Change in the Energy Band Gap and Transmittance IGZO, ZnO, AZO OMO Structure According to Ag Thickness (IGZO, ZnO, AZO OMO 구조의 Ag두께 변화에 따른 투과율과 에너지 밴드 갭의 변화)

  • Lee, Seung-Min;Kim, Hong-Bae;Lee, Sang-Yeol
    • Journal of the Korean Institute of Electrical and Electronic Material Engineers
    • /
    • v.28 no.3
    • /
    • pp.185-190
    • /
    • 2015
  • In this study, we fabricated the indium gallium zinc oxide (IGZO), zinc oxide (ZnO), aluminum zinc oxide (AZO). oxide and silver are deposited by magnetron sputtering and thermal evaporator, respectively transparency and energy bandgap were changed by the thickness of silver layer. To fabricate metal oxide metal (OMO) structure, IGZO sputtered on a corning 1,737 glass substrate was used as bottom oxide material and then silver was evaporated on the IGZO layer, finally IGZO was sputtered on the silver layer we get the final OMO structure. The radio-frequency power of the target was fixed at 30 W. The chamber pressure was set to $6.0{\times}10^{-3}$ Torr, and the gas ratio of Ar was fixed at 25 sccm. The silver thickness are varied from 3 to 15 nm. The OMO thin films was analyzed using XRD. XRD shows broad peak which clearly indicates amorphous phase. ZnO, AZO, OMO show the peak [002] direction at $34^{\circ}$. This indicate that ZnO, AZO OMO structure show the crystalline peak. Average transmittance of visible region was over 75%, while that of infrared region was under 20%. Energy band gap of OMO layer was increased with increasing thickness of Ag layer. As a result total transmittance was decreased.

투명 유연 AMOLED TV 구현을 위한 증착형 SnO2/Ag-Pd-Cu(APC)/SnO2 다층 투명 캐소드 박막 연구

  • Kim, Du-Hui;Kim, Han-Gi
    • Proceedings of the Korean Vacuum Society Conference
    • /
    • 2016.02a
    • /
    • pp.181.2-181.2
    • /
    • 2016
  • OLED 소자는 발광 방향에 따라 Bottom Emission 방식과 Top Emission 방식으로 나뉜다. 이 중 대면적 OLED TV 적용에 개구율이 더 높은 Top Emission방식을 선호하는 추세이다. 높은 개구율을 가진 Top Emission OLED소자를 위해서는 투명하고 전도성이 높은 캐소드가 중요하다. 본 연구에서는 Themal Evaporation 시스템을 이용하여 증착한 $SnO_2/Ag-Pd-Cu(APC)/SnO_2$ hybrid 전극의 특성을 연구하고 Oxide/Metal/Oxide(OMO) hybrid 박막의 bending mechanism을 제시하였다. base pressure는 $1{\times}10^{-6}Torr$로 고정하고 $SnO_2$ 박막은 0.34A / 0.32V, APC 박막은 0.46A / 0.40V의 power로 성막하였다. APC와 $SnO_2$의 두께를 변수로 OMO 전극을 제작하였고 그 전기적, 광학적 특성을 Hall measurement, UV/Visible spectroscopy을 이용하여 분석하고 Figure of merit 값을 바탕으로 최적 두께를 설정하였다. UPS(Ultraviolet Photoelectron Spectroscopy) 분석으로 $SnO_2/APC/SnO_2$ 전극의 일함수을 통해 투명 cathode로 쓰였을 때 $SnO_2$ 층이 buffer layer역할을 함을 확인하였다. XPS(X-ray photoelectron spectroscopy)를 이용하여 정성분석과 정량분석을 하였고 OMO hybrid 전극의 bending mechanism 연구를 위해 다양한 bending test (Inner/Outer dynamic fatigue test, twisting test, rolling test)를 진행하였다. 물리적 힘이 가해진 OMO hybrid 전극의 표면과 구조는 FE-SEM(Field Emission Scanning Electron Microscope) 분석을 통해서 확인할 수 있었다.

  • PDF

Dependences of Oxide layers on the Properties of the IGZO/Ag/IGZO Multi-Layer Films (산화물층에 따른 IGZO/Ag/IGZO 다층 박막의 특성 연구)

  • ;Lee, Sang-Ryeol;Kim, Hong-Bae
    • Proceedings of the Korean Vacuum Society Conference
    • /
    • 2013.02a
    • /
    • pp.351-351
    • /
    • 2013
  • 한국 전체 에너지 사용량 중약 24%의 에너지가 건축물 부분에 소비되고 있다. 건축물의 벽체나 유리창 등을 통해서 에너지 손실이 이루어지는데 유리창은 벽체에 비해 약 10배 이상 낮은 단열 특성을 가지고 있기 때문에 유리창을 통한 열손실량은 더 크다. 이러한 유리창 부분의 열손실 문제를 해결할 수 있는 방안으로 좋은 단열 특성 및 낮은 방사율을 가지고 있는 Low-e coating 방법을 사용하였다. 본 실험에서는 XG glass 기판 위에 IGZO/Ag/IGZO OMO 구조의 다층 박막을 증착하였다. RF magnetron sputtering방법을 이용하여 OMO 구조의 상부와 하부의 Oxide layer로 IGZO 박막을 증착하였다. 사용된 IGZO 타겟은 $In_2O_3$ (99.99%), $Ga_2O_3$ (99.99%), ZnO (99.99%)의 분말을 각각 1:1:1 mol% 조성비로 혼합하여 소결하여 제작하였다. Thermal Evaporator 장비를 이용하여 OMO 구조의 Metal layer로 Ag (99.999%)를 증착하였다. 실험 기판은 크기 $30{\times}30mm$의 0.7T XG glass를 사용하였다. OMO 구조의 산화층 IGZO 박막은 상/하층 동일 조건으로 기판 온도는 실온으로 고정하였으며, 초기 압력 $3.0{\times}10^{-6}$ Torr, 증착 압력 $3.0{\times}10^{-2}$ Torr, RF 파워 50W, Ar 유량 50 sccm로 고정시키고 증착 시간이 변화하면서 박막을 증착하였다. OMO 구조의 Metal layer로 Ag 증착 조건은 초기 진공도가 약 $6.0{\times}10^{-6}$ Torr 이하로 유지하고 기판을 2 Rpm의 속도로 회전시켰다. 이후 0.3 V로 Ag를 10분간 가열하여 충분히 녹인 후 Film Thickness Monitor로 두께를 확인하였다. OMO 다층 박막의 산화물층 변화에 따라 로이다층 박막의 구조적, 광학적 및 전기적 특성을 분석하였다. XRD 분석결과에 의하여 Bragg's 법칙을 만족하는 피크가 나타나지 않는 비정질 구조임을 확인할 수 있으며, AFM 분석결과에 통해서 최소 1.3 nm의 Roughness를 나타내었다. UV-Visible-NIR 분광광도계를 이용하여 다층 박막은 가시광선 영역에서 평균 80%의 광 투과성을 보여 IR 영역에서 평균 30% 투과하고 좋은 차단 특성을 나왔다. Low-e 특성을 갖는 유리창을 통해서 에너지 절약을 이룰 수 있는 것을 확인할 수 있었다.

  • PDF

Basal Area-Stump Diameter Models for Tectona grandis Linn. F. Stands in Omo Forest Reserve, Nigeria

  • Chukwu, Onyekachi;Osho, Johnson S.A.
    • Journal of Forest and Environmental Science
    • /
    • v.34 no.2
    • /
    • pp.119-125
    • /
    • 2018
  • The tropical forests in developing countries are faced with the problem of illegal exploitation of trees. However, dearth of empirical means of expressing the dimensions, structure, quality and quantity of a removed tree has imped conviction of offenders. This study aimed at developing a model that can effectively estimate individual tree basal area (BA) from stump diameter (Ds) for Tectona grandis stands in Omo Forest Reserve, Nigeria, for timber valuation in case of illegal felling. Thirty-six $25m{\times}25m$ temporary sample plots (TSPs) were laid randomly in six age strata; 26, 23, 22, 16, 14, and 12 years specifically. BA, Ds and diameter at breast height were measured in all living T. grandis trees within the 36 TSPs. Least square method was used to convert the counted stumps into harvested stem cross-sectional areas. Six basal area models were fitted and evaluated. The BA-Ds relationship was best described by power model which gave least values of Root mean square error (0.0048), prediction error sum of squares (0.0325) and Akaike information criterion (-15391) with a high adjusted coefficient of determination (0.921). This study revealed that basal area estimation was realistic even when the only information available was stump diameter. The power model was validated using independent data obtained from additional plots and was found to be appropriate for estimating the basal area of Tectona grandis stands in Omo Forest Reserve, Nigeria.

Highly Conductive and Transparent Electrodes for the Application of AM-OLED Display

  • Ryu, Min-Ki;Kopark, Sang-Hee;Hwang, Chi-Sun;Shin, Jae-Heon;Cheong, Woo-Seok;Cho, Doo-Hee;Yang, Shin-Hyuk;Byun, Chun-Won;Lee, Jeong-Ik;Chung, Sung-Mook;Yoon, Sung-Min;Chu, Hye-Yong;Cho, Kyoung-Ik
    • 한국정보디스플레이학회:학술대회논문집
    • /
    • 2008.10a
    • /
    • pp.813-815
    • /
    • 2008
  • We prepared highly transparent and conductive Oxide/Metal/Oxide(OMO) multilayer by sputtering and developed wet etching process of OMO with a clear edge shape for the first time. The transmittance and sheet-resistance of the OMO are about 89% and $3.3\;{\Omega}/sq.$, respectively. We adopted OMO as a gate electrode of transparent TFT (TTFT) array and integrated OLED on top of the TTFT to result in high aperture ratio of bottom emission AM-OLED.

  • PDF

High-functional Transparent Electrode Design and Shielding Effect (금속산화물 기반의 고성능 투명 전극 및 전자파 차단 효과)

  • Seongwon Cho;Wu-shin Cha;Junheon Ha;Junsik Lee;Jiwon Kang;Nguyen Thanh Tai;Joondong Kim
    • Current Photovoltaic Research
    • /
    • v.11 no.1
    • /
    • pp.13-17
    • /
    • 2023
  • Functional transparent electrode was achieved by metal oxide-metal-Metal oxide (OMO) structure. Tailoring of metal oxide and metal layers, optically transparent and electrically excellent OMO films were investigated. Silver (Ag) is adopted for the metal layer and Ag oxide (AgO) is reactively formed by flowing O2 gas during the sputtering process. This spontaneous AgO formation from Ag simultaneously provides the good electrical interface with high transparency. Due to the feature of transparent electrode of OMO, it endows the shielding effect (SE) function of electromagnetic interference. Optically transparent and electrically conductive OMO electrode shows the high transmittance (83.7%) and low sheet resistance (6.5 Ω/☐) with SE of 29.54 dB.

Low Emissivity Property of Amorphous Oxide Multilayer (SIZO/Ag/SIZO) Structure

  • Lee, Sang Yeol
    • Transactions on Electrical and Electronic Materials
    • /
    • v.18 no.1
    • /
    • pp.13-15
    • /
    • 2017
  • Low emissivity glass for high transparency in the visible range and low emissivity in the IR (infrared) range was fabricated and investigated. The multilayers were have been fabricated, and consisted of two outer oxide layers and a middle layer of Ag as a metal layer. Oxide layers were formed by rf sputtering and metal layers were formed using by an evaporator at room temperature. SiInZnO (SIZO) film was used as an oxide layer. The OMO (oxide-metaloxide) structures of SIZO/Ag/SIZO were analyzed by using transmittance, AFM (atomic force microscopye), and XRD (X-ray diffraction). The OMO multilayer structure was designed to investigate the effect of Ag layer thickness on the optical property of the OMO structure.

Structural and Optical Properties of Multilayer Films of IGZO / Ag / IGZO for Low Emissivity Applications (Low-e용 산화물 다층박막 IGZO/Ag/IGZO의 구조적, 광학적 특성 분석)

  • Wang, Hong Rae;Kim, Hong Bae;Lee, Sang Yeol
    • Journal of the Korean Institute of Electrical and Electronic Material Engineers
    • /
    • v.26 no.4
    • /
    • pp.321-324
    • /
    • 2013
  • In this study, The RF magnetron sputter and evaporator was on glass substrates 30 mm ${\times}$ 30 mm OMO multilayer thin film structure is applied to the low-e. Structural and optical properties, a thin film was produced, the variable was placed into a variable deposition time of the oxide layer. According to the XRD measurement results there is no peak that satisfies the Bragg's law ($2dsin{\theta}=n{\lambda}$) which confirmed that it is an amorphous structure. RMS value of the results of the AFM measurement, has a roughness of less than 2 nm. transmittance measurements results, visible light region an average 80%, IR region 40% showed.

다층박막 IGZO/Ag/IGZO의 Ag 두께 변화에 따른 구조적, 광학적 특성 연구

  • Wang, Hong-Rae;Lee, Sang-Ryeol;Kim, Hong-Bae
    • Proceedings of the Korean Vacuum Society Conference
    • /
    • 2013.02a
    • /
    • pp.365-365
    • /
    • 2013
  • 본 실험에서는 RF magnetron sputter장비와 evaporator장비를 이용하여 다층박막 IGZO/Ag/IGZO를 제작하였다. 소결된 타겟은 In:Ga:ZnO 1:1:1mol%로 조성된 타겟을 사용하였으며, Ag는 99.999%의 순도를 가진다.다층박막 OMO구조의 Oxide layer는sputter장비를 이용 IGZO막을 제작하였으며, Metal layer는 evaporator 장비를 이용 Ag막을 제작하였다. 변수로는 Metal layer 두께에 따른 구조적, 광학적 특성 변화를 연구하였다. Oxide layer의 RF sputter 공정 조건으로는 초기압력 $3.0{\times}10^{-6}$ Torr 이하로 하였으며, 증착압력 $2.0{\times}10^{-2}$ Torr, RF power 30 W, Ar 50 sccm으로 고정시켰으며, Metal layer의 evaporator 공정조건으로는 $5.0{\times}10^{-6}$ 이하, 전압은 0.3V, 기판 회전속도는 2RPM 두께는 Thickness moniter로 3. 5. 7. 9. 11. 13. 15 nm를 확인하며 증착하였다. 분석결과로는 AFM측정결과 거칠기는 2 nm이하의 거칠기를 확인했으며, XRD측정결과 Bragg's 법칙($2\;dsin{\Theta}=n{\lambda}$)를 만족하는 피크를 찾을 수 없어 비정질 구조임을 확인할 수 있었다. 투과도 측정결과 가시광 영역에서 최대 80% 이상의 투과율을 보여주었으며, IR영역에서는 30% 이하의 투과율을 보여주었다. 에너지 밴드갬 계산결과 4.5~4.6 eV를 갖는 것을 확인하였으며, Low-e 분야에 사용가능함을 보여주었다.

  • PDF

The Change of Energy Band Gap and Transmittance Depending on Ag Thinkness of IGZO, ZnO, AZO OMO

  • Lee, Seung-Min;Kim, Hong-Bae;Lee, Sang-Ryeol
    • Proceedings of the Korean Vacuum Society Conference
    • /
    • 2014.02a
    • /
    • pp.340.1-340.1
    • /
    • 2014
  • 본 실험에서는 Ag두께 변화에 따른 투과율과 Energy bandgap의 변화를 알아보기 위해 RF Sputter장비와 Evaporator장비를 사용하여 IGZO, ZnO, AZO OMO 구조로 Low-e 코팅된 Glass를 제작하였다. $3cm{\times}3cm$의 Corning1737 유리기판에 RF Sputtering 방식으로 Oxide layer를 증착 하였고 Evaporator장비로는 Metal layer인 Ag막을 증착하였다. Oxide layer 증착 시 RF Sputter장비의 조건은 $3.0{\times}10^{-6}Torr$이하로 하였으며, 증착압력은 $6.0{\times}10^{-3}Torr$, 증착온도는 실온으로 고정하였다. Metal layer 증착 시 Evaporator장비의 조건은 $5.0{\times}10^{-6}Torr$이하, 전압은 0.3 V, Rotate 2 rpm으로 고정하였다. 실험 변수로는 Ag 두께를 5,7,9,11,13 nm로 변화를 주어 실험을 진행하였다. 투과도 측정 장비를 사용하여 각 샘플을 측정한 결과 IGZO의 경우 가시광영역의 평균 투과율이 80% 이상이며 Ag두께가 5nm일 때부터 자외선 영역의 빛을 차단하여 low-e 특성을 나타내었다. 이는 산화물인 IGZO가 결정질인 AZO, ZnO 보다 낮은 표면거칠기를 가지기 때문이다. Ag 두께에 따른 각 물질의 Optical energy bandgap 분석결과 Ag 두께가 증가할수록 IGZO는 4.65~4.5 eV, AZO는 4.6~4.4 eV, ZnO는 4.55~4.45 eV로 Energy bandgap은 감소하였다. AFM장비를 이용하여 각 샘플의 표면 Roughness 측정 결과 Ag 두께가 증가할수록 표면거칠기도 증가하는 경향을 나타내었다.

  • PDF