• Journal of the Korean Society for Heat Treatment
• /
• v.32 no.1
• /
• pp.1-11
• /
• 2019

In this study, microstructure evolution and crystallographic orientation are investigated under various deformation conditions in M1 magnesium alloy. M1 magnesium ingot was rolled at 673 K with the rolling reduction of 30%. The compression test specimens were machined out from rolled plate, and then the specimens were annealed at 823 K for 1h. Uniaxial compression tests were conducted at 723 K and under the strain rate ranging from $5.0{\times}10^{-4}s^{-1}$ to $5.0{\times}10^{-2}s^{-1}$ up to a true strain of -1.0. For observation of crystal orientation distribution, EBSD measurement was performed. Occurrence of the dynamic recrystallization and grain boundary migration were confirmed in all case of the specimens. The distribution of the grains is not uniformed in the experimental conditions.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.10a
• /
• pp.147-149
• /
• 2001

In order to understand the influence of the modification of deformation texture on the formation of annealing texture, the evolution of texture during the clock rolling and the subsequent annealing was investigated by employing X-ray texture measurements and microstructure observation. The $\beta$-fiber orientations were proved to be quite unstable during the clock rolling. The clock rolled texture having uniform orientation densities along $\{011\}//ND$ fiber resulted in the randomization of annealing texture. This indicated that the operation of both the oriented nucleation and the oriented growth was effectively suppressed in the clock-rolled specimen during recrystallization.

• Journal of Magnetics
• /
• v.3 no.4
• /
• pp.127-133
• /
• 1998

I have overviewed the change in GMR on annealing, in conjunction with the change in microstructure. The Co46Al19O35 granular thin films were annealed at 30$0^{\circ}C$ for various annealing time to change the microstructure. The magnitude of GMR decreases considerably with increasing annealing time, although the size of Co granules estimated from TEM observation show a small change. Parameter fits of magnetization curves and magnetoresistance curves to the Langevin function suggest that large clusters consisting of several small Co granules, which are coupled ferromagnetically, are related with the decrease of GMR on annealing. The temperature dependence of electrical resistivity ($\rho$) shows the relationship of log $\rho$ versus $T^{-1/2}$ for the sample annealed for 10 min., 1 hr. and 6 hrs. However, the sample annealed for 38 hrs. shows the relationship of log $\rho$ versus$ T^{-1/4},$ which represents a significant change in the transport mechanism.

• Journal of Power System Engineering
• /
• v.22 no.1
• /
• pp.87-93
• /
• 2018

Specimens were machined out from hot-rolled AZ31 magnesium alloy, and deformed at 623K with rolling reduction of 30%. After hot rolling, specimens were annealed at various range of temperature and time. In this study, static recrystallization was occurred during heat treatment, however, variation of main component and intensity of texture was not revealed. The results of microstructure observation, damping capacity test and dislocation mechanism indicated that increasing of damping capacity was caused by grain growth. It means that grain size is effective factor to damping capacity.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.6
• /
• pp.321-325
• /
• 2019

Triso-type coating layers of silicon carbide and graphite on UO₂ paticulate nuclear fuel were prepared by using fluidized bed type chemical vapor deposition and self-propagating high temperature synthesis methods to make a coated nuclear fuel of a power plant for hydrogen mass-production. The source and carrier gases were the mixture of methyltrichlorosilane and propane, and inert argon. Chemical analysis and microstructure observation showed that the coated layers were inner graphite, middle silicon carbide and outer graphite. The elastic modulus and nano-hardness of the silicon carbide layer were 503 [GPa] and 36 [GPa], respectively.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1086-1090
• /
• 2001

Composition effects on microstructure and metallizing properties of the alumina sintered body were evaluated to develop the metallized alumina tubes having superior properties for electronic devices. SEM observation revealed that resultant micrographs and fractographs were varied with composition chance of additives and $SiO_2$-rich specimens showed better microstructural characteristics with uniform distribution of fine and round particles than other CaO-rich or MgO-rich ones. The resultant interfacial microstructure of the $SiO_2$-rich metallized alumina tubes also showed good metallizing properties with no defects between layers and uniform thickness of metallizing layer.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.303-304
• /
• 2006

The mechanical properties of ferrous powder metallurgy (P/M) materials are directly related to their microstructure. Ferrous P/M materials with sufficient hardenability will develop microstructures containing significant percentages of martensite in the as-sintered condition. Recently, sinter-hardening has developed into a highly cost effective production method through hardened P/M parts without the need for additional heat-treatments. This paper reviews the advances of sinter-hardening as well as some key processing parameters such as sintering temperature, cooling rate, tempering required to produce high quality sinter-hardened components. Specific topics including effect of alloying elements, alloying methods, and the Characterization and observation of microstructure are discussed.

• Journal of the Korean Ceramic Society
• /
• v.31 no.6
• /
• pp.609-616
• /
• 1994

Investigation for the high strength grouts using ordinary cement mortar, melamine formaldehyde condensate (MFC) with various admixtures was carried out. The physical properties of the grouts were investigated through the observation of the microstructure and the application of fracture mechanics. When the lime stone and fly ash was added with 6 wt% to the grouts, the compressive strength was about 72 MPa, 69 MPa respectively, and the flexural strength was about 11.9 MPa, 11.4 MPa respectively, the Young's modulus was about 4.3 GPa, 3.9 GPa, and the critical stress intensity was about 7.3 ×10-1MNm-1.5, 6.8×10-1MNm-1.5 respectively. When the silica fume was added with 6 wt% to the grouts, the compressive strength and the flexural strength were 81 MPa, 12.3 MPa, Young's modulus was 4.8 GPa and the critical stress intensity was about 8.4×10-1MNm-1.5.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2000.04a
• /
• pp.202-205
• /
• 2000

The effect of two step cold rolling and intermediate annealing conditions on the microstructure and texture evolution in type 430 stainless steel has been investigated tin order to improve ridging characteristic and deep drawability. The rolling and recrystallization textures were examined by orientation distributionfunction(ODF) and electron backscattered diffraction(EBSD). The observation showed that the intensity of ${\gamma}$-fiber was increased with two-step cold rolling process and so ridging characteristic and deep drawability were considerably improved. The relation between these properties an texture evolution has been discussed.

• Journal of Biomedical Engineering Research
• /
• v.21 no.6
• /
• pp.537-542
• /
• 2000

Ga이 함유된 Pd-Ga계 합금은 우수한 기계적 성질, 심미성 및 생체적합성등으로 차세대 치과 도재용 합금으로 주목 받고 있다. 본 연구에서는 상용 77.3%Pd-6.0%Ga계 합금을 원심주조법으로 주조하고, 탈개스, 세라믹소성처리한 후 미세조직을 광학현미경, X-선 회절기, 투과전자현미경으로 관찰하였다. X-선 회절분석 및 투과전자현미경 관찰 결과, Pd고용체와 미세한 석출물에 의해 나타나는 줄무늬를 확인하였다. 공정점 86$0^{\circ}C$에서 5시간 유지시킨 상평형 열처리조건에서는 Pd고용체와 금속간화합물 Pd(sub)2Ga에 해당하는 보다 명확한 제한시야회절도형을 얻었다. 이러한 결과로 77.3%Pd-6.0%Ga계 합금은 Pd고용체와 미세한 구형의 금속간화합물 Pd(sub2)Ga으로 구성되었음을 알 수 있었다.