examined by an XPS apparatus. Results: From the data of XPS depth profile of films, it could be seen that the element O as well as the elements Ti and N present in the surface of the film and the relative percentage of the element O was constant at 65 at.% with respect to the depth of film. Conclusions: The color change with thickness of the films had something to do with the change of Ti $ 2p_{3/2}$ peak intensity and shape mixed of $ TiO_2$, TiN, $ TiO_{x}N_{y}$ compound.

• Resources Recycling
• /
• v.21 no.2
• /
• pp.34-40
• /
• 2012

$Pt_{10}$/C, $Pt_9Mn_1$/C, $Pt_7Mn_3$/C electrocatalysts for Polymer Electrolyte Membrane Fuel Cells(PEMFCs) were synthesized by reduction with HCHO and their activity as a oxygen reduction reaction(ORR) was examined at half cell. The electrochemical oxygen reduction reaction(ORR) was studied by using a glaasy carbon electrode through cyclic voltammetric curves(CV) in a 1 M $H_2SO_4$ solution. The ORR activities of $Pt_9Mn_1$/C were higher than $Pt_{10}$/C, $Pt_7Mn_3$/C. Also potential-current curves of $Pt_9Mn_1$/C at 0.9, 0.8, 0.7, 0.6V for 5minutes respectively were higher than $Pt_{10}$/C, $Pt_7Mn_3$/C. Physical characterization was made by using x-ray diffraction(XRD) and transmission electron microscope(TEM). The TEM images of $Pt_9Mn_1$/C, $Pt_{10}$/C catalysts showed homogenous particle distribution with particle size of about 2.7 nm, 3 nm respectively and then the XRD results showed that the crystalline structure of the synthesized catalysts are seen FCC structure.

• Journal of Korean Society of Environmental Engineers
• /
• v.31 no.4
• /
• pp.249-255
• /
• 2009

The performance of microbial fuel cell (MFC) can be affected by many factors including the rate of organic matter oxidation, the electron transfer to electrode by electrochemical bacteria, proton diffusion, the concentration of electron acceptor, the rate of electron acceptor reduction and internal resistance. the performance of MFC using oxygen as electron acceptor can be influenced by oxygen concentration as limit factors in cathode compartment. Many studies have been performed to enhance electricity production from MFC. The series or parallel stacked MFC connected several MFC units can use to increase voltages and currents produced from MFCs. In this study, a single MFC (S-MFC) and a stacked MFC (ST-MFC) using acetate as electron donor and oxygen as electron acceptor were used to investigate the influence of dissolved oxygen (DO) concentrations in cathode compartment on MFC performance. The power density (W/$m^3$) of S-MFC was in order DO 5 > 3 > 7 > 9 mg/L, the maximum power density (W/$m^3$) of S-MFC was 42 W/$m^3$ at DO 5 mg/L. The power density (W/$m^3$) of ST-MFC was in order DO 5 > 7 > 9 > 3 mg/L and the maximum power density (W/$m^3$) of STMFC was 20 W/$m^3$ at DO 5 mg/L. These results suggest that the DO concentration of cathode chamber should be considered as important limit factor of MFC operation and design for stacked MFC as well as single MFC. The results of ST-MFC operation showed the voltage decrease of some MFC units by salt formation on the surface of anode, resulting in decrease total voltage of ST-MFC. Therefore, connecting MFC units in parallel might be more appropriate way than series connections to enhance power production of stacked MFC.

• Membrane Journal
• /
• v.22 no.2
• /
• pp.95-103
• /
• 2012

To treat nitrate and non-biodegradable organics effectively in sewage, industrial wastewater and livestock wastewater, the activated sludge process integrated by a membrane separation and a porous electrode- electrolysis was proposed and its efficiency was investigated. The proposed system was consisted of 3 processes; activated sludge, membrane filtration and electrolysis. In the study, the membrane filtration played a role in reducing the load of the electrolysis to operate the proposed process stably. The electrolysis consisted of a porous electrode to increase the efficiency due to the extension of the specific surface area. Additionally, redox reaction in the electrolysis was induced by decomposing influent water as current was applied. As a result, hydrogen free radicals and oxygen radicals as intermediates were produced and they acted as oxidants to play a role in decomposing non-degradable organics. It was environmentally-friendly process because intermediates produced by porous electrode were used to treat waste matters without supplying external reagent. Experimental data showed that the proposed process was more excellent than activated sludge process. SS removal efficiencies of the proposed process, membrane filtration and activated sludge process were about 100%, about 100% and about 90%, respectively. COD removal efficiencies of the proposed system, membrane filtration and activated sludge process were about 92%, about 84% and about 78%, respectively. T-N removal efficiencies of the proposed system, membrane filtration and activated sludge process were about 88%, about 67%, and about 58%, respectively. The SS data showed that SS was efficiently removed in the single of the membrane filtration. The COD/T-N data showed that COD/T-N of membrane hybrid process was treated by removing a little soluble organics and SS, and that COD/T-N of electrolysis hybrid process was treated by oxidize organics with high removal rate.

• Applied Chemistry for Engineering
• /
• v.18 no.3
• /
• pp.291-295
• /
• 2007

The oxidation treatment of needle cokes with 70 wt% of nitric acid and sodium chlorate ($NaClO_3$) was attempted to achieve an electrochemically active material with a large capacitance. The structure of needle cokes was changed to graphite oxide after oxidation treatment of needle cokes with acidic solution having the composition ratio, $NaClO_3$/needle cokes, of 7.5, and the inter-layer distance of the oxidized needle cokes was extended to $6.9{\AA}$with increasing oxygen content. On the other hand, the electrochemical performance of oxidized needle cokes as a polarized electrode for an Electric Double Layer Capacitor (EDLC) was examined with an electrolyte of 1.2 M $TEABF_4$ (tetraethylammonium tetrafluoroborate) and $TEABF_4$ (triethylmethylammonium tetrafluoroborate) in acetonitrile. The capacitor cell using 1.2 M $TEABF_4$/acetonitrile has exhibited smaller electric resistance of $0.05{\Omega}$, and larger capacitance per weight and volume of 32.0 F/g and 25.5 F/mL at the two-electrode system in the potential range 0~2.5 V than that of the capacitor cell using $TEABF_4$. The observed electrochemical performance was discussed with the correlation between the inter-layer distance in graphite oxide structure and the anionic size of electrolyte.