• International Journal of Concrete Structures and Materials
• /
• v.11 no.2
• /
• pp.365-375
• /
• 2017

An experimental evaluation of crack propagation and post-cracking behavior in steel fiber reinforced concrete (SFRC) beams, using full-field displacements obtained from the digital image correlation technique is presented. Surface displacements and strains during the fracture test of notched SFRC beams with volume fractions ($V_f$) of steel fibers equal to 0.5 and 0.75% are analyzed. An analysis procedure for determining the crack opening width over the depth of the beam during crack propagation in the flexure test is presented. The crack opening width is established as a function of the crack tip opening displacement and the residual flexural strength of SFRC beams. The softening in the post-peak load response is associated with the rapid surface crack propagation for small increases in crack tip opening displacement. The load recovery in the flexural response of SFRC is associated with a hinge-type behavior in the beam. For the stress gradient produced by flexure, the hinge is established before load recovery is initiated. The resistance provided by the fibers to the opening of the hinge produces the load recovery in the flexural response.

• Computers and Concrete
• /
• v.25 no.6
• /
• pp.517-523
• /
• 2020

An experimental system on three point bending notched beams was established to study the fracture process of concrete. In this system, the acoustic emission (AE) was used to build the cumulative generation order (AGO) and dynamically track the process of microcrack evolution in concrete. A grey-cusp catastrophe model was built based on AE parameters. The results show that the concrete beams have significant catastrophe characteristic. The developed grey-cusp catastrophe model, based on AGO, can well describe the catastrophe characteristic of concrete fracture process. This study also provides a theoretical and technical support for the application of AE in concrete fracture prediction.

• Journal of Welding and Joining
• /
• v.5 no.2
• /
• pp.53-59
• /
• 1987

The effect of applied stress, current density and heat-treatment after welding on the time to fracture, fracture behavior was investigated by the method of constant load tensile testing under catholic charging with hydrogen in E.B. welded 250,300 Grade 18% Ni Maraging steel sheet. The main results obtained are as follows: 1. All specimen showed the characteristic delayed failure and the time to fracture showed decreasing tendency with the increase in current density and applied stress. 2. Hydrogen embitterment susceptibility of notched specimen after solution-treatment and aging after welding was more increased than that of aged smooth specimen and as welded specimen. 3. Fracture surface showed a typical intergranular fracture on the border, a dimple pattern in the center of specimen and some quasi-cleavage fracture between the intergranular and the dimple.

• Journal of Advanced Marine Engineering and Technology
• /
• v.25 no.5
• /
• pp.1140-1147
• /
• 2001

This paper describes the effect of various molding pressure for Mode I. Mode II interlaminar fracture toughness of carbon fiber reinforced plastic composites by using double cantilever beam(DCB), end notched flexure(ENF) and end loaded split(ELS) Specimen. The value of $G_{IC}$, $G_{IIC}$ as a function of various molding pressure is almost same at 307, 431, 585 kPa, however it shows highest value under 307kPa molding pressure, The SEM photographs show good fiber distribution and interfacial bonding of composites when the molding pressure is the 307kPa.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2007.11a
• /
• pp.1259-1265
• /
• 2007

This paper presents nonlinear vibration characteristics of a vertical passive zero stiffness isolator. The passive isolator can achieve zero stiffness through buckling of notched flexure caused by a compressive force. First, a simulation model of the isolator was built based on elastic beam theory. As increasing the compression force, time and frequency responses of the isolator were simulated. In addition, further nonlinear vibration characteristics were investigated through a bifurcation diagram and a Poincare's map, which shows that even chaostic vibration could happen. The simulations show that as the compressive force increases, the stiffness goes close to zero and the nonlinear characteristic becomes stronger to have a great effect on the isolation performance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04a
• /
• pp.199-204
• /
• 1998

To analysis the failure character of Low-Heat concrete which is used to prevent the thermal crack caused by hydration heat, static loading test was performed by this test method, "Determination of the Fracture Energy of Motar and Concrete by Means of Three-Point Band Tests on Notched Beam" (suggested by RILEM 50-FMC Committe). This study compared and analysised the fracture energy of Mode I (opening mode), the most general pattern in the view of water-cemente ratio(W/C), compressive strength and age of Ordinary Portland Concrete and Low-Heat Concrete under the same mixture. The test results show that the case of Ordinary Portland Concrete and Low-Heat Concrete, low Water-Cemente ratio(W/C) cause the increase of fracture energy, and high failure-strength decrease failure-deflection, and the fracture energy of Low-Heat Concrete is similar to Ordinary Portland Concrete as the age increase. increase.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.163-164
• /
• 2010

Ultra high performance concrete (UHPC) is a relatively new cementitous material, which has been developed to give significantly higher material performance than conventional concrete or engineered cementitious composites. In this study, reverse analysis of notched UHPC beam was conducted according to the experimental result of load-displacement. Conclusively, tensile strength vs. CMOD (Crack Mouth Opening Displacement) was calculated as an approximated method for the direct tensile strength estimation.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2001.10a
• /
• pp.59-66
• /
• 2001

The post-peak analysis of concrete structures is carried out using a nine-node Reissner-Mindlin(RM) shell element which is formulated by using degenerated solid concepts. In order to avoid element deficiencies inherited in the standard RM shell element, assumed strains are adopted in the present shell element. A microscopic material model is adopted to represent the inelastic characteristic of concrete material. In particular, a concrete softening model is introduced to this material model. The arc-length control method is used to trace the post-peak behaviour of concrete structures. From the numerical test of the single-edge-notched beam, the present shell element shows a reasonable agreement with experimental data.

• Smart Structures and Systems
• /
• v.10 no.6
• /
• pp.547-555
• /
• 2012

Measuring crack length in concrete fracture test is not a trivial problem due to high speed crack propagation. In this study, mechanoluminascent (ML) material, which emits visible light under stress condition, was employed to visualize crack propagation during concrete fracture test. Three-point bending test was conducted with a notched concrete beam specimen. The cracking images due to ML phenomenon were recorded by using a high speed camera as a function of time and external loadings. The experimental results successfully demonstrated the capability of ML material as a promising visualization tool for concrete crack propagation. In addition, an interesting cracking behavior of concrete bending fracture was observed in which the crack propagated fast while the load decreased slowly at early fracture stage.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.177-179
• /
• 2002

A1$_2$ $O_3$기판재료의 $K_{IC}$ 증가를 위한 재료설계를 시도하였다. 먼저 A1$_2$ $O_3$기판을 구성하는 A1$_2$ $O_3$다층구조물에 적절한 다공성 중간층을 삽입하는 샌드위치 구조물을 제조하였다. 제조된 A1$_2$ $O_3$구조물의 미세구조를 관찰하였고, Vickers 경도와 three-point bending test를 통해서 단일조성 구조물과 샌드위치 구조물의 경도와 인성 측정치를 비교하였다. 다공층을 삽입한 A1$_2$ $O_3$샌드위치 구조물의 Single-Edge Notched Beam이 단일 조성의 구조물에 비해 파괴강도와 인성이 향상되는 결과를 얻었다.